KR20160096250A - 난연성 폴리우레탄 접착제 조성물 및 이를 이용한 건축용 난연 패널 - Google Patents
난연성 폴리우레탄 접착제 조성물 및 이를 이용한 건축용 난연 패널 Download PDFInfo
- Publication number
- KR20160096250A KR20160096250A KR1020150017209A KR20150017209A KR20160096250A KR 20160096250 A KR20160096250 A KR 20160096250A KR 1020150017209 A KR1020150017209 A KR 1020150017209A KR 20150017209 A KR20150017209 A KR 20150017209A KR 20160096250 A KR20160096250 A KR 20160096250A
- Authority
- KR
- South Korea
- Prior art keywords
- adhesive composition
- skin layer
- weight
- polyurethane adhesive
- flame retardant
- Prior art date
Abstract
얇은 접착면을 형성하는 습기 경화형 일액형 폴리우레탄 접착제에 난연성을 부여한 폴리우레탄 접착제 조성물 및 이를 이용한 건축용 난연 패널이 개시된다. 상기 습기 경화형 폴리우레탄 일액형 접착제 조성물은, 폴리올과 폴리이소시아네이트가 중합 반응하여 생성된 우레탄 프리폴리머 50 내지 70 중량%; 상기 우레탄 프리폴리머의 경화를 촉진하는 경화제 0.1 내지 0.5 중량%; 디클로로메탄, 트리클로로에틸렌 및 이들의 혼합물로 이루어진 군으로부터 선택되는 염소화 탄화수소 유기용매 4 내지 20 중량%; 및 평균 직경이 80 내지 300 ㎛인 팽창 흑연 25 내지 45 중량%를 포함하며, 수분 함량이 1 중량% 이하이다.
Description
본 발명은 난연성 폴리우레탄 접착제 조성물에 관한 것으로서, 더욱 상세하게는, 얇은 접착면을 형성하는 습기 경화형 일액형 폴리우레탄 접착제에 난연성을 부여한 폴리우레탄 접착제 조성물 및 이를 이용한 건축용 난연 패널에 관한 것이다.
건축용 자재 분야에서는, 서로 다른 특성을 가지는 구조물을 폴리우레탄 접착제로 접착하여 사용하는 경우가 많다. 폴리우레탄 접착제는 복잡한 형태를 가지는 구조물의 접착에 적합할 뿐만 아니라, 종이, 유리, 철판, 합성수지 등 다양한 소재와의 접착성이 우수하고, 내약품성, 내구성, 흡음성, 치수 안정성, 신장률 등의 물리 화학적 특성이 우수하므로, 건축물의 내, 외벽 및 바닥 접착제로서 유용하게 사용되고 있다. 예를 들면, 건축물의 벽체 등으로 사용되는 경량 허니컴 샌드위치 패널에 있어서, 알루미늄, 종이, 합성수지 등으로 이루어진 허니컴 코어의 상하부에 알루미늄, 철판 등으로 이루어진 스킨층이 폴리우레탄 접착제로 부착된다. 또한, 폴리우레탄 접착제를 이용하여, 합판, 파티클 보드 등의 기재(基材)에 화장 시트 등을 접착하여, 패널의 미관 및 내구성을 향상시키기도 한다. 이와 같은 건축용 패널에 있어서, 코어, 기재, 스킨층 등에는 난연제를 첨가하거나, 난연성 물질로 코어, 기재 등을 제조하여 난연성을 용이하게 부여할 수 있으나, 폴리우레탄 접착제 자체에 난연성을 부여하는 것은 실질적으로 구현되지 못하고 있다.
폴리우레탄 접착제는 이액형(二液形)과 일액형(一液形)으로 구분될 수 있다. 이액형 폴리우레탄 접착제의 경우, 이소시아네이트와 장쇄 폴리올이 중합되어 형성된 이소시아네이트 말단 우레탄 프리폴리머(주제 성분) 및 방향족 아민계 경화제와 폴리올의 혼합물(경화제 성분, 필요에 따라, 여기에 유기금속, 납 등의 촉매나 가소제가 첨가됨)을 별도로 준비하고, 이를 정해진 배합비에 따라 시공 현장에서 혼합한 다음, 대상물에 도포하고 경화시켜 사용된다. 이와 같은 이액형 폴리우레탄 접착제는 두 성분을 별도로 관리하여야 할 뿐만 아니라, 주제 성분 및 경화제 성분의 혼합 및 시공 시간을 잘 조절하여야 하고, 시공 상 결함이 발생하기 쉬우므로, 숙련된 전문 인력이 필요한 단점이 있다. 반면, 일액형 폴리우레탄 접착제는 폴리올과 이소시아네이트를 중합 반응시켜 얻은 우레탄 프리폴리머에 충진제, 안정제, 착색제 등을 첨가하여 접착제 성분을 일액형화한 것으로, 대기 중에 노출되었을 때, 습기에 의하여 경화되는 습기 경화형 접착제이다. 상기 일액형 폴리우레탄 접착제는 필요 성분을 모두 포함하는 단일 조성물이므로, 사용 및 시공이 편리한 장점이 있다. 그러나, 보관 중 각 성분이 반응하거나, 서로 극성이나 용해도가 달라 상용성이 부족한 성분들의 상분리가 발생되기 쉬우므로, 각 성분의 선택 및 혼합된 조성물의 관리가 어려운 단점이 있다.
이와 같은 폴리우레탄 접착제 조성물에 통상적인 난연제를 혼합하면, 난연제가 균일 분산되지 않아 실질적인 난연 효과를 얻을 수 없거나 접착성이 저하되는 문제가 있다. 주제와 경화제가 분리되어 있는 이액형 폴리우레탄 접착제의 경우, 난연제를 상대적으로 안정하게 분산시킬 수 있으므로, 난연 3 등급의 획득은 가능하다고 알려져 있지만, 일액형 습기 경화형 폴리우레탄 접착제의 경우, 난연성의 부여에 큰 어려움을 격고 있는 실정이다.
본 발명의 목적은, 일액형으로 사용이 편리할 뿐만 아니라, 난연 성분이 균일하게 분산된 얇은 접착면을 형성하므로 건축 자재용 접착제로서 특히 유용한 난연성 폴리우레탄 접착제 조성물을 제공하는 것이다.
본 발명의 다른 목적은, 난연성, 접착성 및 내구성이 우수한 난연성 폴리우레탄 접착제 조성물 및 이를 이용한 건축용 난연 패널을 제공하는 것이다.
상기 목적을 달성하기 위하여, 본 발명은, 폴리올과 폴리이소시아네이트가 중합 반응하여 생성된 우레탄 프리폴리머 50 내지 70 중량%; 상기 우레탄 프리폴리머의 경화를 촉진하는 경화제 0.1 내지 0.5 중량%; 디클로로메탄, 트리클로로에틸렌 및 이들의 혼합물로 이루어진 군으로부터 선택되는 염소화 탄화수소 유기용매 4 내지 20 중량%; 및 평균 직경이 80 내지 300 ㎛인 팽창 흑연 25 내지 45 중량%를 포함하며, 수분 함량이 1 중량% 이하인 것인 습기 경화형 폴리우레탄 일액형 접착제 조성물을 제공한다.
또한, 본 발명은, 플레이트 형태의 하부 스킨층; 상기 하부 스킨층에 평행하게 위치하는 플레이트 형태의 상부 스킨층; 및 상기 하부 스킨층과 상부 스킨층의 사이에 위치하여 상기 하부 스킨층과 상부 스킨층을 지지하는 허니컴 코어를 포함하며, 상기 하부 스킨층과 상부 스킨층의 내면에는 상기 폴리우레탄 접착제 조성물이 도포되고, 상기 폴리우레탄 접착제 조성물을 통해, 상기 허니컴 코어의 상하면이 상기 하부 스킨층과 상부 스킨층에 부착되는 것인 난연 패널을 제공한다.
본 발명에 따른 난연성 폴리우레탄 접착제 조성물은 난연 성분이 균일하게 분산된 얇은 접착면을 형성하므로 건축 자재용 접착제로서 특히 유용하다.
도 1은 본 발명에 따른 폴리우레탄 접착제 조성물을 이용하여 제조한 건축용 난연 패널의 사시도.
이하, 본 발명에 따른 난연성 폴리우레탄 접착제 조성물 및 이를 이용한 건축용 난연 패널을 상세히 설명한다. 본 발명의 접착제 조성물은 습기 경화형 폴리우레탄 일액형 접착제 조성물로서, 우레탄 프리폴리머, 경화제, 유기용매 및 난연제로서 팽창 흑연을 포함한다.
본 발명에 사용되는 우레탄 프리폴리머는 폴리올과 폴리이소시아네이트의 중합 반응 생성물이다. 상기 폴리이소시아네이트로는, 1액형 폴리우레탄 수지 조성물에 사용되는 통상의 화합물을 사용할 수 있고, 예를 들면, 메틸렌디페닐 디이소시아네이트(MDI: Methylenediphenyl Diisocyanate), 2,4-톨루엔 디이소시아네이트, 2,6-톨루엔 디이소시아네이트, 2,4'-디페닐메탄 디이소시아네이트, 폴리메틸렌폴리페닐렌 폴리이소시아네이트 등의 방향족 폴리이소시아네이트; 헥사메틸렌 디이소시아네이트 등의 지방족 폴리이소시아네이트; 이소포론 디이소시아네이트 등의 지환식 폴리이소시아네이트; 크실렌 디이소시아네이트 등의 아릴 지방족 폴리이소시아네이트 등을 단독 또는 혼합하여 사용할 수 있다. 상기 폴리올로도, 1액형 폴리우레탄 수지 조성물에 사용되는 통상의 화합물을 사용할 수 있고, 예를 들면, 에틸렌글리콜, 디에틸렌글리콜, 프로필렌글리콜, 디프로필렌글리콜, 글리세린, 1,2,5-헥사트리올, 1,3-부탄디올, 1,4-부탄디올, 4,4'-디히드록시페닐 프로판, 4,4'-디히드록시페닐 메탄, 폴리에틸렌글리콜, 폴리프로필렌글리콜, 이들의 혼합물 등을 사용할 수 있다. 이 중, 난연제로 사용되는 팽창흑연의 분산성을 고려하면, 상기 폴리올로서 폴리에틸렌글리콜, 폴리프로필렌글리콜 또는 이들의 혼합물을 사용하는 것이 보다 바람직하며, 폴리프로필렌글리콜을 사용하는 것이 가장 바람직하다. 상기 폴리에틸렌글리콜 또는 폴리프로필렌글리콜의 수평균 분자량은 바람직하게는 1,000 내지 10,000 이고, 더욱 바람직하게는 2,000 내지 6,000 이다. 여기서, 상기 폴리에틸렌글리콜 또는 폴리프로필렌글리콜의 수평균 분자량이 상기 범위를 벗어나면, 난연제가 균일하게 분산되지 못할 우려가 있다.
상기 폴리올 화합물과 폴리이소시아네이트 화합물의 혼합 비율은 통상 폴리올 1 당량(OH 당량)에 대하여, 폴리이소시아네이트 1.2 내지 5.0 당량(NCO 당량), 바람직하게는 1.5 내지 3.0 당량이며, 상기 우레탄 프리폴리머는 통상 0.5 내지 10 중량%, 바람직하게는 1 내지 8 중량%, 더욱 바람직하게는 2 내지 6 중량%의 이소시아네이트기(NCO 함량)를 함유한다. 상기 우레탄 프리폴리머는 상기 두 화합물을 혼합하고, 통상 30 ~ 120 ℃, 바람직하게는 50 ~ 100 ℃로 가열 교반하여 중합된다. 전체 폴리우레탄 접착제 조성물에 대하여, 상기 우레탄 프리폴리머의 함량은 50 내지 70 중량%, 바람직하게는 55 내지 65 중량%이다. 여기서, 상기 우레탄 프리폴리머의 함량이 너무 작으면, 폴리우레탄 접착제의 접착력이 저하될 우려가 있고, 너무 많으면 폴리우레탄 접착제 조성물의 도포성이 저하될 우려가 있다.
본 발명의 폴리우레탄 접착제 조성물에 사용되는 경화제는, 상기 이소시아네이트기의 반응을 촉진하여, 우레탄 프리폴리머의 경화를 촉진하기 위한 촉매로서, 1액형 폴리우레탄 수지 조성물에 사용되는 통상의 화합물을 사용할 수 있고, 예를 들면, 디부틸틴 디라우레이트(Dibutyltin dilaurate), 디옥틸틴디라우레이트, 디부틸틴 디옥토에이트, 디부틸틴디아세테이트, 디부틸틴디클로라이드, 디부틸틴디아세틸아세토네이트 등의 유기주석 화합물; 2,2'-디모포리노디에틸에테르(2,2-Dimorpholinyl diethylether), 1,4-디아자비시클로[2.2.2]옥탄, 트리에틸아민, 테트라에틸렌디아민 등의 3차 아미노기를 포함하는 화합물; 비스무스트리옥토에이트, 비스무스트리스(네오데카노에이트) 등의 비스무스 화합물, 이들의 혼합물 등을 사용할 수 있다. 전체 폴리우레탄 접착제 조성물에 대하여, 상기 경화제의 함량은 0.1 내지 0.5 중량%, 바람직하게는 0.2 내지 0.4 중량%이다. 여기서, 상기 경화제의 함량이 너무 작으면, 폴리우레탄 접착제의 접착력이 저하되고, 너무 많으면 특별한 이익이 없이 경제적으로 바람직하지 못하다.
본 발명의 폴리우레탄 접착제 조성물에 사용되는 유기용매는 폴리우레탄 접착제 조성물의 도포성을 향상시키고, 구성 성분들을 균일하게 분포시키는 역할을 한다. 본 발명의 폴리우레탄 접착제 조성물에 있어서, 상기 팽창흑연의 분산성을 향상시키고, 난연성을 부여하기 위하여, 상기 유기용매로는 디클로로메탄(Dichloromethane, methylene chloride, MC), 트리클로로에틸렌(Trichloro Ethylene: TCE) 등의 염소화 탄화수소 용매를 사용한다. 전체 폴리우레탄 접착제 조성물에 대하여, 상기 유기용매의 함량은 4 내지 20 중량%, 바람직하게는 7 내지 15 중량%이다. 여기서, 상기 유기용매의 함량이 너무 작으면, 폴리우레탄 접착제 조성물의 도포성이 저하되거나, 난연제로 사용되는 팽창흑연 등의 성분이 균일하게 분산되지 못할 우려가 있고, 너무 많으면 폴리우레탄 접착제 조성물의 경화에 장시간이 소요되어 공정 비용이 증가한다. 본 발명의 폴리우레탄 접착제 조성물은 수분 함량이 적은 것을 특징으로 하며, 바람직하게는 수분 함량이 1 중량% 이하, 더욱 바람직하게는 0.5 중량% 이하이고, 예를 들면 0.01 내지 0.2 중량%이다. 본 발명의 접착제 조성물에 있어서, 수분 함량을 감소시키기 위하여, 각 성분 원료들에 포함된 수분 함량이 과도하게 많아지지 않도록 조절하여야 한다. 만일 수분 함량이 상기 범위를 초과하면, 난연제로 사용하는 팽창흑연이 균일하게 분산되지 못할 우려가 있다.
본 발명의 폴리우레탄 접착제 조성물은 난연제로서 팽창 흑연(Expandable Graphite)을 포함한다. 본 발명에 사용되는 팽창 흑연은, 공극률이 높고, 구멍이 많으며, 화학적으로 안정한 플레이크(flake) 또는 파우더(powder) 상태의 물질로서, 통상적으로 난연재료 뿐만 아니라, 밀봉재료, 흡착재료 등으로도 널리 사용되고 있으나, 폴리우레탄 접착제 조성물, 특히 일액형 폴리우레탄 접착제 조성물의 난연 성분으로는 알려진 바 없다. 본 발명에 사용되는 팽창 흑연의 평균 직경은 80 내지 300 ㎛, 바람직하게는 100 내지 200 ㎛, 더욱 바람직하게는 140 내지 170 ㎛(약 80 내지 100 mesh)이다. 전체 폴리우레탄 접착제 조성물에 대하여, 상기 팽창흑연의 함량은 25 내지 45 중량%, 바람직하게는 30 내지 40 중량%이다. 여기서, 상기 팽창흑연의 함량이 너무 작으면, 폴리우레탄 접착제의 난연성이 불충분하게 될 우려가 있고, 너무 많으면 팽창흑연이 응집되거나, 접착제의 접착 성능이 불충분하게 될 우려가 있다.
한편, 폴리우레탄 발포체용 난연제로는 할로겐계 난연제, 인계 난연제, 질소계 난연제, 무기계 난연제 등의 다양한 난연제가 사용되고 있다. 상기 할로겐계 난연제로는 브롬화 디페닐 에테르, 브롬화 방향족/지방족 화합물 등이 사용되고, 상기 무기계 난연제로는 수산화칼슘, 수산화알루미늄, 팽창 흑연 등이 사용되고 있다. 그러나, 본 발명의 폴리우레탄 접착제 조성물에 있어서, 수산화칼슘, 수산화알루미늄 등의 통상적인 수산기(OH) 함유 무기계 난연제를 사용하는 경우, 접착제 조성물의 성분들이 균일하게 분산되지 못하고 침전이 발생하여, 접착성 및 난연성이 저하될 우려가 있다(비교예 1). 이는 수산화칼슘, 수산화알루미늄 등에 포함된 수산기(OH)가 우레탄 프리폴리머 등과 반응하기 때문인 것으로 추정된다. 또한, 할로겐계 난연제를 사용하는 경우에는, 접착제 조성물에 거품이 발생하여 양호한 접착층을 형성하지 못하였다(비교예 2). 따라서, 본 발명의 폴리우레탄 접착제 조성물은 수산기(OH) 함유 무기계 난연제, 할로겐계 난연제, 및 고가의 인계 난연제를 포함하지 않는다.
다음으로 본 발명에 따른 폴리우레탄 접착제 조성물의 제조방법을 설명한다. 본 발명의 접착제 조성물을 제조하기 위해서는, 먼저, 반응기에 폴리이소시아네이트 및 폴리올을 교반하면서 투입하여, 중합 생성물의 이소시아네이트기 함량(NCO 함량)이 0.5 내지 10 중량%가 될 때까지 우레탄 프리폴리머를 중합한다. 상기 중합 반응은 통상 30 ~ 120 ℃, 바람직하게는 50 ~ 100 ℃의 온도에서 1 내지 3시간, 바람직하게는 1.5 내지 2.5 시간 동안 수행된다. 중합이 완료되면, 반응액을 40 ℃ 이하로 냉각하고, 유기용매 및 경화제를 투입한다. 이때, 경화제를 유기용매에 용해시켜 투입하는 것이 바람직하다. 끝으로, 상기 반응 생성물에 팽창흑연을 첨가하여, 폴리우레탄 접착제 조성물을 완성하다. 이때, 완성된 조성물의 점도를 측정하여, 점도가 너무 높거나 낮은 경우에는, 우레탄 프리폴리머의 이소시아네이트기 함량(NCO 함량) 또는 유기용제의 사용량을 적절히 조정한다. 완성된 조성물의 점도가 적절한 경우, 필요에 따라 100 메쉬의 망으로 여과(filter)하고, 질소로 치환하면서, 포장용기로 포장하여 출하한다.
도 1은 본 발명에 따른 폴리우레탄 접착제 조성물을 이용하여 제조한 건축용 난연 패널의 사시도이다. 도 1에 도시된 바와 같이, 본 발명에 따른 난연 패널은 플레이트 형태의 하부 스킨층(10), 상기 하부 스킨층(10)에 평행하게 위치하는 플레이트 형태의 상부 스킨층(12) 및 상기 하부 스킨층(10)과 상부 스킨층(12)의 사이에 위치하여 상기 하부 스킨층(10)과 상부 스킨층(12)을 지지하는 허니컴 코어(20)를 포함한다. 여기서, 상기 하부 스킨층(10)과 상부 스킨층(12)의 내면에는 본 발명에 따른 폴리우레탄 접착제 조성물(30)이 도포되고, 상기 폴리우레탄 접착제 조성물(30)을 통해, 상기 허니컴 코어(20)의 상하면이 상기 하부 스킨층(10)과 상부 스킨층(12)에 부착된다. 다음으로, 열프레스 등을 이용하여, 상기 하부 스킨층(10)과 상부 스킨층(12)을 가열 및 압착하면, 폴리우레탄 접착제 조성물(30)이 경화되어, 허니컴 샌드위치 패널을 제조할 수 있다. 상기 하부 스킨층(10)과 상부 스킨층(12)은 알루미늄, 철판 등의 금속판으로 이루어지고, 상기 허니컴 코어(20)는 금속, 종이, 합성수지 등으로 이루어질 수 있으며, 바람직하게는 난연성을 가지는 재질로 이루어진다. 본 발명에 따른 폴리우레탄 접착제 조성물은 난연이 요구되는 피착제 접착에 다양하게 사용될 수 있으며, 상기 접착제 조성물을 이용하여 제조한 건축용 난연 패널은 방화문 도어, 아파트실외기 도어, 크린룸 칸막이 등에 사용될 수 있다.
이하, 구체적인 실시예 및 비교예를 통하여 본 발명을 더욱 상세히 설명한다. 하기 실시예는 본 발명을 예시하기 위한 것으로서, 본 발명이 하기 실시예에 의해 한정되는 것은 아니다.
[실시예] 폴리우레탄 접착제 조성물 및 이를 이용한 난연 패널 제조
30분 동안 진공 탈수하여 수분이 제거된 반응기에, 메틸렌디페닐 디이소시아네이트(금호석유화학, CAS No.: 9016-87-9) 55 중량부를 투입하고 30 rpm으로 교반하면서, 폴리프로필렌 글리콜(GY-3000, (주)국도화학, CAS No.: 25322-69-4) 10 중량부, 폴리프로필렌 글리콜(DF-1000, (주) KPX, CAS No.: 25322-69-4) 10 중량부, 폴리프로필렌 글리콜(TF-3000, (주)SKC, CAS No.: 25322-69-4) 15 중량부를 투입하고, 교반 속도를 50 rpm으로 증가시켰다. 상기 원료들은 수분을 제거하여 사용하였다. 스팀 보일러를 이용하여, 약 80 ℃에서 1시간 동안 반응시킨 후, 1 시간 이후부터, 중합된 프리폴리머의 NCO 함량을 측정하여, 원하는 NCO 함량이 되면, 반응액을 40 ℃ 이하로 냉각하여, 중합 반응을 정지시켰다. 다음으로, 중합된 프리폴리머 약 51 중량%를 30 rpm으로 교반하면서, 디부틸틴 디라우레이트((주)세호테크, CAS No.: 77-58-7) 0.2 중량% 및 2,2'-디모포리노디에틸에테르(Nitrol, CAS No.: 6425-39-4) 0.15 중량%를 메틸렌 클로라이드(삼성정밀화학, CAS No.: 75-09-2) 13 중량%에 용해시켜 투입한 다음, 팽창 흑연 35 중량%를 투입하여, 폴리우레탄 접착제 조성물을 제조하였다. 상기 접착제 조성물의 수분 함량은 약 0.05 중량% 이하였다. 이와 같이 얻어진 폴리우레탄 접착제 조성물의 난연성을 FITI시험연구원에서 KS F 2819 A법에 따라 측정한 결과 방염 2급을 획득하였다. 또한, 상기 접착제 조성물을 이용하여, 도 1에 도시된 바와 같은 허니컴 난연 패널을 제조한 다음, 접착 특성을 육안으로 평가한 결과, 접착제 조성물의 각 성분이 균일하게 분산되어, 접착력이 우수하였다.
[비교예 1] 폴리우레탄 접착제 조성물 및 이를 이용한 난연 패널 제조
난연제로서 팽창 흑연 35 중량% 대신, 수산화알루미늄 35 중량%를 사용한 것을 제외하고는, 실시예와 동일한 방법으로, 폴리우레탄 접착제 조성물 및 허니컴 난연 패널을 제조하고, 접착 특성을 육안으로 평가한 결과, 접착제 조성물의 성분들이 균일하게 분산되지 못하고 침전이 발생하여, 접착성 및 난연성이 저하되는 것으로 판단되었다.
[비교예 2] 폴리우레탄 접착제 조성물 및 이를 이용한 난연 패널 제조
난연제로서 팽창 흑연 35 중량% 대신, 데카브로모 디페닐 옥사이드 35 중량%를 사용한 것을 제외하고는, 실시예와 동일한 방법으로, 폴리우레탄 접착제 조성물 및 허니컴 난연 패널을 제조하고, 접착 특성을 육안으로 평가한 결과, 접착제 조성물에 거품이 발생하여 양호한 접착층을 형성하지 못하였다.
[비교예 3] 폴리우레탄 접착제 조성물 및 이를 이용한 난연 패널 제조
난연제로서 팽창 흑연 35 중량% 대신, 통상의 이액형 우레탄 난연제인 TCEP(Tris 2-chloroethyl phosphate) 35 중량%를 사용한 것을 제외하고는, 실시예와 동일한 방법으로, 폴리우레탄 접착제 조성물 및 허니컴 난연 패널을 제조하고, 난연 특성을 평가한 결과, 접착제 조성물의 고화 후, 시간 경과에 따라 난연성이 저하되어, 유용한 난연 특성을 얻지 못하였다.
[비교예 4] 폴리우레탄 접착제 조성물 및 이를 이용한 난연 패널 제조
난연제로서 팽창 흑연 35 중량% 대신, 통상의 이액형 우레탄 난연제인 TCPP(Tris 2-chloropropyl phosphate) 35 중량%를 사용한 것을 제외하고는, 실시예와 동일한 방법으로, 폴리우레탄 접착제 조성물 및 허니컴 난연 패널을 제조하고, 난연 특성을 평가한 결과, 접착제 조성물의 고화 후, 시간 경과에 따라 난연성이 저하되어, 유용한 난연 특성을 얻지 못하였다.
Claims (7)
- 폴리올과 폴리이소시아네이트가 중합 반응하여 생성된 우레탄 프리폴리머 50 내지 70 중량%;
상기 우레탄 프리폴리머의 경화를 촉진하는 경화제 0.1 내지 0.5 중량%;
디클로로메탄, 트리클로로에틸렌 및 이들의 혼합물로 이루어진 군으로부터 선택되는 염소화 탄화수소 유기용매 4 내지 20 중량%; 및
평균 직경이 80 내지 300 ㎛인 팽창 흑연 25 내지 45 중량%를 포함하며,
수분 함량이 1 중량% 이하인 것인 습기 경화형 폴리우레탄 일액형 접착제 조성물. - 제1항에 있어서, 상기 폴리올은 폴리에틸렌글리콜, 폴리프로필렌글리콜 및 이들의 혼합물로 이루어진 군으로부터 선택되고, 상기 폴리에틸렌글리콜 또는 폴리프로필렌글리콜의 수평균 분자량은 1,000 내지 10,000 인 것인, 습기 경화형 폴리우레탄 일액형 접착제 조성물.
- 제1항에 있어서, 상기 경화제는 디부틸틴 디라우레이트, 디옥틸틴디라우레이트, 디부틸틴 디옥토에이트, 디부틸틴디아세테이트, 디부틸틴디클로라이드, 디부틸틴디아세틸아세토네이트, 2,2'-디모포리노디에틸에테르, 1,4-디아자비시클로[2.2.2]옥탄, 트리에틸아민, 테트라에틸렌디아민, 비스무스트리옥토에이트, 비스무스트리스(네오데카노에이트) 및 이들의 혼합물로 이루어진 군으로부터 선택되는 것인, 습기 경화형 폴리우레탄 일액형 접착제 조성물.
- 제1항에 있어서, 상기 우레탄 프리폴리머는 0.5 내지 10 중량%의 이소시아네이트기(NCO 함량)를 함유하는 것인, 습기 경화형 폴리우레탄 일액형 접착제 조성물.
- 제1항에 있어서, 상기 접착제 조성물은 수분 함량이 0.01 내지 0.2 중량%인 것인 습기 경화형 폴리우레탄 일액형 접착제 조성물.
- 플레이트 형태의 하부 스킨층;
상기 하부 스킨층에 평행하게 위치하는 플레이트 형태의 상부 스킨층; 및
상기 하부 스킨층과 상부 스킨층의 사이에 위치하여 상기 하부 스킨층과 상부 스킨층을 지지하는 허니컴 코어를 포함하며,
상기 하부 스킨층과 상부 스킨층의 내면에는 청구항 1에 따른 폴리우레탄 접착제 조성물이 도포되고, 상기 폴리우레탄 접착제 조성물을 통해, 상기 허니컴 코어의 상하면이 상기 하부 스킨층과 상부 스킨층에 부착되는 것인 난연 패널. - 제6항에 있어서, 상기 하부 스킨층 및 상부 스킨층은 금속판으로 이루어지고, 상기 허니컴 코어는 금속, 종이 및 합성수지로 이루어진 군으로부터 선택되는 난연성을 가지는 재질로 이루어진 것인, 난연 패널.