MX2017012377A - Lamina de acero para estampado en caliente, metodo para producir lamina de acero para estampado en caliente, y articulo moldeado por estampado en caliente. - Google Patents

Lamina de acero para estampado en caliente, metodo para producir lamina de acero para estampado en caliente, y articulo moldeado por estampado en caliente.

Info

Publication number
MX2017012377A
MX2017012377A MX2017012377A MX2017012377A MX2017012377A MX 2017012377 A MX2017012377 A MX 2017012377A MX 2017012377 A MX2017012377 A MX 2017012377A MX 2017012377 A MX2017012377 A MX 2017012377A MX 2017012377 A MX2017012377 A MX 2017012377A
Authority
MX
Mexico
Prior art keywords
steel sheet
hot
molded article
manufacturing same
stamp molded
Prior art date
Application number
MX2017012377A
Other languages
English (en)
Inventor
Sato Koichi
Suwa Yoshihiro
Azuma Masafumi
Kondo Yusuke
Original Assignee
Nippon Steel & Sumitomo Metal Corp
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Nippon Steel & Sumitomo Metal Corp filed Critical Nippon Steel & Sumitomo Metal Corp
Publication of MX2017012377A publication Critical patent/MX2017012377A/es

Abstract

Una lámina de acero para estampado en caliente incluye una composición que incluye al menos, en % en masa, C: 0.100%-0.600%, Si: 0.50%-3.00%, Mn: 1.20%-4.00%, Ti 0.005%-0.100%, B: 0.0005%-0.100%, P: 0.100% o menos, S: 0.0001%-0.0100%, Al: 90.005%-1.00%, y N: 0.100% o menos, con el resto que comprende Fe e impurezas. La rugosidad de la superficie de la lámina de acero es tal que Rz > 2.5 µm y la superficie se reíste con 50 mg/m2 - 1500 mg/m2 de aceite revestido sobre la misma.
MX2017012377A 2015-03-31 2016-03-29 Lamina de acero para estampado en caliente, metodo para producir lamina de acero para estampado en caliente, y articulo moldeado por estampado en caliente. MX2017012377A (es)

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
JP2015072280 2015-03-31
PCT/JP2016/060145 WO2016158961A1 (ja) 2015-03-31 2016-03-29 ホットスタンプ用鋼板およびその製造方法、並びにホットスタンプ成形体

Publications (1)

Publication Number Publication Date
MX2017012377A true MX2017012377A (es) 2017-12-14

Family

ID=57004387

Family Applications (1)

Application Number Title Priority Date Filing Date
MX2017012377A MX2017012377A (es) 2015-03-31 2016-03-29 Lamina de acero para estampado en caliente, metodo para producir lamina de acero para estampado en caliente, y articulo moldeado por estampado en caliente.

Country Status (12)

Country Link
US (1) US20180044754A1 (es)
EP (1) EP3278895B1 (es)
JP (1) JP6515356B2 (es)
KR (1) KR102000863B1 (es)
CN (1) CN107427889B (es)
BR (1) BR112017020165A2 (es)
CA (1) CA2979978A1 (es)
ES (1) ES2781465T3 (es)
MX (1) MX2017012377A (es)
RU (1) RU2683397C1 (es)
TW (1) TWI597370B (es)
WO (1) WO2016158961A1 (es)

Families Citing this family (25)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
EP3282030B1 (en) 2015-04-08 2020-02-19 Nippon Steel Corporation Heat-treated steel sheet member, and production method therefor
CN107406953B (zh) * 2015-04-08 2019-10-25 日本制铁株式会社 热处理用钢板
MX2017012875A (es) * 2015-04-08 2018-02-21 Nippon Steel & Sumitomo Metal Corp Miembro de lamina de acero con tratamiento termico y metodo para producir el mismo.
DE102016218957A1 (de) * 2016-09-30 2018-04-05 Thyssenkrupp Ag Temporäre Korrosionsschutzschicht
TWI632240B (zh) * 2017-01-17 2018-08-11 新日鐵住金股份有限公司 Hot stamping formed body and method of manufacturing same
WO2018215813A1 (en) * 2017-05-22 2018-11-29 Arcelormittal Method for producing a steel part and corresponding steel part
KR101938092B1 (ko) * 2017-09-26 2019-04-11 현대제철 주식회사 핫 스탬핑 부품의 제조방법 및 이에 의해 제조된 핫 스탬핑 부품
JP7353768B2 (ja) * 2018-03-27 2023-10-02 株式会社神戸製鋼所 ホットスタンプ用鋼板
WO2019188622A1 (ja) * 2018-03-27 2019-10-03 株式会社神戸製鋼所 ホットスタンプ用鋼板
WO2020065372A1 (en) * 2018-09-25 2020-04-02 Arcelormittal High strength hot rolled steel having excellent scale adhesivness and a method of manufacturing the same
CN109136485A (zh) * 2018-09-30 2019-01-04 南京理工大学 汽车稳定杆用超高强度钢及稳定杆的制造方法
US11352684B2 (en) 2019-02-05 2022-06-07 Nippon Steel Corporation Steel member, steel sheet, and methods for manufacturing same
CN109706377A (zh) * 2019-03-01 2019-05-03 本钢板材股份有限公司 一种适合热成形加工的厚规格phs1500钢及其生产工艺
CN110257702B (zh) * 2019-06-24 2021-04-27 鞍钢股份有限公司 一种热冲压成形用钢及其热成形方法
US20220186351A1 (en) * 2019-07-02 2022-06-16 Nippon Steel Corporation Zinc-plated steel sheet for hot stamping, method of manufacturing zinc-plated steel sheet for hot stamping, and hot-stamping formed body
KR102236851B1 (ko) * 2019-11-04 2021-04-06 주식회사 포스코 내구성이 우수한 고항복비형 후물 고강도강 및 그 제조방법
CN111926248B (zh) * 2020-07-14 2021-11-30 辽宁科技学院 一种添加Ce合金的热冲压成形钢及热冲压成形工艺
JPWO2022158469A1 (es) * 2021-01-19 2022-07-28
CN112981069B (zh) * 2021-02-04 2022-04-26 山西太钢不锈钢股份有限公司 一种低光泽度不锈钢面板材料的制备方法
TWI779686B (zh) * 2021-06-25 2022-10-01 中國鋼鐵股份有限公司 熱沖壓用鋼材與鋼材製造方法
CN113755758B (zh) * 2021-09-03 2023-02-03 本钢板材股份有限公司 一种添加铈微合金制备的8mm厚热冲压钢以及其热冲压工艺
CN114012056B (zh) * 2021-10-14 2023-10-13 首钢集团有限公司 一种1500MPa级热成形钢及其制备方法
CN114561590A (zh) * 2022-02-28 2022-05-31 北京理工大学重庆创新中心 一种添加Ce元素的无涂层抗高温氧化热冲压成形钢
CN114561591A (zh) * 2022-02-28 2022-05-31 北京理工大学重庆创新中心 一种添加y元素的无涂层增强抗高温氧化热冲压成形钢
DE102022108111A1 (de) 2022-04-05 2023-10-05 Voestalpine Metal Forming Gmbh Verfahren zum Erzeugen gehärteter Stahlbauteile

Family Cites Families (26)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
GB1265968A (es) * 1967-12-23 1972-03-08
JPH01230715A (ja) 1987-06-26 1989-09-14 Nippon Steel Corp プレス成形性の優れた高強度冷延鋼板の製造方法
JPH0733551B2 (ja) 1989-02-18 1995-04-12 新日本製鐵株式会社 優れた成形性を有する高強度鋼板の製造方法
JP3195509B2 (ja) * 1995-02-01 2001-08-06 株式会社神戸製鋼所 表面性状に優れた熱延鋼板の製造方法
JP3143046B2 (ja) * 1995-07-31 2001-03-07 日本鋼管株式会社 プレス成形性および耐孔あき腐食性に優れた有機複合被覆鋼板
JPH0976004A (ja) * 1995-09-11 1997-03-25 Nisshin Steel Co Ltd プレス加工性にすぐれた潤滑防錆油塗布鋼板
JP3882474B2 (ja) 2000-07-06 2007-02-14 住友金属工業株式会社 金属板の熱間プレス成形方法
JP2002143935A (ja) 2000-11-13 2002-05-21 Sumitomo Metal Ind Ltd 金属板の温間プレス方法
JP3766626B2 (ja) 2001-11-22 2006-04-12 新日本製鐵株式会社 高強度鋼板プレス成形体の製造方法
JP3504655B2 (ja) * 2001-12-06 2004-03-08 新日本製鐵株式会社 プレス成形性と作業性に優れたフェライト系ステンレス鋼板およびその製造方法
JP4023248B2 (ja) * 2002-07-23 2007-12-19 住友金属工業株式会社 強加工用の潤滑処理鋼帯
JP2004106034A (ja) 2002-09-19 2004-04-08 Nippon Steel Corp シート状金属の加工装置および加工方法
JP4941003B2 (ja) 2007-02-28 2012-05-30 Ｊｆｅスチール株式会社 ダイクエンチ用熱延鋼板およびその製造方法
WO2008110670A1 (fr) * 2007-03-14 2008-09-18 Arcelormittal France Acier pour formage a chaud ou trempe sous outil a ductilite amelioree
JP4782056B2 (ja) * 2007-03-27 2011-09-28 新日本製鐵株式会社 熱間プレス時のスケール密着性に優れた高強度鋼板およびその製造方法
RU2439189C1 (ru) * 2007-10-29 2012-01-10 Ниппон Стил Корпорейшн Горячештампованная нетермообработанная сталь мартенситного класса и горячештампованная нетермообработанная стальная деталь
EP2373770B1 (de) * 2008-12-04 2018-04-18 voestalpine Stahl GmbH Verfahren zum herstellen von formkörpern aus einseitig oder beidseitig verzinktem stahlblech
JP2010174302A (ja) * 2009-01-28 2010-08-12 Jfe Steel Corp ダイクエンチ用鋼板
MX2012014594A (es) * 2010-06-14 2013-02-21 Nippon Steel & Sumitomo Metal Corp Articulo moldeado y estampado en caliente, proceso para produccion de placa de acero para estampado en caliente, y proceso para produccion de un articulo moldeado y estampado en caliente.
JP5029749B2 (ja) * 2010-09-17 2012-09-19 Ｊｆｅスチール株式会社 曲げ加工性に優れた高強度熱延鋼板およびその製造方法
BR112013009520B1 (pt) * 2010-10-22 2019-05-07 Nippon Steel & Sumitomo Metal Corporation Métodos para produção de chassi estampado a quente e chassi estampado a quente
CN103168106B (zh) * 2010-10-22 2014-11-12 新日铁住金株式会社 钢板及钢板制造方法
MX366958B (es) * 2012-03-07 2019-08-01 Nippon Steel Corp Star Plancha de acero para estampado en caliente, metodo para producirla y material de acero para estampado en caliente.
JP5973953B2 (ja) * 2012-04-23 2016-08-23 株式会社神戸製鋼所 ホットスタンプ用合金化溶融亜鉛めっき鋼板とその製造方法
KR101663207B1 (ko) * 2013-03-27 2016-10-06 닛폰 스틸 앤드 스미킨 스테인레스 스틸 코포레이션 연마 후의 표면 내식성이 우수한 페라이트계 스테인리스강 및 그 제조 방법
CN103614640B (zh) * 2013-12-12 2016-10-05 马鸣图 一种抗高温氧化的非镀层热冲压成形用钢

Also Published As

Publication number Publication date
JP6515356B2 (ja) 2019-05-22
WO2016158961A1 (ja) 2016-10-06
US20180044754A1 (en) 2018-02-15
CN107427889B (zh) 2019-10-25
ES2781465T3 (es) 2020-09-02
RU2683397C1 (ru) 2019-03-28
TW201702403A (zh) 2017-01-16
CA2979978A1 (en) 2016-10-06
KR20170122823A (ko) 2017-11-06
CN107427889A (zh) 2017-12-01
EP3278895B1 (en) 2020-03-11
EP3278895A1 (en) 2018-02-07
KR102000863B1 (ko) 2019-07-16
JPWO2016158961A1 (ja) 2018-01-18
EP3278895A4 (en) 2018-09-05
BR112017020165A2 (pt) 2018-06-05
TWI597370B (zh) 2017-09-01

Similar Documents

Publication Publication Date Title
MX2017012377A (es) Lamina de acero para estampado en caliente, metodo para producir lamina de acero para estampado en caliente, y articulo moldeado por estampado en caliente.
MX2013011084A (es) Chapa de acero con superficie tratada y metodo para fabricarla.
MX351086B (es) Lámina de acero para miembro de estampado en caliente y método para producir la misma.
MX2017002415A (es) Lamina de acero electrico de grano no orientado y metodo de fabricacion para la misma.
MY176155A (en) Ni-plated steel sheet, and method for producing ni-plated steel sheet
IN2015DN01908A (es)
IN2014DN07662A (es)
MX2017003310A (es) Partes formadas en prensa caliente que tienen excelente resistencia a la pulverizacion durante la formacion en prensa caliente y metodo para fabricar las mismas.
MX2017003551A (es) Articulo formado en prensa en caliente que tiene excelente resisitencia a la deslaminacion y metodo para fabricar el mismo.
MX2015014132A (es) Lamina de aleacion de aluminio para formacion por prensado, proceso para manufactura del mismo, y producto formado por prensado del mismo.
TR201902032T4 (tr) Bir alüminyum alaşımından oluşan bir korozyon koruma kaplamasına sahip çelik ürünü ve aynı zamanda bunun üretilmesine yönelik yöntem.
WO2016084378A8 (ja) 方向性電磁鋼板の製造方法
EP2102375A4 (en) Method of forming {100} texture on surface of iron or iron-base alloy sheet, method of manufacturing non-oriented electrical steel sheet by using the same and non-oriented electrical steel sheet manufactured by using the same
WO2015039763A3 (en) Steel for hot forming
MX2017002066A (es) Lamina de acero electrico de grano no orientado que tiene excelentes propiedades magneticas.
WO2016190538A8 (ko) 내박리성이 우수한 hpf 성형부재 및 그 제조방법
MY158372A (en) Aluminum-zinc plated steel sheet and method for producing the same
IN2015DN01523A (es)
MX2015001224A (es) Lamina de acero galvanizada por inmersion en caliente y metodo de fabricacion de la misma.
MX2016000008A (es) Lamina de acero laminada en caliente de alto contenido en carbono y metodo para la produccion de la misma.
AR085117A1 (es) HERRAMIENTAS CON RECUBRIMIENTOS DE CR-Si-N, PARA LA CONFORMACION O ESTAMPADO DE CHAPAS DE METAL EN CALIENTE
MX2016000009A (es) Lamina de acero laminada en caliente de alto contenido en carbono y metodo para la produccion de la misma.
MY153967A (en) High-strength hot rolled steel sheet having good formability and method for manufacturing the same
MX2015015064A (es) Lamina de acero galvanizado y metodo para producir el mismo.
MX2016014783A (es) Procedimiento para la fabricacion de una pieza de construccion de acero dotada de un revestimiento metalico anticorrosivo y pieza de construccion de acero.