RU2014132898A - Фибролит и продукты, содержащие фибролиты - Google Patents

Фибролит и продукты, содержащие фибролиты Download PDF

Info

Publication number
RU2014132898A
RU2014132898A RU2014132898A RU2014132898A RU2014132898A RU 2014132898 A RU2014132898 A RU 2014132898A RU 2014132898 A RU2014132898 A RU 2014132898A RU 2014132898 A RU2014132898 A RU 2014132898A RU 2014132898 A RU2014132898 A RU 2014132898A
Authority
RU
Russia
Prior art keywords
hybrid
fibrolite
fibers
fiberboard
glass fibers
Prior art date
Application number
RU2014132898A
Other languages
English (en)
Other versions
RU2669166C2 (ru
Inventor
Эльвира РЕМПТ
Штефан ГРЕГЕР
Original Assignee
Джонс Мэнвилл Юроп Гмбх
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Джонс Мэнвилл Юроп Гмбх filed Critical Джонс Мэнвилл Юроп Гмбх
Publication of RU2014132898A publication Critical patent/RU2014132898A/ru
Application granted granted Critical
Publication of RU2669166C2 publication Critical patent/RU2669166C2/ru

Abstract

1. Фибролит, а именно гибридный фибролит, включающий стеклянные волокна, полимерные волокна и связующие агенты, имеющий следующие признаки:стеклянные волокна имеют средний диаметр между 6 и 13 мкм и среднюю длину между 6 и 15 мм;полимерные волокна представляют собой штапельные волокна, имеющие среднюю тонкость между 0,2 и 0,6 дтекс и среднюю длину между 2 и 4 мм;процентное содержание полимерных волокон по массе составляет между 5 и 20% от сухого фибролита.2. Гибридный фибролит по п. 1, отличающийся тем, что процентное содержание связующего агента по массе составляет между 15 и 35% от сухого фибролита.3. Гибридный фибролит по п. 2, отличающийся тем, что процентное содержание связующего агента по массе составляет между 20 и 30% от сухого фибролита.4. Гибридный фибролит по п. 1, отличающийся тем, что полимерные волокна имеют среднюю тонкость между 0,3 и 0,4 дтекс.5. Гибридный фибролит по п. 1, отличающийся тем, что полимерные волокна имеют среднюю длину между 2,5 и 3,5 мм.6. Гибридный фибролит по п. 1, отличающийся тем, что полимерные волокна состоят из ПЭТ.7. Гибридный фибролит по п. 1, отличающийся тем, что стеклянные волокна имеют средний диаметр между 7 и 10 мкм.8. Гибридный фибролит по п. 1, отличающийся тем, что диаметр стеклянных волокон составляет максимум 10 мкм, и тем, что длина стеклянных волокон составляет максимум 15 мм.9. Гибридный фибролит по п. 1, отличающийся тем, что стеклянные волокна имеют среднюю длину между 7 и 9 мм.10. Гибридный фибролит по п. 1, отличающийся тем, что связующий агент включает мочевинную смолу, предпочтительно смесь мочевинной смолы и полимерной дисперсии.11. Гибридный фибролит по п. 1, отличающийся тем, что связующий агент включает связующее из полиакриловой кислоты, предпочтительно смесь связующего и

Claims (21)

1. Фибролит, а именно гибридный фибролит, включающий стеклянные волокна, полимерные волокна и связующие агенты, имеющий следующие признаки:
стеклянные волокна имеют средний диаметр между 6 и 13 мкм и среднюю длину между 6 и 15 мм;
полимерные волокна представляют собой штапельные волокна, имеющие среднюю тонкость между 0,2 и 0,6 дтекс и среднюю длину между 2 и 4 мм;
процентное содержание полимерных волокон по массе составляет между 5 и 20% от сухого фибролита.
2. Гибридный фибролит по п. 1, отличающийся тем, что процентное содержание связующего агента по массе составляет между 15 и 35% от сухого фибролита.
3. Гибридный фибролит по п. 2, отличающийся тем, что процентное содержание связующего агента по массе составляет между 20 и 30% от сухого фибролита.
4. Гибридный фибролит по п. 1, отличающийся тем, что полимерные волокна имеют среднюю тонкость между 0,3 и 0,4 дтекс.
5. Гибридный фибролит по п. 1, отличающийся тем, что полимерные волокна имеют среднюю длину между 2,5 и 3,5 мм.
6. Гибридный фибролит по п. 1, отличающийся тем, что полимерные волокна состоят из ПЭТ.
7. Гибридный фибролит по п. 1, отличающийся тем, что стеклянные волокна имеют средний диаметр между 7 и 10 мкм.
8. Гибридный фибролит по п. 1, отличающийся тем, что диаметр стеклянных волокон составляет максимум 10 мкм, и тем, что длина стеклянных волокон составляет максимум 15 мм.
9. Гибридный фибролит по п. 1, отличающийся тем, что стеклянные волокна имеют среднюю длину между 7 и 9 мм.
10. Гибридный фибролит по п. 1, отличающийся тем, что связующий агент включает мочевинную смолу, предпочтительно смесь мочевинной смолы и полимерной дисперсии.
11. Гибридный фибролит по п. 1, отличающийся тем, что связующий агент включает связующее из полиакриловой кислоты, предпочтительно смесь связующего из полиакриловой кислоты и полимерную дисперсию.
12. Гибридный фибролит по п. 1, отличающийся тем, что стеклянные волокна состоят из С-стекла и/или Е-стекла.
13. Гибридный фибролит по п. 1, отличающийся тем, что он имеет массу поверхности между 25 г/м2 и 80 г/м3, предпочтительно между 40 г/м2 и 60 г/м2.
14. Гибридный фибролит по п. 1, отличающийся тем, что процентное содержание полимерных волокон по массе составляет между 10 и 15% от сухого фибролита.
15. Гибридный фибролит по п. 1, отличающийся тем, что его получают дополнительным импрегнированием.
16. Гибридный фибролит по п. 15, отличающийся тем, что импрегнирующее средство представляет собой пластизоль.
17. Амортизированное виниловое покрытие для полов, имеющее используемый слой и структурный слой, при этом структурный слой включает в себя гибридный фибролит, снабженный импрегнированием по п. 15 или 16.
18. Применение гибридного фибролита по п. 1 в качестве покрытия для элементов интерьера, в частности, в качестве потолочной панели или другого элемента интерьерной облицовки.
19. Применение гибридного фибролита по п. 1 в качестве покрытия поверхности строительной панели, в частности, минеральной потолочной панели или стенной панели.
20. Применение гибридного фибролита по п. 1 в качестве покрытия для стен.
21. Способ получения гибридного фибролита по п. 1, где воду, которая содержит полимерные волокна и стеклянные волокна, пропускают в контуре через ленточное сито, при этом смесь волокон, в этом случае - в форме слоя волокон с заранее определенной толщиной слоя, затем осаждают на ленточном сите, избыток контурной воды удаляют из слоя волокон, добавляют связующий агент к слою волокон и высушивают слой волокон, к которому добавили связующий агент.
RU2014132898A 2013-08-09 2014-08-08 Фибролит и продукты, содержащие фибролиты RU2669166C2 (ru)