KR930703470A - 진공 제련로에서 탈탄반응을 촉진하는 방법 - Google Patents
진공 제련로에서 탈탄반응을 촉진하는 방법Info
- Publication number
- KR930703470A KR930703470A KR1019930701692A KR930701692A KR930703470A KR 930703470 A KR930703470 A KR 930703470A KR 1019930701692 A KR1019930701692 A KR 1019930701692A KR 930701692 A KR930701692 A KR 930701692A KR 930703470 A KR930703470 A KR 930703470A
- Authority
- KR
- South Korea
- Prior art keywords
- bed
- ore
- carbon
- manganese ore
- oxygen
- Prior art date
Abstract
본 발명은 망간광석을 용융강철에 첨가하여 진공 제련로에서 용융강철의 탈탄반응을 촉진하는 방법을 설명한다.
첨가된 망간광석은 용융되어 강철배드에 산소를 방출하며 부가의 용해산소 함량은 탄소강의 탈탄반응을 50ppm 이하 수준의 초미량 탄소함량으로 효과적으로 촉진한다. 망간광석의 첨가는 용융강철의 산소함량을 증가시키고 진공 탈기체 처리가 진공챔버 내면의 과도한 내화 마멸없는 기체 산소 취입의 효과와 유사한 효과를 갖게한다. 이 방법으로, 비교적 높은 탄소함량 및/또는 낮은 용해산소 함량을 갖는 배드는 초미량의 탄소수준으로 효과적으로 탈탄될 수 있다. 본 발명 및 첨가기술은 RH 진공 탈기체 장치에 대한 적용에 제한되지 않는다. 대부분의 진공로는 일반적으로 초미량의 탄소강 제조를 용이하게 하기 위해 이 망간광석 첨가를 적용하는 데 적합하다.
Description
본 내용은 요부공개 건이므로 전문내용을 수록하지 않았음
제1도는 RH 진공 탈기체기에서 처리시간에 따른 탄소 및 산소함량의 감소경로를 나타낸다. 제2도는 1600℃에서 진공 압력 하에 탄소-산소 반응의 평형곡선을 나타낸다. 제3도는 10토르 이하의 진공에서 RH 방법에 관한 대표적인 탈탄 경로를 나타내고, A는 초기 탄소 및 산소함량을 나타내고 B는 망간광석의 첨가없는 최종 결과를 나타낸다. 제4도는 초기 단계에서 RH 진공 탈기체기로의 망간광석 첨가하에 산소 함량 대 처리시간을 나타낸다. 제5도는 중간단계 망간광석 첨가 직후 망간광석 유발 산소증가를 나타내는 산소함량 곡선상의 스파이크를 나타낸다. 제6도는 망간광석이 RH 진공 탈기체기로 첨가된 실험으로 얻은 진공 처리결과를 나타낸다.
Claims (12)
- 하기로 구성되는, 용융강철 배드를 0.005% 이하의 초미량 수준의 탄소로 탈탄하는 방법으로서, 용융강철 배드는 약500ppm 이하의 비교적 낮은 수준의 용해산소를 함유하며, 상기 탈탄은 진공하의 용기에서 일어나는 방법:배드의 초기 탄소함량과 초기 산소함량을 근거로 하 목표의 최종 함량을 얻기 위해 배드에 첨가하는데 필요한 용해산소 증가량을 결정하여; 배드에 첨가될 망간광석의 양을 계산하되, 상기 망간광석은 주성분으로서 이산화망간(MnO2)을 갖고 예정된 산소 회수율을 가지며, 상기 양은 산소 회수율을 근거로 계산하여 적어도 필요한 용해산소 증가량을 제공하고; 상기 망간광석의 계산된 양을 상기 배드에 첨가하며; 상기 광석 및 상기 배드를 예정시간 동안 진공상태 하에 방치하되, 상기 예정시간은 망간광석 분해에 의해 배드에 필요한 산소 증가량을 공급하고 배드의 탄소함량을 저하시키기 위해 배드내의 탄소와 광석으로부터의 산소를 반응시키기에 충분하다.
- 제1항에 있어서, 용기는 적어도 10토르의 진공 하인 방법.
- 제2항에 있어서, 망간광석은 배드로 참가되기 전에 분쇄되어 일정한 크기로 만들어지고, 배드로 첨가되는 광석은 직경 2인치(50.4㎜)이하인 방법.
- 제3항에 있어서, 배드로 첨가되는 망간광석은 직경3/8인치(9.5㎜)이상인 방법.
- 제2항에 있어서, 망간광석은 분말로 분쇄되고 분말은 배드로 첨가되기 전에 소비성 금속관에 넣어지는 방법.
- 제5항에 있어서, 탈탄 용기는 RH 탈기체기인 방법.
- 제4항에 있어서, 탈탄 용기는 RH 탈기체기인 방법.
- 하기로 구성되는 0.005 이하의 초미량 탄소 수준을 갖는 강철을 제조하는 개선된 방법:탄소수준을 약0.025 내지 0.005% 탄소로 감소시키기에 충분한 양으로 산소를 용융금속 배드로 취입하며 배드의 용해산소 수준은 약 0.050% 산소 이하인 기본 산소방법을 통해 용융금속 배드를 초기에 제련하고; 배드의 탄소함량 및 산소함량을 근거로 한 목표의 최종 탄소수준으로 배드를 탈탄하는데 필요한 용해산소 증가량을 결정하고; 제련된 용융금속 배드를 10토르 이하의 진공하에 방치하고; 용융배드를 10토르 이하의 진공하에서 예정시간동안 유지하고; 계산된 양의 망간광석을 배드에 첨가하되, 상기 망간광석은 주성분으로서 이산화망간(MnO2)을 갖고 예정된 산소 회수율을 가지며, 상기 광석의 양을 계산하여 광석의 산소 회수율을 근거로한 적어도 상기 필요한 최소 용해산소 증가량을 제공하며; 상기 예정시간은 망간광석의 분해 및 배드의 탄소함량을 적어도 목표의 초미량 탄소수준으로 저하시키기 위해 망간광석의 용융시 방출된 산소와 배드 내의 충분한 탄소와의 반응에 충분하다.
- 제8항에 있어서, 망간광석은 괴상 형태로 첨가되고, 광석은 첨가되기 전에 분쇄되며, 광석은 또한 광석 첨가를 위해 직경3/8내지 2인치(9.5㎜ 내지 50.8㎜)로 크기가 만들어진 방법.
- 제9항에 있어서, 용융금속 배드는 RH 탈기체기에서 진공하에 유지되는 방법.
- 제8항에 있어서, 망간광석은 배드에 첨가되기 전에 분말로 분쇄되고 건조되며 소비성 금속관에 넣어지는 방법.
- 제11항에 있어서, 용융 금속배드는 RH 탈기체기에서 진공하에 유지되는 방법.※ 참고사항 : 최초출원 내용에 의하여 공개하는 것임.