Abstract
Description
Изобретение относится к области технологии силикатов и касается составов керамических масс для производства керамического кирпича.The invention relates to the field of technology of silicates and relates to compositions of ceramic masses for the production of ceramic bricks.
Известна керамическая масса следующего состава, мас.%: глина тугоплавкая 20,0-30,0; кварциты 70,0-80,0 [1].Known ceramic mass of the following composition, wt.%: Refractory clay 20.0-30.0; quartzites 70.0-80.0 [1].
Задачей изобретения является повышение прочности кирпича, полученного из керамической массы.The objective of the invention is to increase the strength of bricks obtained from ceramic mass.
Технический результат достигается тем, что керамическая масса, содержащая глину тугоплавкую, кварциты, дополнительно содержит пегматит при следующем соотношении компонентов, мас.%: глина тугоплавкая 20,0-40,0; кварциты 35,0-45,0; пегматит 25,0-35,0.The technical result is achieved in that the ceramic mass containing refractory clay, quartzite, additionally contains pegmatite in the following ratio of components, wt.%: Refractory clay 20,0-40,0; quartzites 35.0-45.0; pegmatitis 25.0-35.0.
В составе керамической массы могут быть использованы: глины тугоплавкие, содержащие, мас.%: SiO2 42,0-80,0; Аl2О3 13,0-35,0; ТiO2 0,3-1,6; Fe2О3 1,2-11,0; СаО от следов до 1,7; MgO 0,2-1,6; Na2O 0,1-3,6; К2О 0,1-4,4; ппп 2,6-15,7; кварциты, химический состав которых представлен, главным образом, кварцем; пегматиты, включающие, мас.%: SiO2 72,88; Fе2О3 0,17; Аl2O3 15,1; СаО 0,87; MgO 0,18; К2О 7,1; Na2О 3,34; п.п.п.0,36.The composition of the ceramic mass can be used: refractory clay, containing, wt.%: SiO 2 42,0-80,0; Al 2 O 3 13.0-35.0; TiO 2 0.3-1.6; Fe 2 O 3 1.2-11.0; CaO from traces to 1.7; MgO 0.2-1.6; Na 2 O 0.1-3.6; K 2 O 0.1-4.4; ppb 2.6-15.7; quartzites, the chemical composition of which is mainly represented by quartz; pegmatites, including, wt.%: SiO 2 72.88; Fe 2 O 3 0.17; Al 2 O 3 15.1; CaO 0.87; MgO 0.18; K 2 O 7.1; Na 2 O 3.34; p.p.p. 0.36.
В таблице приведены составы керамической массы.The table shows the composition of the ceramic mass.
Пегматит и кварцит размалывают до получения порошков с удельной поверхностью 2000-4000 см2/г, добавляют измельченную глину и смешивают. Массу увлажняют до 8-13 % и прессуют из нее кирпич, который обжигают при температуре 1050-1150°С.Pegmatite and quartzite are ground to obtain powders with a specific surface of 2000-4000 cm 2 / g, crushed clay is added and mixed. The mass is moistened to 8-13% and a brick is pressed from it, which is burned at a temperature of 1050-1150 ° C.
Источники информацииInformation sources
1. SU 1542932, С04В 33/00, 1990.1. SU 1542932, C04B 33/00, 1990.
Claims (1)
Priority Applications (1)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
RU2010117905/03A RU2430057C1 (en) | 2010-05-04 | 2010-05-04 | Ceramic mass |
Applications Claiming Priority (1)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
RU2010117905/03A RU2430057C1 (en) | 2010-05-04 | 2010-05-04 | Ceramic mass |
Publications (1)
Publication Number | Publication Date |
---|---|
RU2430057C1 true RU2430057C1 (en) | 2011-09-27 |
Family
ID=44804118
Family Applications (1)
Application Number | Title | Priority Date | Filing Date |
---|---|---|---|
RU2010117905/03A RU2430057C1 (en) | 2010-05-04 | 2010-05-04 | Ceramic mass |
Country Status (1)
Country | Link |
---|---|
RU (1) | RU2430057C1 (en) |
Cited By (1)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
RU2473507C1 (en) * | 2011-10-24 | 2013-01-27 | Юлия Алексеевна Щепочкина | Ceramic mass for brick production |
-
2010
- 2010-05-04 RU RU2010117905/03A patent/RU2430057C1/en active
Cited By (1)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
RU2473507C1 (en) * | 2011-10-24 | 2013-01-27 | Юлия Алексеевна Щепочкина | Ceramic mass for brick production |
Similar Documents
Publication | Publication Date | Title |
---|---|---|
RU2403224C1 (en) | Ceramic mixture for making bricks | |
RU2332385C1 (en) | Ceramic body | |
RU2388719C1 (en) | Ceramic mixture | |
RU2400448C1 (en) | Ceramic mass for brick production | |
RU2366634C1 (en) | Ceramic mixture for production of facing tiles | |
RU2400449C1 (en) | Ceramic mass for floor tile fabrication | |
RU2382012C1 (en) | Ceramic mass for production of brick | |
RU2387616C1 (en) | Ceramic mass for facing tile fabrication | |
RU2430059C1 (en) | Ceramic mass | |
RU2364578C1 (en) | Ceramic mass | |
RU2430047C1 (en) | Decorative facing material | |
RU2394787C1 (en) | Ceramic mixture | |
RU2403226C1 (en) | Ceramic mixture for making floor tiles | |
RU2430057C1 (en) | Ceramic mass | |
RU2338721C1 (en) | Ceramic mixture for making floor tiles | |
RU2387611C1 (en) | Ceramic mass | |
RU2369578C1 (en) | Raw mixture for manufacturing finish ash ceramic tile | |
RU2312088C1 (en) | Ceramic mix | |
RU2443653C1 (en) | Ceramic mass | |
RU2430901C1 (en) | Ceramic mass for bricks fabrication | |
RU2358947C1 (en) | Raw mix for production of facing tiles | |
RU2387620C1 (en) | Raw mix for facing ash-ceramic tile fabrication | |
RU2379251C1 (en) | Ceramic body for brick manufacture | |
RU2413694C1 (en) | Ceramic mixture for making facing tiles | |
RU2534316C1 (en) | Ceramic mass for production of facing tiles |