Abstract
Description
Изобретение относится к области технологии силикатов и касается составов керамических масс, которые могут быть использованы для изготовления фасадной плитки.The invention relates to the field of technology of silicates and relates to compositions of ceramic masses that can be used for the manufacture of facade tiles.
Известна керамическая масса, содержащая, мас.%: глина 40,0-48,0; стеклобой 8,0-12,0; кварцевый песок 5,0-10,0; гранитные отсевы 28,0-35,0 [1].Known ceramic mass containing, wt.%: Clay 40,0-48,0; cullet 8.0-12.0; silica sand 5.0-10.0; granite screenings 28.0-35.0 [1].
Задача изобретения состоит в повышении водостойкости плитки, полученной из керамической массы.The objective of the invention is to increase the water resistance of tiles obtained from ceramic mass.
Технический результат достигается тем, что в керамической массе для изготовления фасадной плитки, включающей глину, стеклобой, кварцевый песок, гранитные отсевы, компоненты находятся при следующем соотношении, мас.%: глина 20,0-25,0; стеклобой 25,0-30,0; кварцевый песок 25,0-30,0; гранитные отсевы 20,0-25,0.The technical result is achieved in that in the ceramic mass for the manufacture of facade tiles, including clay, cullet, quartz sand, granite screenings, the components are in the following ratio, wt.%: Clay 20.0-25.0; cullet 25.0-30.0; silica sand 25.0-30.0; granite screenings 20.0-25.0.
В таблице приведены составы керамической массы.The table shows the composition of the ceramic mass.
Для приготовления керамической массы могут быть использованы глины следующего химического состава, мас.%: SiO2 64,7-73,0; Al2O3 9,87-13,41; Fe2O3 1,92-2,72; CaO 0,98-1,6; MgO 2,13-2,99; SO3 0,51-0,81; п.п.п. 11,45-14,32. Возможно использование боя любых силикатных стекол (тарного, листового, медицинского и др.).To prepare the ceramic mass, clays of the following chemical composition can be used, wt.%: SiO 2 64.7-73.0; Al 2 O 3 9.87-13.41; Fe 2 O 3 1.92-2.72; CaO 0.98-1.6; MgO 2.13-2.99; SO 3 0.51-0.81; p.p.p. 11.45-14.32. It is possible to use the battle of any silicate glass (container, sheet, medical, etc.).
Компоненты дозируют в требуемых количествах. В шаровые мельницы загружают глину, стеклобой (в данном примере - бой медицинского стекла), кварцевый песок, гранитные отсевы и проводят измельчение каждого из компонентов по отдельности до остатка 3-4% на сите 008. Затем компоненты смешивают, полученную массу увлажняют до 20-25% (в данном примере до 21%) и формуют из нее пластическим способом фасадную плитку. Плитку сушат до влажности 1-8% (в данном примере 5%), наносят на ее поверхность слой глазури и обжигают в интервале температур 900-1050°С (в данном примере 985°С).The components are dosed in the required amounts. The ball mills are loaded with clay, cullet (in this example, the battle of medical glass), quartz sand, granite screenings and each component is crushed separately to a residue of 3-4% on a sieve 008. Then the components are mixed, the resulting mass is moistened to 20- 25% (in this example up to 21%) and form the facade tile from it in a plastic way. The tile is dried to a moisture content of 1-8% (in this example 5%), a layer of glaze is applied to its surface and fired in the temperature range 900-1050 ° C (in this example 985 ° C).
Источники информацииInformation sources
1. SU 1544749, С04В 33/00, 1990.1. SU 1544749, C04B 33/00, 1990.
Claims (1)
Priority Applications (1)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
RU2010106802/03A RU2420489C1 (en) | 2010-02-24 | 2010-02-24 | Ceramic mixture used to make front tiles |
Applications Claiming Priority (1)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
RU2010106802/03A RU2420489C1 (en) | 2010-02-24 | 2010-02-24 | Ceramic mixture used to make front tiles |
Publications (1)
Publication Number | Publication Date |
---|---|
RU2420489C1 true RU2420489C1 (en) | 2011-06-10 |
Family
ID=44736655
Family Applications (1)
Application Number | Title | Priority Date | Filing Date |
---|---|---|---|
RU2010106802/03A RU2420489C1 (en) | 2010-02-24 | 2010-02-24 | Ceramic mixture used to make front tiles |
Country Status (1)
Country | Link |
---|---|
RU (1) | RU2420489C1 (en) |
-
2010
- 2010-02-24 RU RU2010106802/03A patent/RU2420489C1/en active
Similar Documents
Publication | Publication Date | Title |
---|---|---|
RU2403224C1 (en) | Ceramic mixture for making bricks | |
RU2332385C1 (en) | Ceramic body | |
RU2331608C2 (en) | Ceramic mixture for facing tile manufacturing | |
RU2332384C1 (en) | Ceramic mass | |
RU2388719C1 (en) | Ceramic mixture | |
RU2376261C1 (en) | Ceramic mass for faced tiles manufacture | |
RU2364578C1 (en) | Ceramic mass | |
RU2404940C1 (en) | Ceramic mass for brick production | |
RU2338721C1 (en) | Ceramic mixture for making floor tiles | |
RU2374205C1 (en) | Ceramic mixture for making bricks, roofing tiles | |
RU2402505C1 (en) | Ceramic mixture for making facing tiles | |
RU2330827C1 (en) | Ceramic mixture for making face tiles | |
RU2394787C1 (en) | Ceramic mixture | |
RU2413695C1 (en) | Ceramic mixture for making facing tiles | |
RU2420489C1 (en) | Ceramic mixture used to make front tiles | |
RU2403225C1 (en) | Ceramic mixture for making facing tiles | |
RU2420485C1 (en) | Ceramic mixture | |
RU2425006C1 (en) | Ceramic mixture for making facing tiles | |
RU2425005C1 (en) | Ceramic mixture for making facing tiles | |
RU2422397C1 (en) | Ceramic mixture for making facing tiles | |
RU2424208C1 (en) | Ceramic mixture | |
RU2417191C1 (en) | Crude mixture for making facing tiles | |
RU2405754C1 (en) | Ceramic mixture for making facing tiles | |
RU2371419C1 (en) | Ceramic mixture for making facing tiles | |
RU2329991C1 (en) | Ceramic mixture for manufacturing of facade plates |