MD1382Z - Process for corrosion protection of steel in water - Google Patents
Process for corrosion protection of steel in water Download PDFInfo
- Publication number
- MD1382Z MD1382Z MDS20190048A MDS20190048A MD1382Z MD 1382 Z MD1382 Z MD 1382Z MD S20190048 A MDS20190048 A MD S20190048A MD S20190048 A MDS20190048 A MD S20190048A MD 1382 Z MD1382 Z MD 1382Z
- Authority
- MD
- Moldova
- Prior art keywords
- corrosion
- water
- steel
- inhibitor
- bgc
- Prior art date
Abstract
Invenţia se referă la protecţia metalelor de coroziune în apă şi poate fi utilizată pentru a inhiba coroziunea în sistemele închise ale conductelor de oţel.Procedeul de protecţie a oţelului de coroziune în apă constă în introducerea în mediul coroziv a 50-150 mg/l de borogluconat de calciu şi 50-150 mg/l de acetat de sodiu.Rezultatul tehnic al invenţiei constă în reducerea vitezei de coroziune a oţelului în apă.The invention relates to the protection of metals from corrosion in water and can be used to inhibit corrosion in closed systems of steel pipes. calcium and 50-150 mg / l sodium acetate. The technical result of the invention is to reduce the corrosion rate of steel in water.
Description
Invenţia se referă la protecţia metalelor de coroziune în apă şi poate fi utilizată pentru a inhiba coroziunea în sistemele închise ale conductelor de oţel. The invention relates to the protection of metals from corrosion in water and can be used to inhibit corrosion in closed steel pipeline systems.
Se ştie că apa naturală sau de proces care conţine ioni de clor şi sulfat este un mediu destul de agresiv, în care coroziunea oţelului se desfăşoară cu viteză mare. La Chişinău în apa de la robinet, care conţine, în mg/l: Ca2+ - 72,5, Mg2+ - 19,5, HCO3 - - 98,0, SO4 2- - 204,0, Cl- - 57,0 cu un conţinut total de sare de 0,4507 mg/l, viteza de coroziune a oţelului St. 3 la 8 ore de testări este mare, ajungând la 21 g/m2·zi. Pe măsură ce timpul de expunere creşte, viteza de coroziune scade (de exemplu până la 12 g/m2· zi la 24 de ore, 66 g/m2·zi la 72 ore şi 4 g/m2·zi la 240 ore) datorită formării peliculei de oxid-hidroxid pe suprafaţa de corodare a produselor de coroziune, precum şi a calcitului CaCO3. Ionii de SO4 2- provoacă o coroziune generală destul de uniformă. Totuşi, pe suprafaţa interioară a ţevilor se pot forma ciupituri adânci, datorită prezenţei ionilor de clor activ în apă. În plus, fierul ionizat, care trece în apă, se acumulează acolo, afectând calitatea sa (Паршутин В. В., Шолтоян Н. С., Андреева Л. Н., Володина Г. Ф., Лозан В. И., Болога О. А., Гэрбэлэу Н. В. Ингибирование глюконатом кальция коррозии углеродистой стали Ст. 3 в воде. Электронная обработка материалов, 1999, № 1, p. 43-55). It is known that natural or process water containing chlorine and sulfate ions is a rather aggressive environment, in which steel corrosion proceeds at a high rate. In Chisinau in tap water, which contains, in mg/l: Ca2+ - 72.5, Mg2+ - 19.5, HCO3 - - 98.0, SO4 2- - 204.0, Cl- - 57.0 with a total salt content of 0.4507 mg/l, the corrosion rate of St. 3 steel at 8 hours of testing is high, reaching 21 g/m2·day. As the exposure time increases, the corrosion rate decreases (e.g. to 12 g/m2· day at 24 hours, 66 g/m2· day at 72 hours and 4 g/m2· day at 240 hours) due to the formation of an oxide-hydroxide film on the corrosion surface of the corrosion products, as well as calcite CaCO3. SO4 2- ions cause a fairly uniform overall corrosion. However, deep pitting can form on the inner surface of the pipes, due to the presence of active chlorine ions in the water. In addition, ionized iron, which passes into the water, accumulates there, affecting its quality (Паршутин В. В., Шолтоян Н. С., Андреева Л. Н., Володина Г. Ф., Лозан В. И., Болога О. А., Гербелэу Н. В. Ингибирование глуконатом калция корозии угледористой стали St. 3 в воде. Електронная обработа материов, 1999, № 1, pp. 43-55).
Este cunoscută utilizarea borogluconatului de calciu ca inhibitor al coroziunii [1]. S-a constatat că proprietăţile inhibitoare ale compusului sunt îmbunătăţite prin creşterea concentraţiei acestuia. Calcium borogluconate is known to be used as a corrosion inhibitor [1]. It has been found that the inhibitory properties of the compound are improved by increasing its concentration.
Dezavantajul acestui inhibitor este următorul. În apa distilată, care conţine mai puţină sare decât apa de la robinet, efectul borogluconatului de calciu este mai pronunţat. În apa de la robinet, în special în cazul circulaţiei forţate a unui mediu coroziv, efectul este mult mai scăzut. În acelaşi timp, există o scădere foarte inegală a pierderii de coroziune în timp: acţiunea sa deseori slăbeşte odată cu creşterea timpului de expunere a probei, ceea ce este nedorit; se observă o diferenţă în valorile coeficientului de inhibare. La concentraţii scăzute ale inhibitorului (de 5-200 mg/l) efectul său este neglijabil. The disadvantage of this inhibitor is the following. In distilled water, which contains less salt than tap water, the effect of calcium borogluconate is more pronounced. In tap water, especially in the case of forced circulation of a corrosive medium, the effect is much lower. At the same time, there is a very uneven decrease in corrosion loss over time: its action often weakens with increasing sample exposure time, which is undesirable; a difference in the values of the inhibition coefficient is observed. At low concentrations of the inhibitor (5-200 mg/l) its effect is negligible.
Deoarece borogluconatul de calciu este o substanţă destul de costisitoare, pentru reducerea costului inhibitorului, dar în acelaşi timp pentru creşterea efectului său de inhibare a coroziunii, este logic să se găsească aditivii necesari pentru borogluconatul de calciu pentru a reduce concentraţia acestuia şi a conduce la o inhibare mai mare a procesului de coroziune. Since calcium borogluconate is a rather expensive substance, in order to reduce the cost of the inhibitor, but at the same time increase its corrosion inhibition effect, it is logical to find the necessary additives for calcium borogluconate to reduce its concentration and lead to greater inhibition of the corrosion process.
Problema pe care o rezolvă invenţia este de a mări rezistenţa la coroziune a sistemelor închise ale conductelor de oţel, în care purtătorul este apa. The problem solved by the invention is to increase the corrosion resistance of closed steel pipe systems, in which the carrier is water.
Problema propusă este rezolvată prin procedeul de protecţie a oţelului de coroziune în apă, care constă în introducerea în mediul coroziv a 50-150 mg/l de borogluconat de calciu şi 50-150 mg/l de acetat de sodiu. The proposed problem is solved by the process of protecting steel from corrosion in water, which consists of introducing 50-150 mg/l of calcium borogluconate and 50-150 mg/l of sodium acetate into the corrosive environment.
Rezultatul tehnic al invenţiei propuse este o reducere semnificativă a pierderilor prin coroziune, asigurând o suprimare uniformă a coroziunii în timp, reducând costul inhibitorului, datorită introducerii suplimentare a acetatului de sodiu în compoziţia sa. The technical result of the proposed invention is a significant reduction in corrosion losses, ensuring uniform corrosion suppression over time, reducing the cost of the inhibitor, due to the additional introduction of sodium acetate into its composition.
Testele la coroziune ale probelor cu dimensiunile de 50 × 25 × 3 mm au fost efectuate cu imersie completă în soluţie la aceeaşi adâncime cu accesul aerului. Rugozitatea lor iniţială a fost stabilită prin şlefuire. Pierderile la coroziune au fost înregistrate gravimetric. Efectul de acţiune al inhibitorului a fost evaluat cantitativ prin viteza de coroziune k, g/m2 · zi şi valoarea coeficientului de inhibare Γ = k1/k, unde k1, k sunt vitezele de coroziune ale metalului, respectiv cu şi fără utilizarea inhibitorului. Acest coeficient indică de câte ori viteza de coroziune se micşorează ca urmare a acţiunii inhibitorului. Corrosion tests of samples with dimensions of 50 × 25 × 3 mm were carried out with complete immersion in the solution at the same depth as the air access. Their initial roughness was established by grinding. Corrosion losses were recorded gravimetrically. The effect of the inhibitor action was quantitatively evaluated by the corrosion rate k, g/m2 · day and the value of the inhibition coefficient Γ = k1/k, where k1, k are the corrosion rates of the metal, respectively with and without the use of the inhibitor. This coefficient indicates how many times the corrosion rate decreases as a result of the inhibitor action.
Efectul concentraţiei inhibitorului şi a timpului de încercare asupra vitezei de coroziune k, g/m2 · zi şi a coeficientului de inhibare Γ este prezentat în tabel. The effect of inhibitor concentration and test time on the corrosion rate k, g/m2 · day and the inhibition coefficient Γ is presented in the table.
Din datele prezentate se poate observa că atunci, când se utilizează numai borogluconatul de calciu cu o concentraţie de 50-150 mg/l, valoarea maximă a lui Γ nu depăşeşte mărimea de 6,3 (la 150 mg/l, după 24 de ore de testări), iar valoarea coeficientului Γ este extrem de neuniformă în timpul expunerii (de exemplu, la 8 ore şi la o concentraţie de 50 mg/l, Γ = 4,2, iar la 120 de ore de expunere, valoarea sa scade aproape de două ori - până la 2,8). From the presented data it can be seen that when only calcium borogluconate is used with a concentration of 50-150 mg/l, the maximum value of Γ does not exceed 6.3 (at 150 mg/l, after 24 hours of testing), and the value of the Γ coefficient is extremely uneven during exposure (for example, at 8 hours and at a concentration of 50 mg/l, Γ = 4.2, and at 120 hours of exposure, its value decreases almost twice - to 2.8).
Adăugarea suplimentară a acetatului de sodiu în cantitate de 50-150 mg/l la 50 mg/l de borogluconat de calciu măreşte în mod semnificativ inhibarea coroziunii şi uniformizează procesul de inhibare. Astfel, cu introducerea borogluconatului de calciu în cantitate de 50 mg/l, valoarea maximă a lui Γ nu depăşeşte 4,2 la 8 ore de testări, scăzând la 120 ore cu mai mult de 2 ori. Adăugarea acetatului de sodiu în cantitate de 50-150 mg/l măreşte valoarea lui Γ până la 7,3, uniformizând în mod semnificativ inhibarea coroziunii în timp. The additional addition of sodium acetate in the amount of 50-150 mg/l to 50 mg/l of calcium borogluconate significantly increases the corrosion inhibition and evens out the inhibition process. Thus, with the introduction of calcium borogluconate in the amount of 50 mg/l, the maximum value of Γ does not exceed 4.2 at 8 hours of testing, decreasing at 120 hours by more than 2 times. The addition of sodium acetate in the amount of 50-150 mg/l increases the value of Γ up to 7.3, significantly evening out the corrosion inhibition over time.
Adăugarea a 100 mg/l de acetat de sodiu la 150 mg/l de borogluconat de calciu arată că valoarea lui Γ atinge mărimea de 8,3 la 8 ore de testări şi 8,6 la introducerea suplimentară a 150 mg/l de acetat de sodiu. În acelaşi timp, micşorarea valorilor lui Γ în timp este mult mai mică decât în cazul utilizării numai a borogluconatului de calciu. The addition of 100 mg/l of sodium acetate to 150 mg/l of calcium borogluconate shows that the value of Γ reaches the value of 8.3 after 8 hours of testing and 8.6 upon the additional introduction of 150 mg/l of sodium acetate. At the same time, the decrease in Γ values over time is much smaller than in the case of using calcium borogluconate alone.
Tabel Table
Efectul compoziţiei inhibitorilor asupra parametrilor procesului de coroziune a oţelului St. 3 în apă. The effect of inhibitor composition on the corrosion process parameters of St. 3 steel in water.
Concentraţia inhibitorilor, mg/l Timpul încercărilor, h Viteza de coroziune, k, g/m2 · zi Coeficientul de inhibare, Γ 0 8 24 72 120 21,0 12,0 6,6 4,6 - - - - Borogluconatul de calciu (BGC) 50 8 24 72 120 5,0 2,86 2,2 1,64 4,2 4,2 3,0 2,8 BGC 100 8 24 72 120 4,1 2,4 1,69 1,3 5,1 5,0 3,9 3,5 BGC 150 8 24 72 120 3,3 2,4 1,43 1,0 6,3 5,7 4,6 4,6 BGC 50+ CH3COONa 50 8 24 72 120 3,68 2,11 1,38 1,02 5,7 5,7 4,8 4,5 BGC 50+ CH3COONa 100 8 24 72 120 3,04 2,03 1,29 0,96 6,9 5,9 5,1 4,8 BGC 50+ CH3COONa 150 8 24 72 120 2,96 1,64 0,97 0,71 7,1 7,3 6,8 6,5 BGC 100+ CH3COONa 50 8 24 72 120 3,26 1,89 1,17 0,79 6,45 6,36 5,65 5,8 BGC 100+ CH3COONa 100 8 24 72 120 2,92 1,76 0,99 0,78 7,2 6,8 6,7 5,9 BGC 100+ CH3COONa 150 8 24 72 120 2,8 1,74 1,05 0,79 7,5 6,9 6,3 5,8 BGC 150+ CH3COONa 50 8 24 72 120 2,59 1,53 0,87 0,61 8,1 7,85 7,6 7,6 BGC 150+ CH3COONa 100 8 24 72 120 2,53 1,56 0,87 0,61 8,3 7,7 7,6 7,6 BGC 150+ CH3COONa 150 8 24 72 120 2,44 1,52 0,86 0,61 8,6 7,9 7,7 7,6Inhibitor concentration, mg/l Test time, h Corrosion rate, k, g/m2 · day Inhibition coefficient, Γ 0 8 24 72 120 21.0 12.0 6.6 4.6 - - - - Calcium borogluconate (BGC) 50 8 24 72 120 5.0 2.86 2.2 1.64 4.2 4.2 3.0 2.8 BGC 100 8 24 72 120 4.1 2.4 1.69 1.3 5.1 5.0 3.9 3.5 BGC 150 8 24 72 120 3.3 2.4 1.43 1.0 6.3 5.7 4.6 4.6 BGC 50+ CH3COONa 50 8 24 72 120 3.68 2.11 1.38 1.02 5.7 5.7 4.8 4.5 BGC 50+ CH3COONa 100 8 24 72 120 3.04 2.03 1.29 0.96 6.9 5.9 5.1 4.8 BGC 50+ CH3COONa 150 8 24 72 120 2.96 1.64 0.97 0.71 7.1 7.3 6.8 6.5 BGC 100+ CH3COONa 50 8 24 72 120 3.26 1.89 1.17 0.79 6.45 6.36 5.65 5.8 BGC 100+ CH3COONa 100 8 24 72 120 2.92 1.76 0.99 0.78 7.2 6.8 6.7 5.9 BGC 100+ CH3COONa 150 8 24 72 120 2.8 1.74 1.05 0.79 7.5 6.9 6.3 5.8 BGC 150+ CH3COONa 50 8 24 72 120 2.59 1.53 0.87 0.61 8.1 7.85 7.6 7.6 BGC 150+ CH3COONa 100 8 24 72 120 2.53 1.56 0.87 0.61 8.3 7.7 7.6 7.6 BGC 150+ CH3COONa 150 8 24 72 120 2.44 1.52 0.86 0.61 8.6 7.9 7.7 7.6
Cantitatea de inhibitor introdusă în mediul coroziv joacă un rol hotărâtor. The amount of inhibitor introduced into the corrosive environment plays a decisive role.
Limita inferioară atât a borogluconatului de calciu, cât şi a acetatului de sodiu sunt de 50 mg/l, iar reducerea acestei concentraţii conduce la o inhibare mai scăzută a coroziunii. The lower limit of both calcium borogluconate and sodium acetate is 50 mg/l, and reducing this concentration leads to lower corrosion inhibition.
Limita superioară a adăugării acetatului de sodiu este de 150 mg/l, o creştere suplimentară a concentraţiei sale are un efect mic asupra gradului de inhibare a coroziunii, însă duce la creşterea costului inhibitorului. The upper limit of sodium acetate addition is 150 mg/l, a further increase in its concentration has a small effect on the degree of corrosion inhibition, but leads to an increase in the cost of the inhibitor.
Astfel, a fost elaborat un inhibitor eficace, destul de ecologic împotriva coroziunii oţelului în apă, care permite semnificativ de a micşora pierderile la coroziune până la 8,6 ori. Thus, an effective, fairly environmentally friendly inhibitor against steel corrosion in water was developed, which allows significantly reducing corrosion losses by up to 8.6 times.
1. Паршутин В.В., Шолтоян Н.С., Сидельникова С.П., Володина Г.Ф. Ингибирование бороглюконатом кальция коррозии углеродистой стали Ст. 3 в воде. Коррозия в условиях естественной аэрации и принудительной конвекции. Электронная обработка материалов. 1999, № 5, p. 42-56 1. Parshutin V.V., Sholtoyan N.S., Sidelnikova S.P., Volodina G.F. Ингибирование бороглюконатом калция корозии углеродистой стали Ст. 3 in the water. Corrosion in the conditions of natural aeration and forced convection. Electronic processing of materials. 1999, No. 5, p. 42-56
Claims (1)