KR102453713B1 - 강 스트립을 열 처리 및 용융 도금하기 위한 다목적 프로세싱 라인 - Google Patents

강 스트립을 열 처리 및 용융 도금하기 위한 다목적 프로세싱 라인 Download PDF

Info

Publication number
KR102453713B1
KR102453713B1 KR1020167036870A KR20167036870A KR102453713B1 KR 102453713 B1 KR102453713 B1 KR 102453713B1 KR 1020167036870 A KR1020167036870 A KR 1020167036870A KR 20167036870 A KR20167036870 A KR 20167036870A KR 102453713 B1 KR102453713 B1 KR 102453713B1
Authority
KR
South Korea
Prior art keywords
temperature
section
steel strip
cooling
dip plating
Prior art date
Application number
KR1020167036870A
Other languages
English (en)
Other versions
KR20170026400A (ko
Inventor
스타브로스 푼투라키스
장 필리쁘 마스
동웨이 판
Original Assignee
아르셀러미탈
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Family has litigation
First worldwide family litigation filed litigation Critical https://patents.darts-ip.com/?family=52014160&utm_source=google_patent&utm_medium=platform_link&utm_campaign=public_patent_search&patent=KR102453713(B1) "Global patent litigation dataset” by Darts-ip is licensed under a Creative Commons Attribution 4.0 International License.
Priority claimed from PCT/IB2014/003263 external-priority patent/WO2016001711A1/en
Application filed by 아르셀러미탈 filed Critical 아르셀러미탈
Publication of KR20170026400A publication Critical patent/KR20170026400A/ko
Application granted granted Critical
Publication of KR102453713B1 publication Critical patent/KR102453713B1/ko

Abstract

강 스트립을 열 처리 및 용융 도금할 수 있는 다목적 연속 프로세싱 라인은, - 상기 강 스트립을 미리 정해진 어닐링 온도로 가열하고 상기 강 스트립을 상기 어닐링 온도로 유지하기 위한 어닐링 섹션 (1), - 제 1 이송 섹션 (2), - 상기 강 스트립의 온도를 300 ℃ ~ 700 ℃ 로 유지할 수 있는 과시효 섹션 (3), - 상기 스트립의 용융 도금을 허용하도록 상기 강 스트립의 온도를 조절할 수 있는 제 2 이송 섹션 (4) 및 - 용융 도금 섹션 (5) 을 포함하고, 상기 제 1 이송 섹션 (2) 은, 순차적으로, 냉각 수단 (21) 및 가열 수단 (22) 을 포함한다.

Description

강 스트립을 열 처리 및 용융 도금하기 위한 다목적 프로세싱 라인 {MULTIPURPOSE PROCESSING LINE FOR HEAT TREATING AND HOT DIP COATING A STEEL STRIP}
본 발명은 강 스트립을 열 처리 및 용융 도금 (hot dip coating) 하기 위한 다목적 프로세싱 라인에 관한 것이다.
다양한 유형들의 자동차용 구조 부재들 및 보디 패널들을 제조하기 위해서, DP (2 상) 강들 또는 TRIP (변태 유기 소성) 강들로 만들어진 갈바나이징 (galvanized) 되거나 갈바닐링된 (galvannealed) 판들을 사용하는 것이 통례이다. 보다 최근에, 또한 Q&P (켄칭 및 파티셔닝 (partitioning)) 강들을 사용하는 것이 제안되었다. 이러한 판들은 코팅 설비들과 결합된 연속 어닐링 라인들과 같은 연속 프로세싱 라인들에서 스트립들의 형태로 제조된다. 하지만, 처리들이 DP 강들, TRIP 강들 및 Q&P 강들에 대해 상이한, 상기 강판들을 제조하는데 필요한 열 처리들로 인해, 이 강판들은 전용 라인들에서 제조된다.
그리하여, 다양한 특징의 이러한 강판들의 제조는 매우 많은 비용이 드는 복수의 라인들을 필요로 한다.
투자 비용을 줄이기 위해서, 동일한 장비에서 DP, TRIP 또는 Q&P 강들을 제조할 수 있는 것이 바람직하다.
이 목적으로, 본 발명은 강 스트립을 열 처리 및 용융 도금할 수 있는 다목적 연속 프로세싱 라인에 관한 것으로서, 상기 프로세싱 라인은:
- 상기 강 스트립을 미리 정해진 어닐링 온도로 가열하고 상기 강 스트립을 상기 어닐링 온도로 유지하기 위한 어닐링 섹션,
- 제 1 이송 섹션,
- 상기 강 스트립의 온도를 300 ℃ ~ 700 ℃ 로 유지할 수 있는 과시효 섹션,
- 상기 스트립의 용융 도금을 허용하도록 상기 강 스트립의 온도를 조절할 수 있는 제 2 이송 섹션, 및
- 용융 도금 섹션을 포함하고,
상기 제 1 이송 섹션은, 순차적으로, 냉각 수단 및 가열 수단을 포함한다.
본 발명의 다른 유리한 양태들에 따르면, 다목적 프로세싱 라인은, 단독으로 또는 임의의 기술적으로 가능한 조합에 따라 고려되는, 다음 특징들 중 하나 이상을 포함한다:
- 상기 제 1 이송 섹션의 상기 냉각 수단은, 그것의 냉각 능력이 무냉각과 미리 정해진 켄칭 온도로 급속 냉각 사이에서 조절가능하도록 제어가능하고 상기 제 1 이송 섹션의 상기 가열 수단은, 그것의 가열 능력이 무가열과 미리 정해진 과시효 온도로 급속 가열 사이에서 조절가능하도록 제어가능하고;
- 상기 제 1 이송 섹션의 상기 냉각 수단은, 냉각 속도가 0 ℃/초 ~ 적어도 70 ℃/초에서 조절될 수 있고 켄칭 온도가 100 ℃ ~ 500 ℃ 에서 선택될 수 있도록 되어 있고;
- 상기 제 1 이송 섹션의 상기 가열 수단은 적어도 하나의 제어가능한 유도 히터를 포함하고;
- 상기 제 2 이송 섹션은, 순차적으로, 냉각함으로써 또는 가열함으로써 상기 스트립의 온도를 조절하기 위한 제어가능한 냉각 수단 및 제어가능한 가열 수단을 포함하고;
- 상기 제 2 이송 섹션은, 바람직하게 적어도 50 ℃/초인 냉각 속도에서 550 ℃ ~ 700 ℃ 의 온도로부터 용융 도금 온도로 2 ㎜ 까지 두께를 가지는 판을 냉각할 수 있는 제어가능한 냉각 수단을 포함하고;
- 상기 과시효 섹션은 상기 스트립의 온도를 대략 과시효 온도로 유지하거나 상기 스트립의 온도를 입구 온도와 출구 온도 사이에서 서서히 감소시킬 수 있는 제어가능한 수단을 포함하고;
- 상기 어닐링 섹션은, 미리 정해진 어닐링 온도가 700 ℃ ~ 1000 ℃ 사이에서 선택될 수 있도록 제어가능한 수단을 포함하고;
- 상기 용융 도금 섹션은 적어도 액체 금속 욕을 포함하고;
- 상기 용융 도금 섹션은 코팅을 위한 합금 수단을 추가로 포함하고;
- 상기 용융 도금 섹션은 갈바나이징 섹션 또는 갈바닐링 섹션이다.
이하, 본 발명은 도면들을 고려하여 상세하게 제한없이 설명될 것이다.
도 1 은 본 발명에 따른 연속 프로세싱 라인의 개략도이다.
도 2 는 본 발명에 따른 라인에서 수행될 수 있는 프로세싱에서 다양한 열 경로들에 대응하는 온도 대 시간 다이어그램들을 개략적으로 보여준다.
도 1 에 도시된 대로, 다목적 연속 프로세싱 라인은 어닐링 섹션 (1), 제 1 이송 섹션 (2), 과시효 섹션 (3), 제 2 이송 섹션 (4) 및 용융 도금 섹션 (5) 을 포함하고, 여기에서 강 스트립은 화살표들에 의해 나타낸 것처럼 이동한다.
어닐링 섹션 (1) 은, 주위 온도로부터 700 ℃ ~ 1000 ℃ 로 이루어진 미리 정해진 어닐링 온도 (AT) 로 스트립을 가열할 수 있는, 예열 구역 (10), 가열 구역 (11) 및 소킹 구역 (12; soaking zone) 을 포함한다.
이 어닐링 온도는, 제조되는 판들의 유형에 따라, 즉, DP 강들에 대해 약 750 ℃ ~ 840 ℃, TRIP 강들에 대해 약 830 ℃ ~ 860 ℃, Q&P 강들에 대해 약 790 ℃ ~ 950 ℃ 로 선택되어야 한다.
이 목적으로, 예열 구역 및 가열 구역은 본 기술분야의 당업자들에 의해 공지된 제어가능한 가열 수단을 포함한다.
소킹 구역에서, 스트립은 바람직하게 보호 분위기 하에, 바람직하게 적어도 45 초의 시간 동안 어닐링 온도에서 또는 대략 이 온도에서, 즉 바람직하게, 어닐링 온도 - 10 ℃ 와 어닐링 온도 + 10 ℃ 사이에서 유지되어야 한다. 이 목적으로, 소킹 구역은 그 자체가 공지된 소킹로 (soaking furnace) 로 구성되고, 소킹로의 길이는 스트립의 주행 속도를 고려해 볼 때 적어도 최소 요구 시간 동안 온도를 유지하도록 되어 있다.
제 1 이송 섹션 (2) 은 적어도, 순차적으로, 먼저 냉각 수단 (21), 그 후 가열 수단 (22) 을 포함한다.
그 자체가 공지된 복수의 냉각 박스들 (211) 로 구성될 수 있는 냉각 수단 (21) 은, 스트립을 조절가능한 냉각률에서 미리 정해진 켄칭 온도로 냉각할 수 있도록 또는 스트립을 냉각하지 않도록, 무냉각과 최대 냉각 효율 사이에서 제어가능하다. 냉각률과 켄칭 온도는 제조되는 강판의 유형에 따라 선택되어야 한다. 예를 들어, DP 강들로 만들어진 판들에 대해, 스트립은 제 1 이송 섹션에서 냉각될 필요는 없고, 그것은 자연스럽게 과시효 섹션으로 입구 온도로 냉각할 수 있기만 하면 된다. TRIP 강들로 만들어진 판들에 대해, 스트립은 예를 들어 대략 25 ℃/초의 냉각 속도에서, 예를 들어 약 450 ℃ 의 과시효 온도 (OAT) 로 냉각되어야 한다. Q&P 강들로 만들어진 판들에 대해, 스트립은, 예를 들어, 적어도 40 ℃/초, 바람직하게 적어도 50 ℃/초의 냉각 속도에서, 100 ℃ ~ 370 ℃, 바람직하게 140 ℃ ~ 355 ℃ 에서 조절가능한 켄칭 온도 (QT) 로 켄칭되어야 한다. 어닐링 온도와 켄칭 온도 사이 최대 차이는 바람직하게 650 ℃ 미만이다.
이 목적으로, 냉각 수단 (21) 은, 스트립의 냉각 속도가 0 ℃/초 ~ 약 70 ℃/초 사이에서 조절될 수 있고 켄칭 온도가 100 ℃ ~ 500 ℃ 사이에서 조절될 수 있도록 되어야 한다.
바람직하게, 10 초까지는 악영향을 미치지 않을지라도, 스트립은 재가열되기 전 약 1 ~ 2 초 동안 켄칭 온도에서 유지된다.
냉각 수단 (21) 이 복수의 냉각 박스들 (211) 로 구성된다면, 이 냉각 박스들은 바람직하게 독립적으로 제어가능하다.
냉각 박스들 (211) 은, 예를 들어, 스트립에 공기, 가스 또는 공기 또는 가스 및 물의 혼합물을 송풍할 수 있는 자체 공지된 송풍 박스들이다.
예를 들어 4.0 ㎿ 의 동력을 공급받을 수 있는 하나의 유도 코일, 또는 보다 높은 용량 라인을 위해, 4.0 W 의 동력을 각각 공급할 수 있는 2 개의 유도 코일들로 구성될 수 있는 가열 수단 (22) 은, 판들이 Q&P 강들로 만들어진다면 신속하게 스트립들을 미리 정해진 과시효 온도로 가열하고, 또는 판들이 DP 또는 TRIP 강들로 만들어진다면 스트립을 가열하지 않도록 제어가능해야 한다.
Q&P 강들에 대해, 과시효 온도는 일반적으로 340 ℃ ~ 490 ℃, 바람직하게 350 ℃ ~ 480 ℃ 이다.
과시효 섹션 (3) 은, 300 ℃ ~ 700 ℃, 바람직하게, 대략, 스트립이 제 1 이송 섹션의 출력 위치에서 과시효 섹션에 도입되는 온도인 340 ℃ ~ 480 ℃ 의 미리 정해진 과시효 온도로 스트립의 온도를 유지할 수 있는 공지된 제어가능한 수단을 포함하는 소킹로이다. 하지만, 이 섹션은 또한 온도를 유지할 수 없지만 코팅 온도, 즉 수행되어야 하는 코팅을 고려했을 때 용융 도금 섹션 (5) 에 스트립이 도입되어야 하는 온도와 바람직하게 같거나 거의 같은 출력 온도로 지속적으로 감소시킬 수 있도록 허용할 수 있다. 일반적으로, 이 온도는 약 460 ℃ 이다.
판들이 DP 강으로 만들어질 때, 스트립은 일반적으로 650 ℃ ~ 700 ℃ 의 온도로 과시효 섹션에 도입되지만 그것은 550 ℃ ~ 700 ℃ 일 수 있고, 스트립은 바람직하게 코팅 온도와 동일한 출력 온도로 규칙적으로 냉각된다. 스트립은 또한 과시효 섹션에서 도입 온도로 적당한 냉각률로 냉각된 후 모든 과시효 섹션에서 이 온도로 유지되고, 그 후, 바람직하게, 적어도 2 ㎜ 까지의 두께를 가지는 판들에 대해 적어도 50 ℃/초인 냉각 속도에서 코팅 온도로 냉각될 수 있다.
판들이 TRIP 강으로 만들어질 때, 스트립은, 일반적으로 대략 450 ℃ 또는 460 ℃, 또는 400 ℃ ~ 460 ℃ 의 범위 내 과시효 온도로 과시효 섹션에 도입되고 그리고 바람직하게 코팅 온도와 동일한 과시효 출구에서, 이 온도로 또는 대략 그 온도로, 즉 과시효 온도 - 10 ℃ 와 과시효 온도 + 10 ℃ 사이에서 일반적으로 20 초 ~ 60 초의 시간 동안 유지된다.
판들이 Q&P 강들로 만들어질 때, 스트립은 제 1 이송 섹션의 가열 수단에 의해 획득된 과시효 온도로 과시효 섹션에 도입되고, 일반적으로 20 초 ~ 60 초의 시간 동안 즉 과시효 온도 - 10 ℃ 와 과시효 온도 + 10 ℃ 사이의 온도 또는 대략 그 온도로 유지된다.
전술한 대로 과시효 온도는 일반적으로 340 ℃ ~ 480 ℃, 바람직하게 350 ℃ ~ 480 ℃ 이다. 더욱이, 과시효 온도와 켄칭 온도 사이 차이는 330 ℃ 미만으로 유지되어야 한다.
일반적으로, 스트립이 후에 갈바나이징될 때, 과시효 온도에서 유지 시간은 적어도 30 초이다. 스트립이 갈바닐링될 때, 유지 시간은 바람직하게 적어도 45 초이다.
소킹로의 길이는, 라인에서 스트립의 주행 속도를 고려했을 때 유지 시간이 지정된 시간일 수 있도록 되어 있다.
제 2 이송 섹션 (4) 은, 코팅 온도보다 높은 과시효 온도로부터 코팅 온도로, 즉, 예를 들어 460 ℃ 보다 높지만 490 ℃ 미만인 온도와 450 ℃ ~ 460 ℃ 의 온도 사이에서, 스트립을 냉각할 수 있는, 예를 들어, 송풍 박스들 (411) 로 구성된 제어가능한 냉각 수단 (41) 을 포함한다. DP 강들과 같은 일부 강들에 대해, 냉각 수단 (41) 은 바람직하게 적어도 50 ℃/초인 냉각 속도로 550 ℃ ~ 700 ℃ 의 온도로부터 적어도 2 ㎜ 까지의 두께를 가지는 판들을 냉각할 수 있어야 한다. 이 경우에, 냉각 수단이 송풍 박스들 (411) 이라면, 이 송풍 박스들은 이러한 냉각을 할 수 있어야 한다. 이 수단은 냉각이 필요없다면 사용될 수 없다.
제 2 이송 섹션 (4) 은 코팅 온도 미만의 과시효 온도로부터 코팅 온도까지, 즉, 예를 들어, 460 ℃ 보다 낮고 340 ℃ 보다 높은 온도로부터 450 ℃ ~ 460 ℃ 의 온도까지, 즉 400 ℃ 에서 460 ℃ 로 스트립을 가열할 수 있는 유도 히터와 같은 제어가능한 급속 가열 수단 (42) 을 또한 포함한다. 이 가열 수단은, 무가열이 필요하다면 사용될 필요가 없다.
용융 도금 섹션 (5) 은, 본 기술분야의 당업자들에게 공지된 적어도 액체 금속 욕 (51), 합금 수단 (52) 및 냉각 수단 (53) 을 포함한다. 용융 도금 섹션은, 본 기술분야의 당업자들에게 또한 공지된, 후 포트 냉각 (또는 APC) 섹션들 (54, 55) 을 추가로 포함한다.
액체 금속 욕은, 예를 들어, 갈바나이징 또는 갈바닐링을 위한 액체 아연 또는 액체 아연 합금의 욕이다.
합금 수단은, 종종 480 ℃ ~ 570 ℃ 의 합금 온도에서 스트립을 유지할 수 있는 노이고 스트립이 갈바닐링될 때 사용된다.
이 라인으로, DP, TRIP 또는 Q&P 강판들을 제조하는데 필요한 것에 대응하는 열적 사이클을 달성할 수 있다. 이러한 사이클의 온도 대 시간의 다이어그램들은 도 2 에 도시된다.
Q&P 강에 대해, 스트립은 어닐링 섹션 (1) 에서 795 ℃ ~ 910 ℃ 의 어닐링 온도 (AT) 로 가열되고, 이 온도에서 유지된다 (101). 그 후, 제 1 이송 섹션에서, 스트립은 140 ℃ ~ 355 ℃ 의 켄칭 온도 (QT) 로 급속하게 냉각되고 (102) 그 후 340 ℃ ~ 490 ℃ 의 과시효 온도로 재가열된다 (102a 또는 102b). 그 후, 과시효 섹션에서, 스트립은 코팅 온도보다 높거나, 낮거나 동일할 수 있는 과시효 온도로 유지된다 (103a 또는 103b).
그 후, 과시효 온도가 코팅 온도와 동일하지 않다면, 스트립은 코팅 온도로 냉각되거나 (104a) 가열된다 (104b).
스트립은 갈바나이징 (50, 50a) 또는 갈바닐링 (50, 50b) 에 의해 코팅된다.
TRIP 강에 대해, 스트립은 어닐링 섹션 (1) 에서 830 ~ 870 ℃ 의 어닐링 온도로 가열되고 이 온도에서 유지되고 (201), 그 후 스트립은 대략 코팅 온도인 약 450 ℃ 의 과시효 온도로 제 1 이송 섹션 (2) 에서 냉각된다 (202). 그 후, 스트립은 과시효 섹션 (3) 에서 이 온도로 유지되고 (203) 온도를 변경하지 않으면서 또는 필요하다면 온도를 조절함으로써 제 2 이송 섹션 (4) 을 통과한다. 그 후, 스트립은, 예를 들어, 갈바나이징 또는 갈바닐링에 의해 코팅된다.
DP 강에 대해, 어닐링 섹션 (1) 에서, 스트립은 예를 들어 770 ~ 840 ℃ 의 어닐링 온도로 가열되고 이 온도에서 유지된다 (301). 그 후, 650 ℃ 또는 심지어 550 ℃ 내지 700 ℃ 의 온도 (TDP) 에서 과시효 섹션 (3) 에 도입되도록 가열하지 않으면서 그리고 강제 냉각 (302) 하지 않으면서, 스트립은 제 1 이송 섹션 (2) 을 통과한다. 실시형태에서, 과시효 섹션에서, 스트립의 온도는 코팅 온도로 규칙적으로 감소한다 (303). 제 2 이송 섹션에서, 스트립의 온도는 필요하다면 조절된다. 그 후, 스트립은 예를 들어 갈바나이징 또는 갈바닐링에 의해 코팅된다. 다른 실시형태에서, 과시효 섹션에서, 스트립의 온도는 온도 (TDP) 에서 또는 대략 이 온도에서 유지된다 (303'). 제 2 이송 섹션 (4) 에서, 판은 적어도 2 ㎜ 까지의 모든 치수들에 대해 바람직하게 적어도 50 ℃/초인 냉각 속도로 냉각된다 (304). 그 후, 스트립은 예를 들어 갈바나이징 또는 갈바닐링에 의해 코팅된다.
용융 도금은 반드시 아연 코팅이 아니라 모든 유형의 용융 도금 금속 코팅일 수 있음을 알 수 있다.
라인의 모든 섹션들이 독립적으로 제어가능하므로, 동일한 라인에서 TRIP 강들, DP 강들 및 Q&P 강들로 만들어진 다양한 판들을 연속적으로 제조할 수 있다.

Claims (11)

  1. 강 스트립을 열 처리 및 용융 도금 (hot dip coating) 하도록 구성된 다목적 연속 프로세싱 라인으로서:
    상기 다목적 연속 프로세싱 라인은, 순차적으로,
    - 상기 강 스트립을 미리 정해진 어닐링 온도로 가열하고 상기 강 스트립을 상기 어닐링 온도로 유지하기 위한 어닐링 섹션 (1),
    - 제 1 이송 섹션 (2),
    - 상기 강 스트립을 300 ℃ ~ 700 ℃ 과시효 온도에 유지할 수 있는 과시효 (overaging) 섹션 (3),
    - 상기 강 스트립의 용융 도금을 허용하도록 상기 강 스트립의 온도를 조절할 수 있는 제 2 이송 섹션 (4), 및
    - 상기 강 스트립을 코팅 온도에서 용융 도금하기 위한 용융 도금 섹션 (5) 을 포함하고,
    상기 제 1 이송 섹션 (2) 은, 순차적으로, 냉각 수단 (21) 및 가열 수단 (22) 을 포함하며,
    상기 제 2 이송 섹션 (4) 은, 순차적으로, 냉각함으로써 또는 가열함으로써 상기 강 스트립의 온도를 조절하기 위한 제어가능한 냉각 수단 (41) 및 제어가능한 가열 수단 (42) 을 포함하고,
    상기 제어가능한 냉각 수단 (41) 은, 상기 코팅 온도 보다 높은 과시효 온도로부터 상기 코팅 온도로 상기 스트립을 냉각할 수 있고,
    상기 제어가능한 가열 수단 (42) 은, 상기 코팅 온도 미만의 과시효 온도로부터 상기 코팅 온도로 상기 스트립을 가열할 수 있는, 강 스트립을 열 처리 및 용융 도금할 수 있는 다목적 연속 프로세싱 라인.
  2. 제 1 항에 있어서,
    상기 제 1 이송 섹션 (2) 의 상기 냉각 수단 (21) 은, 상기 냉각 수단의 냉각 능력이 무냉각과 미리 정해진 켄칭 온도로 급속 냉각 사이에서 조절가능하도록 제어가능하고 상기 제 1 이송 섹션 (2) 의 상기 가열 수단 (22) 은, 상기 가열 수단의 가열 능력이 무가열과 미리 정해진 과시효 온도로 급속 가열 사이에서 조절가능하도록 제어가능한, 강 스트립을 열 처리 및 용융 도금할 수 있는 다목적 연속 프로세싱 라인.
  3. 제 2 항에 있어서,
    상기 제 1 이송 섹션 (2) 의 상기 냉각 수단 (21) 은, 냉각 속도가 0 ℃/초 ~ 70 ℃/초에서 조절될 수 있고 상기 켄칭 온도가 100 ℃ ~ 500 ℃ 에서 선택될 수 있도록 되어 있는, 강 스트립을 열 처리 및 용융 도금할 수 있는 다목적 연속 프로세싱 라인.
  4. 제 2 항 또는 제 3 항에 있어서,
    상기 제 1 이송 섹션 (2) 의 상기 가열 수단 (22) 은 적어도 하나의 제어가능한 유도 히터 (221) 를 포함하는, 강 스트립을 열 처리 및 용융 도금할 수 있는 다목적 연속 프로세싱 라인.
  5. 제 1 항 내지 제 3 항 중 어느 한 항에 있어서,
    상기 제어가능한 냉각 수단 (41) 은, 적어도 50 ℃/초인 냉각 속도에서 550 ℃ ~ 700 ℃ 의 온도로부터 용융 도금 온도로 2 ㎜ 까지의 두께를 가지는 판을 냉각할 수 있는, 강 스트립을 열 처리 및 용융 도금할 수 있는 다목적 연속 프로세싱 라인.
  6. 제 1 항 내지 제 3 항 중 어느 한 항에 있어서,
    상기 과시효 섹션 (3) 은 상기 강 스트립의 온도를 대략 과시효 온도로 유지하거나 상기 강 스트립의 온도를 입구 온도와 출구 온도 사이에서 서서히 감소시킬 수 있는 제어가능한 수단을 포함하는, 강 스트립을 열 처리 및 용융 도금할 수 있는 다목적 연속 프로세싱 라인.
  7. 제 1 항 내지 제 3 항 중 어느 한 항에 있어서,
    상기 어닐링 섹션 (1) 은, 미리 정해진 어닐링 온도가 700 ℃ ~ 1000 ℃ 사이에서 선택될 수 있도록 제어가능한 수단을 포함하는, 강 스트립을 열 처리 및 용융 도금할 수 있는 다목적 연속 프로세싱 라인.
  8. 제 1 항 내지 제 3 항 중 어느 한 항에 있어서,
    상기 용융 도금 섹션 (5) 은 적어도 액체 금속 욕 (51) 을 포함하는, 강 스트립을 열 처리 및 용융 도금할 수 있는 다목적 연속 프로세싱 라인.
  9. 제 8 항에 있어서,
    상기 용융 도금 섹션 (5) 은 코팅을 위한 합금 수단 (52) 을 더 포함하는, 강 스트립을 열 처리 및 용융 도금할 수 있는 다목적 연속 프로세싱 라인.
  10. 제 8 항에 있어서,
    상기 용융 도금 섹션 (5) 은 갈바나이징 (galvanizing) 섹션 또는 갈바닐링 (galvannealing) 섹션인, 강 스트립을 열 처리 및 용융 도금할 수 있는 다목적 연속 프로세싱 라인.
  11. 삭제
KR1020167036870A 2014-07-03 2015-07-03 강 스트립을 열 처리 및 용융 도금하기 위한 다목적 프로세싱 라인 KR102453713B1 (ko)