RU2007134422A - МЯГКИЕ ПЕНОПЛАСТЫ, ПОЛУЧАЕМЫЕ ИЗ ИНТЕРПОЛИМЕРОВ ЭТИЛЕНА/α-ОЛЕФИНОВ - Google Patents
МЯГКИЕ ПЕНОПЛАСТЫ, ПОЛУЧАЕМЫЕ ИЗ ИНТЕРПОЛИМЕРОВ ЭТИЛЕНА/α-ОЛЕФИНОВ Download PDFInfo
- Publication number
- RU2007134422A RU2007134422A RU2007134422/04A RU2007134422A RU2007134422A RU 2007134422 A RU2007134422 A RU 2007134422A RU 2007134422/04 A RU2007134422/04 A RU 2007134422/04A RU 2007134422 A RU2007134422 A RU 2007134422A RU 2007134422 A RU2007134422 A RU 2007134422A
- Authority
- RU
- Russia
- Prior art keywords
- ethylene
- olefin interpolymer
- soft foam
- interpolymer
- density
- Prior art date
Links
Classifications
-
- C—CHEMISTRY; METALLURGY
- C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
- C08F—MACROMOLECULAR COMPOUNDS OBTAINED BY REACTIONS ONLY INVOLVING CARBON-TO-CARBON UNSATURATED BONDS
- C08F210/00—Copolymers of unsaturated aliphatic hydrocarbons having only one carbon-to-carbon double bond
- C08F210/16—Copolymers of ethene with alpha-alkenes, e.g. EP rubbers
-
- C—CHEMISTRY; METALLURGY
- C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
- C08J—WORKING-UP; GENERAL PROCESSES OF COMPOUNDING; AFTER-TREATMENT NOT COVERED BY SUBCLASSES C08B, C08C, C08F, C08G or C08H
- C08J9/00—Working-up of macromolecular substances to porous or cellular articles or materials; After-treatment thereof
- C08J9/22—After-treatment of expandable particles; Forming foamed products
-
- C—CHEMISTRY; METALLURGY
- C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
- C08F—MACROMOLECULAR COMPOUNDS OBTAINED BY REACTIONS ONLY INVOLVING CARBON-TO-CARBON UNSATURATED BONDS
- C08F10/00—Homopolymers and copolymers of unsaturated aliphatic hydrocarbons having only one carbon-to-carbon double bond
- C08F10/14—Monomers containing five or more carbon atoms
-
- C—CHEMISTRY; METALLURGY
- C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
- C08F—MACROMOLECULAR COMPOUNDS OBTAINED BY REACTIONS ONLY INVOLVING CARBON-TO-CARBON UNSATURATED BONDS
- C08F10/00—Homopolymers and copolymers of unsaturated aliphatic hydrocarbons having only one carbon-to-carbon double bond
-
- C—CHEMISTRY; METALLURGY
- C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
- C08F—MACROMOLECULAR COMPOUNDS OBTAINED BY REACTIONS ONLY INVOLVING CARBON-TO-CARBON UNSATURATED BONDS
- C08F295/00—Macromolecular compounds obtained by polymerisation using successively different catalyst types without deactivating the intermediate polymer
-
- C—CHEMISTRY; METALLURGY
- C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
- C08F—MACROMOLECULAR COMPOUNDS OBTAINED BY REACTIONS ONLY INVOLVING CARBON-TO-CARBON UNSATURATED BONDS
- C08F297/00—Macromolecular compounds obtained by successively polymerising different monomer systems using a catalyst of the ionic or coordination type without deactivating the intermediate polymer
- C08F297/06—Macromolecular compounds obtained by successively polymerising different monomer systems using a catalyst of the ionic or coordination type without deactivating the intermediate polymer using a catalyst of the coordination type
- C08F297/08—Macromolecular compounds obtained by successively polymerising different monomer systems using a catalyst of the ionic or coordination type without deactivating the intermediate polymer using a catalyst of the coordination type polymerising mono-olefins
-
- C—CHEMISTRY; METALLURGY
- C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
- C08F—MACROMOLECULAR COMPOUNDS OBTAINED BY REACTIONS ONLY INVOLVING CARBON-TO-CARBON UNSATURATED BONDS
- C08F297/00—Macromolecular compounds obtained by successively polymerising different monomer systems using a catalyst of the ionic or coordination type without deactivating the intermediate polymer
- C08F297/06—Macromolecular compounds obtained by successively polymerising different monomer systems using a catalyst of the ionic or coordination type without deactivating the intermediate polymer using a catalyst of the coordination type
- C08F297/08—Macromolecular compounds obtained by successively polymerising different monomer systems using a catalyst of the ionic or coordination type without deactivating the intermediate polymer using a catalyst of the coordination type polymerising mono-olefins
- C08F297/083—Macromolecular compounds obtained by successively polymerising different monomer systems using a catalyst of the ionic or coordination type without deactivating the intermediate polymer using a catalyst of the coordination type polymerising mono-olefins the monomers being ethylene or propylene
-
- C—CHEMISTRY; METALLURGY
- C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
- C08F—MACROMOLECULAR COMPOUNDS OBTAINED BY REACTIONS ONLY INVOLVING CARBON-TO-CARBON UNSATURATED BONDS
- C08F297/00—Macromolecular compounds obtained by successively polymerising different monomer systems using a catalyst of the ionic or coordination type without deactivating the intermediate polymer
- C08F297/06—Macromolecular compounds obtained by successively polymerising different monomer systems using a catalyst of the ionic or coordination type without deactivating the intermediate polymer using a catalyst of the coordination type
- C08F297/08—Macromolecular compounds obtained by successively polymerising different monomer systems using a catalyst of the ionic or coordination type without deactivating the intermediate polymer using a catalyst of the coordination type polymerising mono-olefins
- C08F297/083—Macromolecular compounds obtained by successively polymerising different monomer systems using a catalyst of the ionic or coordination type without deactivating the intermediate polymer using a catalyst of the coordination type polymerising mono-olefins the monomers being ethylene or propylene
- C08F297/086—Macromolecular compounds obtained by successively polymerising different monomer systems using a catalyst of the ionic or coordination type without deactivating the intermediate polymer using a catalyst of the coordination type polymerising mono-olefins the monomers being ethylene or propylene the block polymer contains at least three blocks
-
- C—CHEMISTRY; METALLURGY
- C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
- C08L—COMPOSITIONS OF MACROMOLECULAR COMPOUNDS
- C08L23/00—Compositions of homopolymers or copolymers of unsaturated aliphatic hydrocarbons having only one carbon-to-carbon double bond; Compositions of derivatives of such polymers
- C08L23/02—Compositions of homopolymers or copolymers of unsaturated aliphatic hydrocarbons having only one carbon-to-carbon double bond; Compositions of derivatives of such polymers not modified by chemical after-treatment
- C08L23/04—Homopolymers or copolymers of ethene
- C08L23/06—Polyethene
-
- C—CHEMISTRY; METALLURGY
- C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
- C08L—COMPOSITIONS OF MACROMOLECULAR COMPOUNDS
- C08L23/00—Compositions of homopolymers or copolymers of unsaturated aliphatic hydrocarbons having only one carbon-to-carbon double bond; Compositions of derivatives of such polymers
- C08L23/02—Compositions of homopolymers or copolymers of unsaturated aliphatic hydrocarbons having only one carbon-to-carbon double bond; Compositions of derivatives of such polymers not modified by chemical after-treatment
- C08L23/04—Homopolymers or copolymers of ethene
- C08L23/08—Copolymers of ethene
- C08L23/0807—Copolymers of ethene with unsaturated hydrocarbons only containing more than three carbon atoms
- C08L23/0815—Copolymers of ethene with aliphatic 1-olefins
-
- C—CHEMISTRY; METALLURGY
- C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
- C08L—COMPOSITIONS OF MACROMOLECULAR COMPOUNDS
- C08L23/00—Compositions of homopolymers or copolymers of unsaturated aliphatic hydrocarbons having only one carbon-to-carbon double bond; Compositions of derivatives of such polymers
- C08L23/02—Compositions of homopolymers or copolymers of unsaturated aliphatic hydrocarbons having only one carbon-to-carbon double bond; Compositions of derivatives of such polymers not modified by chemical after-treatment
- C08L23/10—Homopolymers or copolymers of propene
-
- C—CHEMISTRY; METALLURGY
- C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
- C08L—COMPOSITIONS OF MACROMOLECULAR COMPOUNDS
- C08L53/00—Compositions of block copolymers containing at least one sequence of a polymer obtained by reactions only involving carbon-to-carbon unsaturated bonds; Compositions of derivatives of such polymers
-
- C—CHEMISTRY; METALLURGY
- C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
- C08L—COMPOSITIONS OF MACROMOLECULAR COMPOUNDS
- C08L53/00—Compositions of block copolymers containing at least one sequence of a polymer obtained by reactions only involving carbon-to-carbon unsaturated bonds; Compositions of derivatives of such polymers
- C08L53/005—Modified block copolymers
-
- C—CHEMISTRY; METALLURGY
- C09—DYES; PAINTS; POLISHES; NATURAL RESINS; ADHESIVES; COMPOSITIONS NOT OTHERWISE PROVIDED FOR; APPLICATIONS OF MATERIALS NOT OTHERWISE PROVIDED FOR
- C09J—ADHESIVES; NON-MECHANICAL ASPECTS OF ADHESIVE PROCESSES IN GENERAL; ADHESIVE PROCESSES NOT PROVIDED FOR ELSEWHERE; USE OF MATERIALS AS ADHESIVES
- C09J9/00—Adhesives characterised by their physical nature or the effects produced, e.g. glue sticks
-
- C—CHEMISTRY; METALLURGY
- C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
- C08F—MACROMOLECULAR COMPOUNDS OBTAINED BY REACTIONS ONLY INVOLVING CARBON-TO-CARBON UNSATURATED BONDS
- C08F110/00—Homopolymers of unsaturated aliphatic hydrocarbons having only one carbon-to-carbon double bond
- C08F110/02—Ethene
-
- C—CHEMISTRY; METALLURGY
- C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
- C08F—MACROMOLECULAR COMPOUNDS OBTAINED BY REACTIONS ONLY INVOLVING CARBON-TO-CARBON UNSATURATED BONDS
- C08F2410/00—Features related to the catalyst preparation, the catalyst use or to the deactivation of the catalyst
- C08F2410/01—Additive used together with the catalyst, excluding compounds containing Al or B
-
- C—CHEMISTRY; METALLURGY
- C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
- C08F—MACROMOLECULAR COMPOUNDS OBTAINED BY REACTIONS ONLY INVOLVING CARBON-TO-CARBON UNSATURATED BONDS
- C08F4/00—Polymerisation catalysts
- C08F4/42—Metals; Metal hydrides; Metallo-organic compounds; Use thereof as catalyst precursors
- C08F4/44—Metals; Metal hydrides; Metallo-organic compounds; Use thereof as catalyst precursors selected from light metals, zinc, cadmium, mercury, copper, silver, gold, boron, gallium, indium, thallium, rare earths or actinides
- C08F4/60—Metals; Metal hydrides; Metallo-organic compounds; Use thereof as catalyst precursors selected from light metals, zinc, cadmium, mercury, copper, silver, gold, boron, gallium, indium, thallium, rare earths or actinides together with refractory metals, iron group metals, platinum group metals, manganese, rhenium technetium or compounds thereof
- C08F4/62—Refractory metals or compounds thereof
- C08F4/64—Titanium, zirconium, hafnium or compounds thereof
- C08F4/659—Component covered by group C08F4/64 containing a transition metal-carbon bond
-
- C—CHEMISTRY; METALLURGY
- C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
- C08F—MACROMOLECULAR COMPOUNDS OBTAINED BY REACTIONS ONLY INVOLVING CARBON-TO-CARBON UNSATURATED BONDS
- C08F4/00—Polymerisation catalysts
- C08F4/42—Metals; Metal hydrides; Metallo-organic compounds; Use thereof as catalyst precursors
- C08F4/44—Metals; Metal hydrides; Metallo-organic compounds; Use thereof as catalyst precursors selected from light metals, zinc, cadmium, mercury, copper, silver, gold, boron, gallium, indium, thallium, rare earths or actinides
- C08F4/60—Metals; Metal hydrides; Metallo-organic compounds; Use thereof as catalyst precursors selected from light metals, zinc, cadmium, mercury, copper, silver, gold, boron, gallium, indium, thallium, rare earths or actinides together with refractory metals, iron group metals, platinum group metals, manganese, rhenium technetium or compounds thereof
- C08F4/62—Refractory metals or compounds thereof
- C08F4/64—Titanium, zirconium, hafnium or compounds thereof
- C08F4/659—Component covered by group C08F4/64 containing a transition metal-carbon bond
- C08F4/65908—Component covered by group C08F4/64 containing a transition metal-carbon bond in combination with an ionising compound other than alumoxane, e.g. (C6F5)4B-X+
-
- C—CHEMISTRY; METALLURGY
- C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
- C08F—MACROMOLECULAR COMPOUNDS OBTAINED BY REACTIONS ONLY INVOLVING CARBON-TO-CARBON UNSATURATED BONDS
- C08F4/00—Polymerisation catalysts
- C08F4/42—Metals; Metal hydrides; Metallo-organic compounds; Use thereof as catalyst precursors
- C08F4/44—Metals; Metal hydrides; Metallo-organic compounds; Use thereof as catalyst precursors selected from light metals, zinc, cadmium, mercury, copper, silver, gold, boron, gallium, indium, thallium, rare earths or actinides
- C08F4/60—Metals; Metal hydrides; Metallo-organic compounds; Use thereof as catalyst precursors selected from light metals, zinc, cadmium, mercury, copper, silver, gold, boron, gallium, indium, thallium, rare earths or actinides together with refractory metals, iron group metals, platinum group metals, manganese, rhenium technetium or compounds thereof
- C08F4/62—Refractory metals or compounds thereof
- C08F4/64—Titanium, zirconium, hafnium or compounds thereof
- C08F4/659—Component covered by group C08F4/64 containing a transition metal-carbon bond
- C08F4/65912—Component covered by group C08F4/64 containing a transition metal-carbon bond in combination with an organoaluminium compound
-
- C—CHEMISTRY; METALLURGY
- C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
- C08F—MACROMOLECULAR COMPOUNDS OBTAINED BY REACTIONS ONLY INVOLVING CARBON-TO-CARBON UNSATURATED BONDS
- C08F4/00—Polymerisation catalysts
- C08F4/42—Metals; Metal hydrides; Metallo-organic compounds; Use thereof as catalyst precursors
- C08F4/44—Metals; Metal hydrides; Metallo-organic compounds; Use thereof as catalyst precursors selected from light metals, zinc, cadmium, mercury, copper, silver, gold, boron, gallium, indium, thallium, rare earths or actinides
- C08F4/60—Metals; Metal hydrides; Metallo-organic compounds; Use thereof as catalyst precursors selected from light metals, zinc, cadmium, mercury, copper, silver, gold, boron, gallium, indium, thallium, rare earths or actinides together with refractory metals, iron group metals, platinum group metals, manganese, rhenium technetium or compounds thereof
- C08F4/62—Refractory metals or compounds thereof
- C08F4/64—Titanium, zirconium, hafnium or compounds thereof
- C08F4/659—Component covered by group C08F4/64 containing a transition metal-carbon bond
- C08F4/6592—Component covered by group C08F4/64 containing a transition metal-carbon bond containing at least one cyclopentadienyl ring, condensed or not, e.g. an indenyl or a fluorenyl ring
-
- C—CHEMISTRY; METALLURGY
- C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
- C08F—MACROMOLECULAR COMPOUNDS OBTAINED BY REACTIONS ONLY INVOLVING CARBON-TO-CARBON UNSATURATED BONDS
- C08F4/00—Polymerisation catalysts
- C08F4/42—Metals; Metal hydrides; Metallo-organic compounds; Use thereof as catalyst precursors
- C08F4/44—Metals; Metal hydrides; Metallo-organic compounds; Use thereof as catalyst precursors selected from light metals, zinc, cadmium, mercury, copper, silver, gold, boron, gallium, indium, thallium, rare earths or actinides
- C08F4/60—Metals; Metal hydrides; Metallo-organic compounds; Use thereof as catalyst precursors selected from light metals, zinc, cadmium, mercury, copper, silver, gold, boron, gallium, indium, thallium, rare earths or actinides together with refractory metals, iron group metals, platinum group metals, manganese, rhenium technetium or compounds thereof
- C08F4/62—Refractory metals or compounds thereof
- C08F4/64—Titanium, zirconium, hafnium or compounds thereof
- C08F4/659—Component covered by group C08F4/64 containing a transition metal-carbon bond
- C08F4/6592—Component covered by group C08F4/64 containing a transition metal-carbon bond containing at least one cyclopentadienyl ring, condensed or not, e.g. an indenyl or a fluorenyl ring
- C08F4/65922—Component covered by group C08F4/64 containing a transition metal-carbon bond containing at least one cyclopentadienyl ring, condensed or not, e.g. an indenyl or a fluorenyl ring containing at least two cyclopentadienyl rings, fused or not
- C08F4/65927—Component covered by group C08F4/64 containing a transition metal-carbon bond containing at least one cyclopentadienyl ring, condensed or not, e.g. an indenyl or a fluorenyl ring containing at least two cyclopentadienyl rings, fused or not two cyclopentadienyl rings being mutually bridged
-
- C—CHEMISTRY; METALLURGY
- C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
- C08J—WORKING-UP; GENERAL PROCESSES OF COMPOUNDING; AFTER-TREATMENT NOT COVERED BY SUBCLASSES C08B, C08C, C08F, C08G or C08H
- C08J2205/00—Foams characterised by their properties
- C08J2205/06—Flexible foams
-
- C—CHEMISTRY; METALLURGY
- C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
- C08J—WORKING-UP; GENERAL PROCESSES OF COMPOUNDING; AFTER-TREATMENT NOT COVERED BY SUBCLASSES C08B, C08C, C08F, C08G or C08H
- C08J9/00—Working-up of macromolecular substances to porous or cellular articles or materials; After-treatment thereof
- C08J9/16—Making expandable particles
-
- C—CHEMISTRY; METALLURGY
- C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
- C08J—WORKING-UP; GENERAL PROCESSES OF COMPOUNDING; AFTER-TREATMENT NOT COVERED BY SUBCLASSES C08B, C08C, C08F, C08G or C08H
- C08J9/00—Working-up of macromolecular substances to porous or cellular articles or materials; After-treatment thereof
- C08J9/22—After-treatment of expandable particles; Forming foamed products
- C08J9/228—Forming foamed products
- C08J9/232—Forming foamed products by sintering expandable particles
-
- C—CHEMISTRY; METALLURGY
- C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
- C08K—Use of inorganic or non-macromolecular organic substances as compounding ingredients
- C08K5/00—Use of organic ingredients
- C08K5/56—Organo-metallic compounds, i.e. organic compounds containing a metal-to-carbon bond
-
- C—CHEMISTRY; METALLURGY
- C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
- C08L—COMPOSITIONS OF MACROMOLECULAR COMPOUNDS
- C08L2203/00—Applications
- C08L2203/14—Applications used for foams
-
- C—CHEMISTRY; METALLURGY
- C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
- C08L—COMPOSITIONS OF MACROMOLECULAR COMPOUNDS
- C08L23/00—Compositions of homopolymers or copolymers of unsaturated aliphatic hydrocarbons having only one carbon-to-carbon double bond; Compositions of derivatives of such polymers
- C08L23/02—Compositions of homopolymers or copolymers of unsaturated aliphatic hydrocarbons having only one carbon-to-carbon double bond; Compositions of derivatives of such polymers not modified by chemical after-treatment
- C08L23/04—Homopolymers or copolymers of ethene
Claims (20)
1. Мягкий пенопласт, содержащий, по меньшей мере, один интерполимер этилена/α-олефина, где плотность мягкого пенопласта составляет от 10 до 150 кг/м3 и где интерполимер этилена/α-олефина представляет собой блок-интерполимер и:
(a) имеет Mw/Mn от приблизительно 1,7 до приблизительно 3,5, по меньшей мере, одну температуру плавления, Tпл, в градусах Цельсия, и плотность, d, в граммах/кубический сантиметр, где числовые значения Tпл и d соответствуют зависимости:
Tпл≥-2002,9+4538,5(d)-2422,2(d)2; или
(b) имеет Mw/Mn от приблизительно 1,7 до приблизительно 3,5, и характеризуется теплотой плавления, ΔH, в Дж/г, и изменением величины, ΔT, в градусах Цельсия, определенной как разница температур между наивысшим пиком ДСК и наивысшим пиком CRYSTAF, где числовые значения ΔT и ΔH удовлетворяют следующим зависимостям:
ΔT>-0,1299(ΔH)+62,81 для ΔH более нуля и до 130 Дж/г,
ΔT≥48°C для ΔH более 130 Дж/г,
где пик CRYSTAF определяют с использованием, по меньшей мере, 5% совокупного полимера, а если идентифицируемому пику CRYSTAF соответствуют менее 5% полимера, тогда температура CRYSTAF составляет 30°C; или
(c) характеризуется упругим восстановлением, Re, в процентах при растяжении 300% и 1 цикле, измеряемом на полученной прямым формованием пленке интерполимера этилена/α-олефина, и имеет плотность, d, в граммах/кубический сантиметр, где числовые значения Re и d удовлетворяют следующей зависимости, когда в интерполимере этилена/α-олефина по существу отсутствует сшитая фаза:
Re>1481-1629(d); или
(d) содержит молекулярную фракцию, элюирующую при фракционировании с применением TREF в интервале от 40 до 130°C, характеризующуюся тем, что содержание сомономеров во фракции, по меньшей мере, на 5% выше, чем содержание сомономеров во фракции сопоставимого статистического интерполимера этилена, элюирующей в том же интервале температур, где указанный сопоставимый статистический интерполимер этилена содержит тот же сомономер(-ы) и имеет показатель расплава, плотность и мольное содержание сомономеров (относительно всего полимера) в пределах 10% от этих показателей у интерполимера этилена/α-олефина; или
(e) имеет динамический модуль упругости при 25°C, G'(25°C), и динамический модуль упругости при 100°C, G'(100°C), где отношение G'(25°C) к G'(100°C) находится в диапазоне от приблизительно 1:1 до приблизительно 9:1.
2. Мягкий пенопласт по п.1, где интерполимер этилена/α-олефина имеет Mw/Mn от приблизительно 1,7 до приблизительно 3,5, по меньшей мере, одну температуру плавления, Tпл, в градусах Цельсия, и плотность, d, в граммах/кубический сантиметр, где числовые значения Tпл и d соответствуют зависимости:
Tпл≥858,91-1825,3(d)+1112,8(d)2.
3. Мягкий пенопласт по п.1, где интерполимер этилена/α-олефина имеет Mw/Mn от приблизительно 1,7 до приблизительно 3,5 и характеризуется теплотой плавления, ΔH, в Дж/г, и изменением величины, ΔT, в градусах Цельсия, определенной как разница температур между наивысшим пиком ДСК и наивысшим пиком CRYSTAF, где числовые значения ΔT и ΔH удовлетворяют следующим зависимостям:
ΔT>-0,1299(ΔH)+62,81 для ΔH более нуля и до 130 Дж/г,
ΔT≥48°C для ΔH более 130 Дж/г,
где пик CRYSTAF определяют с использованием, по меньшей мере, 5% совокупного полимера, а если идентифицируемому пику CRYSTAF соответствуют менее 5% полимера, тогда температура CRYSTAF составляет 30°C.
4. Мягкий пенопласт по п.1, где интерполимер этилена/α-олефина характеризуется упругим восстановлением, Re, в процентах при растяжении 300% и 1 цикле, измеряемом на полученной прямым формованием пленке интерполимера этилена/α-олефина, и имеет плотность, d, в граммах/кубический сантиметр, где числовые значения Re и d удовлетворяют следующей зависимости, когда в интерполимере этилена/α-олефина по существу отсутствует сшитая фаза:
Re>1481-1629(d).
5. Мягкий пенопласт по п.1, где числовые значения Re и d удовлетворяют следующей зависимости:
Re>1491-1629(d).
6. Мягкий пенопласт по п.1, где числовые значения Re и d удовлетворяют следующей зависимости:
Re>1501-1629(d).
7. Мягкий пенопласт по п.1, где числовые значения Re и d удовлетворяют следующей зависимости:
Re>1511-1629(d).
8. Мягкий пенопласт, содержащий, по меньшей мере, один интерполимер этилена/α-олефина, где плотность мягкого пенопласта составляет от приблизительно 10 до 150 кг/м3 и где интерполимер этилена/α-олефина имеет:
(a) по меньшей мере, одну молекулярную фракцию, элюирующую при фракционировании с применением TREF в интервале от 40 до 130°C, характеризующуюся тем, что фракция имеет показатель блочности, по меньшей мере, равный от 0,5 и до приблизительно 1 и молекулярно-массовое распределение, Mw/Mn, более приблизительно 1,3; или
(b) средний показатель блочности от более нуля и до приблизительно 1,0 и молекулярно-массовое распределение, Mw/Mn, более приблизительно 1,3.
9. Мягкий пенопласт по п.1 или 8, где интерполимер этилена/α-олефина содержит молекулярную фракцию, элюирующую при фракционировании с применением TREF в интервале от 40 до 130°C, характеризующуюся тем, что содержание сомономеров во фракции, по меньшей мере, на 5% выше, чем содержание сомономеров во фракции сопоставимого статистического интерполимера этилена, элюирующей в том же интервале температур, где указанный сопоставимый статистический интерполимер этилена содержит тот же сомономер(-ы) и имеет показатель расплава, плотность и мольное содержание сомономеров (относительно всего полимера) в пределах 10% от этих показателей у интерполимера этилена/α-олефина.
10. Мягкий пенопласт по п.1 или 8, где интерполимер этилена/α-олефина имеет динамический модуль упругости при 25°C, G'(25°C) и динамический модуль упругости при 100°C, G'(100°C), где отношение G'(25°C) к G'(100°C) находится в диапазоне от приблизительно 1:1 до приблизительно 9:1.
11. Мягкий пенопласт по п.1 или 8, где α-олефин в интерполимере этилена/α-олефина представляет собой стирол, пропилен, 1-бутен, 1-гексен, 1-октен, 4-метил-1-пентен, норборнен, 1-децен, 1,5-гексадиен или их сочетание.
12. Мягкий пенопласт по п.1 или 8, где мягкий пенопласт содержит менее 5 мас.% геля по ASTM D-2765-84 Method A.
13. Мягкий пенопласт по п.1, дополнительно содержащий полиолефин.
14. Мягкий пенопласт по п.13, где полиолефин представляет собой полиэтилен низкой плотности, полипропилен с высокой прочностью расплава или их сочетание.
15. Мягкий пенопласт по п.13, где отношение полиолефина к интерполимеру этилена/α-олефина составляет от приблизительно 1:10 до приблизительно 10:1 по массе.
16. Вспениваемая композиция, содержащая:
(i) пенообразователь; и
(ii) по меньшей мере, один интерполимер этилена/α-олефина, где интерполимер этилена/α-олефина представляет собой блок-интерполимер и:
(a) имеет Mw/Mn от приблизительно 1,7 до приблизительно 3,5, по меньшей мере, одну температуру плавления, Tпл, в градусах Цельсия, и плотность, d, в граммах/кубический сантиметр, где числовые значения Tпл и d соответствуют зависимости:
Tпл≥-2002,9+4538,5(d)-2422,2(d)2; или
(b) имеет Mw/Mn от приблизительно 1,7 до приблизительно 3,5 и характеризуется теплотой плавления, ΔH, в Дж/г, и изменением величины, ΔT, в градусах Цельсия, определенной как разница температур между наивысшим пиком ДСК и наивысшим пиком CRYSTAF, где числовые значения ΔT и ΔH удовлетворяют следующим зависимостям:
ΔT>-0,1299(ΔH)+62,81 для ΔH более нуля и до 130 Дж/г,
ΔT≥48°C для ΔH более 130 Дж/г,
где пик CRYSTAF определяют с использованием, по меньшей мере, 5% совокупного полимера, а если идентифицируемому пику CRYSTAF соответствуют менее 5% полимера, тогда температура CRYSTAF составляет 30°C; или
(c) характеризуется упругим восстановлением, Re, в процентах при растяжении 300% и 1 цикле, измеряемом на полученной прямым формованием пленке интерполимера этилена/α-олефина, и имеет плотность, d, в граммах/кубический сантиметр, где числовые значения Re и d удовлетворяют следующей зависимости, когда в интерполимере этилена/α-олефина по существу отсутствует сшитая фаза:
Re>1481-1629(d); или
(d) содержит молекулярную фракцию, элюирующую при фракционировании с применением TREF в интервале от 40 до 130°C, характеризующуюся тем, что содержание сомономеров во фракции, по меньшей мере, на 5% выше, чем содержание сомономеров во фракции сопоставимого статистического интерполимера этилена, элюирующей в том же интервале температур, где указанный сопоставимый статистический интерполимер этилена содержит тот же сомономер(-ы) и имеет показатель расплава, плотность и мольное содержание сомономеров (относительно всего полимера) в пределах 10% от этих показателей у интерполимера этилена/α-олефина; или
(e) имеет динамический модуль упругости при 25°C, G'(25°C), и динамический модуль упругости при 100°C, G'(100°C), где отношение G'(25°C) к G'(100°C) находится в диапазоне от приблизительно 1:1 до приблизительно 9:1.
17. Вспениваемая композиция, содержащая:
(i) пенообразователь; и
(ii) по меньшей мере, один интерполимер этилена/α-олефина, где интерполимер этилена/α-олефина имеет:
(a) по меньшей мере, одну молекулярную фракцию, элюирующую при фракционировании с применением TREF в интервале от 40 до 130°C, характеризующуюся тем, что фракция имеет показатель блочности, по меньшей мере, от 0,5 и до приблизительно 1 и молекулярно-массовое распределение, Mw/Mn, более приблизительно 1,3; или
(b) средний показатель блочности от более нуля и до приблизительно 1,0 и молекулярно-массовое распределение, Mw/Mn, более приблизительно 1,3.
18. Вспениваемая композиция по п.16 или 17, дополнительно содержащая полиолефин.
19. Изделие из пенопласта, содержащее мягкий пенопласт по п.1 или 8.
20. Изделие из пенопласта по п.19, где изделие из пенопласта пригодно для звукоизоляции, виброизоляции, смягчения ударов, специальной упаковки, сенсорных клавиш автомобилей, теплоизоляции или демпфирования удара.