KR900000296A - 티탄산 바륨의 제조방법과 티탄산 스트론튬 결정체와 티탄산 바륨 및 티탄산 스트론튬 결정체 - Google Patents

티탄산 바륨의 제조방법과 티탄산 스트론튬 결정체와 티탄산 바륨 및 티탄산 스트론튬 결정체 Download PDF

Info

Publication number
KR900000296A
KR900000296A KR1019890007615A KR890007615A KR900000296A KR 900000296 A KR900000296 A KR 900000296A KR 1019890007615 A KR1019890007615 A KR 1019890007615A KR 890007615 A KR890007615 A KR 890007615A KR 900000296 A KR900000296 A KR 900000296A
Authority
KR
South Korea
Prior art keywords
powder
organic compound
barium
strontium
acid organic
Prior art date
Application number
KR1019890007615A
Other languages
English (en)
Inventor
레로트 루크
와우티어 헨리
Original Assignee
진 피에르 헤르만스
솔베이 앤드시에(소시에떼 아노님)
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 진 피에르 헤르만스, 솔베이 앤드시에(소시에떼 아노님) filed Critical 진 피에르 헤르만스
Publication of KR900000296A publication Critical patent/KR900000296A/ko

Abstract

내용 없음

Description

티탄산 바륨의 제조방법과 티탄산 스트론튬 결정체와 티탄산 바륨 및 티탄산 스트론튬 결정체
본 내용은 요부공개 건이므로 전문내용을 수록하지 않았음
제1도는 본 발명의 방법을 실시하는데 사용되는 실험장치의 정면도.
제2도는 본 발명에 따른 방법의 가수분해 단계후의 얻은 티타늄과 바륨의 혼합 산화물의 무정형 분말 확대 사진.
제3도는 분말 결정화에 의하여 얻은 본 발명에 따른 티탄산 바륨 결정체 분말의 확대 사진.

Claims (10)

  1. 산화 티타늄과 산화 바륨과/또는 산화 스트론튬을 무정형 분말 상태로 함께 침전시키고 무정형 분말을 400℃이상의 온도로 가열하여서 하는 티탄산 바륨과/또는 티탄산 스트론튬 결정체의 제조방법에 있어서, 공동 침전에서, 티타늄 알코올레이트를 산화물, 수산화물과 알코올레이트에서 선택한 바륨과/또는 스트론튬 화합물과 분자에 6개 이상의 탄소원자를 함유하는 산 유기 화합물의 존재하에서 가수분해하고, 무정형 분말을 가열하는 동안, 수증기, 암모니아와 이산화 탄소에서 선택되고 산소가 없는 가스로 이루어진 기류를, 분말과 접촉시켜서 통과시켜 산유기 화합물을 증류 제거하여 이를 형성하는 입자를 분절함을 특징으로하는 상기 제조방법.
  2. 제1항에 있어서, 산 유기 화합물을 분자에 8개 이상의 탄소 원자를 함유하는 카르복실산에서 선택함을 특징으로하는 제조방법.
  3. 제1항 또는 제2항에 있어서, 산 유기 화합물을 티탄산 바륨몰당 20-200g의 양으로 사용하고, 수증기, 암모니아와/또는 이산화 탄소를 기류에서 50체적% 이상의 양으로 사용함을 특징으로하는 제조방법.
  4. 제1항 내지 제3항중 어느 한항에 있어서, 기류의 온도를 350-700℃에서 고정시킴을 특징으로하는 제조방법.
  5. 제1항 내지 제3항중 어느 한항에 있어서, 산 유기 화합물을 증류 제거한 후, 습기가 없는 산화 기체를 분말과 접촉시켜서 통과시킴을 특징으로하는 제조방법.
  6. 제5항에 있어서, 산화기체가 건조 공기임을 특징으로하는 제조방법.
  7. 제5항 또는 제6항에 있어서, 기류를 400-600℃의 온도에서 사용하고, 산화기체를 600-800℃의 온도에서 사용함을 특징으로하는 제조방법.
  8. 제5항 내지 제7항중 어느 한항에 있어서, 분말에 최초 존재하는 80중량% 이상의 산 유기화합물을 제거될 때까지 기류를 무정형 분말과 접촉시켜 통과시킨 다음, 기류와 처리한 후 분말에 존재하는 80중량% 이상의 탄소질 잔유물을 제거할 때까지 산화 기체를 분말과 접촉시켜서 통과시킴을 특징으로하는 제조방법.
  9. 크기가 1미크론이하이고, 불규칙적이고 각 형태를 갖는 입자 상태의 티탄산 바륨과/또는 티탄산 스트론튬 결정체.
  10. 제9항에 있어서, 제1항 내지 제9항중 어느 한 항에 따른 방법에 의하여 얻을 수 있는 결정체.
    ※ 참고사항 : 최초출원 내용에 의하여 공개하는 것임.
KR1019890007615A 1988-06-13 1989-06-02 티탄산 바륨의 제조방법과 티탄산 스트론튬 결정체와 티탄산 바륨 및 티탄산 스트론튬 결정체 KR900000296A (ko)