KR920018156A - 실리카 및 중합체를 기재로하는 신규 혼합 입자, 그를 함유하는 필름 형성 조성물, 상기 조성물로부터 수득한 필름 및 제조방법 - Google Patents

실리카 및 중합체를 기재로하는 신규 혼합 입자, 그를 함유하는 필름 형성 조성물, 상기 조성물로부터 수득한 필름 및 제조방법 Download PDF

Info

Publication number
KR920018156A
KR920018156A KR1019920004649A KR920004649A KR920018156A KR 920018156 A KR920018156 A KR 920018156A KR 1019920004649 A KR1019920004649 A KR 1019920004649A KR 920004649 A KR920004649 A KR 920004649A KR 920018156 A KR920018156 A KR 920018156A
Authority
KR
South Korea
Prior art keywords
silica
radicals
mixed particles
ethylenic unsaturation
mixed
Prior art date
Application number
KR1019920004649A
Other languages
English (en)
Inventor
다니엘 쟝-끌로드
에스삐아르 필리뻬
기요 알렝
Original Assignee
롱-쁠랑 쉬미
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 롱-쁠랑 쉬미 filed Critical 롱-쁠랑 쉬미
Publication of KR920018156A publication Critical patent/KR920018156A/ko

Abstract

내용 없음

Description

실리카 및 중합체를 기재로하는 신규 혼합 입자, 그를 함유하는 필름 형성 조성물, 상기 조성물로부터 수득한 필름 및 제조방법
본 내용은 요부공개 건이므로 전문내용을 수록하지 않았음
제1도는 실시예 2의 시험에서 제조된 라텍스로부터 수득한 필름의 응력/신장 곡선을 나타낸다,
제2도는 실시예 1의 시험에서 제조된 라텍스로부터 수득한 필름의 응력/신장 곡선을 나타낸다.

Claims (13)

  1. 필름-형성 성질을 갖는 중합체 매트릭스내에 캡술화되어 있는 실리카를 포함하며, 상기 매트릭스가 Si-O-Si 실옥산 결합에 의해 상기 실리카의 표면에 화학적으로 결합되어 있는 것을 특징으로 하는 형태의 혼합 입자.
  2. 제1항에 있어서, 평균 크기가 20 나노미터 내지 1미크론임을 특징으로 하는 혼합 입자.
  3. 제1항 또는 제2항에 있어서, 실리칸 함량이 0.1중량% 내지 20중량%임을 특징으로 하는 혼합입자.
  4. 제1항 내지 제3항중 어느 한 항에 있어서, 콜로이드 형태임을 특징으로 하는 혼합 입자.
  5. 미세하게 분쇄된 상태의 실리카의 존재하에 중합성 유기(공)단량체를 (공)중합시켜서, 중합체 매트릭스내에 캡슐화되어 있는 실리카를 포함하는 혼합 입자를 수득하는 것으로 구성되며, 표면이 하기 구조식(1)의 유기실란에 의해 작용화된 실리카를 사용하는 것을 특징으로 하는 제1항 내지 제4항중 어느 한 항에 따른 혼합 입자의 제조방법 :
    〔상기식에서, (ⅰ)라디칼 R1, R2, R3및 R4중 적어도 하나는 에틸렌성 불포화를 함유하는 유기라디칼이고, (ⅱ)라디칼 R1, R2, R3및 R4중 적어도 하나는 알콕시 또는 히드록실 라디칼이고, (ⅲ)나머지 라디칼은 동일하거나 다르며, 라디칼의 상기 부류로부터 선택된다.〕
  6. 제5항에 있어서, 에틸렌성 불포화를 함유하는 상기 유기 라디칼이, ω 불포화를 함유하며, 2 내지 10개의 탄소원자를 함유하는 알케닐 라디칼임을 특징으로 하는 방법.
  7. 제5항에 있어서, 에틸렌성 불포화를 함유하는 상기 유기 라디칼이, 4개 이하의 탄소원자를 함유하는 카르복실산 또는 6개 이하의 탄소원자를 함유하는 알콜로부터 유도된, ω 에틸렌성 불포화를 함유하는, 카르복실산의 에스테르임을 특징으로 하는 방법.
  8. 제5항 내지 제7항중 어느 한 항에 있어서, 상기 유기 실란이 하기 구조식(2)의 화합물임을 특징으로 하는 방법.
    〔상기식에서, R4는 에틸렌성 불포화를 함유하는 유기 라디칼이고,R1, R2, 및 R3는 알킬 라디칼 또는 수소이다.〕
  9. 제5항 내지 제8항중 어느 한 항에 있어서, 중량비 〔사용된 실리카/사용된 (공)단량체(들)〕가 1/1 내지 1/100, 바람직하게는 1/4 내지 1/100임을 특징으로 하는 방법.
  10. 제5항 내지 제9항중 어느 한 항에 있어서, 폴리에틸렌 사슬을 함유하는 비이온성의 유화제를 사용함을 특징으로 하는 방법.
  11. 제1항 내지 제4항중 어느 한 항에 따른 혼합 입자 또는 제5항 내지 제10항중 어느 한 항에 따른 방법에 의해 수득할 수 있는 혼합입자를 포함함을 특징으로 하는 방법.
  12. 제11항에 따른 조성물로부터 수득되는 것을 특징으로 하는 하는 방법.
  13. 제12항에 있어서, 투명함을 특징으로 하는 필름.
    ※ 참고사항 : 최초출원 내용에 의하여 공개하는 것임.
KR1019920004649A 1991-03-22 1992-03-20 실리카 및 중합체를 기재로하는 신규 혼합 입자, 그를 함유하는 필름 형성 조성물, 상기 조성물로부터 수득한 필름 및 제조방법 KR920018156A (ko)