KR940014525A - (코)폴리카보네이트 제조방법 - Google Patents
(코)폴리카보네이트 제조방법 Download PDFInfo
- Publication number
- KR940014525A KR940014525A KR1019930027355A KR930027355A KR940014525A KR 940014525 A KR940014525 A KR 940014525A KR 1019930027355 A KR1019930027355 A KR 1019930027355A KR 930027355 A KR930027355 A KR 930027355A KR 940014525 A KR940014525 A KR 940014525A
- Authority
- KR
- South Korea
- Prior art keywords
- polycarbonate
- reaction mixture
- compound
- prepolymer
- molecular weight
- Prior art date
Abstract
우수한 내열성, 색상 및 충격저항력과 고분자량을 가지는 (코) 폴리카보네이트 제조방법은 탱크반응기에서 에스테르교환반응 촉매의 존재하에서 단량체로서 디히드록시 화합물과 탄산 디에스테르의 용융중축합을 실행하는 단계, 이와 동시에 용융중축합에 의해서 형성된 모노히드록시 화합물을 제거하는 단계, 이것으로 인해 프리폴리머로 이루어진 반응혼합물을 용융상태로 획득하는 단계(제1단계), 제1단계에서 획득된 용융반응혼합물을 응고시키기 위해 냉각시키는 단계(제2단계), 및 수평중축합반응기에서 프리폴리머로 이루어진 반응혼합물을 획득하는 단계(제3단계)로 이루어진다.
Description
본 내용은 요부공개 건이므로 전문내용을 수록하지 않았음
Claims (17)
- 탱크반응기에서 에스테르교환반응 촉매의 존재하에서 단량체로서 디히드록시 화합물 및 탄산 디에스테르의 용융중축합을 실행하는 단계, 이와 동시에 용융중축합에 의해서 형성된 모노히드록시 화합물을 제거하는 단계, 이것으로 인해 용융상태로 프리폴리머로 이루어진 반응혼합물을 획득하는 단계(제1단계), 제1단계에서 획득한 용융상태 반응혼합물을 응고시키기 위해 냉각시키는 단계(제2단계), 및 수평중축합반응기에서 프리폴리머로 이루어진 반응혼합물의 용융중축합을 행하는 단계, 이것으로 인해 고분자량 (코) 폴리카보네이트로 이루어진 반응혼합물을 획득하는 단계(제3단계)로 이루어진 (코) 폴리카보네이트 제조방법.
- 제1항에 있어서, 탄산 디에스테르의 일부분의 제1단계에서 모노히드록시 화합물과 함계 제거되는 것을 특징으로 하는 (코)폴리카보네이트 제조방법.
- 제1항에 있어서, 차단제가 제1단계, 제2단계 도는 제3단계로 부가되는 것을 특징으로 하는 (코) 폴리카보네이트 제조방법.
- 제1항에 있어서, 고분자량 (코) 폴리카보네이트로 이루어진 반응혼합물에 첨가제를 부가하는 것(제4단계) 이 한층 더 포함된 것을 특징으로 하는 (코) 폴리카보네이트 제조방법.
- 제4항에 있어서, 첨가제가 유기인 화합물 또는 장애페놀 화합물인 것을 특징으로 하는 (코) 폴리카보네이트 제조방법.
- 제4항에 있어서, 붕산 또는 붕산염이 제1단계, 제2단계, 제3단계 또는 제4단계에 부가되는 것을 특징으로 하는 (코) 폴리카보네이트 제조방법.
- 제1항에 있어서, 에스테르교환반응 촉매가 전자주는 아민 화합물, 알칼리 금속 화합물과 알칼리 토금속 화합물로 이루어진 군으로부터 선택된 화합물인 것을 특징으로 하는 (코) 폴리카보네이트 제조방법.
- 제1항에 있어서, 에스테르교환반응 촉매가 붕산염은 것을 특징으로 하는 (코) 폴리카보네이트 제조 방법.
- 제1항에 있어서, 용융상태 반응혼합물의 냉각이 제2단계에서 50℃ 또는 그 이하의 온도인 불활성물질로 행해지는 것을 특징으로 하는 (코) 폴리카보네이트 제조방법.
- 제1항에 있어서, 제1단계에서 획득된 프리폴리머로 이루어진 반응혼합물이 0.1 내지 0.4dl/g의 한계점도수[η]를 가지는 것을 특징으로 하는 (코) 폴리카보네이트 제조방법.
- 제1항에 있어서, 제3단계에서 획득된 고분자량 (코) 폴리카보네이트로 이루어진 반응혼합물이 0.3 내지 1.0dl/g의 한계점도수[η]를 가지는 것을 특징으로 하는 (코) 폴리카보네이트 제조방법.
- 제1항에 있어서, 제1단계에서 획득된 프리폴리머로 이루어진 반응혼합물은 1×10-3mol/g 또는 그 이하의 히드록실기 농도를 가지는 것을 특징으로 하는 (코) 폴리카보네이트 제조방법.
- 제1항에 있어서, 제3단계에서 획득된 고분자량 (코) 폴리카보네이트로 이루어진 반응혼합물이 5×10-4mol/g 또는 그 이하의 히드록실기 농도를 가지는 것을 특징으로 하는 (코) 폴리카보네이트 제조방법.
- 제1항에 있어서, 제1단계에서 획득된 프리폴리머가 프리폴리머의 모든 말단기들을 기준으로 하여 50몰% 또는 그 이하의 말단히드록실기 함유량을 가지는 것을 특징으로 하는 (코) 폴리카보네이트 제조방법.
- 제1항에 있어서, 제3단계에서 획득된 고분자량 (코) 폴리카보네이트가 고분자량 (코) 폴리카보네이트의 모든 말단기들을 기준으로 하여 20몰% 또는 그 이하의 말단히드록실기 함유량을 가지는 것을 특징으로 하는 (코) 폴리카보네이트 제조방법.
- 제1항에 있어서, 디히드록시 화합물이 다음 일반식(1), (2), (3) 및 (4)로 나타낸 화합물로 이루어진 군으로부터 선택된 화합물인 것을 특징으로 하는 (코) 폴리카보네이트 제조방법:여기서, R1, R2, R3, R4및 R5는 각각 1 내지 8 탄소원자를 가지는 선형 또는 분지된 알킬기 또는 페닐기를 나타내고, X는 할로겐원자를 나타내고, n은 0도는 정수1 내지 4를 나타내고, m은 정수 1 내지 4를 나타낸다.
- 제1항에 있어서, 다음 일반식(1), (2), (3) 및 (4)로 나타낸 화합물로 이루어진 군으로부터 선택된 2 또는 그 이상의 디히드록시 화합물이 사용되는 것을 특징으로 하는 (코) 폴리카보네이트 제조방법 :여기서, R1, R2, R3, R4및 R5는 각각 1 내지 8 탄소원자를 가지는 선형 또는 분지된 알킬기 또는 페닐기를 나타내고, X는 할로겐원자를 나타내고, n은 0도는 정수1 내지 4를 나타내고, m은 정수 1 내지 4를 나타낸다.※ 참고사항 : 최초출원 내용에 의하여 공개하는 것임.