CA2267939C - Chloride process for making catalyst - Google Patents

Chloride process for making catalyst Download PDF

Info

Publication number
CA2267939C
CA2267939C CA 2267939 CA2267939A CA2267939C CA 2267939 C CA2267939 C CA 2267939C CA 2267939 CA2267939 CA 2267939 CA 2267939 A CA2267939 A CA 2267939A CA 2267939 C CA2267939 C CA 2267939C
Authority
CA
Canada
Prior art keywords
mole
process according
weight
catalyst
olefins
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Lifetime
Application number
CA 2267939
Other languages
French (fr)
Other versions
CA2267939A1 (en
Inventor
Mark Kelly
Dusan Jeremic
Victoria Ker
Charles Russell
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Nova Chemicals Corp
Original Assignee
Nova Chemicals Corp
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Nova Chemicals Corp filed Critical Nova Chemicals Corp
Publication of CA2267939A1 publication Critical patent/CA2267939A1/en
Application granted granted Critical
Publication of CA2267939C publication Critical patent/CA2267939C/en
Anticipated expiration legal-status Critical
Expired - Lifetime legal-status Critical Current

Abstract

The present invention provides a novel process for preparing a catalyst, preferably free of electron donor, useful in gas phase polymerization of olefins having a broad polydispersity. The catalyst is prepared by contacting a dehydrated silica support with a first alkylaluminum compound, an organic chloride, a second alkylaluminum compound and an alkylmagnesium compound, and a source of titanium.

Description

FIELD OF THE INVENTION

The present invention relates to supported Ziegler-Natta catalysts which are useful in olefin polymerization, and more particularly in the fluidized gas phase polymerization of alpha-olefins.

BACKGROUND OF THE INVENTION

Ziegler-Natta type catalysts are well known and have been used since the early 1950's. Generally the catalyst comprises a transition metal compound, typically titanium in the 3 or 4 valence state (e.g. TiCI3 or TiCI4) together with at least one activator, typically an aluminum compound such as a trialkyl aluminum (e.g. triethylaluminum (TEAL)) or an alkyl aluminum halide (e.g. diethylaluminum chloride (DEAC)) and the like. The catalysts may contain magnesium chloride which may be generated from a dialkyl magnesium compound and active chloride. Typically, the catalysts are prepared in conjunction with an electron donor which tends to narrow the molecular weight distribution in the resulting polymer. A good description of these types of catalysts is contained in United States Patent 4,302,566 issued November 24, 1981 to Karol et al., assigned to Union Carbide Corporation. Karol teaches that it is essential to use an electron donor in the preparation of the catalyst. The use of an electron donor has been eliminated from the catalysts of the present invention.

United States Patent 5,633,419 issued May 27, 1997 to The Dow Chemical Company discloses a supported Ziegler-Natta type catalyst or catalyst precursor. However, it is a limitation of the reference that the halide is used in the form of a hydrogen halide (e.g. HCI). The reference M:\Trevor\TTSpec\9140can.doc 2 teaches away from the subject matter of the present invention which is limited to the use of alkyl halides as the halide source. Additionally, the reference appears to teach the use of a support such as silica, which has been treated either thermally or chemically, but not both, which is contrary to the method for preparing the support of the present invention.
European Patent Application 0 744 416 published November 27, 1996 in the name of BP Chemicals Limited (BP) teaches supported catalysts and catalyst precursors. The reference teaches that the support is reacted with either the aluminum compound or the magnesium compound but not a concurrent treatment with a mixture of aluminum and magnesium (e.g. MAGALAT"", a mixture sold by Akzo). The reference teaches against the addition of a second aluminum compound.
Additionally, in view of the examples, the BP patent strongly suggests that an electron donor needs to be used in the preparation of the catalyst, a feature that has been eliminated from the present invention. This reference also teaches that the halogenating agent must be used in a molar ratio such that all of the Mg and Al compounds are converted to their respective halides, a limitation which is not put on the present invention.
That is, in accordance with the present invention, there is an excess of aluminum and magnesium over reactive halide so that not all of the aluminum and magnesium is precipitated.

BP patent EP 0 595 574 B1 granted on January 2, 1997 requires that the catalyst be prepared on a support treated with an organosilicon compound. The supports used in accordance with the present invention M:\Trevor\TTResponse\9140candisclosure. doc are treated thermally and chemically (aluminum alkyls) but not with organosilicon.

BP patent EP 0 453 088 B1 granted on July 31, 1997 teaches that the catalyst be made on dehydrated silica and that the catalyst needs to be pre-polymerized to obtain a useful catalyst for the synthesis of linear low density polyethylene (LLDPE). The catalysts of the present invention do not need to be pre-polymerized to be useful for the polymerization of ethylene to LLDPE. The patent teaches about washing the catalyst to remove excess Mg compounds which is not relevant to our catalyst. This patent also teaches about the need for high Ti:(Mg+Al) ratios, a restriction which is removed in the present invention.

The present invention seeks to provide a supported Ziegler-Natta type catalyst which is prepared preferably in the absence of an electron donor, and provides a polymer having a broad molecular weight distribution. The present invention relates to supported Ziegler-Natta catalysts which are useful in olefin polymerization, and more particularly in the fluidized gas phase polymerization of alpha-olefins.

SUMMARY OF THE INVENTION

The present invention provides a process conducted in a hydrocarbon solvent at a temperature from 0 C to 100 C for preparing a catalyst for the gas phase polymerization of alpha-olefins comprising:

a. contacting a dehydrated silica support containing from 0.1 to 3 weight % aluminum having the formula AI'(R')aXb wherein each R' is independently selected from the group consisting of C,_,o alkyl M:\Trevor\TTSpec\9140can.doc 4 radicals, X is selected from the group consisting of Cl and Br, a and b are 0 or an integer from 1 to 3 provided the sum of a+b=3 with;

b. carbon tetrachloride (CCI4) or a secondary or tertiary alkyl halide of the formula R4CI wherein R4 is selected from the group consisting of C3_6 alkyl radicals. The halide is added to the support in a quantity of 2 to 30 weight %, preferably from 5 to 20 weight %, based on the weight of silica and contacting the resulting product with;

c. in any order or in combination; (i) a mixture of an aluminum compound of the formula AI2(R2)nXm wherein each R 2 is independently selected from the group consisting of C,-,o alkyl radicals, X is selected from the group consisting of CI and Br, m and n are 0 or an integer from 1 to 3 provided the sum of n+m=3, and (ii) Mg(R3)2 wherein each R3 is independently selected from the group consisting of C,_,o alkyl radicals wherein the molar ratio of Mg:A12 in said mixture is from 0.5:1 to 25:1 to provide from 0.25 to 8.0 weight % of Mg based on the weight of the silica, a molar ratio of Cl:Mg from 1:1 to 8:1 in the resulting product and contacting the resulting product with;

d. a titanium compound of the formula Ti(R5)y(CI)Z wherein each R5 is selected from the group consisting of C1_10 alkyl and alkoxide radicals and phenyl radicals which are unsubstituted or substituted by a C1_4 alkyl radical, y and z are 0 or an integer from 1 to 4 and the sum of y+z=4 to provide from 0.1 to 1.5 weight % of Ti based on the silica.

M:\Trevor\TTSpec\9140can.doc 5 In a further embodiment of the present invention in the above process after step d there is added from 0 up to 0.3 mmol of electron donor per g of silica.

The present invention also provides a gas phase process for the polymerization, at a pressure from 10 to 500 psi, of a mixture comprising from 0 to15 mole % hydrogen, from 0 to 30 mole % of one or more C3-e alpha-olefins, from 15 to 100 mole % of ethylene and from 0 to 75 mole %
of an inert gas such as N2, conducted at a temperature from 50 C to 120 C in the presence of a catalyst as described above preferably in the absence of an electron donor.

The present invention further provides a polymer comprising from 0 to 15 mole % of one or more C3_8 alpha-olefins, from 85 to 100 mole % of ethylene having a molecular weight (Mw) greater than 50,000 and a polydispersity (Mw/Mn) from 3.5 to 7 prepared according to the above process.

BEST MODE

The supports useful in accordance with the present invention typically comprise a substrate of alumina or silica having a pendant reactive moiety. The reactive moiety may be a siloxy radical or more typically is a hydroxyl radical. The preferred support is silica or alumina.
The support should have a particle size from about 10 to 250 microns, preferably from about 30 to 150 microns. The support should have a large surface area typically greater than about 3 m2/g, preferably greater than about 50 mZ/g, most preferably from 100 m2/g to 1,000 m2/g. The support M:lTrevor\TTSpec1914ocan.doc 6 will be porous and will have a pore volume from about 0.3 to 5.0 ml/g, typically from 0.5 to 3.0 ml/g. Supports, which are specifically designed to be an agglomeration of subparticies, while useful, are not required.

It is important that the support be dried prior to the initial reaction with an aluminum compound. Generally the support may be heated at a temperature of at least 200 C for up to 24 hours, typically at a temperature from 500 C to 800 C for about 2 to 20 hours. The resulting support will be free of adsorbed water and should have a surface hydroxyl content from about 0.1 to 5 mmol/g of support, preferably from 0.5 to 3 mmol/g.

The first aluminum (AI') is deposited upon the support by contacting the support, preferably silica, with an anhydrous solution of an aluminum alkyl of the formula AI'(R')aXbwherein each R' is independently selected from the group consisting of C,-,o alkyl radicals, preferably C1_6 alkyl radicals, X is selected from the group consisting of Cl and Br, preferably Cl and a and b are 0 or an integer from 1-3 provided the sum of a+b=3. Most preferably, R' is selected from the group consisting of methyl, ethyl and butyl radicals. Preferably, b is 0. From a commercial viewpoint, the most available compound is triethylaluminum (TEAL).

The support is reacted with an aluminum compound such that the amount of aluminum on the support is from about 0.1 to about 3 weight %, preferably from about 0.5 to about 2 weight %, based on the weight of the silica.

The resulting treated support may then be reacted with the remaining components in the specified order.

M:1TrevorlTTSpec19140can.doc 7 The halide in the catalyst is provided by CCI4 or a secondary or tertiary halide of the formula R4CI wherein R4 is selected from the group consisting of C3-6 alkyl radicals. Suitable chlorides include sec-butyl chloride, t-butyl chloride and sec-propyl chloride. The halide is added to the support in a quantity of 2 to 30 weight %, preferably from 5 to 20 weight % based on the weight of silica.

The second aluminum component in the catalyst is of the formula AI2(R2)nXm wherein each R2 is independently selected from the group consisting of C,_,o alkyl radicals, preferably C1-6 alkyl radicals, X is selected from the group consisting of Cl and Br, preferably Cl and n and m are 0 or an integer from 1 to 3 provided the sum of n+m=3. Most preferably, R2 is selected from the group consisting of methyl, ethyl and butyl radicals.

Preferably, m is 0. The second aluminum compound may be the same or different from the first aluminum compound. The amount of the second aluminum (e.g. AI2) is such that it will provide from about 0.20 to 4.0 weight % of the catalyst based on the weight of the silica.

The magnesium component in the catalyst will have the formula Mg(R3)2 wherein each R3 may be independently selected from the group consisting of C1-10 alkyl radicals, preferably C,_6 alkyl radicals. More preferably, R3 is selected from the group consisting of ethyl and butyl radicals. Some suitable magnesium compounds include dibutyl-magnesium and butyl-ethyl-magnesium. The magnesium is used in an amount to provide from 0.25 to 8.0 weight % based on the weight of the silica, preferably from 0.5 to 4.0 weight % based on the weight of the M:\Trevor\TTSpec\9140can.doc 8 silica. The Mg is also used to provide a CI:Mg molar ratio from 1:1 to 8:1, preferably from 1.5:1 to 6:1. The molar ratio of Mg:A12 may range from 0.5:1 to 25:1, preferably from 0.5:1 to 16:1.

The AIZ and Mg may be added as a mixed compound (such as the commercially available MAGALA, a product supplied by Akzo) or sequentially in any order. That is to say, AI2 can be added first followed by the Mg compound or the Mg compound can be added first followed by AIZ.
The titanium in the catalyst is provided by a compound of the formula Ti(RS)YCIZ wherein each R5 is independently selected from the group consisting of C1_10 alkyl and alkoxide radicals and phenyl radicals which are unsubstituted or substituted by a C,-4 alkyl radical, and y and z are 0 or an integer from 1 to 4 provided that the sum of y+z=4. Preferably, R5 is selected from the group consisting of C2_6 alkyl and alkoxy radicals and phenyl and benzyl radicals. The titanium compound is added in an amount to provide from 0.1 to 1.5 weight % of titanium based on the weight of the silica. Preferably, the titanium is present in an amount from 0.25 to 1.0 weight % based on the weight of the silica. In one embodiment of the invention, y is 0.

The catalysts of the present invention will have: a molar ratio of total aluminum (AI'+AI2):Mg from 0.1:1 to 3:1, preferably from 0.4:1 to 3:1;
preferably a molar ratio of halide (CI) to 2Mg +3(AI'+AI2) from 0.25:1 to 4:1; an amount of organic halide from 0.2 to 5 mmol per g of silica; an amount of Mg from 0.1 to 3.5 mmol per g of silica; a total amount of aluminum to provide from 0.3 to 3.0 mmol of aluminum per g of silica; a M:1Trevor\TTSpec19140can.doc 9 molar ratio of titanium to aluminum and magnesium (e.g. Ti:(AI+Mg)) from 0.01:1 to 0.15:1 preferably from 0.02:1 to 0.085:1; an amount of Ti to provide from 0.02 to 0.32 mmol of Ti per g of silica; a molar ratio of Ti:Mg from 0.04:1 to 0.4:1.

The process to prepare the catalyst may be conducted at temperatures from 0 C to 100 C, typically at temperatures from 5 C to 80 C. The individual components (e.g. silica comprising aluminum compound, magnesium compound, second aluminum compound, halide (chloride) compound and titanium compound) are suspended or dissolved in a hydrocarbon medium. The solvent used in the preparation of the catalyst is an inert C5_10 hydrocarbon which may be unsubstituted or substituted by a C, alkyl radical, such as a hydrocarbon that is inert with respect to the catalyst. Such solvents are known and include for example:
pentane, hexane, heptane, octane, cyclohexane, methylcyclohexane and hydrogenated naphtha.

The drying steps may be conducted in a number of different manners. During the synthesis of the catalyst, it is preferred that the solvent not be removed between the halide and Mg addition sequence.
The drying step or steps may be conducted by maintaining the reactants at a temperature from 5 C to 80 C, preferably from 30 C to 80 C, by passing or purging a dry inert gas such as nitrogen through the reactants.
The drying may also be conducted at a reduced pressure under vacuum at a temperature from 10 C to 50 C and at a pressure from 0.1 to 500 mm M:\Trevor\TTSpec\9140can.doc 10 Hg (torr), preferably less than 400 torr (66.65 kPa, preferably less than 53.33 kPa).

The catalyst is recovered as a free flowing powder. The catalyst is then used in combination with a cocatalyst, typically an aluminum compound such as an aluminum alkyl, in the gas phase polymerization of a gaseous mixture comprising from 0 to 15 mole % of hydrogen, from 0 to 30 mole % of one or more C3-8 alpha-olefins, from 15 to 100 mole % of ethylene, and from 0 to 75 mole % of an inert gas at a temperature from 50 C to 120 C, preferably from 75 C to about 110 C, and at pressures typically not exceeding 3447 kPa (about 500 psi), preferably not greater than 2414 kPa (about 350 psi). Preferably, the catalyst is used in the absence of an electron donor. If present the electron donor may be used in amounts from 0 up to 0.3 mmol per g of silica. Suitable electron donors are well known to those skilled in the art and include tetrahydrofuran (THF), dimethyl formamide (DMF), ethyl acetate, methyl isobutyl ketone and the like.

The catalyst may be used in a fluidized bed gas phase reactor or in a stirred bed gas phase reactor. These processes are well known to those skilled in the art. A broad general description of these types of processes is set out in the paper "Gas Phase Ethylene Polymerization:
Production Processes, Polymer Properties, and Reactor Modeling" by Tuyu Xie, Kim B. McAuley, James C. C. Hsu, and David W. Bacon, Ind.
Eng. Chem. Res., 1994, 33, 449-479.

M:\Trevor\TTSpec\9140can.doc 11 Generally, a monomer feed comprising at least ethylene and one or more C3_6 alpha-olefins is fed to a gas phase fluidized bed or stirred bed reactor. The monomer mixture optionally together with hydrogen and/or an inert gas are fed to the fluidized bed. In a fluidized bed reactor, the velocity of the gas is sufficient to suspend the bed in the fluid flow of monomer and other components. In a stirred bed reactor mechanical agitation serves to help suspend the bed. Generally a fluid bed reactor is vertical and a stirred bed reactor is horizontal. Concurrently with the monomers a supported catalyst is fed to the bed. The monomer passing over the catalyst polymerizes on the catalyst and in the pores of the catalyst causing the particle to increase in size and to break. The resulting particle of polymer on catalyst grows as it resides in the catalyst bed. In a stirred tank reactor the bed is stirred to a discharge section and leaves the reactor. In a fluidized bed the reactor typically has a narrower section to keep the fluid velocity sufficiently high to fluidize the bed.
There is an expanded zone at the top of the reactor to reduce the speed of the gas passing through the reactor so the polymer/catalyst particles fall back into the bed. The discharge is from the bed zone in the reactor.

In both the fluidized bed and stirred bed the polymer particles removed from the reactor are degassed to remove any volatile material and the resulting polymer (with entrained catalyst) may then be further treated (e.g. stabilizers added and pelletized if necessary).

Typically the resulting polymer will comprise from 85 to 100 mole %
of ethylene and from 0 to 15 mole % of one or more C3_6 alpha-olefins.

M:\Trevor\TTSpec\9140can.doc 12 The polymer should have a molecular weight (weight average Mw) greater than 50,000. The polymers prepared according to the present invention will have a polydispersity (Mw/Mn) from 3.5 to 7, preferably from 3.75 to 6.

The polymers may be compounded with the usual additives such as heat and light stabilizers (typically hindered phenol type stabilizers such as those sold by Ciba Geigy) and ultraviolet light stabilizers (such as the hindered amine stabilizers sometimes referred to as HALS also sold by Ciba Geigy), processing aids such as the fluoroelastomers optionally in combination with waxes such as low molecular weight esters of polyethylene glycol (i.e. CarbowaxTM ) as sold by 3M and by DuPont .
The resulting polymers, depending on polymer properties, may be used in a number of applications such as film, injection molding and rotomolding.

The present invention will now be illustrated by the following non-limiting examples.

Catalyst Synthesis Support Preparation Silica (200 g) was pre-dried at 150 C for a day prior to heating it to 200 C
under a flow of air for 2 hours. After this time the air was turned off and nitrogen was slowly passed over the silica and the temperature was increased to 600 C for 6 hours. The oven was then turned off and the silica was allowed to cool to room temperature. The silica was then transferred to a reaction vessel and hexane (1 L) was added. With stirring, triethylaluminum (TEAL) (71.4 mL of a 25 weight % TEAL in n-M:\Trevor\TTResponse\9140candisclosure.doc hexane) was added over 10 minutes at room temperature. After stirring the slurry for 15 minutes at room temperature the solvent was removed under vacuum. After the silica reached a free-flowing state, it was dried thoroughly under a high vacuum (0.1 mm of Hg) at 60 C for 2 hours.
Catalyst Preparation To a slurry of a prepared support (15 g) in pentane (100 mL) at 0 C
was added t-butyl chloride (3.24 g diluted with 10 mL of pentane) over 10 minutes. After the addition was complete the cold bath was removed and the reaction mixture was stirred for 2 hours. The slurry was then cooled again to 0 C and MAGALA (24.3 g, 1.75 weight % Mg, 0.24 weight % Al in heptane) was added over 10 minutes. After removing the cold bath and stirring for 2 hours the solvent was removed under vacuum at room temperature. The solid was then slurried again in pentane (100 mL) and cooled to 0 C at which time TiCl4 (0.42 g diluted with 10 mL pentane) was added over 10 minutes. After removing the cold bath and stirring for 2 hours, the solvent was removed under vacuum leaving the catalyst as a white solid which was stored in a glove box.

Polymerization of the Above Catalyst In a 75 L stirred bed catalytic reactor at 88 C containing hydrogen, nitrogen, ethylene and hexene (as described in Table 1) the above catalyst was added at a rate of 0.67 g per hour. The Al, in the cocatalyst (TEAL):Ti ratio was maintained at approximately 40:1. Under these conditions an LLPDE was formed whose properties are shown in Table 1.

M:\Trevor\TTSpec\9140can.doc 14 TABLE I

C6H12/C2H4 molar flow ratio 0.077 H2/C2H4 molar gas ratio 0.084 Nitrogen (mole %) 53.3 M12.16 0.65 MFR 36.5 Bulk density (Ib/ft3) 20.3 Comparative Example For comparative purposes a catalyst prepared following United States Patent 4,302,566 was used to produce an LLDPE. In a 75 L stirred bed catalytic reactor at 88 C containing hydrogen, nitrogen, ethylene and hexene (as described in Table 2) the above catalyst was added at a rate of 0.17 g per hour. The Al, in the cocatalyst (TEAL):Ti ratio was maintained at approximately 40:1. Under these conditions an LLPDE was formed whose properties are shown in Table 2.

C6H12/C2H4 molar flow ratio 0.077 H2/C2H4 molar gas ratio 0.19 Nitrogen (mole %) 48.4 MI216 0.97 MFR 26.5 Bulk density (Ib/ft3) 24.7 When the melt flow ratio (MFR) in Table 1 (36.5) is compared to the MFR in Table 2 (26.5) it is evident that the molecular weight distribution of the polymer prepared in accordance with the present invention is M:1Trevor\TTSpec\9140can.doc 15 significantly broader than the molecular weight distribution for the polymer prepared with the catalyst of the prior art.

M:1TrevorlTTSpec19140can.doc 16

Claims (30)

The embodiments of the invention in which an exclusive property or privilege is claimed are defined as follows:
1. A process conducted in a hydrocarbon solvent at a temperature from 0°C to 100°C for preparing a catalyst for the gas phase polymerization of alpha-olefins comprising:

a. contacting a dehydrated silica support comprising from 0.1 to 3 weight % of Al, the source of aluminum being an aluminum compound of the formula Al1(R1)a X b wherein each R1 is independently selected from the group consisting of C1-10 alkyl radicals, X is selected from the group consisting of Cl and Br, a and b are 0 or an integer from 1 to 3 provided the sum of a+b=3; with b. CCl4 or a secondary or tertiary alkyl halide of the formula R4Cl wherein R4 is selected from the group consisting of C3-6 alkyl radicals, the halide being added to the support in a quantity of 2 to 30 weight %, based on the weight of silica and contacting the resulting product with;

c. in any order or in combination (i) an aluminum compound of the formula Al2(R2)n X m wherein each R 2 is independently selected from the group consisting of C1-10 alkyl radicals, X is selected from the group consisting of Cl and Br, m and n are 0 or an integer from 1 to 3 provided the sum of n+m=3, and (ii) Mg(R3)2 wherein each R3 is independently selected from the group consisting of C1-10 alkyl radicals wherein the molar ratio of Mg:Al2 is from 0.5:1 to 25:1 to provide from 0.25 to 8.0 weight % of Mg based on the weight of the silica, a molar ratio of Cl:Mg from 1:1 to 8:1 in the resulting product and contacting the resulting product with;

d. a titanium compound of the formula Ti(R5)y(Cl)z wherein each R5 is selected from the group consisting of C1-10 alkyl and alkoxide radicals and phenyl radicals which are unsubstituted or substituted by a C1-4 alkyl radical, y and z are 0 or an integer from 1 to 4 and the sum of y+z=4 to provide from 0.1 to 1.5 weight % of Ti based on the silica, wherein said catalyst has a ratio, (Al1 + Al2):Mg of from 0.1:1 to 3:1, an amount of organic halide from 0.2 to 5 mmol per g of silica, a total amount of aluminum of from 0.3 to 3.0 mmol of aluminum per g of silica, and a molar ratio of Ti:Mg from 0.04:1 to 0.4:1.
2. The process according to claim 1, wherein in step c the molar ratio of Mg:Al2 is from 0.5:1 to 16:1.
3. The process according to claim 2, wherein in step c the Mg is provided to the catalyst in an amount from 0.5 to 4 weight % based on the weight of the silica.
4. The process according to claim 3, wherein in step c the molar ratio of Cl to Mg is from 1.5:1 to 6:1.
5. The process according to claim 4, wherein in step d the titanium is deposited on the catalyst in an amount from 0.25 to 1.0 weight % based on the weight of the silica.
6. The process according to claim 5, conducted at temperatures from 0°C to 80°C.
7. The process according to claim 6, wherein R1, R2 and R3 are selected from the group consisting of C1-6 alkyl radicals.
8. The process according to claim 7, wherein R5 is selected from the group consisting of C1-7 alkyl and alkoxy radicals and phenyl and benzyl radicals.
9. The process according to claim 8, wherein X in Al1(R1)a X b and Al2(R2)n X m is Cl.
10. The process according to claim 8, wherein m is 0 and b is 0.
11. The process according to claim 10, wherein R1 and R2 are selected from the group consisting of methyl, ethyl, and butyl radicals, R3 is selected from the group consisting of ethyl and butyl radicals, and R4 is a butyl radical.
12. The process according to claim 11, wherein R5 is an alkoxy radical.
13. The process according to claim 11, wherein y is 0.
14. The process according to claim 11, conducted in one reactor at a temperature from 5°C to 80°C with the removal of the solvent after step d at a temperature from 5°C to 80°C.
15. The process according to claim 14, wherein the removal of solvent is conducted under vacuum from 0.1 to 500 mm Hg at a temperature from 10°C to 80°C.
16. The process according to claim 14, wherein the removal of solvent is conducted at a temperature from 30°C to 80°C by passing a stream of inert gas through said solvent.
17. The process according to claim 11, conducted in one reactor wherein the solvent is removed after each of steps c and d.
18. The process according to claim 17, wherein the removal of solvent is conducted under vacuum from 0.1 to 500 mm Hg at a temperature from 10°C to 80°C.
19. The process according to claim 17, wherein the removal of solvent is conducted at a temperature from 30°C to 80°C by passing a stream of inert gas through said solvent.
20. A gas phase process for the polymerization at a pressure from 10 to 350 psi of a mixture comprising from 0 to 15 mole % of hydrogen, from 0 to 30 mole % of one or more C3-8 alpha-olefins, from 15 to 100 mole % of ethylene and from 0 to 75 mole % of an inert gas conducted at a temperature from 50°C to 120°C in the presence of a catalyst prepared according to the process of claim 1 and in the absence of an electron donor.
21. A gas phase process for the polymerization at a pressure from 10 to 350 psi of a mixture comprising from 0 to 15 mole % of hydrogen, from 0 to 30 mole % of one or more C3-8 alpha-olefins, from 15 to 100 mole % of ethylene and from 0 to 75 mole % of an inert gas conducted at a temperature from 50°C to 120°C in the presence of a catalyst prepared according to the process of claim 11 and in the absence of an electron donor.
22. A gas phase process for the polymerization at a pressure from 10 to 350 psi of a mixture comprising from 0 to 15 mole % of hydrogen, from 0 to 30 mole % of one or more C3-8 alpha-olefins, from 15 to 100 mole % of ethylene and from 0 to 75 mole % of an inert gas conducted at a temperature from 50°C to 120°C in the presence of a catalyst prepared according to the process of claim 13 and in the absence of an electron donor.
23. A gas phase process for the polymerization at a pressure from 10 to 350 psi of a mixture comprising from 0 to 15 mole % of hydrogen, from 0 to 30 mole % of one or more C3-8 alpha-olefins, from 15 to 100 mole % of ethylene and from 0 to 75 mole % of an inert gas conducted at a temperature from 50°C to 120°C in the presence of a catalyst prepared according to the process of claim 16 and in the absence of an electron donor.
24. A gas phase process for the polymerization at a pressure from 10 to 350 psi of a mixture comprising from 0 to 15 mole % of hydrogen, from 0 to 30 mole % of one or more C3-8 alpha-olefins, from 15 to 100 mole % of ethylene and from 0 to 75 mole % of an inert gas conducted at a temperature from 50°C to 120°C in the presence of a catalyst prepared according to the process of 19 and in the absence of an electron donor.
25. A polymer comprising from 0 to 15 mole % of one or more C3-8 alpha-olefins, from 85 to 100 mole % of ethylene having a molecular weight (Mw) greater than 50,000 and a polydispersity from 3.5 to 7 prepared according to claim 20.
26. A polymer comprising from 0 to 15 mole % of one or more C3-8 alpha-olefins, from 85 to 100 mole % of ethylene having a molecular weight (Mw) greater than 50,000 and a polydispersity from 3.5 to 7 prepared according to claim 21.
27. A polymer comprising from 0 to 15 mole % of one or more C3-8 alpha-olefins, from 85 to 100 mole % of ethylene having a molecular weight (Mw) greater than 50,000 and a polydispersity from 3.5 to 7 prepared according to claim 22.
28. A polymer comprising from 0 to 15 mole % of one or more C3-8 alpha-olefins, from 85 to 100 mole % of ethylene having a molecular weight (Mw) greater than 50,000 and a polydispersity from 3.5 to 7 prepared according to claim 23.
29. A polymer comprising from 0 to 15 mole % of one or more C3-8 alpha-olefins, from 85 to 100 mole % of ethylene having a molecular weight (Mw) greater than 50,000 and a polydispersity from 3.5 to 7 prepared according to claim 24.
30. The process according to claim 1, further including adding after step d from 0 up to 0.3 mmol of an electron donor per g of silica.
CA 2267939 1998-05-12 1999-04-06 Chloride process for making catalyst Expired - Lifetime CA2267939C (en)