KR910009792A - 압출-과립화-분쇄에 의해 감열 호변성 중합체 분말을 제조하는 방법. 분쇄되어 이들 분말을 제조하는 과립물 및 수득된 자유 유동성 미세분말 - Google Patents

압출-과립화-분쇄에 의해 감열 호변성 중합체 분말을 제조하는 방법. 분쇄되어 이들 분말을 제조하는 과립물 및 수득된 자유 유동성 미세분말 Download PDF

Info

Publication number
KR910009792A
KR910009792A KR1019900018195A KR900018195A KR910009792A KR 910009792 A KR910009792 A KR 910009792A KR 1019900018195 A KR1019900018195 A KR 1019900018195A KR 900018195 A KR900018195 A KR 900018195A KR 910009792 A KR910009792 A KR 910009792A
Authority
KR
South Korea
Prior art keywords
temperature
polymer
die
anisotropic
aromatic polyester
Prior art date
Application number
KR1019900018195A
Other languages
English (en)
Inventor
바르레 삘립쁘
모소니에 삘립쁘
Original Assignee
롱쁠랑 쉬미
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 롱쁠랑 쉬미 filed Critical 롱쁠랑 쉬미
Publication of KR910009792A publication Critical patent/KR910009792A/ko

Abstract

내용 없음

Description

압출-과립화-분쇄에 의해 감열 호변성 중합체 분말을 제조하는 방법, 분쇄되어 이들 분말을 제조하는 과립물 및 수득된 자유 유동성 미세분말
본 내용은 요부공개 건이므로 전문내용을 수록하지 않았음

Claims (9)

  1. 압출기 내에 용융상태인 중합성 물질을 형성시키고, 용융상태인 물질을 적당한 형사의 맨드릴 없는 다이을 통과시킴으로써 하나 이상의 고체 실린더 형 이형재(들)을 수득하는 것으로 구성된 압출 공정.
    압출 공정후, 소망되는 분말을 수득하기 위한 통상의 기구 또는 장치를 사용하여 수득된 이형재(들)을 과립화 및 분쇄시키는 것으로 구성된 기존의 공정을 연속적으로 연결시켜, 비등방성 용융체를 형성할 수 있는 감열호변성 중합체로 부터 자유 유동성미세 분말을 제조하는 방법으로서, 압출공정 중에 액정 상이 나타나는 용융온도 Tm보다 높은 온도 T1에 있는 용융된 감열호변성 중합체를 다이에 도달하기 전에 냉각시켜 다이에 들어가자마자 온도 Tm보다 70℃ 낮은 온도 내지 최하 온도인 결정화 온도 T0사이에 존재하는 온도 T2에 도달케 하고, 다이를 통과하는 동안 및 임의적으로는 과립화 기구 또는 장치에 들어가기 전까지 감열호변성 중합체의 온도를 상기 온도 T2로 유지시킴을 특징으로 하는 감열호변성 중합체로부터 자유 유동성 미세 분말의 제조방법.
  2. 제1항에 있어서, 적당한 감열호변성 중합체는 완전 방향족 폴리에스테르, 알킬 방향족 폴리에스테르, 완전 방향족 폴리에스테르 아미드,알킬 방향족 폴리에스테르 아미드, 방향족 폴리아조메틴, 방향족 카르보네이트 폴리에스테르 및 이들 중합체의 혼합물인 방법.
  3. 제2항에 있어서, 사용되는 감열호변성 중합체는 완전 방향족 폴리에스테르, 완전 방향적 폴리에스테르 아미드 및 이들 중합체의 혼합물인 방법.
  4. 제1항 내지 제2항중 어느 한 항에 있어서, 감열호변성 중합체는 260℃ 내지 350℃ 범위에 위치된 용융 온도를 가지며 1 내지 4di/g-1범위에 위치된 고유 점도를 가지는 방법.
  5. 제1항 내지 제4항중 어느 한 항에 있어서, 온도 Tm(액정상이 나타남)보다 5℃ 높은 온도 내지 주의를 요하는 투명온 Tc1내에 존재하지만, Tm+50℃를 초과하지 않는 온도T1에서 감열호변성 중합체를 용융시킨후: 감열호변성 중합체를 다이에 넣기 전에 냉각시켜 다이에 들어가는 순간, 온도 Tc보다 70℃낮은 온도 내지 결정화 온도 Te보다 10℃높은 온도 내에 존재하는 온도 T2에 도달시킴을 특징으로 방법.
  6. 각각 비원섬유성 등방서 미세 구조(약간 비등방성일 수 있다)를 가짐을 특징으로 하는, 비등방성 용융체를 형설할 수 있는 감열호변성 중합체로 부터 제조되며, 제1항 내지 제5항 중 어느 한 항에 따른 방법에서 즉시 수득되어질 수 있는 밀한 과립.
  7. 제6항에 있어서, 결정성 배향fc의 정도가 0.3이하인 등방성 상태(약간 비등방성일 수 있다)의 구조임을 특징으로 하는 과립.
  8. 한편으로는 구형의 입자로 구성되며, 또한 다른 한편으로는, 상기 입자 각각은 비원섬유성 등방성 미세구조(약간 비등방성일 수 있음)를 나타냄을 특징으로 하는 제1항 내지 제3항중 어느 한 항에 따른 방법의 결과에서 수득되어질 수 있으며, 비등방성 용융체를 형성할 수 있는 감열호변성 중합체로 부터 만들어지는 자유 유동성 미세 분말.
  9. 제8항에 있어서, 결정성 배향fc의 정도가 0.3이하인 등방성 상태(약간 비등방성일 수 있음)의 입자 구조임을 특징으로 하는 분말.
    ※ 참고사항 : 최초출원 내용에 의하여 공개하는 것임.
KR1019900018195A 1989-11-10 1990-11-10 압출-과립화-분쇄에 의해 감열 호변성 중합체 분말을 제조하는 방법. 분쇄되어 이들 분말을 제조하는 과립물 및 수득된 자유 유동성 미세분말 KR910009792A (ko)