MX390932B - Método e instalación para la producción de láminas de acero galvanizadas de alta resistencia. - Google Patents

Método e instalación para la producción de láminas de acero galvanizadas de alta resistencia.

Info

Publication number
MX390932B
MX390932B MX2017002974A MX2017002974A MX390932B MX 390932 B MX390932 B MX 390932B MX 2017002974 A MX2017002974 A MX 2017002974A MX 2017002974 A MX2017002974 A MX 2017002974A MX 390932 B MX390932 B MX 390932B
Authority
MX
Mexico
Prior art keywords
hot
galvanized steel
subjected
installation
production
Prior art date
Application number
MX2017002974A
Other languages
English (en)
Other versions
MX2017002974A (es
Inventor
Gentaro Takeda
Hideyuki Takahashi
Koichiro Fujita
Yoichi Makimizu
Yoshitsugu Suzuki
Original Assignee
Jfe Steel Corp
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Jfe Steel Corp filed Critical Jfe Steel Corp
Publication of MX2017002974A publication Critical patent/MX2017002974A/es
Publication of MX390932B publication Critical patent/MX390932B/es

Abstract

La invención proporciona un método para la producción de láminas de acero galvanizadas de alta resistencia que tienen excelentes adherencia del recubrimiento, trabajabilidad y aspecto. El método para la producción de láminas de acero galvanizadas de alta resistencia incluye una etapa de laminación en caliente para laminar en caliente un desbaste plano que incluye, en % en masa, C: 0.05 a 0.30%, Si: 0.1 a 2.0% y Mn: 1.0 a 4.0%, después de eso enrollar la lámina de acero en una bobina a una temperatura TC específica, y decapar la lámina de acero, una etapa de laminación en frío para laminar en frío la lámina de acero laminada en caliente que resulta de la etapa de laminación en caliente, una etapa de recocido para recocer la lámina de acero laminada en frío que resulta de la etapa de laminación en frío bajo condiciones específicas, y una etapa de galvanización para galvanizar la lámina recocida que resulta de la etapa de recocido en un baño de galvanización que contiene de 0.12 a 0.22% en masa de Al.
MX2017002974A 2014-09-08 2015-08-20 Método e instalación para la producción de láminas de acero galvanizadas de alta resistencia. MX390932B (es)

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
JP2014182153 2014-09-08
PCT/JP2015/004151 WO2016038801A1 (ja) 2014-09-08 2015-08-20 高強度溶融亜鉛めっき鋼板の製造方法及び製造設備

Publications (2)

Publication Number Publication Date
MX2017002974A MX2017002974A (es) 2017-06-19
MX390932B true MX390932B (es) 2025-03-21

Family

ID=55458576

Family Applications (1)

Application Number Title Priority Date Filing Date
MX2017002974A MX390932B (es) 2014-09-08 2015-08-20 Método e instalación para la producción de láminas de acero galvanizadas de alta resistencia.

Country Status (7)

Country Link
US (1) US10648054B2 (es)
EP (1) EP3159420B1 (es)
JP (1) JP6172297B2 (es)
KR (1) KR101889795B1 (es)
CN (1) CN106715726B (es)
MX (1) MX390932B (es)
WO (1) WO2016038801A1 (es)

Families Citing this family (17)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
CN106065429B (zh) * 2016-07-21 2018-10-02 洛阳Lyc轴承有限公司 一种保证轴承零件热后件表面颜色一致的方法
CN109906285B (zh) * 2016-10-25 2021-07-30 杰富意钢铁株式会社 高强度热镀锌钢板的制造方法
JP6764847B2 (ja) * 2017-03-28 2020-10-07 株式会社神戸製鋼所 溶融亜鉛めっき鋼板の製造方法及び合金化溶融亜鉛めっき鋼板の製造方法
JP6822934B2 (ja) * 2017-10-26 2021-01-27 株式会社神戸製鋼所 溶融亜鉛めっき鋼板の製造方法
MX2020007610A (es) * 2018-01-17 2020-09-03 Jfe Steel Corp Lamina de acero electrogalvano-recocida de alta resistencia y metodo para la fabricacion de la misma.
JP7086666B2 (ja) * 2018-03-23 2022-06-20 株式会社神戸製鋼所 合金化溶融亜鉛めっき鋼板の製造方法
JP6631765B1 (ja) * 2018-05-01 2020-01-15 日本製鉄株式会社 亜鉛系めっき鋼板及びその製造方法
JP2021014605A (ja) * 2019-07-10 2021-02-12 株式会社神戸製鋼所 溶融亜鉛めっき鋼板および合金化溶融亜鉛めっき鋼板の製造方法
CN110964981A (zh) * 2019-11-13 2020-04-07 浙江金洲管道科技股份有限公司 一种镀锌管材及制造方法
TR202016190A2 (tr) * 2020-10-12 2021-01-21 Borcelik Celik San Tic A S Galvani̇zli̇ yüzeylere kaplama i̇çi̇n i̇şlem
EP4296386A4 (en) * 2021-03-08 2025-01-15 Kabushiki Kaisha Kobe Seiko Sho (Kobe Steel, Ltd.) Method for manufacturing hot-dip galvanized steel sheet and method for manufacturing alloyed hot-dip galvanized steel sheet
US20240182998A1 (en) 2021-03-08 2024-06-06 Kabushiki Kaisha Kobe Seiko Sho (Kobe Steel, Ltd.) Method for manufacturing steel sheet
CN116897216A (zh) * 2021-03-08 2023-10-17 株式会社神户制钢所 熔融镀锌用钢板、熔融镀锌钢板及合金化熔融镀锌钢板
EP4299771A4 (en) 2021-03-08 2024-08-07 Kabushiki Kaisha Kobe Seiko Sho (Kobe Steel, Ltd.) HOT DIP GALVANIZING STEEL SHEET, HOT DIP GALVANIZED STEEL SHEET AND ALLOYED HOT DIP GALVANIZING ANNEALED STEEL SHEET
CN113897545A (zh) * 2021-09-02 2022-01-07 河钢股份有限公司承德分公司 一种超厚锌层高强无花热镀锌钢板、超厚锌层高强无花热镀锌钢卷及其制备方法
CN118843703A (zh) * 2022-03-25 2024-10-25 杰富意钢铁株式会社 高强度热镀锌钢板的制造方法
WO2024224582A1 (ja) 2023-04-28 2024-10-31 Ｊｆｅスチール株式会社 高強度溶融亜鉛めっき鋼板の製造方法

Family Cites Families (22)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JPS55122865A (en) 1979-03-12 1980-09-20 Nippon Steel Corp Molten zinc plating method for difficult plating steel sheet
JP2741617B2 (ja) * 1989-03-31 1998-04-22 日本鋼管株式会社 直火式加熱炉の空気比制御方法
JP2587725B2 (ja) 1990-11-30 1997-03-05 新日本製鐵株式会社 Ｐ含有高張力合金化溶融亜鉛めっき鋼板の製造方法
JP2530939B2 (ja) 1990-11-30 1996-09-04 新日本製鐵株式会社 高Ｓｉ含有高張力溶融亜鉛めっき鋼板の製造方法
JP2513532B2 (ja) 1990-11-30 1996-07-03 新日本製鐵株式会社 高Ｓｉ含有鋼の高張力溶融亜鉛めっき鋼板の製造方法
JP2587724B2 (ja) 1990-11-30 1997-03-05 新日本製鐵株式会社 めっき密着性の良好な高Ｓｉ含有高張力溶融亜鉛めっき鋼板の製造方法
JPH04254532A (ja) 1991-02-01 1992-09-09 Nippon Steel Corp 加工性の優れた合金化溶融亜鉛めっき鋼板の製造方法
JPH04254531A (ja) 1991-02-01 1992-09-09 Nippon Steel Corp 高Ｓｉ含有高張力鋼の溶融亜鉛めっき前の焼鈍方法
JP3255765B2 (ja) 1993-07-14 2002-02-12 川崎製鉄株式会社 高張力溶融または合金化溶融亜鉛めっき鋼板の製造方法
JP3184445B2 (ja) 1995-12-27 2001-07-09 川崎製鉄株式会社 合金化溶融亜鉛めっき鋼板の製造方法
JPH11279659A (ja) * 1998-03-30 1999-10-12 Nkk Corp 鋼帯の直火還元加熱方法及び直火還元加熱装置
JP4202632B2 (ja) 2001-09-28 2008-12-24 株式会社東芝 一括封止型半導体パッケージの樹脂封止構造およびその製造装置
JP4254531B2 (ja) 2003-12-25 2009-04-15 豊田合成株式会社 等速ジョイント用ブーツ
JP4254532B2 (ja) 2003-12-26 2009-04-15 ダイキン工業株式会社 ヒートポンプ式給湯装置
JP4972775B2 (ja) * 2006-02-28 2012-07-11 Ｊｆｅスチール株式会社 外観性とめっき密着性に優れる高強度溶融亜鉛めっき鋼板の製造方法
WO2011065591A1 (ja) * 2009-11-30 2011-06-03 新日本製鐵株式会社 耐水素脆化特性に優れた引張最大強度９００ＭＰa以上の高強度鋼板及びその製造方法
JP5434960B2 (ja) 2010-05-31 2014-03-05 Ｊｆｅスチール株式会社 曲げ性および溶接性に優れる高強度溶融亜鉛めっき鋼板およびその製造方法
JP5966528B2 (ja) * 2011-06-07 2016-08-10 Ｊｆｅスチール株式会社 めっき密着性に優れた高強度溶融亜鉛めっき鋼板およびその製造方法
DE102011051731B4 (de) * 2011-07-11 2013-01-24 Thyssenkrupp Steel Europe Ag Verfahren zur Herstellung eines durch Schmelztauchbeschichten mit einer metallischen Schutzschicht versehenen Stahlflachprodukts
JP5978826B2 (ja) 2012-07-23 2016-08-24 Ｊｆｅスチール株式会社 表面安定性に優れた高強度溶融亜鉛めっき鋼板の製造方法
JP5915569B2 (ja) * 2013-03-01 2016-05-11 Ｊｆｅスチール株式会社 溶融亜鉛めっき鋼板の製造方法および連続溶融亜鉛めっき装置
JP5962582B2 (ja) * 2013-05-21 2016-08-03 Ｊｆｅスチール株式会社 高強度合金化溶融亜鉛めっき鋼板の製造方法

Also Published As

Publication number Publication date
CN106715726A (zh) 2017-05-24
US20170253943A1 (en) 2017-09-07
KR101889795B1 (ko) 2018-08-20
KR20170039733A (ko) 2017-04-11
JPWO2016038801A1 (ja) 2017-04-27
CN106715726B (zh) 2018-11-06
JP6172297B2 (ja) 2017-08-02
WO2016038801A1 (ja) 2016-03-17
EP3159420A1 (en) 2017-04-26
EP3159420A4 (en) 2017-07-26
US10648054B2 (en) 2020-05-12
MX2017002974A (es) 2017-06-19
EP3159420B1 (en) 2020-09-16

Similar Documents

Publication Publication Date Title
MX390932B (es) Método e instalación para la producción de láminas de acero galvanizadas de alta resistencia.
RU2018122307A (ru) Способ производства высокопрочной листовой стали, характеризующейся улучшенными прочностью и формуемостью, и полученная высокопрочная листовая сталь
MX376920B (es) Lamina de acero laminada en caliente de alta resistencia y metodo para la produccion de la misma.
UA117134C2 (uk) Холоднокатаний сталевий лист, спосіб його виробництва і автотранспортний засіб
MX363038B (es) Metodo para producir hoja de acero laminada en frio.
EP2752500A4 (en) HOT-ROLLED STEEL PLATE FOR A COLD ROLLED STEEL, HOT-ROLLED STEEL PLATE FOR A HOT-DIP GALVANIZED STEEL SHEET, METHOD FOR PRODUCING THE HOT ROLLED STEEL PLATE FOR A COLD-ROLLED STEEL SHEET AND METHOD FOR PRODUCING THE HOT ROLLED STEEL PLATE FOR A HOT-DIP GALVANIZED STEEL SHEET
MX376693B (es) Lamina de acero laminada en frio y metodo para producir lamina de acero laminada en frio.
FI3741874T3 (fi) Menetelmä tinaa sisältävän ei-raeorientoidun piiteräslevyn valmistamiseksi
MX2012005962A (es) Proceso para fabricar tira de acero electrico de grano orientado y acero electrico de grano orientado producido por el mismo.
MX2014002935A (es) Metodo para producir una cinta electrica superiormente resistente de grano no orientado y su uso.
RU2016151402A (ru) Способ изготовления высокопрочного стального листа с покрытием или без покрытия и полученный стальной лист
IN2015DN00610A (es)
IN2015DN00612A (es)
MX2016013771A (es) Metodo para la produccion de lamina de acero galvanizada de alta resistencia y lamina de acero galvano-recocida de alta resistencia.
RU2012143206A (ru) Высокопрочный с высоким отношением предела текучести к пределу прочности стальной лист, высокопрочный с высоким отношением предела текучести к пределу прочности холоднокатаный стальной лист, высокопрочный с высоким отношением предела текучести к пределу прочности оцинкованный стальной лист, высокопрочный с высоким отношением предела текучести к пределу прочности оцинкованный погружением стальной лист, высокопрочный с высоким отношением предела текучести к пределу прочности отожженный оцинкованный погружением стальной лист, способ изготовления высокопрочного с высоким отношением предела текучести к пределу прочности холоднокатаного стального листа, способ изготовления высокопрочного с высоким отношением предела текучести к пределу прочности оцинкованного погружением стального листа и способ изготовления высокопрочного с высоким отношением предела текучести к пределу прочности отожженного оцинкованного погружением стального листа
MX2018006419A (es) Metodo para la fabricacion de lamina de acero galvanizada de alta resistencia, metodo para la fabricacion de lamina de acero laminada en caliente para laminas de acero galvanizadas de alta resistencia, metodo para la fabricacion de lamina de acero laminada en frio para laminas de acero galvanizadas de alta resistencia, y lamina de acero galvanizada de alta resistencia.
MX354352B (es) Lámina de acero galvanizado de alta resistencia excelente en términos de adherencia de recubrimiento y método para la fabricación de la misma.
MX386813B (es) Método para producir una hoja de acero galvano-recocido de ultra alta resistencia y hoja de acero galvano-recocido obtenida.
ATE551131T1 (de) Verfahren zur kontinuierlichen herstellung von kaltgewalztem stahl
RU2012143205A (ru) Высокопрочный с низким отношением предела текучести к пределу прочности оцинкованный погружением стальной лист, высокопрочный с низким отношением предела текучести к пределу прочности отожженный оцинкованный погружением стальной лист, способ изготовления высокопрочного с низким отношением предела текучести к пределу прочности оцинкованного погружением стального листа и способ изготовления высокопрочного с низким отношением предела текучести к пределу прочности отожженного оцинкованного погружением стального листа
MY180218A (en) Method for manufacturing high strenght coll rolled steel sheet having excellent workability
MX373472B (es) Lámina de acero y metodo para producir la misma.
KR102209612B9 (ko) 버링성이 우수한 고강도 냉연강판 및 합금화 용융아연도금강판과 이들의 제조방법
TH175856A (th) วิธีการและโรงผลิตสำหรับผลิตแผ่นเหล็กกล้าชุบสังกะสีที่มีความแข็งแรงสูง
TH124815A (th) แผ่นเหล็กกล้ารีดเย็นทนแรงดึงสูงยิ่งยวดและวิธีการผลิต