LT4111B - Process for preparing the electrical conductive coatings on polyethylene - Google Patents
Process for preparing the electrical conductive coatings on polyethylene Download PDFInfo
- Publication number
- LT4111B LT4111B LT95-047A LT95047A LT4111B LT 4111 B LT4111 B LT 4111B LT 95047 A LT95047 A LT 95047A LT 4111 B LT4111 B LT 4111B
- Authority
- LT
- Lithuania
- Prior art keywords
- solution
- coatings
- polyethylene
- preparing
- water
- Prior art date
Description
Išradimas priklauso polimerinių medžiagų savybių modifikavimo sričiai ir gali būti panaudotas elektrai laidžių sulfidinių dangų ant jų sudarymui, įgalinant šias medžiagas galvaniškai metalizuoti.
Žinomas elektrai laidžių sulfidinių dangų ant kai kurių polimerinių medžiagų (poliamido, polistirolo) gavimo būdas, kai polimerinės medžiagos paviršius veikiamas metalų druskų tirpalu, vėliau- natrio sulfido tirpalu ( žiūr. buv. TSRS autor. liud. Nr. 1110819, TPK C 23 C 3/02, 1984).
Šiuo būdu negaunamos pakankamai laidžios elektrai sulfidinės dangos ant kai kurių polimerinių medžiagų.
Artimiausias siūlomam sprendimui yra elektrai laidžių sulfidinių dangų gavimo būdas, kai pradžioje polimerinės medžiagos sierinamos šarminiu sieros tirpalu, nuplaunamos parūgštintu vandeniu ir po to veikiamos vario druskos tirpalu (žiūr. buv. TSRS autor. liud. Nr.895542, TPK B 05 D 5/12, C 23 C 3/02, 1982).
v
Šiuo būdu gautos sulfidinės dangos ant mažo tankumo polietileno nėra pakankamai laidžios ir netinka tolesnei galvaninei metalizacijai. Šiame išradime polimerinių medžiagų sierinimui naudojamas stipriai šarminis sieros tirpalas, o tai tinka ne visoms medžiagoms. Be to, naudojami vario druskos tirpalai nėra stabilūs.
Siūlomo išradimo tikslas- gauti elektrai laidžias dangas ant mažo tankumo polietileno naudojant rūgštų sierinimo tirpalą- politionines rūgštis.
Tikslas pasiekiamas tuo, kad polietileno plėvelė sierinama 0,002M politioninės rūgšties H2SnO6, kur n- vidutinis sieros atomų skaičius molekulėje, tirpale, nuplaunama vandeniu ir veikiama vario druskos su reduktoriumi (hidrochinonu) tirpalu.
PAVYZDYS:
Mažo tankumo polietileno plėvelės bandiniai veikiami maišomu 60-80°C temperatūros 0,002M politioninės rūgšties tirpalu 304-90 minučių, plaunami 2v5s vandeniu ir merkiami į vario druskos su v
hidrochinonu tirpalą, turintį vienvalenčio vario jonų. Šiuo 50-80°C temperatūros tirpalu sierinti bandiniai veikimi 0,254-2,5 minutės, po to 2^-5s plaunami vandeniu. Matuojama sausų polietileno plėvelės bandinių su vario sulfido danga paviršiaus varža. Paviršiaus varžos yra 184-65Ω/Ο. Duomenys pateikti 1 lentelėje.
lentelė
| Sierini- | Tirpalo | Sierinimo | Vario druskos | Veikimo | Pavir- | ||
| mo | molinė | sąlygos | tirpalo sudėtis, | vario | šiauš | ||
| agentas | koncen- | g | druskos | varža, | |||
| tracija | tirpalu | Ω/Ο | |||||
| sąlygos | |||||||
| Tem | Laik | Tem | Laik | ||||
| perą | as, | perą | as, | ||||
| tūra, | min. | tūra, | min. | ||||
| °C | °C | ||||||
| Η2δ33θ6 | 0,002 | 60 | 60 | Vario sulfato kristalohidra- | 80 | 0.5 | 38-44 |
| • | tas 10 | ||||||
| Hidrochinonas | |||||||
| 1,1 | |||||||
| Vanduo 100 | |||||||
| u | zz | _Zf_ | 90 | ZZ | zz | 0,25 | 35-40 |
| r f _ | J! | JI - | ZZ | zz | zz | 0,5 | 18-22 |
| tf | zz | zz | zz | zz | zz | 1,0 | 20-30 |
| ^zz_ | J! | ji ~ | Jf _ | 50 | 2,5 | 41-48 | |
| zz | zz | 80 | 30 | zz | 80 | 0,5 | 55-65 |
| H2S21°6 | n | 60 | 90 | _zz_ | ZZ | 1,0 | 47-50 |
lentelės tęsinys
| Sierini- mo agentas | Tirpalo molinė koncen- tracija | Sierinimo sąlygos | Vano druskos tirpalo sudėtis, g | Veikimo vario druskos tirpalu sąlygos | Pavir- šiaus varža, Ω/α | ||
| Tem perą tūra, °C | Laik as, min. | Tem perą tūra, °C | Laik as, min. | ||||
| Analo- gas v Šarminis sieros tirpalas ff | 2,0 ff | 80 ff | 5 ff | Vario sulfato kristalohidratas 10 Kalio chloridas 0,1 Natrio sulfitas 1,0 Vanduo 100 Vario chloridas 0,1 Vanduo 100 Kone. druskos rūgštis 0,1 | 70 ff | 1.0 JI _ | 40000- 55000 1200- 1700 |
Iš lentelės matome, kad naudojant praskiestą politioninės rūgšties tirpalą polietileno plėvelės bandinių sierinimui, o vėliau juos paveikus vario druskos su hidrochinonu tirpalu, gaunamos sulfidinės dangos su! žymiai mažesnėmis nei analoge paviršiaus varžomis.
Siūlomas išradimas, palyginus j j su žinomu, pasižymi šiais privalumais:
- leidžia žymiai sumažinti mažo tankumo polietileno plėvelės paviršiaus varžą;
- naudojant tokią plėvelę elektrocheminei metalizacijai, lengvai gaunamos geros kokybės dangos;
- polimero sierinimui naudojamas nedidelės koncentracijos politioninės rūgšties tirpalas, todėl mažiau teršiama aplinka; -naudojamos medžiagos yra nedeficitinės ir pigios.
Claims (1)
- IŠRADIMO APIBRĖŽTISElektrai laidžių dangų ant polietileno gavimo būdas, kuriame polimerines medžiagas sierina, nuplauna vandeniu, po to veikia druskos tirpalu, besiskiriantis tuo, kad polietileno plėvelę sierina 0,002 M politioninės rūgšties tirpale ir veikia vario druskos su hidrochinonu tirpalu.