RU2002130497A - Двуосно-ориентированные полипропиленовые пленки - Google Patents
Двуосно-ориентированные полипропиленовые пленкиInfo
- Publication number
- RU2002130497A RU2002130497A RU2002130497/04A RU2002130497A RU2002130497A RU 2002130497 A RU2002130497 A RU 2002130497A RU 2002130497/04 A RU2002130497/04 A RU 2002130497/04A RU 2002130497 A RU2002130497 A RU 2002130497A RU 2002130497 A RU2002130497 A RU 2002130497A
- Authority
- RU
- Russia
- Prior art keywords
- polymer
- content
- range
- propylene
- copolymer
- Prior art date
Links
- 239000005026 oriented polypropylene Substances 0.000 title 1
- 229920001577 copolymer Polymers 0.000 claims 22
- 229920001155 polypropylene Polymers 0.000 claims 13
- 239000005977 Ethylene Substances 0.000 claims 11
- VGGSQFUCUMXWEO-UHFFFAOYSA-N ethene Chemical compound C=C VGGSQFUCUMXWEO-UHFFFAOYSA-N 0.000 claims 11
- 239000000203 mixture Substances 0.000 claims 11
- 229920000642 polymer Polymers 0.000 claims 9
- 125000004805 propylene group Chemical group [H]C([H])([H])C([H])([*:1])C([H])([H])[*:2] 0.000 claims 9
- 229920005604 random copolymer Polymers 0.000 claims 9
- 239000011127 biaxially oriented polypropylene Substances 0.000 claims 6
- CTQNGGLPUBDAKN-UHFFFAOYSA-N o-xylene Chemical compound CC1=CC=CC=C1C CTQNGGLPUBDAKN-UHFFFAOYSA-N 0.000 claims 5
- 239000008096 xylene Substances 0.000 claims 5
- 239000004711 α-olefin Substances 0.000 claims 5
- 238000002844 melting Methods 0.000 claims 3
- AXTGDCSMTYGJND-UHFFFAOYSA-N 1-dodecylazepan-2-one Chemical compound CCCCCCCCCCCCN1CCCCCC1=O AXTGDCSMTYGJND-UHFFFAOYSA-N 0.000 claims 1
- 239000000155 melt Substances 0.000 claims 1
- BLRPTPMANUNPDV-UHFFFAOYSA-N silane Chemical compound [SiH4] BLRPTPMANUNPDV-UHFFFAOYSA-N 0.000 claims 1
- 229910000077 silane Inorganic materials 0.000 claims 1
Claims (7)
1. Двуосно-ориентированная полипропиленовая пленка (ВОРР), у которой по меньшей мере один слой содержит пропиленовый полимер, содержащий по меньшей мере 0,8 мас.% этилена и возможно одного или нескольких С4-С10 α-олефинов, или пропиленовую полимерную композицию, содержащую по меньшей мере 0,8 мас.% одного или нескольких сомономеров, выбираемых из этилена и С4-С10 α-олефинов, причем упомянутые полимер или полимерная композиция обладают следующими признаками: 1) температура плавления 155°С или выше, 2) содержание фракции, растворимой в ксилоле при комнатной температуре (приблизительно 25°С), менее 3 мас.%, а величина отношения количества полимерной фракции, собранной при температурном диапазоне от 25 до 95°С, к количеству фракции, растворимой в ксилоле при комнатной температуре, превышает 8 мас.%/мас.%.
2. ВОРР по п.1, где скорость течения расплава (MFR в соответствии с ISO 1133, 230°С, нагрузка 2,16 кг) упомянутых пропиленовых полимера или полимерной композиции находится в диапазоне от 1 до 10 г/10 мин.
3. ВОРР по п.1, где по меньшей мере один слой содержит пропиленовый статистический сополимер (I), в котором, если в качестве сомономера присутствует только этилен, он содержится в диапазоне от 0,8 до 1,5 мас.% в расчете на массу полимера, а если присутствуют С4-С10 α-олефины, то их содержание в общем случае будет находиться в диапазоне от 1 до 4 мас.% в расчете на массу полимера.
4. ВОРР по п.1, где по меньшей мере один слой содержит пропиленовую полимерную композицию (II), содержащую первый пропиленовый (со)полимер (где сополимер представляет собой статистический сополимер) с содержанием этилена в диапазоне от 0 до 1,5 мас.% и второй пропиленовый статистический сополимер с содержанием этилена в диапазоне от 0,8 до 5 мас.%, причем массовое отношение содержания второго сополимера к содержанию первого (со)полимера находится в диапазоне от приблизительно 20:80 до приблизительно 80:20, а разница в содержании этилена между двумя сополимерами предпочтительно находится в диапазоне от 1 до 4 процентных единиц при расчете на массу рассматриваемого (со)полимера.
5. ВОРР по п.1 где по меньшей мере один слой содержит пропиленовую полимерную композицию (II), содержащую первый пропиленовый (со)полимер (где сополимер представляет собой статистический сополимер) с содержанием сомономера в диапазоне от 0 до 2 мас.% и второй пропиленовый статистический сополимер с содержанием сомономера в диапазоне от 1,5 до 12 мас.%, причем массовое отношение содержания второго сополимера к содержанию первого (со)полимера находится в диапазоне от приблизительно 20:80 до приблизительно 80:20, а разница в содержании сомономера между двумя предпочтительно находится в диапазоне от 1,5 до 10 процентных единиц при расчете на массу рассматриваемого (со)полимера, где упомянутый сомономер выбирают из С4-С10 α-олефинов и их смесей, при том, что этилен присутствует необязательно.
6. Пропиленовая полимерная композиция, содержащая первый пропиленовый (со)полимер (где сополимер представляет собой статистический сополимер) с содержанием этилена в диапазоне от 0 до 1,5 мас.% и второй пропиленовый статистический сополимер с содержанием этилена в диапазоне от 0,8 до 5 мас.%, причем массовое отношение содержания второго сополимера к содержанию первого (со)полимера находится в диапазоне от приблизительно 20:80 до приблизительно 80:20, а разница в содержании этилена между двумя сополимерами предпочтительно находится в диапазоне от 1 до 4 процентных единиц при расчете на массу рассматриваемого (со)полимера, причем упомянутая композиция обладает следующими признаками: 1) температура плавления 155°С или выше, 2) содержание фракции, растворимой в ксилоле при комнатной температуре (приблизительно 25°С), менее 3 мас.%, а величина отношения количества полимерной фракции, собранной в температурном диапазоне от 25 до 95°С, к количеству фракции, растворимой в ксилоле при комнатной температуре, превышает 8 мас.%/мас.%.
7. Пропиленовая полимерная композиция, содержащая первый пропиленовый (со)полимер (где сополимер представляет собой статистический сополимер) с содержанием сомономера в диапазоне от 0 до 2 мас.% и второй пропиленовый статистический сополимер с содержанием сомономера в диапазоне от 1,5 до 12 мас.%, причем массовое отношение содержания второго сополимера к содержанию первого (со)полимера находится в диапазоне от приблизительно 20:80 до приблизительно 80:20, а разница в содержании сомономера между двумя сополимерами предпочтительно находится в диапазоне от 1,5 до 10 процентных единиц при расчете на массу рассматриваемого (со)полимера, где упомянутый сомономер выбирают из С4-С10 α-олефинов и их смесей, при том, что этилен присутствует необязательно, причем упомянутая композиция обладает следующими признаками: 1) температура плавления 155°С или выше, 2) содержание фракции, растворимой в ксилоле при комнатной температуре (приблизительно 25°С), менее 3 мас.%, а величина отношения количества полимерной фракции, собранной в температурном диапазоне от 25 до 95°С, к количеству фракции, растворимой в ксилоле при комнатной температуре, превышает 8 мас.%/мас.%.