MX2015001772A - Plancha de acero para uso en prensado en caliente, metodo para producirla, y miembro de plancha de acero de prensado en caliente. - Google Patents

Plancha de acero para uso en prensado en caliente, metodo para producirla, y miembro de plancha de acero de prensado en caliente.

Info

Publication number
MX2015001772A
MX2015001772A MX2015001772A MX2015001772A MX2015001772A MX 2015001772 A MX2015001772 A MX 2015001772A MX 2015001772 A MX2015001772 A MX 2015001772A MX 2015001772 A MX2015001772 A MX 2015001772A MX 2015001772 A MX2015001772 A MX 2015001772A
Authority
MX
Mexico
Prior art keywords
steel plate
content
less
hot
steel
Prior art date
Application number
MX2015001772A
Other languages
English (en)
Spanish (es)
Inventor
Akari Tamaki
Kazuo Hikida
Original Assignee
Nippon Steel & Sumitomo Metal Corp
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Nippon Steel & Sumitomo Metal Corp filed Critical Nippon Steel & Sumitomo Metal Corp
Publication of MX2015001772A publication Critical patent/MX2015001772A/es

Links

Classifications

    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D8/00—Modifying the physical properties by deformation combined with, or followed by, heat treatment
    • C21D8/02—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips
    • C21D8/0247—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips characterised by the heat treatment
    • C21D8/0263—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips characterised by the heat treatment following hot rolling
    • B—PERFORMING OPERATIONS; TRANSPORTING
    • B32—LAYERED PRODUCTS
    • B32B—LAYERED PRODUCTS, i.e. PRODUCTS BUILT-UP OF STRATA OF FLAT OR NON-FLAT, e.g. CELLULAR OR HONEYCOMB, FORM
    • B32B15/00—Layered products comprising a layer of metal
    • B32B15/01—Layered products comprising a layer of metal all layers being exclusively metallic
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D1/00—General methods or devices for heat treatment, e.g. annealing, hardening, quenching or tempering
    • C21D1/18—Hardening; Quenching with or without subsequent tempering
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D1/00—General methods or devices for heat treatment, e.g. annealing, hardening, quenching or tempering
    • C21D1/62—Quenching devices
    • C21D1/673—Quenching devices for die quenching
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D6/00—Heat treatment of ferrous alloys
    • C21D6/001—Heat treatment of ferrous alloys containing Ni
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D6/00—Heat treatment of ferrous alloys
    • C21D6/002—Heat treatment of ferrous alloys containing Cr
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D6/00—Heat treatment of ferrous alloys
    • C21D6/004—Heat treatment of ferrous alloys containing Cr and Ni
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D6/00—Heat treatment of ferrous alloys
    • C21D6/005—Heat treatment of ferrous alloys containing Mn
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D6/00—Heat treatment of ferrous alloys
    • C21D6/008—Heat treatment of ferrous alloys containing Si
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D7/00—Modifying the physical properties of iron or steel by deformation
    • C21D7/13—Modifying the physical properties of iron or steel by deformation by hot working
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D8/00—Modifying the physical properties by deformation combined with, or followed by, heat treatment
    • C21D8/02—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D8/00—Modifying the physical properties by deformation combined with, or followed by, heat treatment
    • C21D8/02—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips
    • C21D8/0221—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips characterised by the working steps
    • C21D8/0226—Hot rolling
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D8/00—Modifying the physical properties by deformation combined with, or followed by, heat treatment
    • C21D8/02—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips
    • C21D8/0221—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips characterised by the working steps
    • C21D8/0236—Cold rolling
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D8/00—Modifying the physical properties by deformation combined with, or followed by, heat treatment
    • C21D8/02—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips
    • C21D8/0247—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips characterised by the heat treatment
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D9/00—Heat treatment, e.g. annealing, hardening, quenching or tempering, adapted for particular articles; Furnaces therefor
    • C21D9/46—Heat treatment, e.g. annealing, hardening, quenching or tempering, adapted for particular articles; Furnaces therefor for sheet metals
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/001—Ferrous alloys, e.g. steel alloys containing N
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/002—Ferrous alloys, e.g. steel alloys containing In, Mg, or other elements not provided for in one single group C22C38/001 - C22C38/60
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/005—Ferrous alloys, e.g. steel alloys containing rare earths, i.e. Sc, Y, Lanthanides
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/02—Ferrous alloys, e.g. steel alloys containing silicon
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/04—Ferrous alloys, e.g. steel alloys containing manganese
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/06—Ferrous alloys, e.g. steel alloys containing aluminium
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/08—Ferrous alloys, e.g. steel alloys containing nickel
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/12—Ferrous alloys, e.g. steel alloys containing tungsten, tantalum, molybdenum, vanadium, or niobium
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/14—Ferrous alloys, e.g. steel alloys containing titanium or zirconium
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/16—Ferrous alloys, e.g. steel alloys containing copper
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/18—Ferrous alloys, e.g. steel alloys containing chromium
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/18—Ferrous alloys, e.g. steel alloys containing chromium
    • C22C38/22—Ferrous alloys, e.g. steel alloys containing chromium with molybdenum or tungsten
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/18—Ferrous alloys, e.g. steel alloys containing chromium
    • C22C38/24—Ferrous alloys, e.g. steel alloys containing chromium with vanadium
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/18—Ferrous alloys, e.g. steel alloys containing chromium
    • C22C38/26—Ferrous alloys, e.g. steel alloys containing chromium with niobium or tantalum
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/18—Ferrous alloys, e.g. steel alloys containing chromium
    • C22C38/28—Ferrous alloys, e.g. steel alloys containing chromium with titanium or zirconium
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/18—Ferrous alloys, e.g. steel alloys containing chromium
    • C22C38/32—Ferrous alloys, e.g. steel alloys containing chromium with boron
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/18—Ferrous alloys, e.g. steel alloys containing chromium
    • C22C38/38—Ferrous alloys, e.g. steel alloys containing chromium with more than 1.5% by weight of manganese
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/18—Ferrous alloys, e.g. steel alloys containing chromium
    • C22C38/40—Ferrous alloys, e.g. steel alloys containing chromium with nickel
    • C22C38/50—Ferrous alloys, e.g. steel alloys containing chromium with nickel with titanium or zirconium
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/18—Ferrous alloys, e.g. steel alloys containing chromium
    • C22C38/40—Ferrous alloys, e.g. steel alloys containing chromium with nickel
    • C22C38/54—Ferrous alloys, e.g. steel alloys containing chromium with nickel with boron
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/18—Ferrous alloys, e.g. steel alloys containing chromium
    • C22C38/40—Ferrous alloys, e.g. steel alloys containing chromium with nickel
    • C22C38/58—Ferrous alloys, e.g. steel alloys containing chromium with nickel with more than 1.5% by weight of manganese
    • C—CHEMISTRY; METALLURGY
    • C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
    • C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
    • C23C2/00—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor
    • C23C2/02—Pretreatment of the material to be coated, e.g. for coating on selected surface areas
    • C—CHEMISTRY; METALLURGY
    • C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
    • C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
    • C23C2/00—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor
    • C23C2/02—Pretreatment of the material to be coated, e.g. for coating on selected surface areas
    • C23C2/022—Pretreatment of the material to be coated, e.g. for coating on selected surface areas by heating
    • C23C2/0224—Two or more thermal pretreatments
    • C—CHEMISTRY; METALLURGY
    • C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
    • C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
    • C23C2/00—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor
    • C23C2/02—Pretreatment of the material to be coated, e.g. for coating on selected surface areas
    • C23C2/024—Pretreatment of the material to be coated, e.g. for coating on selected surface areas by cleaning or etching
    • C—CHEMISTRY; METALLURGY
    • C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
    • C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
    • C23C2/00—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor
    • C23C2/04—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor characterised by the coating material
    • C23C2/06—Zinc or cadmium or alloys based thereon
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D2211/00—Microstructure comprising significant phases
    • C21D2211/002—Bainite
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D2211/00—Microstructure comprising significant phases
    • C21D2211/005—Ferrite
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D2211/00—Microstructure comprising significant phases
    • C21D2211/008—Martensite

Landscapes

  • Chemical & Material Sciences (AREA)
  • Engineering & Computer Science (AREA)
  • Materials Engineering (AREA)
  • Mechanical Engineering (AREA)
  • Metallurgy (AREA)
  • Organic Chemistry (AREA)
  • Thermal Sciences (AREA)
  • Physics & Mathematics (AREA)
  • Crystallography & Structural Chemistry (AREA)
  • Chemical Kinetics & Catalysis (AREA)
  • Heat Treatment Of Sheet Steel (AREA)
  • Heat Treatment Of Articles (AREA)
  • Coating With Molten Metal (AREA)
MX2015001772A 2012-08-15 2013-08-15 Plancha de acero para uso en prensado en caliente, metodo para producirla, y miembro de plancha de acero de prensado en caliente. MX2015001772A (es)

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
JP2012180186 2012-08-15
PCT/JP2013/071971 WO2014027682A1 (ja) 2012-08-15 2013-08-15 熱間プレス用鋼板、その製造方法、及び熱間プレス鋼板部材

Publications (1)

Publication Number Publication Date
MX2015001772A true MX2015001772A (es) 2015-05-08

Family

ID=50101304

Family Applications (1)

Application Number Title Priority Date Filing Date
MX2015001772A MX2015001772A (es) 2012-08-15 2013-08-15 Plancha de acero para uso en prensado en caliente, metodo para producirla, y miembro de plancha de acero de prensado en caliente.

Country Status (12)

Country Link
US (1) US10570470B2 (cg-RX-API-DMAC10.html)
EP (1) EP2886674B1 (cg-RX-API-DMAC10.html)
JP (1) JP5505574B1 (cg-RX-API-DMAC10.html)
KR (1) KR101674331B1 (cg-RX-API-DMAC10.html)
CN (2) CN109023051A (cg-RX-API-DMAC10.html)
CA (1) CA2880946C (cg-RX-API-DMAC10.html)
IN (1) IN2015DN00705A (cg-RX-API-DMAC10.html)
MX (1) MX2015001772A (cg-RX-API-DMAC10.html)
RU (1) RU2599934C2 (cg-RX-API-DMAC10.html)
TW (1) TWI481729B (cg-RX-API-DMAC10.html)
WO (1) WO2014027682A1 (cg-RX-API-DMAC10.html)
ZA (1) ZA201501490B (cg-RX-API-DMAC10.html)

Families Citing this family (28)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
KR101417260B1 (ko) * 2012-04-10 2014-07-08 주식회사 포스코 재질 균일성이 우수한 고탄소 열연강판 및 이의 제조방법
JP2015196890A (ja) * 2014-04-02 2015-11-09 本田技研工業株式会社 ホットスタンプ成形体
EP3279353B1 (en) * 2015-04-01 2019-03-27 JFE Steel Corporation Hot-rolled steel sheet and method for producing same
WO2017006144A1 (en) 2015-07-09 2017-01-12 Arcelormittal Steel for press hardening and press hardened part manufactured from such steel
CN105316601B (zh) * 2015-10-28 2017-03-22 安徽省三方新材料科技有限公司 一种顽石破碎机用衬板及其制备方法
KR20170075046A (ko) 2015-12-22 2017-07-03 주식회사 포스코 내식성이 우수한 열간 프레스 성형품 및 그 제조방법
CN107127238B (zh) * 2016-02-26 2019-12-27 宝山钢铁股份有限公司 一种锌系镀覆钢板或钢带的热冲压成型方法
KR101819345B1 (ko) 2016-07-07 2018-01-17 주식회사 포스코 균열전파 저항성 및 연성이 우수한 열간성형 부재 및 이의 제조방법
KR101963936B1 (ko) 2016-11-08 2019-07-31 한국과학기술원 전자파 신호 송수신 안테나 및 em-터널이 내장된 구조를 갖는 인쇄회로기판 및 그 제작 방법
WO2018220430A1 (en) 2017-06-02 2018-12-06 Arcelormittal Steel sheet for manufacturing press hardened parts, press hardened part having a combination of high strength and crash ductility, and manufacturing methods thereof
KR101977474B1 (ko) * 2017-08-09 2019-05-10 주식회사 포스코 표면 품질, 강도 및 연성이 우수한 도금강판
EP3701058B1 (en) 2017-10-24 2024-05-15 ArcelorMittal A method for the manufacture of a galvannealed steel sheet
KR102206929B1 (ko) * 2017-10-24 2021-01-25 아르셀러미탈 코팅된 강 시트의 제조 방법
CN107604266A (zh) * 2017-10-31 2018-01-19 桂林加宏汽车修理有限公司 一种高韧性钢合金
WO2019097440A1 (en) 2017-11-17 2019-05-23 Arcelormittal A method for the manufacturing of liquid metal embrittlement resistant zinc coated steel sheet
CN109365606A (zh) * 2018-11-30 2019-02-22 宝山钢铁股份有限公司 一种耐腐蚀性优良的锌系镀层钢板或钢带的成形方法
KR102543424B1 (ko) 2019-02-22 2023-06-14 제이에프이 스틸 가부시키가이샤 열간 프레스 부재 및 그의 제조 방법, 그리고 열간 프레스 부재용 강판의 제조 방법
BR112022010285A2 (pt) * 2019-11-27 2022-08-16 Tata Steel Ijmuiden Bv Método de moldagem por prensagem a quente de artigo de aço e artigo de aço
JP7648620B2 (ja) * 2019-12-20 2025-03-18 ポスコホールディングス インコーポレーティッド 熱間成形用鋼材、熱間成形部材及びこれらの製造方法
CN111676417A (zh) * 2020-05-07 2020-09-18 天津英利模具制造有限公司 一种轻量化汽车用高强钢板及其热冲压成型工艺
JP7436917B2 (ja) * 2020-05-13 2024-02-22 日本製鉄株式会社 ホットスタンプ用鋼板およびホットスタンプ成形体
CN115151669B (zh) 2020-05-13 2023-12-26 日本制铁株式会社 热冲压成形体
MX2023002961A (es) * 2020-10-16 2023-04-11 Nippon Steel Corp Lamina de acero para estampado en caliente, metodo de fabricacion de la misma, componente estampado en caliente, y metodo de fabricacion del mismo.
CN117120636A (zh) * 2021-03-17 2023-11-24 塔塔钢铁艾默伊登有限责任公司 钢带材、片材或坯料以及用于生产热成形零件或热处理的预成形零件的方法
EP4379084A4 (en) * 2021-07-30 2025-11-19 Hyundai Steel Co STEEL SHEET FOR HOT PRESSING AND ALUMINUM-COATED FLAN MADE USING SAID SHEET
JP7512987B2 (ja) * 2021-09-22 2024-07-09 Ｊｆｅスチール株式会社 熱間プレス用鋼板、その製造方法、熱間プレス部材およびその製造方法
WO2023079344A1 (en) * 2021-11-05 2023-05-11 Arcelormittal Method for producing a steel sheet having excellent processability before hot forming, steel sheet, process to manufacture a hot stamped part and hot stamped part
TWI876779B (zh) * 2023-12-18 2025-03-11 中國鋼鐵股份有限公司 高平坦度及超高強度鋼材及其製造方法

Family Cites Families (37)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP2001226741A (ja) * 2000-02-15 2001-08-21 Kawasaki Steel Corp 伸びフランジ加工性に優れた高強度冷延鋼板およびその製造方法
JP3389562B2 (ja) 2000-07-28 2003-03-24 アイシン高丘株式会社 車輌用衝突補強材の製造方法
JP3879459B2 (ja) 2001-08-31 2007-02-14 Ｊｆｅスチール株式会社 高焼入れ性高炭素熱延鋼板の製造方法
JP3468239B2 (ja) * 2001-10-01 2003-11-17 住友金属工業株式会社 機械構造用鋼及びその製造方法
EP1577412B2 (en) * 2002-12-24 2014-11-12 Nippon Steel & Sumitomo Metal Corporation High strength steel sheet exhibiting good burring workability and excellent resistance to softening in heat-affected zone and method for production thereof
JP4160840B2 (ja) * 2003-02-19 2008-10-08 新日本製鐵株式会社 形状凍結性に優れた高加工性高強度熱延鋼板とその製造方法
JP4292986B2 (ja) 2003-04-16 2009-07-08 Ｊｆｅスチール株式会社 高張力冷延鋼板およびその製造方法
JP3885763B2 (ja) 2003-04-25 2007-02-28 住友金属工業株式会社 焼入用溶融亜鉛系めっき鋼板とその製造方法及び用途
JP2005126733A (ja) * 2003-10-21 2005-05-19 Nippon Steel Corp 高温加工性にすぐれた熱間プレス用鋼板及び自動車用部材
JP4671959B2 (ja) * 2003-12-19 2011-04-20 新日本製鐵株式会社 低温靱性に優れた超高強度ラインパイプ用鋼板及び鋼管並びにそれらの製造方法
JP4288216B2 (ja) * 2004-09-06 2009-07-01 新日本製鐵株式会社 耐水素脆化特性に優れたホットプレス用鋼板、自動車用部材及びその製造方法
JP4575799B2 (ja) * 2005-02-02 2010-11-04 新日本製鐵株式会社 成形性に優れたホットプレス高強度鋼製部材の製造方法
RU2277594C1 (ru) * 2005-03-30 2006-06-10 Открытое акционерное общество "Северсталь" Способ производства холоднокатаных листов для глубокой вытяжки
EP1865085B1 (en) * 2005-03-31 2016-03-09 Kabushiki Kaisha Kobe Seiko Sho High-strength cold-rolled steel sheet excellent in coating adhesion, workability and hydrogen embrittlement resistance, and steel component for automobile
KR100973627B1 (ko) * 2005-07-07 2010-08-02 수미도모 메탈 인더스트리즈, 리미티드 무방향성 전자 강판 및 그 제조 방법
JP4967360B2 (ja) * 2006-02-08 2012-07-04 住友金属工業株式会社 熱間プレス用めっき鋼板およびその製造方法ならびに熱間プレス成形部材の製造方法
EP1832667A1 (fr) * 2006-03-07 2007-09-12 ARCELOR France Procédé de fabrication de tôles d'acier à très hautes caractéristiques de résistance, de ductilité et de tenacité, et tôles ainsi produites
JP5008173B2 (ja) * 2006-05-17 2012-08-22 日産自動車株式会社 抵抗溶接用高張力鋼板及びその接合方法
EP3696292B1 (en) 2007-10-25 2024-03-13 JFE Steel Corporation A high tensile strength galvanized steel sheet with excellent formability and anti-crush properties and method of manufacturing the same
JP5167487B2 (ja) 2008-02-19 2013-03-21 Ｊｆｅスチール株式会社 延性に優れる高強度鋼板およびその製造方法
JP5418047B2 (ja) * 2008-09-10 2014-02-19 Ｊｆｅスチール株式会社 高強度鋼板およびその製造方法
JP5347392B2 (ja) 2008-09-12 2013-11-20 Ｊｆｅスチール株式会社 延性に優れたホットプレス部材、そのホットプレス部材用鋼板、およびそのホットプレス部材の製造方法
JP2010174301A (ja) * 2009-01-28 2010-08-12 Jfe Steel Corp ダイクエンチ用鋼板
JP4811528B2 (ja) 2009-07-28 2011-11-09 Ｊｆｅスチール株式会社 高強度冷延鋼板およびその製造方法
JP5786317B2 (ja) 2010-01-22 2015-09-30 Ｊｆｅスチール株式会社 材質安定性と加工性に優れた高強度溶融亜鉛めっき鋼板およびその製造方法
JP4903915B2 (ja) 2010-01-26 2012-03-28 新日本製鐵株式会社 高強度冷延鋼板及びその製造方法
JP5779907B2 (ja) 2010-02-26 2015-09-16 新日鐵住金株式会社 熱処理用鋼材
EP2374910A1 (de) 2010-04-01 2011-10-12 ThyssenKrupp Steel Europe AG Stahl, Stahlflachprodukt, Stahlbauteil und Verfahren zur Herstellung eines Stahlbauteils
JP5440371B2 (ja) 2010-05-12 2014-03-12 新日鐵住金株式会社 熱処理用鋼板およびその製造方法
CN102409235A (zh) * 2010-09-21 2012-04-11 鞍钢股份有限公司 高强度冷轧相变诱导塑性钢板及其制备方法
BR112013009520B1 (pt) 2010-10-22 2019-05-07 Nippon Steel & Sumitomo Metal Corporation Métodos para produção de chassi estampado a quente e chassi estampado a quente
TWI452148B (zh) 2011-05-13 2014-09-11 Nippon Steel & Sumitomo Metal Corp 熱壓印成形品、熱壓印成形品之製造方法、能量吸收構件及能量吸收構件之製造方法
PL2803744T3 (pl) 2012-01-13 2018-11-30 Nippon Steel & Sumitomo Metal Corporation Blacha stalowa cienka walcowana na zimno i sposób jej wytwarzania
PL2803746T3 (pl) 2012-01-13 2019-09-30 Nippon Steel & Sumitomo Metal Corporation Stal wytłaczana na gorąco i sposób jej wytwarzania
RU2586387C2 (ru) 2012-01-13 2016-06-10 Ниппон Стил Энд Сумитомо Метал Корпорейшн Холоднокатаный стальной лист и способ изготовления холоднокатаного стального листа
US10072324B2 (en) 2012-08-06 2018-09-11 Nippon Steel & Sumitomo Metal Corporation Cold-rolled steel sheet and method for manufacturing same, and hot-stamp formed body
CA2879069C (en) 2012-08-07 2016-08-16 Nippon Steel & Sumitomo Metal Corporation Galvanized steel sheet for hot forming

Also Published As

Publication number Publication date
KR101674331B1 (ko) 2016-11-08
US10570470B2 (en) 2020-02-25
JP5505574B1 (ja) 2014-05-28
EP2886674B1 (en) 2020-09-30
KR20150029742A (ko) 2015-03-18
TWI481729B (zh) 2015-04-21
RU2015108067A (ru) 2016-10-10
JPWO2014027682A1 (ja) 2016-07-28
CA2880946C (en) 2018-06-12
RU2599934C2 (ru) 2016-10-20
WO2014027682A1 (ja) 2014-02-20
CN109023051A (zh) 2018-12-18
ZA201501490B (en) 2016-01-27
CA2880946A1 (en) 2014-02-20
EP2886674A1 (en) 2015-06-24
EP2886674A4 (en) 2016-11-30
CN104583437A (zh) 2015-04-29
IN2015DN00705A (cg-RX-API-DMAC10.html) 2015-06-26
TW201410878A (zh) 2014-03-16
US20150284819A1 (en) 2015-10-08

Similar Documents

Publication Publication Date Title
MX2015001772A (es) Plancha de acero para uso en prensado en caliente, metodo para producirla, y miembro de plancha de acero de prensado en caliente.
US10662495B2 (en) High-strength steel sheet and production method for same, and production method for high-strength galvanized steel sheet
US10550446B2 (en) High-strength steel sheet, high-strength hot-dip galvanized steel sheet, high-strength hot-dip aluminum-coated steel sheet, and high-strength electrogalvanized steel sheet, and methods for manufacturing same
KR101449222B1 (ko) 열처리 강재와 그 제조 방법 및 그 소재 강재
US10570475B2 (en) High-strength steel sheet and production method for same, and production method for high-strength galvanized steel sheet
KR101621639B1 (ko) 강판, 도금 강판 및 그들의 제조 방법
US20190106760A1 (en) Steel sheet, coated steel sheet, and methods for manufacturing same
US20170306435A1 (en) High-strength steel sheet, high-strength hot-dip galvanized steel sheet, high-strength hot-dip aluminum-coated steel sheet, and high-strength electrogalvanized steel sheet, and methods for manufacturing same
KR102245332B1 (ko) 고강도 강판 및 그 제조 방법
CN105518173A (zh) 热冲压成型体以及其制造方法
JP6288248B2 (ja) ホットスタンプ鋼材
KR102483105B1 (ko) 피복 강 부재, 피복 강판 및 그것들의 제조 방법
US10435761B2 (en) Heat-treated steel material and method of manufacturing the same
US20170204490A1 (en) High-strength steel sheet and production method for same, and production method for high-strength galvanized steel sheet
US20190276907A1 (en) Steel sheet, coated steel sheet, and methods for manufacturing same
CN103781932A (zh) 冷轧钢板
KR20150119362A (ko) 고강도 합금화 용융 아연 도금 강판 및 그 제조 방법
US20250066887A1 (en) Steel sheet for hot-stamping, method for manufacturing steel sheet for hot-stamping, and hot-stamped formed body
JP6314511B2 (ja) 冷延鋼板
WO2024122117A1 (ja) ホットスタンプ成形体
WO2024122124A1 (ja) ホットスタンプ成形体
CN120380182A (zh) 热冲压成形体