CN1038672A - 奥氏体不锈钢中辐照加速应力腐蚀开裂的抑制处理 - Google Patents

奥氏体不锈钢中辐照加速应力腐蚀开裂的抑制处理 Download PDF

Info

Publication number
CN1038672A
CN1038672A CN89101613A CN89101613A CN1038672A CN 1038672 A CN1038672 A CN 1038672A CN 89101613 A CN89101613 A CN 89101613A CN 89101613 A CN89101613 A CN 89101613A CN 1038672 A CN1038672 A CN 1038672A
Authority
CN
China
Prior art keywords
stainless steel
austenitic stainless
stress corrosion
maximum
alloy
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN89101613A
Other languages
English (en)
Other versions
CN1024564C (zh
Inventor
阿尔温·约瑟夫·雅各斯
杰拉尔德·迈龙·戈登
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
General Electric Co
Original Assignee
General Electric Co
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by General Electric Co filed Critical General Electric Co
Publication of CN1038672A publication Critical patent/CN1038672A/zh
Application granted granted Critical
Publication of CN1024564C publication Critical patent/CN1024564C/zh
Anticipated expiration legal-status Critical
Expired - Fee Related legal-status Critical Current

Abstract

在不锈钢以及镍—铬合金中抑制辐照加速应力腐蚀开裂的一种热处理方法。

Description

本发明涉及在强辐照环境中（如在核裂变反应堆内部）应用的奥氏体不锈钢和镍-铬合金。本发明与核反应堆内部和周围通常应用的不锈钢和其它合金的断裂有关，这种断裂主要由于受到高水平辐照导致出现应力腐蚀开裂。
高铬-镍型不锈钢合金，由于其众所周知的高耐腐蚀性和高耐其他腐蚀条件的性质，通常用作核裂变反应堆中的构件。例如，核燃料组件、中子吸收控制装置和中子源夹具等常常被包覆或被置于304型或类似合金成分的不锈钢包壳或屏蔽套中。这类组件（包括指出的那些）常常被放在核反应堆的裂变燃料的芯体内部和周围，在此区域极强的腐蚀条件（如强辐照和高温）最为恶劣和具破坏性。
普遍认为固溶或轧制退火的（Solution        or        mill        annealed）不锈钢合金商品，对其他损坏源造成的晶粒间应力腐蚀开裂和本身破坏，基本上是不敏感的。然而，已经发现不锈钢在受到强辐照之后，例如最典型的是在水冷却核裂变反应堆的裂变燃料芯体中和其附近使用时，由于晶粒间应力腐蚀开裂而碎裂和破坏。虽然不锈钢合金已经处在所谓的固溶或轧制退火状态，也就是说已经过热处理，即加热至温度在约1，850°F至2，050°F范围内，然后迅速冷却以使碳化物溶解，并防止碳化物自溶液进入晶粒边界成核和沉淀析出，但是仍然发生了这种与辐照有关的晶粒间应力腐蚀开裂破坏。
一种理论认为，由强场或广泛暴露，或两者兼有而导致的高水平辐照是引起不锈钢合金碎裂的一个重要原因，除了其他可能的因素外，这是由于辐照促进了合金的杂质成分的偏析所致。
过去为减少不锈钢合金中与辐照有关的晶间应力腐蚀开裂的努力，包括研制耐蚀合金组合物。例如，已经提出含有低水平杂质的不锈钢。
本发明包括一种处理高铬-镍型及其类似合金的奥氏体不锈钢合金组合物和由其构成的零件和装置的方法，此方法可抑制由于高水平的和/或长时间的辐照暴露导致的将来可能发生的应力腐蚀开裂。本预防性处理包括一种精密的热处理过程，或强化的固溶退火步骤，这种处理可使这类合金即使受到强辐照也具有高度的抗应力腐蚀开裂的性能。
本发明的主要目的，是提供一种抑制奥氏体不锈钢中，其他高镍-铬合金中，以及由其构成的部件中，由于受到辐照而发生应力腐蚀开裂的方法。
本发明的又一目的，是提供一种在经受强辐照的奥氏体不锈钢合金以及由其制造的制品中，赋予抗辐照加速应力腐蚀开裂的性能的有效和可行的处理方法。
本发明的再一个目的，是提供一种抑制用于核反应堆的奥氏体不锈钢构件和经受高辐照的其他不锈钢制造的部件，由于应力腐蚀开裂而断裂的经济和实用的方法。
本发明的另外一个目的，是提供一种解决奥氏体不锈钢合金中辐照后发生应力腐蚀开裂问题的有效方法，此方法对这些合金或它们的制品不会产生任何有害的作用。
图1曲线表示不锈钢的应力腐蚀敏感度与热处理不同水平的温度以及对应时间之间的关系;
图2是一种条线图，它表示经本发明热处理的不锈钢的相对延伸率;和
图3是一种条线图，它表示受到本发明热处理的不锈钢在应力腐蚀试验中达到的相对最大应力。
本发明主要与由（或包括）奥氏体不锈钢（例如304型）制造的结构单元和部件，或它们的组合件有关，这些构件，部件或组合件设计用在核裂变反应堆的放射性环境中或用在其他与辐照有关的设备或环境中。本发明特别针对阻止在这种使用中的奥氏体不锈钢（包括单相奥氏体不锈钢）发生辐照加速碎裂的一种预防手段。
本发明进而适用于奥氏体的、高镍-铬合金，其中含有约30%（重量）至约76%（重量）的镍和约15%（重量）至约24%（重量）的较小量铬，例如商品因科镍铬不锈钢（Incoloy）和因科内尔镍合金（Inconel）系列产品。
本发明特别是针对包括商品纯和高纯度两种304型铬-镍奥氏体不锈钢，使其对于辐照造成的碎裂具有潜在的不敏感性。商品304型不锈钢的技术规范在C.L.Mautell编辑的《工程材料手册》（Engineering        Materials        Handbook）一书1958年版5-12页和第5-13页的表5-4中有详细说明。这种合金一般含有约18-20%（重量）的铬和约8-14%（重量）的镍，以及最大重量百分含量为0.08的碳、2.0的锰、1.0的硅和3.0的钼，其余为铁及某些少量无意义的杂质。
组件，如燃料和吸收棒的包壳、中子源夹持器等，均包含有上述类型的奥氏体不锈钢合金，并应用于核裂变反应堆的燃料芯体中，这些组件往往由于称为“辐照加速的应力腐蚀开裂”现象而断裂。这种形式的碎裂是应力腐蚀开裂的一种特殊形式，尽管不锈钢合金已进行了固溶或轧制退火，但它仍可发生。已经过温度1850°F至2050°F常规固溶或轧制退火的不锈钢，在工业中被认为可免于发生晶粒间应力腐蚀开裂。然而，当这样处理过的不锈钢合金受到高水平辐照时（如在核反应堆的燃料芯体的内部和周围受到的典型辐照），强辐照场在促使发生晶粒间应力腐蚀开裂中起了某些复杂的作用。一种理论认为，这种现象可能的机理或原因是辐照促进了合金内部的杂质（如磷、硫、硅和氮）在晶粒边界偏析。
本发明包括一种严格的温度和保温时间条件的预防性热处理，它可以显著地减少辐照对奥氏体不锈钢合金通常表现出的不利影响或作用，以及减少辐照在促使这种合金发生晶粒间应力腐蚀开裂的有害有作用。本发明的方法包括使奥氏体不锈钢合金，经过温度为至少2050°F（1121℃）直至约2400°F（1316℃）、保温时间至少1分钟直至约45分钟的特殊热处理步骤。在此范围内的保温时间应与温度近似成反比。例如，在有效实施本发明本发明的条件范围内，当温度在给定范围的较低区域时，所用时间应当较长些;反之，当温度在给定范围的较高区域时，所用时间应以较短些为宜。
阻止发生辐照引致的应力腐蚀开裂的本方法，最好是使奥氏体不锈钢合金在温度接近最佳范围（2200°F至2400°F）内保温较短时间（约5分钟至约20分钟）。由实施例将会清楚地看到，为获得有效的耐腐蚀性，在该温度条件下可允许的保温时间，对于商品纯级的304型不锈钢比高纯级的同种合金，要普遍短一些。
本发明处理方法的特殊的温度和时间条件，可有效地抑制辐照加速的应力腐蚀开裂，以及起因于敏化作用的普通晶粒间应力腐蚀开裂。本发明的固溶退火处理温度/时间所产生的减轻应力腐蚀开裂的作用，似应是合金晶粒界面杂质较有效的脱附的结果。
下述的评估试验可做为实施本发明的特定实例，以及说明本发明在减少奥氏体不锈钢合金由于强辐照而发生晶粒间应力腐蚀开裂方面有显著的抑制作用。
进行应力腐蚀评估的不锈钢合金的成分如下：
Figure 891016139_IMG2
在制备不锈钢合金评估用的试验样品时，首先使样品都经过固溶退火热处理（如下文的详细说明），其条件包括本发明范围内的和以外的，之后将所有样品在核反应堆中在温度550°F下进行辐照，使快中子积分通量范围达到2.22×1021中子/厘米2至3.08×1021中子/厘米2（E＞1兆电子伏）。用扫描电子显微镜在辐照试验样品的断裂面上所观察到的晶粒间应力腐蚀程度，做为辐照加速应力腐蚀开裂现象的计量。
试验样品所用的热处理的温度和时间条件在下列表3中给出：
Figure 891016139_IMG4
试验样品的应力腐蚀试验结果，对于热处理的温度及时间的关系在图1曲线中给出。由图1的数据可知，经温度2200°F约20分钟、或温度2300°F约5分钟、或温度2400°F约1分钟的热处理，商品纯轧制退火的304型不锈钢的辐照加速的应力腐蚀开裂（以晶粒间应力腐蚀开裂百分数计量）可从约90%降至约0%。此外，高纯度轧制退火的304型不锈钢经2200°F约45分钟的热处理，其辐照加速的应力腐蚀开裂可由约50%降至约0%。
值得注意的是，对于有效热处理存在有明显的最大加热时间，如图1所示，例如对于商品纯304型不锈钢在2400°F加热时间若比1分钟长时，就不能完全消除辐照加速应力腐蚀开裂。随着加热时间的增加，腐蚀开裂呈现显著增加，因此对于商品纯304型不锈钢在2400°F时的近似最大加热时间约为1分钟。
本发明的固溶退火温度和时间条件，在奥氏体不锈钢中不仅可以消除辐照加速的应力腐蚀开裂，而且还提高了这种合金在辐照时的机械性能。例如，图2表明经应力腐蚀试验的商品纯304型不锈钢，其延伸率的峰值范围增长至13-16%，与之相比，对于轧制退火商品纯304型不锈钢约为0.6%，以上结果是两者被辐照至相同的中子积分通量后获得的。由温度/时间固溶退火而获得的增强的延展性，对于采用经受辐照的不锈钢组合件的设计人员来说，是非常有利的，因为根据轧制退火不锈钢辐照试验结果，设计人员目前普遍采用在温度550°F和中子积分通量大于6×1020中子/厘米2时的延伸率下限是1.1%。与此类似，图3表明，在应力腐蚀试验中达到的最大应力（或抗拉强度极限）可增加至峰值范围101-117千磅/吋2（ksi），与之相比，对于辐照的商品纯轧制退火304型不锈钢为45ksi。

Claims (12)

1、抑制在含有高镍和铬的奥氏体合金中主要由于高强辐照而发生应力腐蚀开裂的一种方法，该方法是通过将大块该合金在温度范围为至少2050°F内保持至少1分钟直至约45分钟，该合金的热处理时间与热处理温度近似成反比。
2、抑制在奥氏体不锈钢中主要由于高强辐照而发生的应力腐蚀开裂和提高其物理性能的一种方法，此方法包括单相奥氏体不锈钢热处理，将其大块该不锈钢在温度范围为至少2050°F直至2400°F内保持至少1分钟直至约45分钟，此不锈钢的热处理时间与热处理温度近似成反比。
3、根据权利要求2的在奥氏体不锈钢中抑制应力腐蚀开裂的方法，其中热处理包括将大块奥氏体不锈钢在温度在约2200°F至约2400°F范围内保持1分钟至约20分钟。
4、根据权利要求2的在奥氏体不锈钢中抑制应力腐蚀开裂的方法，其中所述的奥氏体不锈钢包括304型。
5、根据权利要求2的在奥氏体不锈钢中抑制应力腐蚀开裂的方法，其中所述的不锈钢由近似的重量百分组成如下的一种合金构成：
铬        18-20
镍        8-14
碳        最大0.08
锰        最大2.0
硅        最大1.0
钼        最大3.0
铁        余量。
6、抑制奥氏体不锈钢中主要由于高强辐照发生应力腐蚀开裂的一种方法，其中包括热处理由近似重量百分组成如下的一种合金构成的不锈钢：
铬        18-20
镍        8-14
碳        最大0.08
锰        最大2.0
硅        最大1.0
钼        最大3.0
铁        余量
将大块所述合金在温度至少2050°F至约2400°F范围内保持至少约1分钟至约45分钟。
7、根据权利要求6的抑制奥氏体不锈钢中应力腐蚀开裂的方法，其中包括将大量奥氏体不锈钢在温度约2200°F至2400°F范围内保持约1分钟至约20分钟。
8、根据权利要求6的抑制奥氏体不锈钢中应力腐蚀开裂的方法，其中所述的不锈钢包括304型。
9、根据权利要求6的抑制奥氏体不锈钢中应力腐蚀开裂的方法，其中所述的不锈钢由近似重量百分组成如下的合金构成：
铬        18-20
镍        8-12
碳        最大0.08
锰        最大2.0
硅        最大1.0
铁        余量。
10、根据权利要求6的抑制奥氏体不锈钢应力腐蚀开裂的方法，其中热处理包括将大块该单相奥氏体不锈钢在温度约2300°F下保持约1分钟至约20分钟。
11、抑制奥氏体不锈钢中主要由于高强辐照而发生应力腐蚀开裂的一种方法，其中包括热处理由近似重量百分组成如下的一种合金构成的不锈钢：
铬        18-20
镍        8-12
碳        最大0.08
锰        最大2.0
硅        最大1.0
铁        余量
将大块所述的合金在温度约2200°F至约2400°F范围内保持约1分钟至约20分钟，此钢材的热处理时间与热处理温度范围近似成反比。
12、抑制在单相奥氏体不锈钢中主要由于高强辐照而发生应力腐蚀开裂的一种方法，此方法包括热处理该单相奥氏体不锈钢，将大块该不锈钢在温度范围至少2050°F直至约2400°F内保持至少1分钟直至约45分钟，此钢材热处理时间与热处理温度近似成反比。
CN89101613A 1988-06-13 1989-03-23 抑制奥氏体不锈钢中辐照加速应力腐蚀开裂的方法 Expired - Fee Related CN1024564C (zh)