KR900009718A - 내구성이 우수한 흡수성 수지 및 그의 제조방법 - Google Patents
내구성이 우수한 흡수성 수지 및 그의 제조방법 Download PDFInfo
- Publication number
- KR900009718A KR900009718A KR1019890018165A KR890018165A KR900009718A KR 900009718 A KR900009718 A KR 900009718A KR 1019890018165 A KR1019890018165 A KR 1019890018165A KR 890018165 A KR890018165 A KR 890018165A KR 900009718 A KR900009718 A KR 900009718A
- Authority
- KR
- South Korea
- Prior art keywords
- water
- ethylenically unsaturated
- unsaturated monomer
- absorbent resin
- weight
- Prior art date
Abstract
내용 없음
Description
본 내용은 요부공개 건이므로 전문내용을 수록하지 않았음
제1도는 팽윤겔의 통액성을 측정하는 장치의 단면도이다.
Claims (30)
- (A)수용성 에틸렌성 불포화 단량체, 이 단량체에 대하여 (B)가교제 0.005~5몰% 및 (C)수용성 연쇄이동제 0.001~1몰%를 함유하는 30중량% 내지 포화농지의 이 단량체(A)수용액을 중합시켜서 되는 내구성이 우수한 (D)흡수성 수지의 제조방법.
- 제1항에 있어서, 중합이 라디칼 중합개시제 존재하에서 수행하는 것이 특징인 방법.
- 제1항에 있어서, 수용성 연쇄이동제 (C)가 차아인산염인 것인 특징인 방법.
- 제1항에 있어서, 가교제 (B)의 사용량이 수용성 에틸렌성 불포화 단량체에 대해 0.02~1몰%인 것이 특징인 방법.
- 제1항에 있어서, 수용성 에틸렌성 불포화 단량체 (A)수용액의 농도가 35중량% 내지 포화농도인 것이 특징인 방법.
- 제1항에 있어서, 수용성 에틸렌성 불포화 단량체 (A)가 아크릴산 및 그의 염을 적어도 50중량% 함유하는 것이 특징인 방법.
- 제1항에 있어서, 수용성 에틸렌성 불포화 단량체 (A)수용액을 회전 교반축을 갖는 반응기 내에서 수용액 중합시키는 것이 특징인 방법.
- 제7항에 있어서, 회전 교반축을 갖는 반응용기가 복수의 회전교반 날개를 갖는 것이 특징인 방법.
- 제8항에 있어서, 복수의 회전교반 날개를 갖는 반응용기가 쌍날개형 니더인 것이 특징인 방법.
- 제1항에 있어서, 수용성 에틸렌성 불포화 단량체 (A)수용액을 분산제 존재하에서 중합 불활성인 소수성 유기용매 중에서 분산시켜 역상 현탁 중합시키는 것이 특징인 방법.
- 제10항에 있어서, 분산제가 HLB 2~7의 비이온계 계면활성제인 것이 특징인 방법.
- 제11항에 있어서, 바이온 계면활성제가 소르비탄 지방산 에스테르인 것인 특징인 방법.
- (A)수용성 에틸렌성 불포화 단량체, 이 단량체에 대하여 (B)가교제 0.005~5몰% 및 (C)수용성 연쇄이동제 0.001~1몰%를 함유하는 30중량% 내지 포화농도의 단량체(A) 수용액을 중합시켜 얻은 (D)흡수성 수지의 표면 근방을 흡수성 수지의 관능기와 반응할 수 있는 (E)친수성 가교제로 가교시켜서 되는 내구성이 우수한 (F)흡수성 수지의 제조방법.
- 제13항에 있어서, 중합이 라디칼 중합개시제 존재하에서 수행하는 것이 특징인 방법.
- 제13항에 있어서, 수용성 연쇄이동제(C)가 치아인산염인 것이 특징인 방법.
- 제13항에 있어서, 수용성 에틸렌성 불포화 단량체(A)가 아크릴산 및 그의 염을 적어도 50중량% 함유하는 것이 특징인 방법.
- 제13항에 있어서, 수용성 에틸렌성 불포화 단량체(A) 수용액을 회전 교반축을 갖는 반응기 용기내에서 수용액 중합시키는 것이 특징인 방법.
- 제13항에 있어서, 수용성 에틸렌성 불포화 단량체(A)수용액을 분산제 존재하에서 중합불활성인 소수성 유기용매중에서 분산시키고, 역상현탁 중합시키는 것이 특징인 방법.
- 제13항에 있어서, 수용성 에틸렌성 불포화 단량체(A)를 중합시켜 얻은 흡수성수지(D)100중량부에 대하여 물 및 친수성 유기용매로 구성된 군에서 선택된 적어도 1종을 0~20중량부 존재하에서 카르복실기와 반응할 수 있는 적어도 2개의 관능기를 갖는 화합물(E-1) 및 다가금속염(E-2)으로 구성되는 군에서 선택된 적어도 1종의 친수성 가교제(E)를 0.005~5중량부를 혼합하고, 40~250℃의 온도에서 가열하는 것이 특징인 방법.
- 제19항에 있어서, 친수성 가교제(E)가 화합물(E-1)인 것이 특징인 방법.
- 제19항에 있어서, 화합물(E-1)이 다가알코올 화합물, 다가글리시딜 에테르화합물, 다가옥사졸린 화합물 및 다가아민 화합물로 구성된 군에서 선택된 것이 특징인 방법.
- 제19항에 있어서, 물이 흡수성수지(D)100중량부에 대하여 0.5~10중량부의 양으로 사용하는 것이 특징인 방법.
- 제19항에 있어서, 친수성 유기용매(G)가 흡수성수지(D)에 대하여 0~8중량부의 양으로 사용하는 것이 특징인 방법.
- 제19항에 있어서, 90~220℃에서 수행하는 것이 특징인 방법.
- (A)수용성 에틸렌성 불포화 단량체, 이 단량체에 대해 (B)가교제 0.005~5몰% 및 (C)수용성 연쇄이동제 0.001~1몰%를 함유하는 30중량%내지 포화농도의 단량체(A)수용액을 중합시켜 얻은 내구성이 우수한 (D)흡수성수지.
- 제25항에 있어서, 수용성 에틸렌성 불포화단량체(A)가 아크릴산 및 그의 염을 적어도 50중량% 함유한 흡수성수지.
- (A)수용성 에틸렌성 불포화단량체, 이단량체에 대하여 (B)가 교제 0.005~5몰% 및 (C)수용성 연쇄이동제 0.001~1몰%를 함유하는 30중량% 내지 포화농도의 단량체(A)수용액을 중합시켜 얻은 (D)흡수성 수지의 표면근방을 흡수성지의 관능기와 반응할 수 있는 (E)친수성 가교제로 가교시켜 얻어진 내구성이 우수한 (F)흡수성수지.
- 제27항에 있어서, 수용성 에틸렌성 불포화 단량체(A)가 아크릴산 및 그의 염을 적어도 50중량% 함유한 흡수성수지.
- 제27항에 있어서, 수용성 에틸렌성 불포화 단량체(A) 수용액을 분산제 존재하에 중합 불활성인 소수성 유기용매중에 분산하여 역상현탁 중합시킨 흡수성수지.
- 제27항에 있어서, 친수성 가교제(E)가 카르복실기와 반응을 할 수 있는 적어도 2개의 관능기를 갖는 화합물인 흡수성 수지.※ 참고사항 : 최초출원 내용에 의하여 공개하는 것임.