KR840003267A - 유리섬유 강화 염화폴리비닐 물질로부터 형성시킨 성형체의 제조방법 - Google Patents

유리섬유 강화 염화폴리비닐 물질로부터 형성시킨 성형체의 제조방법 Download PDF

Info

Publication number
KR840003267A
KR840003267A KR1019830000342A KR830000342A KR840003267A KR 840003267 A KR840003267 A KR 840003267A KR 1019830000342 A KR1019830000342 A KR 1019830000342A KR 830000342 A KR830000342 A KR 830000342A KR 840003267 A KR840003267 A KR 840003267A
Authority
KR
South Korea
Prior art keywords
weight
parts
polyvinyl chloride
glass fiber
coating
Prior art date
Application number
KR1019830000342A
Other languages
English (en)
Inventor
부디히 볼프강 (외 4)
Original Assignee
한스 헤르베르트 슈베르트,마르코트 뮐러-게르베스
다이나미트 노벨 아크티엔게젤샤프트
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 한스 헤르베르트 슈베르트,마르코트 뮐러-게르베스, 다이나미트 노벨 아크티엔게젤샤프트 filed Critical 한스 헤르베르트 슈베르트,마르코트 뮐러-게르베스
Publication of KR840003267A publication Critical patent/KR840003267A/ko

Abstract

내용 없음

Description

유리섬유 강화 염화폴리비닐 물질로부터 형성시킨 성형체의 제조방법
본 내용은 요부공개 건이므로 전문내용을 수록하지 않았음
제 7도는 다중층 주형제조를 위한 압출장치를 개략적으로 나타낸 것.

Claims (11)

  1. 55 및 75사이의 K-치를 갖는 염화폴리비닐의중량으로 100부, 5 및 25㎛ 사이의 직경으로 12mm까지의 길이인 유리섬유의 중량으로 40내지 100부와 50㎛이하의 평균 입자직경의 광물 충전제의 중량으로0 내지 25, 특히 1내지 20부의 물질을 가소화시키고 압출방향으로 23℃에서 적어도8000N/m²의 영모듈을 갖는 성형체로 압출시킴을 특징으로하는 염화 폴리비닐, 유리섬유 및 유리섬유와는 다른 무기 충전제와 필요하다면 활탁제, 안정제, 작업조제, 발색제로부터 형성한 유리섬유 강화 염화 폴리비닐로부터 특히 압출 주형에 의한 성형체의 제조방법.
  2. 상기 1항에서 추가하여 그 물질중에 조절제의 중량으로 30부까지 나타나게 함을 특징으로 하는 상기의 방법.
  3. 상기 1 또는 2항에서 추가하여 그 물질중에 활탁제의 중량으로 2.5내지 5.5부가 나타나게 함을특징으로 하는 상기의 방법.
  4. 상기 1내지 3항의 하나에서 55 및 75사이의 K-치를 갖는 염화폴리비닐의중량으로 100부, 5 및 25㎛ 사이의 직경으로 0.5내지 12mm까지의 길이인 유리섬유의 중량으로 40 내지 80부, 50㎛ 이하의 평균 입자 크기를 갖는 분상 광물 충전제의 중량으로 1 내지 15부 및 활탁제의 중량으로 2.5내지 5.0부 및 조절제의 중량으로 30부까지 나타나는 물질로 제조함을 특징으로하는 상기의 방법.
  5. 행심층 주형을 55 및 75사이의 K-치를 갖는 염화폴리비닐의중량으로 100부, 기초하여 5 및 25㎛ 사이의 직경으로 12mm 까지의 길이인 유리섬유의 중량으로 40 내지 100부 및 50㎛ 이하의 평균 입자 직경과 쉽게 거칠어지는 미세공 표면을 갖는 광물충진제의 중량으로 0내지 25부를 함유하는 유리섬유-강화PVC-조성물로부터 축조하여 PVC와 혼화할 수 있는 플라스틱 물질로부터 형성한 충격강도가 핵심층 주형보다 더 강한 피복에 결합함을 특징으로 하여 상기 1내지 4항의 하나의 방법에 따라 제조한 핵심층 주위에 플라스틱으로 형성한 피복과 강화 플라스틱으로부터 형성한 임의로 동공핵심층 주형으로 된, 특히 창문 또는 도어용 프레임의 제조를 위한 성형주형.
  6. 상기 5항에 있어 핵심층 주형은 55 및 75사이의 K-치를 갖는 염화폴리비닐의중량으로 100부에 기초하여 5 및 25㎛ 사이의 직경으로 12mm까지의 길이인 유리섬유의 중량으로 40내지 80부, 50㎛ 이하의 평균입자 크기의 분상 광물충진제의 중량으로 1내지 15부 및 활탁제의 중량으로 2.5내지 5.0부 및 조절제의 중량으로 30부 까지를 포함함을 특징으로하는 상기의 성형주형.
  7. 상기 5 또는 6항의 하나에서, 핵심층 주형은 1.0내지 10mm, 바람직하게 2.0내지 4.0mm 사이의 벽두께를 가지며 피복은 0.2 내지 4.0mm, 바람직하게 0.3 내지 1.5mm의 벽 뚜께를 가짐을 특징으로 하는 상기의 성형주형.
  8. 상기 5내지 7항의 하나에서 피복은, 염소화한 단량체 및 예를들어 에틸렌-비닐아세테이트, 아크릴레이트, 비닐아세테이트, 염소화한 폴리에틸렌, 부타디엔, 폴리올레핀등과 같은 동종-또는 공-또는 그라프트 중합체와 같이 적어도 하나의 단량체와 공중합할 수 있는 중합체로부터 PVC, 염화 폴리비리레덴, 기 - 염소화한 PVC및 안정제, 활탁제, 색소, UV-흡착제, 작업조제, 조절제와 같은 첨가제뿐만 아니라 그것의 혼합물에 기초하여 형성함을 특징으로 하는 상기의 성형주형.
  9. 상기 5내지 8항의 하나에서 피복은 다른 하나와 다른 두개의 물질로 부분적으로 구성하거나 다른 것과 다른 두개의물질로 적어도 부분적으로 구성함을 특징으로 하는 상기의 성형주형.
  10. 상기의 1내지 9항의 하나에서 피복은 흠, 돌기, 웹, 언더 컷 또는 그와같은 성형주형의 측벽을 갖게 형성함을 특징으로 하는 성형주형.
  11. 상기 5내지 10항의 하나에서 0.1 내지 1.2mm의 두께로 특히 아크릴레이트에 기초하여 내풍화성 플라스틱으로부터 형성하여 부분적으로 피복을 차폐하는 표면층이 제공됨을 특징으로 하는 성형주형.
    ※ 참고사항 : 최초출원 내용에 의하여 공개하는 것임.
KR1019830000342A 1982-01-19 1983-01-28 유리섬유 강화 염화폴리비닐 물질로부터 형성시킨 성형체의 제조방법 KR840003267A (ko)