RU2018115132A - Производство составов фосфата кальция - Google Patents
Производство составов фосфата кальция Download PDFInfo
- Publication number
- RU2018115132A RU2018115132A RU2018115132A RU2018115132A RU2018115132A RU 2018115132 A RU2018115132 A RU 2018115132A RU 2018115132 A RU2018115132 A RU 2018115132A RU 2018115132 A RU2018115132 A RU 2018115132A RU 2018115132 A RU2018115132 A RU 2018115132A
- Authority
- RU
- Russia
- Prior art keywords
- solution
- calcium
- phosphate
- calcium phosphate
- corresponds
- Prior art date
Links
Classifications
-
- C—CHEMISTRY; METALLURGY
- C01—INORGANIC CHEMISTRY
- C01B—NON-METALLIC ELEMENTS; COMPOUNDS THEREOF; METALLOIDS OR COMPOUNDS THEREOF NOT COVERED BY SUBCLASS C01C
- C01B25/00—Phosphorus; Compounds thereof
- C01B25/16—Oxyacids of phosphorus; Salts thereof
- C01B25/26—Phosphates
- C01B25/32—Phosphates of magnesium, calcium, strontium, or barium
-
- C—CHEMISTRY; METALLURGY
- C01—INORGANIC CHEMISTRY
- C01B—NON-METALLIC ELEMENTS; COMPOUNDS THEREOF; METALLOIDS OR COMPOUNDS THEREOF NOT COVERED BY SUBCLASS C01C
- C01B25/00—Phosphorus; Compounds thereof
- C01B25/16—Oxyacids of phosphorus; Salts thereof
- C01B25/26—Phosphates
- C01B25/32—Phosphates of magnesium, calcium, strontium, or barium
- C01B25/322—Preparation by neutralisation of orthophosphoric acid
-
- C—CHEMISTRY; METALLURGY
- C01—INORGANIC CHEMISTRY
- C01B—NON-METALLIC ELEMENTS; COMPOUNDS THEREOF; METALLOIDS OR COMPOUNDS THEREOF NOT COVERED BY SUBCLASS C01C
- C01B25/00—Phosphorus; Compounds thereof
- C01B25/16—Oxyacids of phosphorus; Salts thereof
- C01B25/26—Phosphates
- C01B25/32—Phosphates of magnesium, calcium, strontium, or barium
- C01B25/327—After-treatment
-
- C—CHEMISTRY; METALLURGY
- C01—INORGANIC CHEMISTRY
- C01F—COMPOUNDS OF THE METALS BERYLLIUM, MAGNESIUM, ALUMINIUM, CALCIUM, STRONTIUM, BARIUM, RADIUM, THORIUM, OR OF THE RARE-EARTH METALS
- C01F11/00—Compounds of calcium, strontium, or barium
- C01F11/02—Oxides or hydroxides
- C01F11/04—Oxides or hydroxides by thermal decomposition
- C01F11/06—Oxides or hydroxides by thermal decomposition of carbonates
-
- C—CHEMISTRY; METALLURGY
- C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
- C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
- C04B2/00—Lime, magnesia or dolomite
- C04B2/10—Preheating, burning calcining or cooling
-
- C—CHEMISTRY; METALLURGY
- C01—INORGANIC CHEMISTRY
- C01P—INDEXING SCHEME RELATING TO STRUCTURAL AND PHYSICAL ASPECTS OF SOLID INORGANIC COMPOUNDS
- C01P2002/00—Crystal-structural characteristics
- C01P2002/04—Compounds with a limited amount of crystallinty, e.g. as indicated by a crystallinity index
-
- C—CHEMISTRY; METALLURGY
- C01—INORGANIC CHEMISTRY
- C01P—INDEXING SCHEME RELATING TO STRUCTURAL AND PHYSICAL ASPECTS OF SOLID INORGANIC COMPOUNDS
- C01P2002/00—Crystal-structural characteristics
- C01P2002/70—Crystal-structural characteristics defined by measured X-ray, neutron or electron diffraction data
- C01P2002/72—Crystal-structural characteristics defined by measured X-ray, neutron or electron diffraction data by d-values or two theta-values, e.g. as X-ray diagram
-
- C—CHEMISTRY; METALLURGY
- C01—INORGANIC CHEMISTRY
- C01P—INDEXING SCHEME RELATING TO STRUCTURAL AND PHYSICAL ASPECTS OF SOLID INORGANIC COMPOUNDS
- C01P2004/00—Particle morphology
- C01P2004/01—Particle morphology depicted by an image
- C01P2004/03—Particle morphology depicted by an image obtained by SEM
-
- C—CHEMISTRY; METALLURGY
- C01—INORGANIC CHEMISTRY
- C01P—INDEXING SCHEME RELATING TO STRUCTURAL AND PHYSICAL ASPECTS OF SOLID INORGANIC COMPOUNDS
- C01P2004/00—Particle morphology
- C01P2004/54—Particles characterised by their aspect ratio, i.e. the ratio of sizes in the longest to the shortest dimension
-
- C—CHEMISTRY; METALLURGY
- C01—INORGANIC CHEMISTRY
- C01P—INDEXING SCHEME RELATING TO STRUCTURAL AND PHYSICAL ASPECTS OF SOLID INORGANIC COMPOUNDS
- C01P2004/00—Particle morphology
- C01P2004/60—Particles characterised by their size
-
- C—CHEMISTRY; METALLURGY
- C01—INORGANIC CHEMISTRY
- C01P—INDEXING SCHEME RELATING TO STRUCTURAL AND PHYSICAL ASPECTS OF SOLID INORGANIC COMPOUNDS
- C01P2004/00—Particle morphology
- C01P2004/60—Particles characterised by their size
- C01P2004/62—Submicrometer sized, i.e. from 0.1-1 micrometer
-
- C—CHEMISTRY; METALLURGY
- C01—INORGANIC CHEMISTRY
- C01P—INDEXING SCHEME RELATING TO STRUCTURAL AND PHYSICAL ASPECTS OF SOLID INORGANIC COMPOUNDS
- C01P2004/00—Particle morphology
- C01P2004/60—Particles characterised by their size
- C01P2004/64—Nanometer sized, i.e. from 1-100 nanometer
-
- C—CHEMISTRY; METALLURGY
- C01—INORGANIC CHEMISTRY
- C01P—INDEXING SCHEME RELATING TO STRUCTURAL AND PHYSICAL ASPECTS OF SOLID INORGANIC COMPOUNDS
- C01P2006/00—Physical properties of inorganic compounds
- C01P2006/12—Surface area
-
- C—CHEMISTRY; METALLURGY
- C01—INORGANIC CHEMISTRY
- C01P—INDEXING SCHEME RELATING TO STRUCTURAL AND PHYSICAL ASPECTS OF SOLID INORGANIC COMPOUNDS
- C01P2006/00—Physical properties of inorganic compounds
- C01P2006/14—Pore volume
-
- C—CHEMISTRY; METALLURGY
- C01—INORGANIC CHEMISTRY
- C01P—INDEXING SCHEME RELATING TO STRUCTURAL AND PHYSICAL ASPECTS OF SOLID INORGANIC COMPOUNDS
- C01P2006/00—Physical properties of inorganic compounds
- C01P2006/80—Compositional purity
Landscapes
- Chemical & Material Sciences (AREA)
- Organic Chemistry (AREA)
- Inorganic Chemistry (AREA)
- Life Sciences & Earth Sciences (AREA)
- Geology (AREA)
- Physics & Mathematics (AREA)
- Thermal Sciences (AREA)
- Ceramic Engineering (AREA)
- Engineering & Computer Science (AREA)
- Environmental & Geological Engineering (AREA)
- General Life Sciences & Earth Sciences (AREA)
- Materials Engineering (AREA)
- Structural Engineering (AREA)
- Materials For Medical Uses (AREA)
- Compounds Of Alkaline-Earth Elements, Aluminum Or Rare-Earth Metals (AREA)
- Solid-Sorbent Or Filter-Aiding Compositions (AREA)
- Cosmetics (AREA)
Claims (34)
1. Способ, содержащий:
получение первого раствора гидроксида кальция, содержащего первую концентрацию ионов кальция, и второго раствора гидроксида кальция, содержащего вторую концентрацию ионов кальция;
добавление раствора фосфорной кислоты к первому раствору гидроксида кальция для получения объединенного раствора, содержащего водную суспензию частиц дигидрофосфата кальция; и
добавление второго раствора гидроксида кальция к этому объединенному раствору для получения раствора продукта, содержащего водную суспензию частиц материала фосфата кальция.
2. Способ по п. 1, в котором первая и вторая концентрации ионов кальция различаются.
3. Способ по п. 1, в котором получение первого раствора гидроксида кальция содержит объединение первого множества частиц, содержащих оксид кальция, с водой, причем эти частицы имеют удельную площадь поверхности по меньшей мере 10,0 м2/г.
4. Способ по п. 3, в котором получение второго раствора гидроксида кальция содержит объединение второго множества этих частиц с водой.
5. Способ по п. 3, в котором частицы имеют удельную пористость по меньшей мере 15,0 см3/г.
6. Способ по п. 1, содержащий добавление раствора фосфорной кислоты к первому раствору гидроксида кальция до тех пор, пока значение pH объединенного раствора не станет находиться в диапазоне от 1 до 2.
7. Способ по п. 6, содержащий добавление раствора фосфорной кислоты к первому раствору гидроксида кальция до тех пор, пока значение pH объединенного раствора не станет приблизительно равным 1,66.
8. Способ по п. 1, содержащий добавление раствора фосфорной кислоты к первому раствору гидроксида кальция тремя частями, причем после добавления первой из этих трех частей значение pH первого раствора гидроксида составляет от 8,5 до 9,5.
9. Способ по п. 8, в котором объединение первого раствора гидроксида кальция и первой части раствора фосфорной кислоты формирует первый буферный раствор ионов фосфата и ионов бифосфата.
10. Способ по п. 9, в котором после добавления второй из этих трех частей значение pH первого раствора гидроксида кальция составляет от 3,5 до 4,5.
11. Способ по п. 10, в котором объединение первого раствора гидроксида кальция и первой и второй частей раствора фосфорной кислоты формирует второй буферный раствор ионов бифосфата и ионов дигидрофосфата.
12. Способ по п. 1, в котором значение pH раствора продукта составляет от 6,5 до 7,5.
13. Способ по п. 1, в котором значение pH раствора продукта составляет от 11,5 до 12,5.
14. Способ по п. 1, содержащий:
выделение материала фосфата кальция из раствора продукта; и
нагревание материала фосфата кальция до температуры по меньшей мере 700°C в течение по меньшей мере 1 час.
15. Способ по п. 14, содержащий нагревание материала фосфата кальция до температуры по меньшей мере 800°C.
16. Способ по п. 14, содержащий нагревание материала фосфата кальция до температуры по меньшей мере 900°C.
17. Способ по п. 14, в котором продолжительность нагревания составляет от 1,5 до 2,5 час.
18. Способ по п. 1, содержащий подвергание материала фосфата кальция обработке термическим ударом путем увеличения температуры материала фосфата кальция по меньшей мере на 450°C в течение меньше чем 15 мин для удаления водяного пара из материала фосфата кальция.
19. Способ по п. 1, в котором материал фосфата кальция содержит две фазы, каждая из которых соответствует различному соединению фосфата кальция.
20. Способ по п. 19, в котором первая из фаз соответствует гидроксиапатиту, а вторая из фаз соответствует β-трикальцийфосфату.
21. Способ по п. 19, в котором первая из фаз соответствует гидроксиапатиту, а вторая из фаз соответствует аморфному фосфату кальция.
22. Способ по п. 19, в котором первая из фаз соответствует β-трикальцийфосфату, а вторая из фаз соответствует аморфному фосфату кальция.
23. Способ по п. 1, в котором материал фосфата кальция содержит три фазы, каждая из которых соответствует различному соединению фосфата кальция.
24. Способ по п. 23, в котором первая из фаз соответствует гидроксиапатиту, вторая из фаз соответствует β-трикальцийфосфату, а третья из фаз соответствует аморфному фосфату кальция.
25. Способ по п. 23, в котором первая из фаз соответствует дигидрату гидрофосфата кальция, вторая из фаз соответствует безводному гидрофосфату кальция, а третья из фаз соответствует моногидрату β-трикальцийфосфата.
26. Способ по п. 14, в котором частицы материала фосфата кальция имеют кристалличность 80% или больше.
27. Способ по п. 26, в котором кристалличность составляет 95% или больше.
28. Способ по п. 18, в котором частицы материала фосфата кальция имеют удельную площадь поверхности 60 м2/г или больше.
29. Способ по п. 28, в котором удельная площадь поверхности составляет 80 м2/г или больше.