RU2005125415A - Состав для нанесения покрытий - Google Patents
Состав для нанесения покрытий Download PDFInfo
- Publication number
- RU2005125415A RU2005125415A RU2005125415/02A RU2005125415A RU2005125415A RU 2005125415 A RU2005125415 A RU 2005125415A RU 2005125415/02 A RU2005125415/02 A RU 2005125415/02A RU 2005125415 A RU2005125415 A RU 2005125415A RU 2005125415 A RU2005125415 A RU 2005125415A
- Authority
- RU
- Russia
- Prior art keywords
- particles
- acid
- composition according
- resistant
- coating
- Prior art date
Links
- 239000000203 mixture Substances 0.000 title claims 36
- 238000000576 coating method Methods 0.000 title claims 13
- 239000011248 coating agent Substances 0.000 title claims 12
- 239000002245 particle Substances 0.000 claims 45
- 239000002253 acid Substances 0.000 claims 37
- 150000007513 acids Chemical class 0.000 claims 8
- 239000008199 coating composition Substances 0.000 claims 7
- AZDRQVAHHNSJOQ-UHFFFAOYSA-N alumane Chemical class [AlH3] AZDRQVAHHNSJOQ-UHFFFAOYSA-N 0.000 claims 6
- 229910052751 metal Inorganic materials 0.000 claims 6
- 239000002184 metal Substances 0.000 claims 6
- 239000000758 substrate Substances 0.000 claims 5
- VYPSYNLAJGMNEJ-UHFFFAOYSA-N Silicium dioxide Chemical compound O=[Si]=O VYPSYNLAJGMNEJ-UHFFFAOYSA-N 0.000 claims 4
- 229920000620 organic polymer Polymers 0.000 claims 3
- 229910018072 Al 2 O 3 Inorganic materials 0.000 claims 2
- 229910004298 SiO 2 Inorganic materials 0.000 claims 2
- 239000011159 matrix material Substances 0.000 claims 2
- 229910044991 metal oxide Inorganic materials 0.000 claims 2
- 150000004706 metal oxides Chemical class 0.000 claims 2
- 239000011146 organic particle Substances 0.000 claims 2
- 235000012239 silicon dioxide Nutrition 0.000 claims 2
- 239000000377 silicon dioxide Substances 0.000 claims 2
- XUIMIQQOPSSXEZ-UHFFFAOYSA-N Silicon Chemical compound [Si] XUIMIQQOPSSXEZ-UHFFFAOYSA-N 0.000 claims 1
- RTAQQCXQSZGOHL-UHFFFAOYSA-N Titanium Chemical compound [Ti] RTAQQCXQSZGOHL-UHFFFAOYSA-N 0.000 claims 1
- QCWXUUIWCKQGHC-UHFFFAOYSA-N Zirconium Chemical compound [Zr] QCWXUUIWCKQGHC-UHFFFAOYSA-N 0.000 claims 1
- XAGFODPZIPBFFR-UHFFFAOYSA-N aluminium Chemical compound [Al] XAGFODPZIPBFFR-UHFFFAOYSA-N 0.000 claims 1
- 229910052782 aluminium Inorganic materials 0.000 claims 1
- 230000005484 gravity Effects 0.000 claims 1
- 230000003993 interaction Effects 0.000 claims 1
- 238000000034 method Methods 0.000 claims 1
- 229920000642 polymer Polymers 0.000 claims 1
- 229910052710 silicon Inorganic materials 0.000 claims 1
- 239000010703 silicon Substances 0.000 claims 1
- 229910052719 titanium Inorganic materials 0.000 claims 1
- 239000010936 titanium Substances 0.000 claims 1
- XLYOFNOQVPJJNP-UHFFFAOYSA-N water Substances O XLYOFNOQVPJJNP-UHFFFAOYSA-N 0.000 claims 1
- 229910052726 zirconium Inorganic materials 0.000 claims 1
Classifications
-
- C—CHEMISTRY; METALLURGY
- C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
- C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
- C23C22/00—Chemical surface treatment of metallic material by reaction of the surface with a reactive liquid, leaving reaction products of surface material in the coating, e.g. conversion coatings, passivation of metals
- C23C22/05—Chemical surface treatment of metallic material by reaction of the surface with a reactive liquid, leaving reaction products of surface material in the coating, e.g. conversion coatings, passivation of metals using aqueous solutions
- C23C22/06—Chemical surface treatment of metallic material by reaction of the surface with a reactive liquid, leaving reaction products of surface material in the coating, e.g. conversion coatings, passivation of metals using aqueous solutions using aqueous acidic solutions with pH less than 6
- C23C22/34—Chemical surface treatment of metallic material by reaction of the surface with a reactive liquid, leaving reaction products of surface material in the coating, e.g. conversion coatings, passivation of metals using aqueous solutions using aqueous acidic solutions with pH less than 6 containing fluorides or complex fluorides
-
- C—CHEMISTRY; METALLURGY
- C09—DYES; PAINTS; POLISHES; NATURAL RESINS; ADHESIVES; COMPOSITIONS NOT OTHERWISE PROVIDED FOR; APPLICATIONS OF MATERIALS NOT OTHERWISE PROVIDED FOR
- C09D—COATING COMPOSITIONS, e.g. PAINTS, VARNISHES OR LACQUERS; FILLING PASTES; CHEMICAL PAINT OR INK REMOVERS; INKS; CORRECTING FLUIDS; WOODSTAINS; PASTES OR SOLIDS FOR COLOURING OR PRINTING; USE OF MATERIALS THEREFOR
- C09D5/00—Coating compositions, e.g. paints, varnishes or lacquers, characterised by their physical nature or the effects produced; Filling pastes
- C09D5/08—Anti-corrosive paints
- C09D5/082—Anti-corrosive paints characterised by the anti-corrosive pigment
- C09D5/084—Inorganic compounds
-
- Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
- Y10—TECHNICAL SUBJECTS COVERED BY FORMER USPC
- Y10T—TECHNICAL SUBJECTS COVERED BY FORMER US CLASSIFICATION
- Y10T428/00—Stock material or miscellaneous articles
- Y10T428/27—Web or sheet containing structurally defined element or component, the element or component having a specified weight per unit area [e.g., gms/sq cm, lbs/sq ft, etc.]
- Y10T428/273—Web or sheet containing structurally defined element or component, the element or component having a specified weight per unit area [e.g., gms/sq cm, lbs/sq ft, etc.] of coating
-
- Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
- Y10—TECHNICAL SUBJECTS COVERED BY FORMER USPC
- Y10T—TECHNICAL SUBJECTS COVERED BY FORMER US CLASSIFICATION
- Y10T428/00—Stock material or miscellaneous articles
- Y10T428/31504—Composite [nonstructural laminate]
- Y10T428/31678—Of metal
- Y10T428/31681—Next to polyester, polyamide or polyimide [e.g., alkyd, glue, or nylon, etc.]
Landscapes
- Chemical & Material Sciences (AREA)
- Organic Chemistry (AREA)
- Engineering & Computer Science (AREA)
- Materials Engineering (AREA)
- Life Sciences & Earth Sciences (AREA)
- Wood Science & Technology (AREA)
- Inorganic Chemistry (AREA)
- General Chemical & Material Sciences (AREA)
- Chemical Kinetics & Catalysis (AREA)
- Mechanical Engineering (AREA)
- Metallurgy (AREA)
- Paints Or Removers (AREA)
- Application Of Or Painting With Fluid Materials (AREA)
Claims (40)
1. Состав для нанесения покрытий, включающий водную смесь, содержащую стойкие к кислоте частицы и одну или несколько фторзамещенных кислот, при этом содержание стойких к кислоте частиц составляет от 0,005 до 8 мас.% в расчете на сухую массу.
2. Состав по п.1, в котором стойкие к кислоте частицы представляют собой модифицированные алюминием частицы диоксида кремния, при этом содержание стойких к кислоте частиц в составе для нанесения покрытий составляет от 0,005 до 5 мас.% в расчете на сухую массу.
3. Состав по п.1, в котором стойкие к кислоте частицы представляют собой не модифицированные алюминием частицы диоксида кремния, при этом содержание стойких к кислоте частиц в составе для нанесения покрытий составляет от 0,005 до 5 мас.% в расчете на сухую массу.
4. Состав по п.1, в котором стойкие к кислоте частицы представляют собой полимерные органические частицы.
5. Состав по п.1, в котором смесь дополнительно включает продукт взаимодействия стойких к кислоте частиц и одной или нескольких фторзамещенных кислот.
6. Состав по п.2, в котором модифицированные алюминием частицы составляют приблизительно от 0,006 до 1 мас.% в расчете на сухую массу.
7. Состав по п.2, в котором модифицированные алюминием частицы имеют весовое отношение SiO2:Al2O3 от 80:1 до 240:1.
8. Состав по п.2, в котором модифицированные алюминием частицы имеют весовое отношение SiO2:Al2O3 от 120:1 до 220:1.
9. Состав по п.3, в котором не модифицированные алюминием частицы составляют от приблизительно от 0,006 до 1 мас.% в расчете на сухую массу.
10. Состав по п.1, в котором стойкие к кислоте частицы изменяют вязкость за десять секунд и менее.
11. Состав по п.1, имеющий рН от 3 до 6.
12. Состав по п.1, имеющий рН от 3,5 до 5.
13. Состав по п.1, в котором стойкие к кислоте частицы изменяют вязкость за три секунды и менее.
14. Состав по п.1, в котором содержание стойких к кислоте частиц составляет от 0,006 до 2 мас.% в расчете на сухую массу.
15. Состав по п.1, в котором содержание стойких к кислоте частиц составляет от 0,007 до 0,5 мас.% в расчете на сухую массу.
16. Состав по п.1, в котором содержание одной или нескольких фторзамещенных кислот составляет приблизительно от 5 до 1000 м.д.
17. Состав по п.1, в котором стойкие к кислоте частицы изменяют вязкость за одну секунду и менее.
18. Покрытие на металлическом субстрате, включающее стойкие к кислоте частицы, прикрепленные к металлическому субстрату посредством матрицы из оксида металла, при этом удельная плотность покрытия металлического субстрата составляет от 5 до 50 мг/кв. фут (53,82-538,2 мг/м2).
19. Покрытие по п.18, в котором матрица из оксида металла включает один или несколько элементов, выбранных из группы, включающей титан, цирконий и кремний.
20. Покрытие по п.18, в котором стойкие к кислоте частицы выбраны из одной или нескольких групп, включающих модифицированные алюминием частицы, не модифицированные алюминием частицы и органические полимерные частицы.
21. Покрытие по п.18, в котором удельная плотность покрытия металлического субстрата составляет от 8 до 30 мг/кв. фут (86,11-322,92 мг/м2).
22. Покрытие по п.18, в котором стойкие к кислоте частицы присутствуют в количестве от 5 до 25 мг/кв. фут (53,82-269,10 мг/м2)
23. Покрытие по п.18, в котором металл присутствует в количестве от 0,5 до 6 мг/кв. фут. (5,38-64,58 мг/м2).
24. Покрытие по п.18, в котором стойкие к кислоте частицы присутствуют в количестве от 10 до 20 мг/кв. фут. (107,64-215,28 мг/м2).
25. Покрытие по п.18, имеющее толщину, составляющую от 75 до 125% среднего диаметра стойких к кислоте частиц.
26. Состав для покрытий, полученный способом, включающим получение стойких к кислоте частиц и одной или нескольких фторзамещенных кислот и смешивание стойких к кислоте частиц и одной или нескольких фторзамещенных кислот в воде, при этом рН состава для покрытий составляет от 2 до 7, а содержание стойких к кислоте частиц в составе для покрытий составляет от 0,005 до 8 мас.% в расчете на сухую массу.
27. Состав по п.26, в котором стойкие к кислоте частицы выбраны из одной или нескольких групп, включающих модифицированные алюминием частицы, не модифицированные алюминием частицы и органические полимерные частицы.
28. Состав по п.27, в котором содержание модифицированных алюминием частиц составляет приблизительно от 0,006 до 1 мас.% в расчете на сухую массу композиции.
29. Состав по п.27, в котором содержание не модифицированных алюминием стойких к кислоте частиц составляет приблизительно от 0,006 до 1 мас.% в расчете на сухую массу композиции.
30. Состав по п.27, в котором содержание органических частиц составляют приблизительно от 0,01 до 5 мас.% в расчете на сухую массу композиции.
31. Состав по п.26, имеющий рН от 3 до 6.
32. Состав по п.26, имеющий рН от 3,5 до 5.
33. Состав по п.26, в котором количество стойких к кислоте частиц составляет приблизительно от 0,006 до 2 мас.% в расчете на сухую массу.
34. Состав по п.26, в котором содержание одной или нескольких фторзамещенных кислот составляет приблизительно от 5 до 1000 м.д.
35. Состав по п.26, в котором стойкие к кислоте частицы изменяют вязкость за три секунды и менее.
36. Состав для покрытий, по существу содержащий от 0,006 до 2 мас.%, в расчете на сухую массу, стойких к кислоте частиц и одну или нескольких фторзамещенных кислот, имеющих рН приблизительно от 3 до 6, при этом состав для покрытий в отвердевшем состоянии обеспечивает удельную плотность покрытия на металлическом субстрате от 8 до 30 мг/кв. фут (86,11-322,92 мг/м2).
37. Состав по п.36, в котором стойкие к кислоте частицы выбраны из группы, включающей модифицированные алюминием частицы, не модифицированные алюминием частицы и органические полимерные частицы.
38. Состав по п.36, в котором содержание стойких к кислоте частиц составляет приблизительно от 0,007 до 0,5 мас.% в расчете на сухую массу.
39. Состав по п.36, в котором содержание одной или нескольких фторзамещенных кислот составляет приблизительно от 5 до 1000 м.д.
40. Состав по п.36, в котором стойкие к кислоте частицы изменяют вязкость за три секунды и менее.