KR970070229A - 플라스틱용 금형의 제조를 위한 저 합금강 - Google Patents
플라스틱용 금형의 제조를 위한 저 합금강 Download PDFInfo
- Publication number
- KR970070229A KR970070229A KR1019970016098A KR19970016098A KR970070229A KR 970070229 A KR970070229 A KR 970070229A KR 1019970016098 A KR1019970016098 A KR 1019970016098A KR 19970016098 A KR19970016098 A KR 19970016098A KR 970070229 A KR970070229 A KR 970070229A
- Authority
- KR
- South Korea
- Prior art keywords
- steel
- steel according
- zirconium
- titanium
- weight
- Prior art date
Abstract
화학 조성이 중량%로서 0.35%≤C≤0.5%, 0%≤Si≤0.5%, 0.2%≤Mn≤2.5%, 0%≤Ni≤4%, 0%≤Cr≤4%, 0%≤Mo+W/2≤2%, 0%≤Cu≤1%, 0%≤V+Nb/2+Ta/4≤0.5%, 0.005%≤Al≤0.2%, 0%≤B≤0.015%, 0%≤Ti+Zr/2≤0.3%, 0%≤S+Se+Te≤0.2%, 0%≤Pb+Bi≤0.2%, 0%≤Ca≤0.1% 이고, 나머지의 철 및 생산에서 발생된 불순물을 함유하며, 동시에 관계식 Cr+3×(Mo+W/2)+10×(V+Nb/2+Ta/4)≥1, R=3.8×C+10×Si+3.3×Mn+2.4×Ni+1.4×(Cr+Mo+W/2)≤11, Qu=3.8×C+1.1×Mn+0.7×Ni+0.6 ×Cr+1.6×(Mo+W/2)+kB≥3 (B≥0.0005% 이라면 kB=0.5, 그렇지 않다면 kB=0) 및 R≤Max(2.33×Qu-1, 0.9×Qu+4)을 만족하는 분석치를 갖는, 플라스틱의 사출 성형을 위한 금형의 제조용 강철.
Description
본 내용은 요부공개 건이므로 전문내용을 수록하지 않았음
Claims (11)
- 화학 조성이 중량%로서 0.35%≤C≤0.5%, 0%≤Si≤0.5%, 0.2%≤Mn≤2.5%, 0%≤Ni≤4%, 0%≤Cr≤4%, 0%≤Mo+W/2≤2%, 0%≤Cu≤1%, 0%≤V+Nb/2+Ta/4≤0.5%, 0.005%≤Al≤0.2%, 0%≤B≤0.015%을 함유하고, -임의로, 티타늄 함량 및 지르코늄 함량의 1/2의 합이 0.3중량%이하가 되는 양으로 티타늄 및 지르코늄에서 선택된 하나 이상의 원소, -임의로, 황, 셀레늄 및 텔루륨의 함량의 합이 0.2중량% 이하가 되는 양으로 황, 셀레늄 및 텔루륨에서 선택된 하나 이상의 원소, -임의로, 납 및 비스무트의 함량의 합이 0.2중량% 이하가 되는 양으로 납 및 비스무트에서 선택된 하나 이상의 원소, -임의로, 0.1중량% 이하의 칼슘을 함유하고, 나머지의 철 및 생산에서 발생된 불순물을 함유하며; 동시에 하기 관계식; Cr+3×(Mo+W/2)+10 ×(V+Nb/2+Ta/4)≥1, R=3.8×C+10×Si+3.3×Mn+2.4×Ni+1.4×(Cr+Mo+W/2)≤11, Qu=3.8×C+1.1×Mn+0.7×Ni+0.6 ×Cr+1.6×(Mo+W/2)+kB≥3, (B≥0.0005% 이라면 kB= 0.5, 그렇지 않다면 kB=0) 및 R≤Max(2.33×Qu-1, 0.9×Qu+4)을 만족하는 분석치를 갖는 플라스틱의 사출 성형을 위한 금형의 제조용 강철.
- 제1항에 있어서, Si≤0.15%임을 특징으로 하는 강철.
- 제1항 또는 제2항에 있어서 B≥0.0005%임을 특징으로 하는 강철.
- 제1항 내지 제3항 중 어느 한 항에 있어서, R≤9임을 특징으로 하는 강철.
- 제1항 내지 제4항 중 어느 한 항에 있어서, Qu≥4.3임을 특징으로 하는 강철.
- 제1항 내지 제5항 중 어느 한 항에 있어서, Si≤0.1%임을 특징으로 하는 강철.
- 제1항 내지 제6항 중 어느 한 항에 있어서, 0.37%≤C≤0.45%, 0%≤Si≤0.15%, 0.2%≤Mn≤1.5%, 0%≤Ni≤0.5%, 0%≤Cr≤2.5%, 0%≤Mo+W/2≤1%, 0%≤Cu≤1%, 0%≤V+Nb/2+Ta/4≤0.2%, 0.005%≤Al≤0.2%, 0.0005%≤B≤0.015%, 0%≤Ti+Zr/2≤0.3% 및 R≤2.33×Qu-2.4임을 특징으로 하는 강철.
- 제1항 내지 제7항 중 어느 한 항에 있어서, 티타늄, 지르코늄 및 질소 함량(중량%)이 바람직하게는 0.00003≤(N)×(Ni+Zr/2)≤0.0016의 범위내이고, 고체 상태에서 미소축쇄 면의 1㎟영역에서 계수된 0.1㎛초과의 크기를 가진 질소화 티타늄 또는 질소화 지르코늄 침전물의 수가, 질소화물의 형태로 침전된 티타늄의 총 함량 및 질소화물의 형태로 침전된 지르코늄의 총 함량의 1/2의 합(1/1000단위의 중량%로 표현됨)의 4배 미만임을 특징으로 하는 강철.
- 특징적인 치수가 20mm 내지 1500mm이고, 모든 부위에서 강철의 구조가 마텐자이트 또는 베이나이트 구조이며, 모든 부위에서 250 브리넬 내지 370 브리넬의 경도를 가짐을 특징으로 하는 제1항 내지 제8항 중 어느 한 항에 따른 강철의 블록.
- 주물 기술에 의해 플라스틱용 금형을 제조하기 위한 제1항 내지 제8항 중 어느 한 항에 따른 강철의 용도.
- 제1항 내지 제8항 중 어느 한 항에 따른 강철로 구성됨을 특징으로 하는 용접용 또는 용점 전극의 제조용 와이어.※ 참고사항 : 최초출원 내용에 의하여 공개하는 것임.