SE435494B - Forfarande for framstellning av en halvreflekterande tennoxidfilm - Google Patents
Forfarande for framstellning av en halvreflekterande tennoxidfilmInfo
- Publication number
- SE435494B SE435494B SE7801761A SE7801761A SE435494B SE 435494 B SE435494 B SE 435494B SE 7801761 A SE7801761 A SE 7801761A SE 7801761 A SE7801761 A SE 7801761A SE 435494 B SE435494 B SE 435494B
- Authority
- SE
- Sweden
- Prior art keywords
- compound
- fluorine compound
- powder
- temperature
- glass
- Prior art date
Description
15 20 25 30 35 7801761-3 Dessa förfaranden har hittills inte varit helt till- fredsställande, i det att samtliga har vissa olägenheter, an- tingen på grund av på att det erhållna tunna tennoxidfilmens kvalitet (häftning, jämn tjocklek, transparens, optiska egenskaper eller elektriska ledningsförmåga) är_otillräcklig eller på grund av att de är svåra eller komplicerade att genomföra: preparering av den yta, som.skall beläggas, kemiska hjälpreagenser, bered- ning av lösningar, som skall finfördelas, avlägsnande av över- skottslösning samt lösningsmedelsångor eller sönderfallsprodukter.
Förfarandet enligt uppfinningen undanröjer dessa olägenheter, och det består i att man på den yta, som skall be- läggas, och som hålles vid en temperatur av UÜO till 650°C, an- bringar en fast organisk tennförening, som vid denna temperatur kan sönderfalla till tennoxid i form av pulver med högst 20 um korn- storlek, suspenderad ien.vattenfri bärgasström, som innehåller en viss mängd gasformig fluorförening, lämpligen en fluorid, såsom bortrifluorid, brompentafluorid, klortrifluorid, kiseltetrafluorid, volframhexafluorid eller molybdenflourid eller i synnerhet vattenfri vätefluorid.
' Den fluorhaltiga gasen tillsättes enligt uppfinningen företrädesvis samtidigt med appliceringen genom pâstick i den led- ning, genom vilken de suspenderade partiklarna av organisk tenn- förening leds uppströms sprutmnnstycket.
Dä man arbetar enligt uppfinningen, kan man som organisk tennförening använda tenndibutyloxid, vilken är en särskilt ekonomisk förening, som införes med en ström av torr luft under tryck. ,¿ Beroende på dimensionerna hos den glasskiva eller det glasband, som skall behandlas, kan man använda ett eller flera fasta eller rörliga sprutmunstycken, framför vilka man leder det underlag, som skall beläggas.
Förfarandet enligt uppfinningen skiljer sig från äldre förfaranden genom attdet är enkelt och billigt. Man behöver inte bereda någon sprutlösning. Man behöver inte använda något lösnings- medeL och det behövs inga andra kemiska hjälpmedel än den gasformiga fluorföreningen, företrädesvis fluorväte, som är ekonomiskt och mycket lätt att framställa genom förångning av flytande vattenfritt fluorväte, vars kokpunkt är under 20°C vid atmosfärtryck. (n 10 15 20 25 30 7801761-3 Erfarenheten visar också, att den enligt uppfinningen erhållna tennoxidfilmen har god häftning och tillfredsställande >korrosionsbeständighet. Den har vidare önskade optiska egen- skaper i fråga om transparens inom det synliga området av spektret och reflexionnförmåga inom det infraröda området, i synnerhet för våglängder över 2 um.
Den erhållna tennoxidfilmen har god elektrisk lednings- förmåga, så att glasskivor med sådan beläggning kan användas som värmefönster.
En annan fördel med förfarandet enligt uppfinningen är, att det kan genomföras med glaset vid en temperatur av omkring 50000, så att det kan tillämpas på rutor, som kommer från en värme- härdningsstation, eller på rutor, som undergått kemisk härdníng.
Nedan beskrivs ett utföringsexempel av uppfinningen.
Pulverformig tenndibutyloxid tas in i en behållare på en porös botten. Tryckluft används som bärgas och införes under den porösa bottnen, och när luften trängt genom denna, med- bringar den en viss mängd tennföreningskorn i en matarledning för sprutmunstycket eller -styckena. Matarluften används vid omgiv- ningstemperatur, och den står under ett tryck av 0,5 bar.
Uppströms om varje munstycke finns ett intag för gasfor- migt vattenfritt fluorväte från flaskor med flytande fluorväte, som hålls vid en temperatur av storleksordningen HOOC. Sprutmun- styckena är anordnade på 25 cm avstånd från varandra och riktade horisontellt. Framför munstyckena leder man vertikalt hängande flytglasskivor med formatet 500 X 500 mm och 6 mm tfiocklek, vilka förut har värmts genom att ledas vertikalt hängande genom en ugn, som hålls vid sso°c.
Då glasskivorna passerar framför sprutmunstyckena är deras temperatur omkring 610 till 620OC. Deras hastighet vid passagen regleras efter matningen, så att 50 g tenndibutyloxid för- brukas per kvadratmeter behandlat glas (endast en del av den mängden fastnar på glaset i form av tennoxid). 35 g fluorväte förbrukas per kvadratmeter behandlat glas.
Provstycken med så framställda beläggningar av tenn- oxid undersöks beträffande reflexionsförmåga och transmissíonskoeffi- cient som funktion av våglängden. Resultaten visas som kurvor på de bifogade figurerna. Kurvan T återger provkroppens transmission ut- tryckt i procentuell ljusgenomsläppning för varje våglängd. Kurvan R är provets reflexionskurva. 10 15 7801761-3 Därav framgår, att på grund av den höga reflexionen glasets transmission är mycket svag inom det infraröda området för våglängder över omkring 1,5 um.
Man mätte också tennoxidfilmens elektriska motstånd i flera punkter på provkroppens yta (punkter på 10 cm avstånd i två vinkelräta riktningar). ' I nedanstående tabell anges de erhållna värdena i' -ohm per kvadrat. ëlyktrisk resistans i ohm, mätt i hörnen av 10 cm kvadrater 16 12 12 13 15 13 11 11 11 1H 14 11 10 12 15 12 9 9 10 13 15 11 11 11 13 Värdena motsvarar en elektrisk ledningsförmåga, som gör glaset fullt användbart som värmeglasrutor.
Claims (6)
1. Förfarande för framställning av en halvreflekterande tennoxidfilm genom pyrolys på ytan av ett underlag, såsom en skiva av glas eller glaskeram, vid vilket man mot den för be- läggning avsedda ytan, som hålls vid en temperatur av 400 till 650°C, sprutar en organisk tennförening, som vid den temperatu- ren kan sönderdelas till oxid, i form av ett pulver, k ä n n e t e c k n a t av att pulvret har en kornstorlek avi högst 20 pm och suspenderas i en ström av vattenfri bärgas, som innehåller en viss mängd gasformig fluorförening.
2. Förfarande enligt patentkravet 1, klä n n e - t e c k n a t av att den gasformiga fluorföreningen tillsättes vid själva sprutningen genom ett påstick i matarledningen för pulvret av organisk tennförening uppströms om sprutmunstycket.
3. Förfarande enligt något av de föregående patentkraven, k ä n n e t e c k n a t av att den organiska tennföreningen är dibutyltennoxid och att bärgasen är torr luft.
4. Förfarande enligt något av de föregående patentkraven, k ä n n e t e c k n a t av att fluorföreningen utgöres av bor- trifluorid, brompentafluorid, klortrifluorid, kiseltetrafluorid, volframhexafluorid eller molybdenfluorid.
5. Förfarande enligt något av patentkraven 1 - 3, k ä n n e t e c k n a t av att fluorföreningen är vattenfri vätefluorid.
6. Förfarande enligt något av patentkraven 3 - 5 där under- laget är en värmehärdad eller kemiskt härdad glasskiva, k ä n n e t e c k n a t av att arbetstemperaturen är högst 520°C.