KR850000040A - 내마모성 재료 및 그의 제조방법 - Google Patents
내마모성 재료 및 그의 제조방법 Download PDFInfo
- Publication number
- KR850000040A KR850000040A KR1019840002997A KR840002997A KR850000040A KR 850000040 A KR850000040 A KR 850000040A KR 1019840002997 A KR1019840002997 A KR 1019840002997A KR 840002997 A KR840002997 A KR 840002997A KR 850000040 A KR850000040 A KR 850000040A
- Authority
- KR
- South Korea
- Prior art keywords
- iron alloy
- resistant iron
- tough wear
- alloy
- weight
- Prior art date
Abstract
내용 없음.
Description
본 내용은 요부공개 건이므로 전문내용을 수록하지 않았음
Claims (40)
- 과공정 백주철로 이루어진 인성 마멸저항성 철합금에 있어서, 과공정 백주철이 철에 존재하는 부수적인 불순물은 별문제로 하고 4.0%(중량비) 이상의 탄소, 25-45%(중량비) 크롬, 0-15%(중량비) 망간, 0-10%(중량비)몰리브덴, 0-10% 니켈(중량비), 0-2%(중량비) 보론, 티타늄, 텅스텐, 탄탈, 바나듐 및 니오브중에서 선택된 원소를 형성하며 0-5%(중량비)로 존재하는 탄소 적어도 한 종류를 갖고 있고, 원소를 형성하는 상기 탄화물 적어도 한 종류가 총 15%보다 크지 않게 존재하고, 주조물로써의 합금이 적어도 10㎜크기의 최소두께를 가지며 미세구조가 부피비로 20%이상 존재하는 바늘모양 M7C3형으로된 일차탄화물과 공정 조성물로된 매트릭스로 이루어지고, 실질적으로 합금 전체에 걸쳐서 M7C3형으로된 일차탄화물의 평균 횡단면 크기가 75M보다 크지 않음을 특징으로 하는 인성 마멸 저항성 철합금.
- 제1항에 있어서, 원소를 형성하는 상기 탄화물 적어도 두종류가 적어도 총 10%(중량비)로 또 망간이 적어도 5%(중량비)로 존재함을 특징으로 하는 인성 마멸 저항성 철 합금.
- 제1항 또는 제2항에 있어서, 적어도 한 종류의 망간과 니켈이 각각 2%(중량비)와 4%(중량비)보다 작지 않은 수준으로 존재함을 특징으로 하는 인성 마멸 저항성 철 합금.
- 제1항 내지 제3항 중 어느한 항에 있어서, 보론이 1-2%(중량비)로 또 망간이 적어도 5%(중량비)로 존재함을 특징으로 하는 인성 마멸저항성 철합금.
- 제1항 내지 제4항중 어느 한항에 있어서, 보론이 1-2%(중량비)로 또 망간이 적어도 5%(중량비)로 존재함을 특징으로 하는 인성 마멸저항성 철합금.
- 제1항에 있어서, 상기 매트릭스가 공정 탄화물, 오오스테나이트와 마르텐사이트의 혼합물 및 이차탄화물로 이루어짐을 특징으로 하는 인성 마멸저항성 철합금.
- 제6항에 있어서, 오오스테나이트와 다른 것에 관계된 마르텐사이트의 한종류가 40-60%로 존재함을 특징으로 하는 인성 마멸저항성 철합금.
- 제1항에 있어서, 상기 매트릭스가 실질적으로 마르텐사이트가 없은 공정 탄화물, 오오스테나이트 및 이차 탄화물로 이루어짐을 특징으로 하는 인성 마멸저항성 철합금.
- 제1항 내지 제8항 중 어느 한항에 있어서, 탄소가 4.0-7.5%(중량비)로 존재함을 특징으로 하는 인성마멸 저항성 철합금.
- 제9항에 있어서, 탄소가 4.5-5.5%(중량비)로 존재함을 특징으로 하는 인성 마멸 저필성 철합금.
- 제1항 내지 제10항 중 어느 한항에 있어서, 크롬이 적어도 30%(중량비)의 수준으로 존재함을 특징으로 하는 인성 마멸 저항성 철합금.
- 제11항에 있어서, 크롬이 30-40%(중량비)로 존재함을 특징으로 하는 인성 마멸 저항성 철합금.
- 제1항 내지 제12항중 어느 한항에 있어서, 티타늄, 텅스텐, 탄탈, 바다듐 및 니오브중 적어도 한 종류가 1-5%(중량비)로 존재하나 총 15%(중량비)를 초과하지 않으며 미세한 입자 탄화물로써 합금을 주조하는 용해된 금속에 첨가되어 있음을 특징으로 하는 인성 마멸 저항성 철합금.
- 제1항 내지 제13항 중 어느 한항에 있어서, 최고 2%(중량비)까지 존재하는 보론이 미세한 입자탄화보론으로써 합금을 주조하는 용해된 금속에 첨가되어 있음을 특징으로 하는 인성 마멸 저항성 철합금.
- 제1항 내지 제14항중 어느 한항에 있어서, 1-10%(중량비)로 존재하는 몰리브덴이 미세한 입자 탄화몰리브덴으로써 합금을 주조하는 용해된 금속에 첨가되어 있음을 특징으로 하는 인성 마멸 저항성 철합금.
- 제1항 내지 제15항 중 어느 한항에 있어서, 일차 탄화물의 부피비가 30-60%임을 특징으로 하는 인성 마멸 저항성 철합금.
- 제1항 내지 제16항 중 어느 한항에 있어서, 일차탄화물의 부피비가 40-70%임을 특징으로 하는인성 마멸저항성 철합금.
- 제1항 내지 제16항 중 어느 한항에 있어서, 일차탄화물의 부피비가 30-80%임을 특징으로 하는 인성마멸저항성 철합금.
- 제18항에 있어서, 일차 탄화물의 부피비가 55-80%임을 특징으로 하는 인성 마멸 저항성 철합금.
- 제1항 내지 제19항중 어느 한항에 있어서, 상기 M7C3일차 탄화물의 평균 횡단면 크기가 60마이크론 이하임을 특징으로 하는 인성 마멸 저항성 철합금.
- 제20항에 있어서, 상기 M7C3일차 탄화물의 평균 횡단면 크기가 50마이크론 이하임을 특징으로 하는 인성 마멸 저항성 철합금.
- 제1항 내지 제21항중 어느 한항에 있어서, 상기 합금을 열처리 시킴을 특징으로 하는 인성마멸 저항성 철합금.
- 제22항에 있어서, 상기 열처리가 상기 합금을 750-1000℃의 온도로 가열한 다음 로내냉각 하거나 공기 냉각 하는 것으로 이루어짐을 특징으로 하는 인성 마멸 저항성 철합금.
- 제23항에 있어서, 상기 열처리가 약 900℃의 온도로 3시간 동안 처리하는 것임을 특징으로 하는 인성 마멸 저항성 철합금.
- 제1항 내지 제24항중 어느 한항에 청구된 합금에 금속 결합을 갖고 있는 금속 기재로 이루어진 복합물품.
- 제25항에 있어서, 상기 기재가 비교적 연성이고 상기 합금이 상기 기재에 대해서 주조됨으로써 결합됨을 특징으로 하는 복합물품.
- 제26항에 있어서, 상기 기재가 상기 합금내에서 주조됨을 특징으로 하는 복합물품.
- 제25항에 있어서, 상기 기재가 비교적 연성이고 상기 합금이 예비주조되며 진공 납땜에 의하여 상기 기재에 결합됨을 특징으로 하는 복합물품.
- 제26항 내지 제28항중 어느 한 항에 있어서, 용가재가 상기 합금이 상기 기재에 결합되기 전에 상기 기재에 도포됨을 특징으로 하는 복합물품.
- 제29항에 있어서, 상기 용가재가 구리임을 특징으로 하는 복합물품.
- 제25항 내지 제30항중 어느 한항에 있어서, 상기 기재가 복합물품 중량의 적어도 10%를 차지함을 특징으로 하는 복합물품.
- 제1항내지 제24항중 어느 한항에 의한 철합금의 용해된 금속을 주조한 것으로 이루어진 인성 마멸 저항성 철합금을 제조하는 방법에 있어서, 상기 용해된 금속을 합금에 대한 액상 온도보다 20℃이상 작지 않으며 100℃보다는 크지않은 온도에서 부은다음 최소두께가 적어도 10㎜를 가지는 부피로 주조함을 특징으로 하는 인성 마멸저항성 철합금을 제조하는 방법.
- 제32항에 있어서, 상기 용해된 금속을 상기 액상온도 보다 40℃ 이상 크지 않은 온도에서 부음을 특징으로 하는 인성 마멸저항성 철합금을 제조하는 방법.
- 제32항에 있어서, 상기 용해된 금속을 상기 액상온도 보다 20℃이상 크지 않은 온도에서 부음을 특징으로 하는 인성 마멸저항성 철합금을 제조하는 방법.
- 제32항에 있어서, 상기 용해된 금속을 실질적인 상기 액상온도에서, 어떤 경우 상기 액상온도보다 5℃이상 크지않은 온도에서 부음을 특징으로 하는 인성 마멸저항성 철합금을 제조하는 방법.
- 제32항 내지 제35항중 어느 한 항에 있어서, 상기 용해된 금속을 합금이 분당 적어도 50℃의 속도로 고상 온도로 내려가도록 냉각함을 특징으로 하는 인성 마멸저항성 철합금을 제조하는 방법.
- 제36항에 있어서, 상기 용해된 금속을 분당 적어도 100℃의 속도로 상기 고상온도로 내려가도록 냉감함을 특징으로 하는 인성 마멸저항성 철합금을 제조하는 방법.
- 제32항 내지 제37항중 어느 한항에 있어서, 상기 용해된 금속을 금속기재에 대하여 주조하여서 응고함으로써 합금을 상기 기재에 금속결합시켜 복합물품을 제공함을 특징으로 하는 인성 마멸저항성 철합금을 제조하는 방법.
- 제38항에 있어서, 기재가 물품 중량의 적어도 10%를 차지하는 부피로 합금을 주조함을 특징으로 하는 인성 마멸저항성 철합금을 제조하는 방법.
- 제32항 내지 제37항중 어느 한항에 있어서, 주조될 때 상기 합금이 기재에 부착되고 진공 납땜에 의하여 기재에 금속 결합되어서 복합물품을 제공함을 특징으로 하는 인성마멸저항성 철합금을 제조하는 방법.※ 참고사항 : 최초출원 내용에 의하여 공개하는 것임.