KR950703669A - 500℃ 이하의 온도에서 부식 및 침식작용으로 부터 크롬강 기판의 보호(protection of chromium-steel substrates aghinst corrosive and erosive attack at temperatures up to about 500℃) - Google Patents

500℃ 이하의 온도에서 부식 및 침식작용으로 부터 크롬강 기판의 보호(protection of chromium-steel substrates aghinst corrosive and erosive attack at temperatures up to about 500℃) Download PDF

Info

Publication number
KR950703669A
KR950703669A KR1019950701281A KR19950701281A KR950703669A KR 950703669 A KR950703669 A KR 950703669A KR 1019950701281 A KR1019950701281 A KR 1019950701281A KR 19950701281 A KR19950701281 A KR 19950701281A KR 950703669 A KR950703669 A KR 950703669A
Authority
KR
South Korea
Prior art keywords
substrate
erosion
corrosion
temperatures
metal layer
Prior art date
Application number
KR1019950701281A
Other languages
English (en)
Inventor
프리트헬름 쉬미츠
Original Assignee
디터 크리스트, 게르하르트 퀼
지멘스 악티엔게젤샤프트
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 디터 크리스트, 게르하르트 퀼, 지멘스 악티엔게젤샤프트 filed Critical 디터 크리스트, 게르하르트 퀼
Publication of KR950703669A publication Critical patent/KR950703669A/ko

Abstract

본 발명은 약 500℃ 이하의 온도에서 부식 및 침식작용으로 부터 크롬강 기판의 보호방법에 관한 것이다. 기판상에는 알루미늄을 함유한 보호층이 형성된다. 본 발명에 따라, 먼저 알루미늄을 함유한 금속층을 제공한 다음 적어도 그 표면을 경화 또는 어닐링시킴으로써 보호층을 형성한다. 본 발명에 의해 간단한 수단으로 그 표면을 경화 또는 어닐링시킴으로써 보호층을 형성한다. 본 발명에 의해 간단한 수단으로 터빈 특히 압축기의 블레이드가 부식 및 침식으로 부터 매우 효과적으로 보호될 수 있다.

Description

500℃ 이하의 온도에서 부식 및 침식작용으로 부터 크롬강 기판의 보호(PROTECTION OF CHROMIUM-STEEL SUBSTRATES AGHINST CORROSIVE AND EROSIVE ATTACK AT TEMPERATURES UP TO ABOUT 500℃)
본 내용은 요부공개 건이므로 전문내용을 수록하지 않았음

Claims (20)

  1. 알루미늄을 함유한 보호층을 기판상에 형성하는 방식으로 500℃ 이하의 온도에서 부식 및 침식작용으로 부터 크롬강 기판을 보호하기 위한 방법에 있어서, 기판상에 알루미늄을 함유한 금속층을 제공하는 단계, 및 적어도 그 표면을 경화 또는 어닐링함으로써 보호층을 형성하는 단계로 이루어지는 것을 특징으로 하는 500℃ 이하의 온도에서 부식 및 침식작용으로 부터 크롬강 기판의 보호방법.
  2. 제1항에 있어서, 주로 알루미늄으로, 특히 마그네슘, 구리 및 아연중 적어도 한 요소를 첨가한 알루미늄 합금으로 이루어진 금속층이 제공되는 것을 특징으로 하는 50o℃ 이하의 온도에서 부식 및 침식작용으로 부터 크롬강 기판의 보호방법.
  3. 제1항 또는 2항에 있어서, 보호층의 형성을 위해 적어도 금속층의 표면이 경화층으로 변환되는 것을 특징으로 하는 500℃ 이하의 온도에서 부식 및 침식작용으로 부터 크롬강 기판의 보호방법.
  4. 제3항에 있어서, 금속층이 적어도 장소별로 경화층으로 완전히 변환되는 것을 특징으로 하는 500℃ 이하의 온도에서 부식 및 침식작용으로 부터 크롬강 기판의 보호방법.
  5. 제3항 또는 4항에 있어서, 경화층 아래 적어도 장소별로 금속층의 일부가 남아 있는 것을 특징으로 하는 500℃ 이하의 온도에서 부식 및 침식작용으로 부터 크롬강 기판의 보호방법.
  6. 제3항, 4항 또는 5항에 있어서, 경화층이 금속층의 산화에 의해 형성되는 것을 특징으로 하는 500℃ 이하의 온도에서 부식 및 침식작용으로 부터 크롬근 기판의 보호방법.
  7. 제6항에 있어서, 산화가 양극 산화인 것을 특징으로 하는 500℃ 이하의 온도에서 부식 및 침식작용으로 부터 크롬강 보호방법.
  8. 제7항에 있어서, 경화층이 끓는 물 또는 끓는 수성 염용액으로 처리함으로써 응축되는 것을 특징으로 하는 500℃ 이하의 온도에서 부식 및 침식작용으로 부터 크롬강 기판의 보호방법.
  9. 제3항 내지 5항중 어느 한 항에 있어서, 금속층이 어닐링 가능한 합금으로 형성되고 경화층의 형성을 위해 어닐링되는 것을 특징으로 하는 500℃ 이하의 온도에서 부식 및 침식작용으로 부터 크롬강 기판의 보호방법.
  10. 제9항에 있어서, 합금이 마그네슘 및 구리 또는 아연을 첨가한 알루미늄 기초로 한 합금인 것을 특징으로 하는 500℃ 이하의 온도에서 부식 및 침식작용으로 부터 크롬강 기판의 보호방법.
  11. 상기 항들중 어느 한 항에 있어서, 15㎛ 내지 200㎛, 바람직하게는 40㎛ 내지 100㎛ 두께의 금속층이 형성되는 것을 특징으로 하는 500℃ 이하의 온도에서 부식 및 침식작용으로 부터 크롬강 기판의 보호방법.
  12. 상기 항들중 어느 한 항에 있어서, 금속층이 전기 화학적으로, 특히 아연도금에 의해 제공되는 것을 특징으로 하는 500℃ 이하의 온도에서 부식 및 침식작용으로 부터 크롬강 기판의 보호방법.
  13. 상기 항들중 어느 한 항에 있어서, 보호층이 기판상에 직접 제공되는 것을 특징으로 하는 500℃ 이하의 온도에서 부식 및 침식작용으로 부터 크롬강 기판의 보호방법.
  14. 상기 항들중 어느 한 항의 방법에 따라 제조된, 약 500℃ 이하의 온도에서 부식 및 침식작용으로 부터 보호를 수행하는 크롬강 기판상의 보호층.
  15. 약 500℃ 이하의 온도에서 부식 및 침식작용으로 부터의 보호를 위해 제 14항에 따른 보호층을 포함하는 기판.
  16. 제15항에 있어서, 기판이 터빈, 특히 터보 압축이의 블레이드, 특히 회전 블레이드 또는 가이드 블레이드에 속하는 것을 특징으로 하는 기판.
  17. 제15항에 있어서, 블레이드가 하단부 및 블레이드부를 포함하며 기판이 블레이드부에 속하는 것을 특징으로 하는 기판.
  18. 제15항 내지 17항중 어느 한 항에 있어서, 기판이 하기 조성(중량 퍼센트)의 크롬강으로 이루어지는 것을 특징으로 하는 기판: 0.1 내지 0.3% 탄소, 11 내지 17% 크롬, 0 내지 6% 니켈, 0 내지 1.5% 몰리브덴, 0 내지 1% 바나듐, 0 내지 1% 실리콘, 0 내지 1% 망간, 나머지는 철 및 제조로 인한 불순물.
  19. 제15항 내지 18항중 어느 한 항에 있어서, 기판이 적어도 부분적으로 페라이트 또는 마르텐사이트 구조를 갖는 것을 특징으로 하는 기판.
  20. 약 500℃ 이하의 온도에서 부식 및 침식작용으로 부터 보호되는 기판의 제조방법에 있어서, 제1항 내지 13항에 따른 보호방법이 기판의 제조방법에 사용되는 것을 특징으로 하는 기판의 제조방법.
    ※ 참고사항 : 최초출원 내용에 의하여 공개하는 것임.
KR1019950701281A 1992-10-05 1993-09-17 500℃ 이하의 온도에서 부식 및 침식작용으로 부터 크롬강 기판의 보호(protection of chromium-steel substrates aghinst corrosive and erosive attack at temperatures up to about 500℃) KR950703669A (ko)