KR940021465A - 광학상 투명한 감마 알루미늄 산화질소화물로 제조된 세라믹용 분말의 제조 방법 및 이 방법으로 수득한 분말 - Google Patents
광학상 투명한 감마 알루미늄 산화질소화물로 제조된 세라믹용 분말의 제조 방법 및 이 방법으로 수득한 분말 Download PDFInfo
- Publication number
- KR940021465A KR940021465A KR1019940006605A KR19940006605A KR940021465A KR 940021465 A KR940021465 A KR 940021465A KR 1019940006605 A KR1019940006605 A KR 1019940006605A KR 19940006605 A KR19940006605 A KR 19940006605A KR 940021465 A KR940021465 A KR 940021465A
- Authority
- KR
- South Korea
- Prior art keywords
- alumina
- powder
- specific surface
- less
- aluminum nitride
- Prior art date
Abstract
본 발명의 방법은 알루미늄 질소화물을 알파 알루미나 및 비표면적이 큰 알루미나 또는 비표면적이 큰 알루미나를 생성하는 전구체와 반응시키는 것이다. 보다 상세히 말한다면, 본 발명은 알루미늄 질소화물, 알파 알루미나 및 비표면적이 큰 알루미나 또는 이와 같은 알루미나의 전구체를 혼합하고, 이 혼합물을 건조시킨 후, 감마 알루미늄 산화질소화물 분말을 수득하기에 충분한 온도로 상기 혼합물을 가열하고, 수득한 분말을 연마시키는 것이다.
응집된 감마 알루미늄 산화질소화물 분말은 응집체의 다공도가 75% 이상이라는 특징을 가지고 있다.
연마된 감마 알루미늄 산화질소물 분말은 임자의 100%가 10㎛ 이하의 크기를 가지며, 3.33%의 감마 알루미늄 산화질소화물을 함유하는 0.9mm 두께의 KBr 디스크 상에서 2500cm-1에서 측정한 투과율이 8% 이상을 나타내고 있는 것을 특징으로 한다.
Description
본 내용은 요부공개 건이므로 전문내용을 수록하지 않았음
제1도는 본원 발명에 의해 수득한 감마 알루미늄 산화질소화물 분말의 현미경 사진이다.
제2도는 본원 발명에 의한 응집된 감마 알루미늄 산화질소화물의 블록을 붕괴시켜 수득한 6~15㎛ 크기의 고체 그레인으로 구성된 분말의 현미경 사진이다.
제3도는 연마하기가 매우 어려운 응집체 형태를 수득한 본원 발명의 감마 알루미늄 산화질소화물 분말의 현미경 사진이다.
Claims (17)
- 알루미늄 질소화물을 알파 알루미나 및 비표면적이 큰 알루미나 또는 비표면적이 큰 알루미나를 생성하는 알루미나의 전구체와 반응시키는 것을 특징으로 하는 광학상 투명한 세라믹용의 감마 알루미늄 산화질소화물 분말의 제조방법.
- 제1항에 있어서, 알루미늄 질소화물, 알파 알루미나 및 비표면적이 큰 알루미나 또는 이와 같은 알루미나의 전구체로 구성된 혼합물이 하기 비율로 구성된 것을 특징으로 하는 제조방법 : 16~40몰%의 알루미늄 질소화물, 알파 알루미나 및 비표면적이 큰 알루미나 또는 이와같은 알루미나의 전구체로 구성된 60~84몰%의 혼합물.
- 제1항 또는 제2항에 있어서, 알파 알루미나 및 비표면적이 큰 알루민나 또는 이와 같은 알루미나의 전구체로 구성된 혼합물중 알파 알루미나의 양이 5~95중량%인 것을 특징으로 하는 제조방법.
- 제1항 내지 제3항중 어느 한 항에 있어서, 입자들의 평균 직경이 10㎛보다 작으며, 순도가 높은 알루미늄 질소화물로부터 알루미늄 질소화물을 선택하는 것을 특징으로 하는 제조방법.
- 제1항 내지 제4항중 어느 한 항에 있어서, 알루미늄 질소화물이 3중량% 이하의 산소 함량을 가지며, 금속 분순물 농도가 5000ppm을 초과하지 않는 것을 특징으로 하는 제조방법.
- 제1항 내지 제5항중 어느 한 항에 있어서, 알파 알루미나 및 비표면적이 큰 알루미나 또는 이와 같은 알루미나의 전구체를 비표면적이 6~350㎡/g이고, 겉보기 밀도가 1㎏/dm³ 이하인 이들의 혼합물로부터 선택하는 것을 특징으로 하는 제조방법.
- 제1항 내지 제6항중 어느 한 항에 있어서, a) 알루미늄 질소화물을 알파 알루미나 및 비표면적이 큰 알루미나 또는 이와 같은 알루미나의 전구체와 혼합시키고, b) 이 혼합물을 건조시키며, c)이 혼합물을 감마 알루미늄 산화질소화물 분말을 수득하기에 충분한 온도로 가열하고, d) 수득한 분말을 연마시키는 단계로 구성된 것을 특징으로 하는 제조방법.
- 제7항에 있어서, 건조 공정을 700℃ 이하의 온도에서 질소, 아르곤, 헬륨, 크세논 및 공기로부터 선택한 건조한 기체 또는 기체 혼합물 도움하에 진행시키는 것을 특징으로 하는 제조방법.
- 제7항 또는 제8항에 있어서, 반응 온도가 1650~1900℃인 것을 특징으로 하는 제조방법.
- 제7항 내지 제9항중 어느 한 항에 있어서, 산소 원자를 전혀 함유하지 않는 질소 또는 질소 함유 기체 혼합물로부터 선택한 건조한 기체 존재하에 가열을 하는 것을 특징으로 하는 제조방법.
- 제1항 내지 제10항중 어느 한 항의 제조방법에 의해 수득한 감마 알루미늄 산화질소화물 분말.
- 제11항에 있어서, 응집된 형태를 하고 있는 것을 특징으로 하는 분말.
- 제12항에 있어서, 응집체의 다공도가 75% 이상인 것을 특징으로 하는 분말.
- 제12항 또는 제13항에 있어서, 300ppm 이하의 탄소함량 및 2중량% 미만의 알루미늄 질소화물과 2중량% 미만의 알루미나를 함유하는 것을 특징으로 하는 분말.
- 제11항에 있어서, 연마된 형태인 것을 특징으로 하는 분말.
- 제15항에 있어서, 입자의 100%가 10㎛ 이하의 크기를 가지며, 3.33%의 감마 알루미늄 산화질소화물을 함유하는 0.9mm 두께의 KBr 디스크상에서 2500cm-1에서 측정한 투과율이 8% 이상을 나타내는 것을 특징으로 하는 분말.
- 제15항 또는 제16항에 있어서, 300ppm 이하의 탄소함량 및 2중량% 미만의 알루미늄 질소화물과 2중량% 미만의 알루미나를 함유하는 것을 특징으로 하는 분말.※ 참고사항 : 최초출원 내용에 의하여 공개하는 것임.