KR900000485A - 스테인레스 스틸의 열처리 방법 - Google Patents

스테인레스 스틸의 열처리 방법 Download PDF

Info

Publication number
KR900000485A
KR900000485A KR1019890007920A KR890007920A KR900000485A KR 900000485 A KR900000485 A KR 900000485A KR 1019890007920 A KR1019890007920 A KR 1019890007920A KR 890007920 A KR890007920 A KR 890007920A KR 900000485 A KR900000485 A KR 900000485A
Authority
KR
South Korea
Prior art keywords
stainless steel
heat treatment
austenitic stainless
stress corrosion
weight
Prior art date
Application number
KR1019890007920A
Other languages
English (en)
Other versions
KR920004702B1 (ko
Inventor
조세프 제이컵 앨빌
마이런 고든 제랄드
Original Assignee
존 알.라프터
제너럴 일렉트릭 캄파니
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 존 알.라프터, 제너럴 일렉트릭 캄파니 filed Critical 존 알.라프터
Publication of KR900000485A publication Critical patent/KR900000485A/ko
Application granted granted Critical
Publication of KR920004702B1 publication Critical patent/KR920004702B1/ko

Abstract

내용 없음

Description

스테인레스 스틸의 열처리 방법
본 내용은 요부공개 건이므로 전문내용을 수록하지 않았음
제1도는 스테인레스 스틸의 열처리 온도 및 처리시간의 변화에 비례한 다양한 응력 부식 감응도를 나타낸 그래프.
제2도는 본 발명의 열처리 방법으로 행한 스테인레스 스틸의 상대적 연성력을 도시한 막대 그래프.
제3도는 본 발명의 열처리를 행한 후의 스테인레스 스틸의 응력 부식 검사에 의해 획득된 상대적 최대 응력을.

Claims (12)

  1. 접속 방사선에 노출된 니켈과 크롬을 성분으로 하는 오스테나이트 합금체를, 상기 방사선으로 인한 응력 부식 균열을 방지하기 위한 열처리 방법에 있어서, 상기 합금체를 최소 2050°F 내지 약 2400°F 범위의 온도에서, 적어도 1분 내지 약 45분동안 열처리를 행하며, 상기 열처리를 행하는 시간은 열처리 온도에 근사적으로 반비례하여 정하는 것을 특징으로 하는 오스테나이트 합금체의 응력 부식 균열 방지 열처리 방법.
  2. 물리적 특성을 강화하여, 집속 방사선에 노출된 오스테나이트 스테인레스 스틸의 응력 부식 균열 방지 열처리 방법에 있어서, 오스테나이트 스테인레스 스틸을 최소 2050°F 내지 약 2400°F 범위의 온도에서, 최소한 약 1분 내지 약 45분동안 열처리를 행하며, 열처리를 행하는 시간을 상기 열처리 온도에 근사적으로 반비례하여 정하는 것을 특징으로 하는 오스테나이트 스테인레스 스틸의 응력 부식 규열 방지 열처리 방법.
  3. 제2항에 있어서, 상기 오스테나이트 스테인레스 스틸의 열처리 방법은, 약 2200°F 내지 약 2400°F의 온도로 하여 약 1분 내지 약 20분동안 행하는 것을 특징으로 하는 오스테나이트 스테인레스 스틸의 응력 부식 균열 방지 열처리 방법.
  4. 제2항에 있어서, 상기 오스테나이트 스테인레스 스틸은 Type 304인 것을 특징으로 하는 오스테나이트 스테인레스 스틸의 응력 부식 균열방지 열처리 방법.
  5. 제2항에 있어서, 상기 오스테나이트 스테인레스 스틸의 합금 조성물 및 그 조성물의 중량 백분율(%)
    크롬 18 내지 20중량%
    니켈 8 내지 14중량%
    탄소 최대 0.08중량%
    망간 최대 2.0중량%
    실리콘 최대 1.0중량%
    몰리브덴 최대 3.0중량%
    철 그외의 나머지 중량%
    인 것을 특징으로 하는 오스테나이트 스테인레스 스틸의 응력 부식 균열 방지 열처리 방법.
  6. 합금 조성물 및 조성물 중량 백분율(%)의
    크롬 18 내지 20중량%
    니켈 8 내지 14중량%
    탄소 최대 0.08중량%
    망간 최대 2.0중량%
    실리콘 최대 1.0중량%
    몰리브덴 최대 3.0중량%
    철 그외의 나머지 중량%
    인 오스테나이트 스테인레스 스틸을, 집속 방사선으로 인한 응력 부식 균열 방지 열처리 방법에 있어서, 상기 오스테나이트 스테인레스 스틸을 최소 약 2050°F 내지 약 2400°F의 온도 범위로 하여 최소 약 1분 내지 약 45분 동안 열처리를 행하는 것을 특징으로 하는 오스테나이트 스테인레스 스틸의 응력 부식 균열 방지 열처리 방법.
  7. 제6항에 있어서, 상기 오스테나이트 스테인레스 스틸을, 약 2200°F 내지 약 2400°F의 온도 범위에서 약 1분 내지 약 20분동안 열처리를 행하는 것을 특징으로 하는 오스테나이트 스테인레스 스틸의 응력 부식 균열방지 열처리 방법.
  8. 제6항에 있어서, 상기 오스테나이트 스테인레스 스틸은 Type 304인 것을 특징으로 하는 오스테나이트 스테인레스 스틸의 응력 부식 균열 방지 열처리 방법.
  9. 제6항에 있어서, 상기 오스테나이트 스테인레스 스틸의 합금 조성물 및 조성물의 중량 백분율(%)은
    코롬 18 내지 20중량%
    니켈 8 내지 12중량%
    탄소 최대 0.08중량%
    망간 최대 2.0중량%
    실리콘 최대 1.0중량%
    철 그외의 나머지 중량%
    인 것을 특징으로 하는 오스테나이트 스테인레스 스틸의 응력 부식 균열 방지 열처리 방법.
  10. 제6항에 있어서, 상기 오스테나이트 스테인레스 스틸은 약 2300°F의 온도에서 약 1분 내지 약 20분동안 열처리를 행하는 것을 특징으로 하는 오스테나이트 스테인레스 스틸의 응력 부식 균열 방지 열처리 방법.
  11. 집속된 방사선에 노출에 인한 오스테나이트 스테인레스 스틸의 응력 부식 균열 방지 열처리 방법에 있어서, 합금 조성물 및 조성물 중량 백분율(%)이
    코롬 18 내지 20중량%
    니켈 8 내지 12중량%
    탄소 최대 0.08중량%
    망간 최대 2.0중량%
    실리콘 1.0중량%
    철 그외의 나머지 중량%
    인 오스테나이트 스테인레스 스틸을, 약 2200°F 내지 약 2400°F 온도 범위로 약 1분 내지 약 20분동안 열처리를 행하며, 열처리 시간을 열처리 온도에 근사적 반비례하는 것을 특징으로 하는 응력 부식 균열 방지 열처리방법.
  12. 집속방사선에 노출로 인한 단일면의 오스테나이트 스테인레스 스틸의 응력 부식 균열 방지 열처리방법에 있어서, 상기 단일면에 오스테나이트 스테인레스 스틸을 최소한 약 2050°F 내지 2400°F 온도 범위에서 1분 내지 약 45분동안 행하며, 상기 열처리 시간은 열처리 온도에 반비례하여 정해지는 것을 특징으로 하는 응력 부식 균열 방지 열처리 방법.
    ※ 참고사항 : 최초출원 내용에 의하여 공개하는 것임.
KR1019890007920A 1988-06-13 1989-06-09 스테인레스 스틸의 열처리 방법 KR920004702B1 (ko)