PL2762600T3 - Blacha stalowa cienka cynkowana zanurzeniowo na gorąco oraz sposób jej wytwarzania - Google Patents

Blacha stalowa cienka cynkowana zanurzeniowo na gorąco oraz sposób jej wytwarzania

Info

Publication number
PL2762600T3
PL2762600T3 PL12834953T PL12834953T PL2762600T3 PL 2762600 T3 PL2762600 T3 PL 2762600T3 PL 12834953 T PL12834953 T PL 12834953T PL 12834953 T PL12834953 T PL 12834953T PL 2762600 T3 PL2762600 T3 PL 2762600T3
Authority
PL
Poland
Prior art keywords
hot
steel sheet
galvanized steel
dip galvanized
producing same
Prior art date
Application number
PL12834953T
Other languages
English (en)
Inventor
Masafumi Azuma
Chisato Wakabayashi
Takayuki Nozaki
Manabu Takahashi
Nobuhiro Fujita
Original Assignee
Nippon Steel & Sumitomo Metal Corporation
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Nippon Steel & Sumitomo Metal Corporation filed Critical Nippon Steel & Sumitomo Metal Corporation
Publication of PL2762600T3 publication Critical patent/PL2762600T3/pl

Links

Classifications

    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B32—LAYERED PRODUCTS
    • B32B—LAYERED PRODUCTS, i.e. PRODUCTS BUILT-UP OF STRATA OF FLAT OR NON-FLAT, e.g. CELLULAR OR HONEYCOMB, FORM
    • B32B15/00—Layered products comprising a layer of metal
    • B32B15/01—Layered products comprising a layer of metal all layers being exclusively metallic
    • B32B15/013—Layered products comprising a layer of metal all layers being exclusively metallic one layer being formed of an iron alloy or steel, another layer being formed of a metal other than iron or aluminium
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D8/00—Modifying the physical properties of ferrous metals or ferrous alloys by deformation combined with, or followed by, heat treatment
    • C21D8/02—Modifying the physical properties of ferrous metals or ferrous alloys by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips
    • C21D8/0221—Modifying the physical properties of ferrous metals or ferrous alloys by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips characterised by the working steps
    • C21D8/0226—Hot rolling
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D8/00—Modifying the physical properties of ferrous metals or ferrous alloys by deformation combined with, or followed by, heat treatment
    • C21D8/02—Modifying the physical properties of ferrous metals or ferrous alloys by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips
    • C21D8/0221—Modifying the physical properties of ferrous metals or ferrous alloys by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips characterised by the working steps
    • C21D8/0236—Cold rolling
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D8/00—Modifying the physical properties of ferrous metals or ferrous alloys by deformation combined with, or followed by, heat treatment
    • C21D8/02—Modifying the physical properties of ferrous metals or ferrous alloys by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips
    • C21D8/0247—Modifying the physical properties of ferrous metals or ferrous alloys by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips characterised by the heat treatment
    • C21D8/0273—Final recrystallisation annealing
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C18/00—Alloys based on zinc
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/001—Ferrous alloys, e.g. steel alloys containing N
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/002—Ferrous alloys, e.g. steel alloys containing In, Mg, or other elements not provided for in one single group C22C38/001 - C22C38/60
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/02—Ferrous alloys, e.g. steel alloys containing silicon
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/04—Ferrous alloys, e.g. steel alloys containing manganese
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/06—Ferrous alloys, e.g. steel alloys containing aluminium
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/12—Ferrous alloys, e.g. steel alloys containing tungsten, tantalum, molybdenum, vanadium, or niobium
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/14—Ferrous alloys, e.g. steel alloys containing titanium or zirconium
    • C—CHEMISTRY; METALLURGY
    • C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
    • C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
    • C23C2/00—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor
    • C23C2/02—Pretreatment of the material to be coated, e.g. for coating on selected surface areas
    • C—CHEMISTRY; METALLURGY
    • C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
    • C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
    • C23C2/00—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor
    • C23C2/02—Pretreatment of the material to be coated, e.g. for coating on selected surface areas
    • C23C2/022—Pretreatment of the material to be coated, e.g. for coating on selected surface areas by heating
    • C23C2/0224—Two or more thermal pretreatments
    • C—CHEMISTRY; METALLURGY
    • C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
    • C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
    • C23C2/00—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor
    • C23C2/02—Pretreatment of the material to be coated, e.g. for coating on selected surface areas
    • C23C2/024—Pretreatment of the material to be coated, e.g. for coating on selected surface areas by cleaning or etching
    • C—CHEMISTRY; METALLURGY
    • C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
    • C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
    • C23C2/00—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor
    • C23C2/04—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor characterised by the coating material
    • C23C2/06—Zinc or cadmium or alloys based thereon
    • C—CHEMISTRY; METALLURGY
    • C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
    • C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
    • C23C2/00—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor
    • C23C2/26—After-treatment
    • C23C2/28—Thermal after-treatment, e.g. treatment in oil bath
    • C23C2/29—Cooling or quenching
    • C—CHEMISTRY; METALLURGY
    • C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
    • C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
    • C23C2/00—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor
    • C23C2/34—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor characterised by the shape of the material to be treated
    • C23C2/36—Elongated material
    • C23C2/40—Plates; Strips
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D2211/00—Microstructure comprising significant phases
    • C21D2211/002—Bainite
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D2211/00—Microstructure comprising significant phases
    • C21D2211/008—Martensite
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D8/00—Modifying the physical properties of ferrous metals or ferrous alloys by deformation combined with, or followed by, heat treatment
    • C21D8/02—Modifying the physical properties of ferrous metals or ferrous alloys by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips
    • C21D8/0278—Modifying the physical properties of ferrous metals or ferrous alloys by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips involving a particular surface treatment 
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D9/00—Heat treatment, e.g. annealing, hardening, quenching or tempering, adapted for particular articles; Furnaces therefor
    • C21D9/46—Heat treatment, e.g. annealing, hardening, quenching or tempering, adapted for particular articles; Furnaces therefor for sheet metals
    • Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
    • Y10—TECHNICAL SUBJECTS COVERED BY FORMER USPC
    • Y10T—TECHNICAL SUBJECTS COVERED BY FORMER US CLASSIFICATION
    • Y10T428/00—Stock material or miscellaneous articles
    • Y10T428/12—All metal or with adjacent metals
    • Y10T428/12493—Composite; i.e., plural, adjacent, spatially distinct metal components [e.g., layers, joint, etc.]
    • Y10T428/12771—Transition metal-base component
    • Y10T428/12785—Group IIB metal-base component
    • Y10T428/12792—Zn-base component
    • Y10T428/12799—Next to Fe-base component [e.g., galvanized]

Landscapes

  • Chemical & Material Sciences (AREA)
  • Engineering & Computer Science (AREA)
  • Materials Engineering (AREA)
  • Mechanical Engineering (AREA)
  • Metallurgy (AREA)
  • Organic Chemistry (AREA)
  • Chemical Kinetics & Catalysis (AREA)
  • Physics & Mathematics (AREA)
  • Thermal Sciences (AREA)
  • Crystallography & Structural Chemistry (AREA)
  • Oil, Petroleum & Natural Gas (AREA)
  • Heat Treatment Of Sheet Steel (AREA)
  • Coating With Molten Metal (AREA)
PL12834953T 2011-09-30 2012-09-28 Blacha stalowa cienka cynkowana zanurzeniowo na gorąco oraz sposób jej wytwarzania PL2762600T3 (pl)

Applications Claiming Priority (4)

Application Number Priority Date Filing Date Title
JP2011217108 2011-09-30
JP2011218046 2011-09-30
EP12834953.7A EP2762600B1 (en) 2011-09-30 2012-09-28 Hot-dip galvanized steel sheet and process for producing same
PCT/JP2012/075215 WO2013047820A1 (ja) 2011-09-30 2012-09-28 溶融亜鉛めっき鋼板及びその製造方法

Publications (1)

Publication Number Publication Date
PL2762600T3 true PL2762600T3 (pl) 2019-09-30

Family

ID=47995843

Family Applications (1)

Application Number Title Priority Date Filing Date
PL12834953T PL2762600T3 (pl) 2011-09-30 2012-09-28 Blacha stalowa cienka cynkowana zanurzeniowo na gorąco oraz sposób jej wytwarzania

Country Status (14)

Country Link
US (1) US10407760B2 (pl)
EP (1) EP2762600B1 (pl)
JP (1) JP5569647B2 (pl)
KR (3) KR101935112B1 (pl)
CN (1) CN103827341B (pl)
BR (1) BR112014007500A2 (pl)
CA (1) CA2850044C (pl)
ES (1) ES2732799T3 (pl)
MX (1) MX373591B (pl)
PL (1) PL2762600T3 (pl)
RU (1) RU2566131C1 (pl)
TW (1) TWI500780B (pl)
WO (1) WO2013047820A1 (pl)
ZA (1) ZA201402259B (pl)

Families Citing this family (75)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
CN103827341B (zh) * 2011-09-30 2016-08-31 新日铁住金株式会社 热浸镀锌钢板及其制造方法
JP6246621B2 (ja) * 2013-05-08 2017-12-13 株式会社神戸製鋼所 引張強度が１１８０ＭＰａ以上の強度−曲げ性バランスに優れた溶融亜鉛めっき鋼板もしくは合金化溶融亜鉛めっき鋼板
CN105452509B (zh) * 2013-08-02 2017-06-30 杰富意钢铁株式会社 高强度高杨氏模量钢板及其制造方法
KR101753511B1 (ko) 2013-08-02 2017-07-19 제이에프이 스틸 가부시키가이샤 고강도 고영률 강판 및 그 제조 방법
JP5821912B2 (ja) * 2013-08-09 2015-11-24 Ｊｆｅスチール株式会社 高強度冷延鋼板およびその製造方法
MX387576B (es) * 2013-12-11 2025-03-18 Arcelormittal Acero martensítico con resistencia a fractura retardada y método de fabricación.
WO2015185956A1 (en) * 2014-06-06 2015-12-10 ArcelorMittal Investigación y Desarrollo, S.L. High strength multiphase galvanized steel sheet, production method and use
PL3492608T3 (pl) 2014-07-03 2020-08-24 Arcelormittal Sposób wytwarzania niepowlekanej blachy stalowej o ultrawysokiej wytrzymałości oraz wytworzona blacha
US10507629B2 (en) 2014-11-05 2019-12-17 Nippon Steel Corporation Hot-dip galvanized steel sheet
MX2017005507A (es) 2014-11-05 2017-06-20 Nippon Steel & Sumitomo Metal Corp Hoja de acero galvanizad por inmersion en caliente.
ES2748019T3 (es) 2014-11-05 2020-03-12 Nippon Steel Corp Lámina de acero galvanizada por inmersión en caliente
EP3243923B1 (en) * 2015-01-07 2019-10-23 Posco Super high strength plated steel sheet having tensile strength of 1300 mpa or more
JP6082451B2 (ja) * 2015-03-18 2017-02-15 株式会社神戸製鋼所 熱間プレス用鋼板およびその製造方法
JP6453140B2 (ja) * 2015-03-31 2019-01-16 株式会社神戸製鋼所 切断端面の耐遅れ破壊性に優れた高強度鋼板およびその製造方法
CN107636184A (zh) * 2015-06-11 2018-01-26 新日铁住金株式会社 合金化热浸镀锌钢板及其制造方法
CN107849667B (zh) 2015-07-13 2020-06-30 日本制铁株式会社 钢板、热浸镀锌钢板和合金化热浸镀锌钢板、以及它们的制造方法
EP3323907B1 (en) 2015-07-13 2020-03-04 Nippon Steel Corporation Steel sheet, hot-dip galvanized steel sheet, galvannealed steel sheet, and manufacturing methods therefor
TWI551695B (zh) * 2015-07-13 2016-10-01 新日鐵住金股份有限公司 鋼板、熔融鍍鋅鋼板及合金化熔融鍍鋅鋼板以及其等之製造方法
JP6724320B2 (ja) * 2015-09-10 2020-07-15 日本製鉄株式会社 伸びと穴広げ性に優れた高強度溶融亜鉛めっき鋼板及びその製造方法
JP2017066508A (ja) * 2015-10-02 2017-04-06 株式会社神戸製鋼所 熱間プレス用亜鉛めっき鋼板および熱間プレス成形品の製造方法
JP2017075394A (ja) * 2015-10-16 2017-04-20 株式会社神戸製鋼所 高強度溶融亜鉛めっき鋼板及び高強度溶融亜鉛めっき鋼板の製造方法
KR101758485B1 (ko) * 2015-12-15 2017-07-17 주식회사 포스코 표면품질 및 점 용접성이 우수한 고강도 용융아연도금강판 및 그 제조방법
JP6164280B2 (ja) 2015-12-22 2017-07-19 Ｊｆｅスチール株式会社 表面外観および曲げ性に優れるＭｎ含有合金化溶融亜鉛めっき鋼板およびその製造方法
JP2017115205A (ja) * 2015-12-24 2017-06-29 日新製鋼株式会社 めっき密着性に優れた溶融Ｚｎ−Ａｌ−Ｍｇ合金めっき鋼板の製造方法
KR102490989B1 (ko) * 2015-12-29 2023-01-19 아르셀러미탈 초고강도 갈바닐링된 강판을 제조하기 위한 방법 및 획득된 갈바닐링된 강판
KR102170060B1 (ko) * 2016-01-27 2020-10-26 제이에프이 스틸 가부시키가이샤 고항복비형 고강도 아연 도금 강판 및 그의 제조 방법
KR101767818B1 (ko) 2016-03-08 2017-08-11 주식회사 포스코 소부경화성 및 내시효성이 우수한 용융 아연계 도금강판 및 그 제조방법
US11993823B2 (en) 2016-05-10 2024-05-28 United States Steel Corporation High strength annealed steel products and annealing processes for making the same
BR112018073175B1 (pt) 2016-05-10 2022-08-16 United States Steel Corporation Produto de chapa de aço laminada a frio de alta resistência, e, método para produzir um produto de chapa de aço laminada a frio de alta resistência
US11560606B2 (en) 2016-05-10 2023-01-24 United States Steel Corporation Methods of producing continuously cast hot rolled high strength steel sheet products
CN105925887B (zh) * 2016-06-21 2018-01-30 宝山钢铁股份有限公司 一种980MPa级热轧铁素体贝氏体双相钢及其制造方法
CN105908089B (zh) * 2016-06-28 2019-11-22 宝山钢铁股份有限公司 一种热浸镀低密度钢及其制造方法
JP6852736B2 (ja) 2016-07-15 2021-03-31 日本製鉄株式会社 溶融亜鉛めっき冷延鋼板
TWI613300B (zh) * 2016-09-06 2018-02-01 新日鐵住金股份有限公司 高強度冷軋鋼板
MX2019002662A (es) * 2016-09-13 2019-07-15 Nippon Steel Corp Lamina de acero.
JP2019537666A (ja) 2016-11-04 2019-12-26 ニューコア・コーポレーション 多相冷間圧延超高強度鋼
US11021776B2 (en) 2016-11-04 2021-06-01 Nucor Corporation Method of manufacture of multiphase, hot-rolled ultra-high strength steel
KR101889181B1 (ko) 2016-12-19 2018-08-16 주식회사 포스코 굽힘성 및 신장플랜지성이 우수한 고장력강 및 이의 제조방법
US11377708B2 (en) 2016-12-27 2022-07-05 Jfe Steel Corporation High-strength galvanized steel sheet and method for producing the same
WO2018138791A1 (ja) * 2017-01-25 2018-08-02 新日鐵住金株式会社 鋼板
BR112019006995A2 (pt) * 2017-01-30 2019-06-25 Nippon Steel & Sumitomo Metal Corp chapa de aço
KR20190044669A (ko) * 2017-01-31 2019-04-30 닛폰세이테츠 가부시키가이샤 강판
WO2018146828A1 (ja) * 2017-02-10 2018-08-16 Ｊｆｅスチール株式会社 高強度亜鉛めっき鋼板及びその製造方法
CN107287542A (zh) * 2017-05-18 2017-10-24 当涂县宏宇金属炉料有限责任公司 一种加强热浸镀锌钢板防腐蚀性能的处理工艺
DE102017218704A1 (de) 2017-10-19 2019-04-25 Thyssenkrupp Ag Verfahren zur Herstellung eines mit einem metallischen, vor Korrosion schützenden Überzug versehenen Stahlbauteils
WO2019092468A1 (en) 2017-11-08 2019-05-16 Arcelormittal A hot-dip coated steel sheet
WO2019092467A1 (en) 2017-11-08 2019-05-16 Arcelormittal A galvannealed steel sheet
US11208705B2 (en) 2017-11-15 2021-12-28 Nippon Steel Corporation High-strength cold-rolled steel sheet
WO2019122965A1 (en) 2017-12-19 2019-06-27 Arcelormittal Cold rolled and coated steel sheet and a method of manufacturing thereof
KR102020411B1 (ko) 2017-12-22 2019-09-10 주식회사 포스코 가공성이 우수한 고강도 강판 및 이의 제조방법
KR102031454B1 (ko) 2017-12-24 2019-10-11 주식회사 포스코 저온 밀착성과 가공성이 우수한 용융아연도금강판 및 그 제조방법
US11492677B2 (en) 2017-12-27 2022-11-08 Jfe Steel Corporation High-strength steel sheet and method for producing the same
US11884990B2 (en) * 2018-02-07 2024-01-30 Tata Steel Nederland Technology B.V. High strength hot rolled or cold rolled and annealed steel and method of producing it
WO2019189849A1 (ja) 2018-03-30 2019-10-03 Ｊｆｅスチール株式会社 高強度亜鉛めっき鋼板、高強度部材およびそれらの製造方法
CN111971408B (zh) * 2018-03-30 2021-10-29 日本制铁株式会社 钢板及其制造方法
WO2019194251A1 (ja) * 2018-04-03 2019-10-10 日本製鉄株式会社 鋼板及び鋼板の製造方法
WO2020058748A1 (en) 2018-09-20 2020-03-26 Arcelormittal Cold rolled and coated steel sheet and a method of manufacturing thereof
WO2020065381A1 (en) 2018-09-28 2020-04-02 Arcelormittal Hot rolled steel sheet and a method of manufacturing thereof
KR102222614B1 (ko) * 2018-11-27 2021-03-05 주식회사 포스코 수소취성 저항성이 우수한 초고강도 냉연강판 및 그 제조 방법
EP3992314A4 (en) * 2019-06-28 2023-07-19 Nippon Steel Corporation GALVANISED STEEL
JP2021014605A (ja) * 2019-07-10 2021-02-12 株式会社神戸製鋼所 溶融亜鉛めっき鋼板および合金化溶融亜鉛めっき鋼板の製造方法
US20210040578A1 (en) * 2019-08-07 2021-02-11 United States Steel Corporation High ductility zinc-coated steel sheet products
CN110564928A (zh) * 2019-10-18 2019-12-13 山东钢铁集团日照有限公司 一种生产不同屈服强度级别热镀锌dp980钢的方法
KR102321301B1 (ko) * 2019-12-09 2021-11-02 주식회사 포스코 내해수성이 우수한 구조용 강판 및 이의 제조방법
US12378626B2 (en) 2020-02-13 2025-08-05 Jfe Steel Corporation High-strength steel sheet and method for manufacturing the same
CN112267069B (zh) * 2020-09-30 2022-03-29 江苏省沙钢钢铁研究院有限公司 2100MPa级镀锌钢丝用盘条及其制造方法
KR102502605B1 (ko) * 2020-12-18 2023-02-24 주식회사 포스코 표면품질과 전기저항 점용접성이 우수한 고강도 용융아연도금 강판 및 그 제조방법
KR102457023B1 (ko) * 2020-12-21 2022-10-21 주식회사 포스코 표면품질과 점 용접성이 우수한 고강도 용융아연도금 강판 및 그 제조방법
CN116635541B (zh) * 2020-12-24 2025-07-25 杰富意钢铁株式会社 热浸镀锌钢板及其制造方法
MX2023012578A (es) * 2021-04-27 2023-10-31 Nippon Steel Corp Miembro soldado de acero.
CN117242200B (zh) * 2021-05-21 2026-01-13 日本制铁株式会社 合金化热浸镀锌钢板
KR20240037287A (ko) 2021-08-27 2024-03-21 닛폰세이테츠 가부시키가이샤 강판 및 프레스 성형품
CN114107818B (zh) * 2021-11-19 2023-03-28 本钢板材股份有限公司 一种1000MPa级热镀锌双相钢及其生产方法
CN114875336A (zh) * 2022-05-31 2022-08-09 山东钢铁集团日照有限公司 一种增塑性热镀锌复相钢的生产调控方法
MY206044A (en) * 2024-03-28 2024-11-26 Wei Dat Steel Wire Sdn Bhd Steel Product and Its Producing Method Thereof

Family Cites Families (23)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JPS59219473A (ja) 1983-05-26 1984-12-10 Nippon Steel Corp カラ−エツチング液及びエツチング方法
JPH11293383A (ja) 1998-04-09 1999-10-26 Nippon Steel Corp 水素性欠陥の少ない厚鋼板およびその製造方法
JP3882474B2 (ja) * 2000-07-06 2007-02-14 住友金属工業株式会社 金属板の熱間プレス成形方法
US7267890B2 (en) * 2001-06-06 2007-09-11 Nippon Steel Corporation High-strength hot-dip galvanized steel sheet and hot-dip galvannealed steel sheet having fatigue resistance corrosion resistance ductility and plating adhesion after servere deformation and a method of producing the same
PL1634975T3 (pl) 2003-03-31 2010-11-30 Nippon Steel Corp Stopowana blacha stalowa powlekana zanurzeniowo na gorąco cynkiem oraz sposób jej wytwarzania
PL1612288T3 (pl) 2003-04-10 2011-02-28 Nippon Steel Corp Sposób wytwarzania blachy stalowej o wysokiej wytrzymałości powlekanej na gorąco cynkiem
JP4192051B2 (ja) 2003-08-19 2008-12-03 新日本製鐵株式会社 高強度合金化溶融亜鉛めっき鋼板の製造方法と製造設備
CN101336308B (zh) * 2006-01-30 2012-08-29 新日本制铁株式会社 成形性及镀覆性优良的高强度热浸镀锌钢板和高强度合金化热浸镀锌钢板及其制造方法和制造装置
JP4837459B2 (ja) * 2006-06-30 2011-12-14 新日本製鐵株式会社 外観が良好な耐食性に優れた高強度溶融亜鉛めっき鋼板及びその製造方法
JP2007270176A (ja) * 2006-03-30 2007-10-18 Nippon Steel Corp 表面外観及びめっき密着性に優れた合金化溶融亜鉛めっき鋼板
JP4411326B2 (ja) 2007-01-29 2010-02-10 株式会社神戸製鋼所 リン酸塩処理性に優れた高強度合金化溶融亜鉛めっき鋼板
JP5369663B2 (ja) * 2008-01-31 2013-12-18 Ｊｆｅスチール株式会社 加工性に優れた高強度溶融亜鉛めっき鋼板およびその製造方法
JP4894863B2 (ja) * 2008-02-08 2012-03-14 Ｊｆｅスチール株式会社 加工性に優れた高強度溶融亜鉛めっき鋼板およびその製造方法
JP5402007B2 (ja) * 2008-02-08 2014-01-29 Ｊｆｅスチール株式会社 加工性に優れた高強度溶融亜鉛めっき鋼板およびその製造方法
JP5438302B2 (ja) * 2008-10-30 2014-03-12 株式会社神戸製鋼所 加工性に優れた高降伏比高強度の溶融亜鉛めっき鋼板または合金化溶融亜鉛めっき鋼板とその製造方法
BRPI1007868B1 (pt) * 2009-03-03 2020-09-15 Hexagon Technology As Aparelho compreendendo gatilho de liga de memória de forma para válvula de alívio de pressão
JP4737319B2 (ja) * 2009-06-17 2011-07-27 Ｊｆｅスチール株式会社 加工性および耐疲労特性に優れた高強度合金化溶融亜鉛めっき鋼板およびその製造方法
JP5435340B2 (ja) * 2009-07-17 2014-03-05 富士ゼロックス株式会社 蓋装置および画像形成装置
US20110019800A1 (en) * 2009-07-24 2011-01-27 Martin Spahn X-ray detector for recording x-ray images and x-ray recording system
JP4949536B2 (ja) * 2009-11-30 2012-06-13 新日本製鐵株式会社 耐水素脆化特性に優れた引張最大強度９００ＭＰａ以上の高強度鋼板及びその製造方法
JP5499663B2 (ja) * 2009-11-30 2014-05-21 新日鐵住金株式会社 機械切断特性に優れた引張最大強度９００ＭＰａ以上の高強度冷延鋼板及びその製造方法、並びに、高強度亜鉛めっき鋼板及びその製造方法
CA2782777C (en) * 2010-01-13 2014-11-18 Nippon Steel Corporation High tensile steel sheet superior in formability and method of manufacturing the same
CN103827341B (zh) * 2011-09-30 2016-08-31 新日铁住金株式会社 热浸镀锌钢板及其制造方法

Also Published As

Publication number Publication date
RU2566131C1 (ru) 2015-10-20
EP2762600A4 (en) 2015-09-23
ES2732799T3 (es) 2019-11-26
EP2762600B1 (en) 2019-04-17
WO2013047820A1 (ja) 2013-04-04
MX2014003716A (es) 2014-06-23
KR20160075850A (ko) 2016-06-29
BR112014007500A2 (pt) 2017-04-04
KR101951081B1 (ko) 2019-02-21
KR20160075849A (ko) 2016-06-29
TWI500780B (zh) 2015-09-21
JPWO2013047820A1 (ja) 2015-03-30
CA2850044A1 (en) 2013-04-04
MX373591B (es) 2020-05-15
EP2762600A1 (en) 2014-08-06
JP5569647B2 (ja) 2014-08-13
ZA201402259B (en) 2015-04-29
US20140234657A1 (en) 2014-08-21
CN103827341A (zh) 2014-05-28
CN103827341B (zh) 2016-08-31
KR101935112B1 (ko) 2019-01-03
CA2850044C (en) 2016-08-23
TW201319268A (zh) 2013-05-16
KR20140068122A (ko) 2014-06-05
US10407760B2 (en) 2019-09-10

Similar Documents

Publication Publication Date Title
PL2762600T3 (pl) Blacha stalowa cienka cynkowana zanurzeniowo na gorąco oraz sposób jej wytwarzania
PL2762579T3 (pl) Blacha stalowa cienka cynkowana na gorąco o dużej wytrzymałości i sposób jej wytwarzania
EP2811047A4 (en) FIREPLATED STEEL PLATE AND METHOD OF MANUFACTURING THEREOF
PL2738280T3 (pl) Blacha stalowa cienka ocynkowana o dużej wytrzymałości mająca doskonałą zginalność oraz sposób jej wytwarzania
PL2835440T3 (pl) Blacha stalowa cienka walcowana na gorąco i cynkowana z przeżarzaniem zanurzeniowo na gorąco oraz sposób jej wytwarzania
ZA201402256B (en) High-strength hot-dip galvanized steel sheet
PL2716783T3 (pl) Blacha stalowa cienka walcowana na gorąco i sposób jej wytwarzania
ZA201402216B (en) Galvanized steel sheet and method of manufacturing the same
PL2692895T3 (pl) Blacha stalowa cienka walcowana na zimno i sposób jej wytwarzania
AU2012276644A1 (en) High-corrosion-resistance hot-dip galvanized steel sheet having excellent appearance uniformity and manufacturing method thereof
ZA201400359B (en) Hot-dip plated cold-rolled steel sheet and process for producing same
ZA201307002B (en) Hot-rolled steel sheet and associated production method
EP2762581A4 (en) HOT-ROLLED STEEL PLATE AND MANUFACTURING METHOD THEREFOR
PL2738276T3 (pl) Blacha stalowa cienka ocynkowana o dużej wytrzymałości i blacha stalowa cienka o dużej wytrzymałości mająca doskonałą formowalność oraz sposób ich wytwarzania
PL2918696T3 (pl) Stopowa blacha stalowa cienka cynkowana zanurzeniowo na gorąco i sposób jej wytwarzania
PL2653582T3 (pl) Blacha stalowa cienka cynkowana zanurzeniowo na gorąco i sposób jej wytwarzania
ZA201402308B (en) Alloyed hot-dip galvanized steel sheet
EP2762584A4 (en) HOT-ROLLED STEEL SHEET, AND METHOD FOR MANUFACTURING THE SAME
EP2735623A4 (en) HIGH STRENGTH STEEL SHEET FOR HOT FORMING AND METHOD FOR MANUFACTURING THE SAME
PL2610357T3 (pl) Blacha stalowa cienka walcowana na zimno i sposób jej wytwarzania
PL2944705T3 (pl) Stopowa blacha stalowa cynkowana zanurzeniowo na gorąco i sposób jej wytwarzania
EP2548664A4 (en) Process for producing hot-rolled steel sheet and process for producing hot-dip galvanized steel sheet
EP2781615A4 (en) THIN STEEL SHEET AND PROCESS FOR PRODUCING THE SAME
EP2796584A4 (en) HIGH STRENGTH STEEL SHEET AND METHOD FOR MANUFACTURING THE SAME
MY165649A (en) Molten zn-al alloy-plated steel sheet and manufacturing method thereof