RU2002129220A - Моновинилиден-ароматические полимеры с улучшенными ударной вязкостью и жесткостью и способ их получения - Google Patents
Моновинилиден-ароматические полимеры с улучшенными ударной вязкостью и жесткостью и способ их получения Download PDFInfo
- Publication number
- RU2002129220A RU2002129220A RU2002129220/04A RU2002129220A RU2002129220A RU 2002129220 A RU2002129220 A RU 2002129220A RU 2002129220/04 A RU2002129220/04 A RU 2002129220/04A RU 2002129220 A RU2002129220 A RU 2002129220A RU 2002129220 A RU2002129220 A RU 2002129220A
- Authority
- RU
- Russia
- Prior art keywords
- rubber
- viscosity
- solution
- monovinylidene
- range
- Prior art date
Links
Classifications
-
- C—CHEMISTRY; METALLURGY
- C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
- C08F—MACROMOLECULAR COMPOUNDS OBTAINED BY REACTIONS ONLY INVOLVING CARBON-TO-CARBON UNSATURATED BONDS
- C08F12/00—Homopolymers and copolymers of compounds having one or more unsaturated aliphatic radicals, each having only one carbon-to-carbon double bond, and at least one being terminated by an aromatic carbocyclic ring
- C08F12/02—Monomers containing only one unsaturated aliphatic radical
-
- C—CHEMISTRY; METALLURGY
- C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
- C08F—MACROMOLECULAR COMPOUNDS OBTAINED BY REACTIONS ONLY INVOLVING CARBON-TO-CARBON UNSATURATED BONDS
- C08F279/00—Macromolecular compounds obtained by polymerising monomers on to polymers of monomers having two or more carbon-to-carbon double bonds as defined in group C08F36/00
- C08F279/02—Macromolecular compounds obtained by polymerising monomers on to polymers of monomers having two or more carbon-to-carbon double bonds as defined in group C08F36/00 on to polymers of conjugated dienes
-
- C—CHEMISTRY; METALLURGY
- C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
- C08F—MACROMOLECULAR COMPOUNDS OBTAINED BY REACTIONS ONLY INVOLVING CARBON-TO-CARBON UNSATURATED BONDS
- C08F257/00—Macromolecular compounds obtained by polymerising monomers on to polymers of aromatic monomers as defined in group C08F12/00
- C08F257/02—Macromolecular compounds obtained by polymerising monomers on to polymers of aromatic monomers as defined in group C08F12/00 on to polymers of styrene or alkyl-substituted styrenes
-
- C—CHEMISTRY; METALLURGY
- C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
- C08L—COMPOSITIONS OF MACROMOLECULAR COMPOUNDS
- C08L51/00—Compositions of graft polymers in which the grafted component is obtained by reactions only involving carbon-to-carbon unsaturated bonds; Compositions of derivatives of such polymers
- C08L51/003—Compositions of graft polymers in which the grafted component is obtained by reactions only involving carbon-to-carbon unsaturated bonds; Compositions of derivatives of such polymers grafted on to macromolecular compounds obtained by reactions only involving unsaturated carbon-to-carbon bonds
-
- C—CHEMISTRY; METALLURGY
- C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
- C08L—COMPOSITIONS OF MACROMOLECULAR COMPOUNDS
- C08L51/00—Compositions of graft polymers in which the grafted component is obtained by reactions only involving carbon-to-carbon unsaturated bonds; Compositions of derivatives of such polymers
- C08L51/04—Compositions of graft polymers in which the grafted component is obtained by reactions only involving carbon-to-carbon unsaturated bonds; Compositions of derivatives of such polymers grafted on to rubbers
Landscapes
- Chemical & Material Sciences (AREA)
- Health & Medical Sciences (AREA)
- Chemical Kinetics & Catalysis (AREA)
- Medicinal Chemistry (AREA)
- Polymers & Plastics (AREA)
- Organic Chemistry (AREA)
- Graft Or Block Polymers (AREA)
- Compositions Of Macromolecular Compounds (AREA)
- Manufacture Of Macromolecular Shaped Articles (AREA)
- Addition Polymer Or Copolymer, Post-Treatments, Or Chemical Modifications (AREA)
Claims (15)
1. Модифицированный каучуком моновинилиден - ароматический полимер, содержащий а) матрицу моновинилиден - ароматического полимера, b) диспергированные в ней частицы каучука, отличающийся тем, что частицы каучука получают из диенового каучука, содержащего I) от 20 до 80%, в расчете на общую массу упомянутых частиц каучука, компонента с высокой вязкостью раствора, величина вязкости которого находится в диапазоне от 110 до 500 сантипуаз, и II) от 80 до 20%, в расчете на общую массу упомянутых частиц каучука, компонента с низкой вязкостью раствора, величина вязкости которого находится в диапазоне от 1 до 100 сантипуаз, кроме того, характеризующиеся тем, что отношение вязкости раствора компонента с высокой вязкостью раствора к вязкости раствора компонента с низкой вязкостью раствора находится в диапазоне от 1,1 до 500, где оба компонента I и II имеют содержание 1,4-цис-звеньев, свыше 30%, и III) на каучук прививают моновинилиден - ароматический полимер в такой степени, что в виде привитых цепей на каучуке присутствует, по меньшей мере, 30% моновинилиден - ароматического полимера.
2. Модифицированный каучуком моновинилиден - ароматический полимер по п.1, где компонент с высокой вязкостью раствора отличается значением вязкости в диапазоне от 120 до 450 сантипуаз, компонент с низкой вязкостью раствора отличается значением вязкости в диапазоне от 5 до 95 сантипуаз, а отношение вязкостей растворов находится в диапазоне от 1,26 до 90.
3. Модифицированный каучуком моновинилиден - ароматический полимер по п.1, где компонент с высокой вязкостью раствора имеет значение вязкости в диапазоне от 150 до 430 сантипуаз, компонент с низкой вязкостью раствора имеет значение вязкости в диапазоне от 20 до 85 сантипуаз, а отношение вязкостей растворов находится в диапазоне от 1,76 до 21,5.
4. Модифицированный каучуком моновинилиден - ароматический полимер по п.1, где количество каучука в упомянутом полимере находится в диапазоне от 2 до 20% в расчете на общую массу упомянутого полимера.
5. Модифицированный каучуком моновинилиден - ароматический полимер по п.1, где частицы каучука диспергированы в виде малых и больших частиц, где усредненный по объему диаметр частиц для малых частиц находится в диапазоне от 0,1 до 2 мкм, а усредненный по объему диаметр частиц для больших частиц находится в диапазоне от 2 до 6 мкм.
6. Модифицированный каучуком моновинилиден - ароматический полимер по п.1, где моновинилиден - ароматическим полимером является полистирол.
7. Модифицированный каучуком моновинилиден - ароматический полимер по п.1, где каучуком является полибутадиен.
8. Модифицированный каучуком моновинилиден - ароматический полимер по п.1, где диеновый каучук разветвлен.
9. Модифицированный каучуком моновинилиден - ароматический полимер по п.1, где содержание 1,4-цис-звеньев в диеновом каучуке превышает 30%.
10. Способ получения модифицированного каучуком моновинилиден - ароматического полимера, включающий стадии (а) непрерывной подачи в систему реактора реакционной смеси, содержащей моновинилиден - ароматический мономер и растворенный диеновый каучук, (b) непрерывной полимеризации в системе реактора моновинилиден - ароматического мономера в присутствии растворенного диенового каучука в условиях, при которых впоследствии происходит обращение фаз, (с) непрерывного отвода из системы реактора упрочненного диеновым каучуком моновинилиден - ароматического полимера, где данный способ отличается тем, что (d) диеновый каучук, который растворяют в реакционной смеси, содержит I) от 20 до 80%, в расчете на общую массу упомянутого диенового каучука, компонента с высокой вязкостью раствора, величина вязкости которого находится в диапазоне от 120 до 500 сантипуаз, и II) от 80 до 20%, в расчете на общую массу упомянутого диенового каучука, компонента с низкой вязкостью раствора, величина вязкости которого находится в диапазоне от 1 до 100 сантипуаз, и, кроме этого, характеризуется тем, что отношение вязкости раствора компонента с высокой вязкостью раствора к вязкости раствора компонента с низкой вязкостью раствора находится в диапазоне от 1,2 до 500, где оба компонента I и II имеют содержание 1,4-цис-звеньев, свыше 30%, и необязательно (е) условия процесса до обращения фаз регулируют с целью получения из компонентов диенового каучука с высокой и низкой вязкостями раствора различающихся групп частиц диенового каучука, причем каждой группе соответствует отличный от другой средний размер частиц каучука.
11. Способ по п.10, где моновинилиден - ароматическим полимером является полистирол.
12. Способ по п.10, где каучуком является полибутадиен.
13. Способ по п.10, где диеновый каучук разветвлен.
14. Способ по п.10, где содержание 1,4-цис-звеньев в диеновом каучуке превышает 30%.
15. Изделие, полученное из модифицированного каучуком полимера по п.1.