KR910014406A - 지글러-나타형 촉매의 제조방법 - Google Patents
지글러-나타형 촉매의 제조방법 Download PDFInfo
- Publication number
- KR910014406A KR910014406A KR1019910000003A KR910000003A KR910014406A KR 910014406 A KR910014406 A KR 910014406A KR 1019910000003 A KR1019910000003 A KR 1019910000003A KR 910000003 A KR910000003 A KR 910000003A KR 910014406 A KR910014406 A KR 910014406A
- Authority
- KR
- South Korea
- Prior art keywords
- vanadium
- compound
- liquid hydrocarbon
- electron
- support
- Prior art date
Abstract
내용 없음
Description
본 내용은 요부공개 건이므로 전문내용을 수록하지 않았음
Claims (10)
- 하기 단계 : (1) (ⅰ)Mg-C결합을 함유하는 임의의 생성물이 실질적으로 없는 80∼99.5몰%의 MgCl2및 (ⅱ)불안정한 수소가 없는 0.5∼20몰%의 전자-공여체 화합물(D1)을 함유하는, 10∼100미크론의 질량 평균 직경 Dm 및 입자 수평균 직경 Dn에 대한 Dm의 비가 3 이하인 입자 크기 분포를 갖는 타원체 입자 형태의 지지체를 불안정한 수소를 함유하는 전자-공여체 화합물 1종 이상, 및 이어서 바나듐 화합물을 환원시킬 수 있는 유기 금속 화합물 1종 이상과 액체 탄화수소중에서 연속적으로 접촉시키는 단계, (2) 단계(1)에서 수득된 고체 생성물을 액체 탄화수소로 세척하는 단계, 및 (3)세척된 고체 생성물을 액체 탄화수소에 용해되는 동일하거나 상이한 바나듐 원자에 결합된 할로겐 원자 X및 알콕시기 OR1을 함유한 바나듐 화합물 1종 이상과 접촉시키는 단계를 특징으로 하는, 바나듐을 환원시킴으로써 염화 마그네슘 지지체 상에 침전시킨 바나듐 화합물을 기재로 한 지글러-나타(Zierler-Natta)형 촉매의 제조방법.
- 제1항에 있어서, 전자-공여체 화합물(D1)이 에테르, 티오에테르, 카르복실산 에스테르, 술폰, 술폭시드, 3차 포스틴, 포스포르아미드, 3차 아민 및 2차 아미드에서 선택됨을 특징으로 하는 방법.
- 제1항에 있어서, 전자-공여체 화합물(D2)가 알코올, 페놀, 1차 또는 2차 포스핀, 1차 또는 2차 아민, 1차 아미드 및 카르복실산에서 선택됨을 특징으로 하는 방법.
- 제1항에 있어서, 지지체의 마그네슘 1몰당 0.1∼2몰 미만의 화합물 D2가 사용됨을 특징으로 하는 방법.
- 제1항에 있어서, 유기 금속 화합물이 유기 알루미늄 화합물, 유기 마그네슘 화합물 및 유기 아연 화합물에서 선택됨을 특징으로 하는 방법.
- 제1항에 있어서, 지지체의 마그네슘 1몰당 0.1∼2몰의 유기 금속화합물이 사용됨을 특징으로 하는 방법.
- 제1항에 있어서, 바나듐 화합물(들)이 할로겐 원자 X및 알콕시기 OR을 0.05∼20의 X/OR 몰비로 함유함을 특징으로 하는 방법.
- 제1항에 있어서, 바나듐 화합물(들)이 하기 두개의 일반식에 상응함을 특징으로 하는 방법.V(OR1)4-mXm또는 VO(OR1)3-nXn(식중, R1은 1∼12의 탄소원자를 함유하는 알킬기를 나타내고, X는 할로겐 원자이며, m은 0.2∼3.8 범위의 정수 또는 분수이고, n은 0.14∼2.85범위의 정수 또는 분수이다).
- 제1항에 있어서, 지지체의 마그네슘 1몰당 0.05∼2몰의 바나듐 화합물(들)이 사용됨을 특징으로 하는 방법.
- 하기 단계:(1) (ⅰ)Mg-C 결합을 함유하는 임의의 생성물이 실질적으로 없는 80∼99.5몰%의 MgCl2및 (ⅱ)불안정한 수소가 없는 0.5∼20몰%의 전자-공여체 화합물(D1)을 함유하는, 10∼100미크론의 질량 평균 직경 Dm 및 입자 수평균 직경 Dn에 대한 Dm의 비가 3 이하인 입자 크기 분포를 갖는 타원체 입자 형태의 지지체를 불안정한 수소를 함유하는 전자-공여체 화합물(D2) 1종 이상 및 이어서 바나듐 화합물을 환원시킬 수 있는 유기금속 화합물 1종 이상과 액체 탄화수소중에서 연속적으로 접촉시키는 단계, (2)단계(1)에서 수득된 고체 생성물을 액체 탄화수소로 세척하는 단계, 및 (3)세척된 고체 생성물을 액체 탄화수소에 용해되는 동일하거나 상이한 바나듐 원자에 결합된 할로겐 원자 X 및 알콕시기 OR1을 함유한 바나듐 화합물 1종 이상과 접촉시키는 단계에 따라 제조된 바나듐을 환원 시킴으로써 염화마그네슘 지지체상에 침전시킨 바나듐을 기재로한 지글러-나타형촉매의 프로필렌의 제조, 에틸렌과 3∼12의 탄소원자를 함유하는 α-올레핀과의 공중합체의 제조, 및 프로필렌, 에틸렌 및/또는 1-부펜, 및 임의로 비공액 디엔의 탄성 공중합체 제조를 위한 용도.※ 참고사항 : 최초출원 내용에 의하여 공개하는 것임.