PL151581B1 - Method of manufacturing of hydrogel dressing - Google Patents

Method of manufacturing of hydrogel dressing

Info

Publication number
PL151581B1
PL151581B1 PL1986263410A PL26341086A PL151581B1 PL 151581 B1 PL151581 B1 PL 151581B1 PL 1986263410 A PL1986263410 A PL 1986263410A PL 26341086 A PL26341086 A PL 26341086A PL 151581 B1 PL151581 B1 PL 151581B1
Authority
PL
Poland
Prior art keywords
weight
percent
dressing
agar
synthetic
Prior art date
Application number
PL1986263410A
Other languages
English (en)
Other versions
PL263410A1 (en
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed filed Critical
Priority to PL1986263410A priority Critical patent/PL151581B1/pl
Priority to DE19873744289 priority patent/DE3744289A1/de
Priority to DD87311494A priority patent/DD273200A5/de
Priority to GB8730243A priority patent/GB2200643B/en
Priority to HU876086A priority patent/HU204866B/hu
Priority to US07/140,150 priority patent/US4871490A/en
Publication of PL263410A1 publication Critical patent/PL263410A1/xx
Publication of PL151581B1 publication Critical patent/PL151581B1/pl

Description

RZECZPOSPOLITA POLSKA OPIS PATENTOWY 151581
Patent dodatkowy CZYTELHU
do patentu nr- 0 G fl lłi A
URZĄD Zgłoszono: 12 3θ /Ρ· 263410/ Pierwszeństwo - Int. Cl.5 A61L 15/03
PATENTOWY Zgłoszenie ogłoszono: B8 08 18
RP Opis patentowy opublikowano: 1991 02 28
Twórcy wynalazku: Janusz Rosiak, Anna Rucińska-Rybus, Władysław Pękala
Uprawniony z patentu: Politechnika Łódzka,
Łódź /Rolska/
SPOSÓB WYTWARZANIA OPATRUNKÓW HYDROŻELOWYCH
Przedmiotem wynalazku jest sposób wytwarzania opatrunków hydrożelowych.
Znany jest sposób wytwarzania opatrunków w postaci żeli biologicznych, polegający na sporządzeniu wodnej zawiesiny polimeru naturalnego tj. żelatyny, zawierającej ponadto pektyny, substancje bakteriobójcze, sole żelaza dwuwartościowego oraz ewentualnie karboksymetylocelulozę i poliizobutylen, którą poddaje się sterylizacji. Opatrunki otrzymane tym sposobem mają postać papki i muszą byó nanoszone na ranę w postaci warstwy o grubości co najmniej 3 cm, przy czym znajdują one zastosowanie prawie wyłącznie do leczenia łagodnych poparzeń.
Znane są także sposoby wytwarzania opatrunków hydrożelowych, polegające na tym, że polimer syntetyczny tj. poliakryloamid lub jego mieszaninę z polimerem naturalnym poddaje się polimeryzacji i sieciowaniu chemicznemu, następnie konfekcjonuje i poddaje sterylizacji. Niedogodnością tych sposobów jest konieczność usunięcia z takich opatrunków katalizatorów, inicjatorów i nie zużytych reagentów procesu polimeryzacji i sieciowania chemicznego, co jest operacją skomplikowaną i pracochłonną.
Znany jest także, z polskiego opisu patentowego nr 128 392, sposób wytwarzania opatrunków zawierających środki lecznicze, polegający na tym, że na podłoże mechaniczne opatrunku, po lub przed nasyceniem go lekiem, nanosi się warstwę żelu hydrofiłowego, otrzymanego w wyniku radiacyjnej polimeryzacji polimerów syntetycznych takich jak poliakryloamid, poliwinylopirolidon, alkohol poliwinylowy, politlenek etylenu, ich monomerów bądź ich mieszanin, po czym opatrunek suszy się i sterylizuje. Opatrunki te charakteryzują się wprawdzie stosunkowo długim czasem uwalniania leku, a żel stosowany do ich otrzymania nie zawiera domieszek żadnych katalizatorów i substancji chemicznych, ale nie stanowią dostatecznego zabezpieczenia przed utratą wody i przedostaniem się bakterii do rany, są nieprzeźroczyste, co uniemożliwia obserwaoję procesu gojenia się rany, a ponadto długi i skomplikowany jest proces ich wytwarzania·
151 5B1
151 581
Sposób wytwarzanie opatrunków hydrożelowyoh z polimerów syntetycznych i naturalnych, na drodze polimeryzacji i sieciowania, według wynalazku polega na tym, że wodny roztwór poliwinylopirolidonu lub jego monomeru, agaru, poliglikolu etylenowego lub poliglikolu propylenowego, o składzie w procentach wagowych: 2-10% poliwinylopirolidonu lub jego monomeru, nie więcej niż 5% agaru, nie mniej niż 75% wody destylowanej i 1-3% poliglikolu etylenowego lub propylenowego, wylewa się do formy nadającej kształt opatrunkowi, szczelnie zamyka w tej formie i poddaje napromieniowaniu dawką promieniowania jonizującego nie mniejszą niż 25 kGy.
Opatrunki otrzymane sposobem według wynalazku znajdują zastosowanie do opatrywania wszelkich rodzajów ran, cechuje je duża elastyczność, wystarczająco dobra przylepność do skóry, przeźroczystość, dzięki czemu zapobiegają przedostaniu się bakterii do rany, umożliwiają obserwację procesu gojenia się rany oraz chronią przed utratą wody. Opatrunki otrzymane sposobem według wynalazku posiadają następujące cechy:
- wytrzymałość na rozciąganie - 20-40 kPa /próby wiosełkowe/,
- wydłużenie względne przy zerwaniu - 140-275%,
- sorpcja wody - 50-140% w stosunku do masy wyjściowej opatrunku,
- przepuszczalność tlenu - 5 x 10 urno la/cm /min. wg metody opisanej w czasopiśmie Radiat. Phys. Chem. 26/6/, 625-633/1985/.
W sposobie według wynalazku wyeliminowano proces oddzielnej sterylizacji opatrunku, ponieważ proces wytwarzania i sterylizacji opatrunku odbywa się podczas jednej, wspólnej operacji napromieniowania. W sposobie według wynalazku wyeliminowano także operację oczyszczania żelu, ponieważ stosowany przez nas skład materiału nie zawiera katalizatorów i innych substancji chemicznych, które muszą być eliminowane w innych sposobach.
Sposób według wynalazku ilustrują bliżej niżej podane przykłady nie ograniczając jego zakresu.
Przykład I. Sporządzono roztwór wodny poliwinylopirolidonu, agaru i poliglikolu propylenowego o składzie w częściach wagowych: 5 części poliwinylopirolidonu, 3 części agaru, 2 części poliglikolu propylenowego i 90 części wody destylowanej. Roztwór ten wylano do foremki w takiej ilości, aby powstała warstwa płynu o grubości około 4 nm. Po zastygnięciu roztworu foremkę zapakowano w folię polietylenową zgrzewająo brzegi folii i całość wraz z zawartością poddano napromieniowaniu dawką promieniowania gamma 30 kGy. Otrzymany opatrunek był całkowicie sterylny, elastyczny, przeźroczysty, przylegał dobrze do zdrowej skóry i rany stanowiąc barierę z zewnątrz i chroniąc przed utratą wody.
Przykład II. Sporządzono wodny roztwór poliwinylopirolidonu, poliglikolu etylenowego i agaru o składzie w częściach wagowych: 10 części poliwinylopirolidonu, 1,5 części poliglikolu etylenowego, 1,5 części agaru i 87 części wody destylowanej. Dalej postępowano jak w przykładzie I, przy czym napromieniowanie przeprowadzono za pomocą promieniowania jonizującego pochodzącego z akceleratora elektronów. Otrzymany opatrunek posiadał własności podobne jak opatrunek otrzymany w przykładzie I.
Przykład III. Sporządzono roztwór wodny winylopirolidonu, poliglikolu etylenowego, agaru i chlorku sodowego, o składzie w częściach wagowych: 10 części winylopirolidonu, 1,5 części agaru, 0,9 części chlorku sodowego oraz 87,6 części wody destylowanej.
Dalej postępowano jak w przykładzie I stosując dawkę promieniowania gamma 35 kGy. Otrzymany opatrunek posiadał własności analogiczne jak opatrunek otrzymany w przykładzie I·

Claims (1)

  1. Zastrzeżenie patentowe
    Sposób wytwarzania opatrunków hydrożelowyoh z polimerów syntetycznych i naturalnych, na drodze polimeryzacji i sieciowania, znamienny tym, źe wodny roztwór poliwinylopirolidonu lub jego monomeru, agaru, poliglikolu etylenowego lub poliglikolu propylenowego, o składzie w procentach wagowych: 2-10% poliwinylopirolidonu lub jego monomeru, nie więcej niż 3% agaru, nie mniej niż 75% wody destylowanej i 1-3% poliglikolu etylenowego lub propylenowego, wylewa się do formy nadającej kształt opatrunkowi, szczelnie zaząyka w tej formie i poddaje napromieniowaniu dawką promieniowania jonizującego nie mniejszą niż 25 kGy.
    Zakład Wydawnictw UP RP. Nakład 100 egz.
    Cena 3000 zł
PL1986263410A 1986-12-30 1986-12-30 Method of manufacturing of hydrogel dressing PL151581B1 (en)