KR900018400A - 강자성 Ni-Fe 계합금 및 상기한 합금의 우수한 표면성 상태를 갖인 슬래브를 제조하는 방법 - Google Patents

강자성 Ni-Fe 계합금 및 상기한 합금의 우수한 표면성 상태를 갖인 슬래브를 제조하는 방법 Download PDF

Info

Publication number
KR900018400A
KR900018400A KR1019890006336A KR890006336A KR900018400A KR 900018400 A KR900018400 A KR 900018400A KR 1019890006336 A KR1019890006336 A KR 1019890006336A KR 890006336 A KR890006336 A KR 890006336A KR 900018400 A KR900018400 A KR 900018400A
Authority
KR
South Korea
Prior art keywords
less
range
sulfur
oxygen
unavoidable impurity
Prior art date
Application number
KR1019890006336A
Other languages
English (en)
Other versions
KR920006583B1 (ko
Inventor
다다시 이노우에
도모요시 오오기다
Original Assignee
니이미야 유우
엔케이케이 코오포레이숀
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 니이미야 유우, 엔케이케이 코오포레이숀 filed Critical 니이미야 유우
Publication of KR900018400A publication Critical patent/KR900018400A/ko
Application granted granted Critical
Publication of KR920006583B1 publication Critical patent/KR920006583B1/ko

Abstract

내용 없음

Description

강자성 Ni-Fe 계합금 및 상기한 합금의 우수한 표면성 상태를 갖인 슬래브를 제조하는 방법
본 내용은 요부공개 건이므로 전문내용을 수록하지 않았음
제1도는 보론(boron)함유량이 상이한 Ni-Fe계 합금인 소재에서, 수축의 값과 인장시험온도와의 사이의 관계를 보여주는 도표, 제2도는 Ni-Fe계합금의 소재에서, 보론함유량과 800-1000℃의 인장시험온도 범위내에서의 최저수축 값과의 사이의 관계를 보여주는 도표.

Claims (8)

  1. 본질적으로 다음과 같은것을 특징으로 하는 강자성 Ni-Fe계 합금으로 니켈 : 75에서 82까지 wt.% 몰리브덴 : 2에서 6까지 wt.% 붕소 : 0.001에서 0.005까지 wt.% 칼슘 : 불가피적인 불순물로서 산소의 함유량이 0.001-0.003wt.%의 범위내인 경우는 불가피적인 불순물로서의 유황에 대한 중량비에서 다음식을 만족하는 범위내
    1.5Ca/s3.5 (1)
    또는 불가피적인 불순물로서의 산소의 함유량이 이하인 경우는 불가피적인 불순물로서의 유황에 대한 중량비에서 다음식을 만족케하는 범위내
    1.15Ca3.50 (2)
    그리고 나머지 철 및 불가피적인 불순물, 여기서 상기한 불가피적인 불순물로서의 유황, 인, 카아본, 산소 및 질소의 각각의 함유량은 유황에서는 0.002wt.% 이하 인에서는 0.006wt.% 이하 카아본에서는 0.003wt.% 이하 산소에서는 0.003wt.% 이하 그리고, 질소에서는 0.0015wt.% 이하
  2. 제1항에 있어서 Ni-Fe계 합금에서 상기한 계 합금이 1-5wt.% 범위내의 량의 구리(copper)를 더욱 부가적으로 함유하고 있는 Ni-Fe 계 합금
  3. 제1항에 있어서 Ni-Fe계 합금에서 상기한 계 합금이 0.1-0.4wt.%의 범위내의 량의 망간을 더욱 부가적으로 함유하고 있는 Ni-Fe 계 합금
  4. 제2항에 있어서 Ni-Fe 계 합금에서 상기한 Ni-Fe계 합금은 0.1-0.4wt.%의 범위내의 량의 망간을 더욱 부가적으로 함유하고 있는 Ni-Fe계 합금.
  5. 다음과 같은 단계로 되는 것을 특징으로 하는 강자성 Ni-Fe계 합금의 우수한 표면성 상태를 갖는 슬래브를 제조하기 위한 방법, 즉 본질적으로 다음의 것으로 된 소재를 사용하고 : 니켈 : 75에서 82까지 wt.% 몰리브텐 : 2에서 6까지 wt.% 붕소 : 0.001에서 0.005까지 wt.% 칼슘 : 불가피적인 불순물로서의 산소의 함유량이 0.001-0.003wt.%의 범위내의 경우에는 불가피적인 불순물로서의 유황에 대한 중량비에서 다음식을 만족하는 범위내
    1.5Ca/s3.5 (1)
    또는 불가피적인 불순물로서의 산소의 함유량이 0.001wt.%이하의 경우는 불가피적인 불순물로서의 유황에 대한 중량비에서 다음식을 만족케하는 범위내
    1.15Ca3.50 (2)
    그리고 나머지 철 및 불가피적인 불순물, 여기서 상기한 불가피적인 불순물로서의 유황, 인 카아본 산소 및 질소의 각각의 함유량은 유황에서는 0.002wt.% 이하 인에서는 0.006wt.% 이하 카아본에서는 0.003wt.% 이하 산소에서는 0.003wt.%이하 그리고, 질소에서는 0.0015wt.% 이하 상기한 소재를 1100-1250℃의 범위내의 온도에 가열하고 그리하여 이와 같이 가열한 상기한 소재를 800℃ 이상의 다듬질 온도에서 열간가공하여 강자성 Ni-Fe 계합금의 우수한 표면성상태를 갖인 슬래브를 제조한다.
  6. 제5항에 있어서, 상기 소재가 1-5wt.%의 범위내의 량의 망간을 더욱 부가적으로 함유하고 있는 방법.
  7. 제5항에 있어서, 상기한 소재가 0.1-0.4wt.%의 범위내의 량의 망간을 더욱 부가적으로 함유하고 있는 방법
  8. 제6항에 있어서, 상기한 소재가 0.1-0.4wt.%의 범위내의 량의 망간을 더욱 부가적으로 함유하고 있는 방법.
    ※ 참고사항 : 최초출원 내용에 의하여 공개하는 것임.
KR1019890006336A 1988-05-13 1989-05-11 강자성 Ni-Fe계 합금 및 이 합금의 우수한 표면성상을 가진 합금 물품의 제조방법 KR920006583B1 (ko)