KR102239212B1 - 포토폴리머 조성물 - Google Patents
포토폴리머 조성물 Download PDFInfo
- Publication number
- KR102239212B1 KR102239212B1 KR1020190165053A KR20190165053A KR102239212B1 KR 102239212 B1 KR102239212 B1 KR 102239212B1 KR 1020190165053 A KR1020190165053 A KR 1020190165053A KR 20190165053 A KR20190165053 A KR 20190165053A KR 102239212 B1 KR102239212 B1 KR 102239212B1
- Authority
- KR
- South Korea
- Prior art keywords
- carbon atoms
- group
- sulfur
- oxygen
- formula
- Prior art date
Abstract
본 발명은, 신규한 구조의 화합물과 상기 화합물을 염료로 포함하는 포토폴리머 조성물과 상기 포토폴리머 조성물로부터 제조된 홀로그램 기록 매체와, 상기 홀로그램 기록 매체를 포함한 광학 소자 상기 홀로그램 기록 매체을 이용한 홀로그래픽 기록 방법에 관한 것이다.
Description
본 발명은 포토폴리머 조성물, 홀로그램 기록 매체, 광학 소자 및 홀로그래픽 기록 방법에 관한 것이다.
홀로그램(hologram) 기록 미디어는 노광 과정을 통하여 상기 미디어 내 홀로그래픽 기록층 내 굴절률을 변화시킴으로써 정보를 기록하고 이와 같이 기록된 미디어 내 굴절률의 변화를 판독하여 정보를 재생한다.
포토폴리머(감광성 수지, photopolymer)를 이용하는 경우 저분자 단량체의 광중합에 의하여 광 간섭 패턴을 홀로그램으로 용이하게 저장할 수 있기 때문에, 광학 렌즈, 거울, 편향 거울, 필터, 확산 스크린, 회절 부재, 도광체, 도파관, 영사 스크린 및/또는 마스크의 기능을 갖는 홀로그래픽 광학 소자, 광메모리 시스템의 매질과 광확산판, 광파장 분할기, 반사형, 투과형 컬러필터 등 다양한 분야에 사용될 수 있다.
통상적으로 홀로그램 제조용 포토폴리머 조성물은 고분자 바인더, 단량체 및 광개시제를 포함하며, 이러한 조성물로부터 제조된 감광성 필름에 대하여 레이저 간섭광을 조사하여 국부적인 단량체의 광중합을 유도한다.
이러한 광중합 과정에서 단량체가 상대적으로 많이 존재하는 부분에서는 굴절율이 높아지고, 고분자 바인더가 상대적으로 많이 존재하는 부분에서는 굴절율이 상대적으로 낮아져서 굴절율 변조가 생기게 되며, 이러한 굴절율 변조에 의해서 회절 격자가 생성된다. 굴절율 변조값 n은 포토폴리머층의 두께와 회절효율(DE)에 영향을 받으며, 각도 선택성은 두께가 얇을수록 넓어지게 된다.
최근에서는 높은 회절효율과 안정적으로 홀로그램을 유지할 수 있는 재료의 개발에 대한 요구와 함께, 얇은 두께를 가지면서도 굴절율 변조값이 큰 포토폴리머층의 제조를 위한 다양한 시도가 이루어지고 있다.
본 발명은, 얇은 두께를 가지면서도 큰 굴절율 변조값을 구현하고, 상대적으로 빠른 반응 속도를 가져서 기록 시간을 단축할 수 있으며, 온도 및 습도에 대한 내구성이 향상된 홀로그램 기록 매체를 제공할 수 있는 포토폴리머 조성물을 제공하기 위한 것이다.
또한, 본 발명은, 얇은 두께를 가지면서도 큰 굴절율 변조값을 구현하고, 상대적으로 빠른 반응 속도를 가져서 기록 시간을 단축할 수 있으며, 온도 및 습도에 대한 내구성이 향상된 홀로그램 기록 매체를 제공하기 위한 것이다.
또한, 본 발명은 홀로그램 기록 매체를 포함한 광학 소자를 제공하기 위한 것이다.
또한, 본 발명은 가간섭성의 레이저에 의해 상기 홀로그램 기록 매체에 포함된 광반응성 단량체를 선택적으로 중합시키는 단계를 포함하는, 홀로그래픽 기록 방법을 제공하기 위한 것이다.
본 명세서에서는, 신규한 구조의 염료 화합물을 포함한 홀로그램 기록용 포토폴리머 조성물이 제공된다.
또한, 본 명세서에서는, 상기 포토폴리머 조성물로부터 제조된 홀로그램 기록 매체가 제공된다.
또한, 본 명세서에서는, 상기 홀로그램 기록 매체를 포함한 광학 소자가 제공된다.
또한, 본 명세서에서는, 가간섭성 광원에 의해 상기 포토폴리머 조성물에 포함된 광반응성 단량체를 선택적으로 중합시키는 단계를 포함하는, 홀로그래픽 기록 방법이 제공된다.
이하 발명의 구체적인 구현예에 따른 포토폴리머 조성물, 홀로그램 기록 매체, 광학 소자, 및 홀로그래픽 기록 방법에 관하여 보다 상세하게 설명하기로 한다.
본 명세서에서, (메트)아크릴레이트는 메타크릴레이트 또는 아크릴레이트를 의미한다.
본 명세서에서, (공)중합체는 단독중합체 또는 공중합체(랜덤공중합체, 블록공중합체, 그라프트 공중합체를 포함)를 의미한다.
또한, 본 명세서에서, 홀로그램(hologram)은 노광 과정을 통하여 전체 가시 범위 및 근자외선 범위(300-800 nm)에서 광학적 정보가 기록된 기록 미디어를 의미하며, 예를 들어 인-라인 (가버(Gabor)) 홀로그램, 이축(off-axis) 홀로그램, 완전-천공(full-aperture) 이전 홀로그램, 백색광 투과 홀로그램 ("무지개 홀로그램"), 데니슈크(Denisyuk) 홀로그램, 이축 반사 홀로그램, 엣지-리터러츄어(edge-literature) 홀로그램 또는 홀로그래피 스테레오그램(stereogram) 등의 시각적 홀로그램(visual hologram)을 모두 포함한다.
본 명세서에 있어서, 알킬기는 직쇄 또는 분지쇄일 수 있고, 탄소수는 특별히 한정되지 않으나 1 내지 40인 것이 바람직하다. 일 실시상태에 따르면, 상기 알킬기의 탄소수는 1 내지 20이다. 또 하나의 실시상태에 따르면, 상기 알킬기의 탄소수는 1 내지 10이다. 또 하나의 실시상태에 따르면, 상기 알킬기의 탄소수는 1 내지 6이다. 알킬기의 구체적인 예로는 메틸, 에틸, 프로필, n-프로필, 이소프로필, 부틸, n-부틸, 이소부틸, tert-부틸, sec-부틸, 1-메틸-부틸, 1-에틸-부틸, 펜틸, n-펜틸, 이소펜틸, 네오펜틸, tert-펜틸, 헥실, n-헥실, 1-메틸펜틸, 2-메틸펜틸, 4-메틸-2-펜틸, 3,3-디메틸부틸, 2-에틸부틸, 헵틸, n-헵틸, 1-메틸헥실, 시클로펜틸메틸, 시클로헥틸메틸, 옥틸, n-옥틸, tert-옥틸, 1-메틸헵틸, 2-에틸헥실, 2-프로필펜틸, n-노닐, 2,2-디메틸헵틸, 1-에틸-프로필, 1,1-디메틸-프로필, 이소헥실, 2-메틸펜틸, 4-메틸헥실, 5-메틸헥실 등이 있으나, 이들에 한정되지 않는다.
본 명세서에 있어서, 알킬렌기는 알케인(alkane)으로부터 유래한 2가의 작용기로, 예를 들어, 직쇄형, 분지형 또는 고리형으로서, 메틸렌기, 에틸렌기, 프로필렌기, 이소부틸렌기, sec-부틸렌기, tert-부틸렌기, 펜틸렌기, 헥실렌기 등이 될 수 있다.
발명의 일 구현예에 따르면, 고분자 매트릭스 또는 이의 전구체; 하기 화학식1의 화합물을 포함하는 염료; 광반응성 단량체; 및 광개시제;를 포함하는, 홀로그램 기록용 포토폴리머 조성물이 제공될 수 있다.
[화학식1]
상기 화학식1에서, X는 산소 또는 황이고,
R1 내지 R4는 각각 수소; 탄소수 1 내지 20의 알킬기; 탄소수 1 내지 20의 알콕시기; 탄소수 4 내지 20의 사이클로알킬기; 탄소수 6 내지 20의 방향족 탄화수소기; 시아노아크릴레이트 또는 이의 에스터기가 결합된 탄소수 6 내지 20의 방향족 탄화수소기; 아민기; 할로겐;
산소, 황 또는 질소를 1이상 포함하는 탄소수 4 내지 20의 지환족 또는 방향족 헤테로 고리; 또는
산소, 황 또는 질소를 1이상 포함하는 탄소수 4 내지 20의 지환족 또는 방향족 헤테로 고리가 1이상 치환된 탄소수 4 내지 20의 사이클로알킬기 또는 탄소수 6 내지 20의 방향족 탄화수소기; 이다.
본 발명자들은, 상기 화학식1의 화합물을 새로 합성해냈으며, 이러한 화학식1의 화합물이 상술한 신규한 구조에 따라서, 높은 광증감제(Photosensitizer) 특성과 우수한 내광성 및 용매에 대한 높은 용해성을 가질 수 있으며, 향상된 휘도 및 색재현율을 구현할 수 있고, 홀로그래픽 매체에서 높은 굴절율 변조를 구현할 수 있다. 특히, 상기 화학식1의 화합물은 이전에 알려진 염료들에 비하여 홀로그래픽 매체 적용시 상대적으로 빠른 반응 속도를 가져서 기록 시간을 단축할 수 있다는 점을 실험을 통하여 확인하고 발명을 완성하였다.
보다 구체적으로, 상기 화학식1의 화합물은 홀로그램 기록 매체를 제공하는 포토폴리머 조성물에서 염료로서 사용될 수 있다.
상기 화학식1에서, 각각의 작용기에 대한 설명은 상술한 바와 같다.
상기 화학식1의 작용기의 보다 구체적인 예로는,
상기 화학식1에서,
X는 산소 또는 황이고,
R1 내지 R4 중 적어도 하나는 산소, 황 또는 질소를 1이상 포함하는 탄소수 4 내지 20의 지환족 또는 방향족 헤테로 고리; 또는
산소, 황 또는 질소를 1이상 포함하는 탄소수 4 내지 20의 지환족 또는 방향족 헤테로 고리가 1이상 치환된 탄소수 4 내지 20의 사이클로알킬기 또는 탄소수 6 내지 20의 방향족 탄화수소기;인 화합물을 들 수 있다.
또한, 상기 화학식 1에서,
X는 산소 또는 황이고,
상기 R2 및 R3는 수소, 탄소수 1 내지 20의 알킬기, 또는 할로겐이고,
상기 R1 및 R4 중 하나는 아민기이고, 다른 하나는 R1 내지 R4 중 적어도 다른 하나는 산소, 황 또는 질소를 1이상 포함하는 탄소수 4 내지 20의 지환족 또는 방향족 헤테로 고리; 또는 산소, 황 또는 질소를 1이상 포함하는 탄소수 4 내지 20의 지환족 또는 방향족 헤테로 고리가 1이상 치환된 탄소수 4 내지 20의 사이클로알킬기 또는 탄소수 6 내지 20의 방향족 탄화수소기;일 수 있다.
또한, 상기 화학식1에서,
X는 산소 또는 황이고,
상기 R2 및 R3는 각각 탄소수 1 내지 5의 알콕시기이고,
상기 R1 및 R4는 각각 R1 내지 R4 중 적어도 다른 하나는 산소, 황 또는 질소를 1이상 포함하는 탄소수 4 내지 20의 지환족 또는 방향족 헤테로 고리; 또는 산소, 황 또는 질소를 1이상 포함하는 탄소수 4 내지 20의 지환족 또는 방향족 헤테로 고리가 1이상 치환된 탄소수 4 내지 20의 사이클로알킬기 또는 탄소수 6 내지 20의 방향족 탄화수소기;일 수 있다.
또한, 상기 화학식1에서,
X는 산소 또는 황이고,
상기 R2 및 R3는 각각 탄소수 1 내지 5의 알콕시기이고,
상기 R1 및 R4는 각각 시아노아크릴레이트 또는 이의 에스터기가 결합된 탄소수 6 내지 20의 방향족 탄화수소기일 수 있다.
상기 시아노아크릴레이트 에스터기는 시아노아크릴레이트의 카르복실기(-COOH)의 수소가 탄소수 1 내지 20의 지방족 작용기, 탄소수 3 내지 20의 지환족 작용기, 탄소수 1 내지 20의 지방족 작용기가 1이상 치환된 탄소수 3 내지 20의 지환족 작용기, 탄소수 6 내지 20의 방향족 작용기, 또는 탄소수 1 내지 20의 지방족 작용기가 1이상 치환된 탄소수 6 내지 20의 방향족 작용기 일 수 있다.
또한, 상기 화학식1의 화합물의 보다 구체적인 예로는, 하기 화학식 2 내지 5의 화합물 또는 이들의 혼합물을 들 수 있다.
[화학식 2]
[화학식3]
[화학식4]
[화학식5]
통상 홀로그램 기록 매체를 제공하는 포토폴리머 조성물에서 굴절율 변조값 및 회절 효율을 높이기 위해서 사용하는 고분자 매트릭스나 기록 단량체에 일정한 변화를 주거나 특정의 첨가제를 사용하는 등의 방법이 알려져 있으나, 상술한 화학식1의 화합물은 그리 높지 않은 사용량을 적용하여서도 굴절율 변조값 및 회절 효율을 보다 용이하게 향상시킬 수 있으며, 홀로그래픽 매체 적용시 상대적으로 빠른 반응 속도를 가져서 기록 시간을 단축할 수 있다.
한편, 상기 고분자 매트릭스 또는 이의 전구체는 상기 홀로그램 기록 매체 및 이로부터 제조된 최종 제품의 지지체 역할을 할 수 있으며, 상기 광반응성 단량체는 기록 단량체로서의 역할을 할 수 있으며, 이들의 사용에 따라 홀로그래픽 기록시 상기 고분자 매트릭스 상에서 상기 광반응성 단량체를 선택적으로 중합되어, 굴절률이 상이한 부분으로 인한 굴절률 변조가 나타날 수 있다.
상기 고분자 매트릭스 또는 이의 전구체로는 홀로그램 기록 매체를 제공하는 포토폴리머 조성물에서 통상적으로 사용 가능한 화합물이며 큰 제한 없이 사용할 수 있다.
상기 고분자 매트릭스 또는 이의 전구체의 구체적인 예로는 1) 1이상의 이소시아네이트기를 포함한 화합물과 폴리올 간의 반응 생성물; 또는 2) 실란계 작용기가 분지쇄에 위치하는 (메트)아크릴레이트계 (공)중합체 및 실란 가교제를 포함하는 고분자 매트릭스일 수 있다.
상기 실란계 작용기가 분지쇄에 위치하는 (메트)아크릴레이트계 (공)중합체 및 실란 가교제를 포함하는 고분자 매트릭스 또는 이의 전구체를 포함한 포토폴리머 조성물로부터 형성되는 홀로그램이 보다 얇은 두께 범위에서도 이전에 알려진 홀로그램에 비하여 크게 향상된 굴절율 변조값 및 우수한 온도, 습도에 대한 내구성을 구현할 수 있다.
상기 실란 가교제와 실란계 작용기가 분지쇄에 위치하는 (메트)아크릴레이트계 (공)중합체를 포함한 고분자 매트릭스 또는 이의 전구체를 사용함에 따라서, 상기 포토폴리머 조성물로부터 코팅 필름이나 홀로그램을 제조시에 가교밀도가 최적화되어 기존 매트릭스 대비 온도와 습도에 대해 우수한 내구성을 확보할 수 있다. 뿐만 아니라, 상술한 가교밀도 최적화를 통해, 높은 굴절률을 갖는 광반응성 단량체와 낮은 굴절률을 갖는 성분간의 유동성(mobility)을 높임으로서 굴절률 변조를 극대화시켜 기록특성이 향상될 수 있다.
특히, 실란계 작용기를 포함하는 변성 (메트)아크릴레이트계 (공)중합체와 말단의 실란계 작용기를 포함하는 실란 가교제간에는 졸겔반응을 통해 실록산 결합을 매개로하는 가교구조를 용이하게 도입할 수 있으며, 이러한 실록산 결합을 통해 온도와 습도에 대해 우수한 내구성이 확보될 수 있다.
상기 고분자 매트릭스 상에서 상술한 실란계 작용기가 분지쇄에 위치하는 (메트)아크릴레이트계 (공)중합체와 실란 가교제는 각각 별개의 성분으로 존재할 수 있으며, 또한 이들이 서로 반응하여 형성되는 복합체의 형태로도 존재할 수 있다.
상기 (메트)아크릴레이트계 (공)중합체에서 실란계 작용기가 분지쇄에 위치할 수 있다. 상기 실란계 작용기는 실란 작용기 또는 알콕시 실란 작용기를 포함할 수 있으며, 바람직하게는 알콕시 실란 작용기로 트리메톡시실란기를 사용할 수 있다.
상기 실란계 작용기는 상기 실란 가교제에 포함된 실란계 작용기와 졸겔반응을 통해 실록산 결합을 형성하여 상기 (메트)아크릴레이트계 (공)중합체와 실란 가교제를 가교시킬 수 있다.
상기 실란 가교제는 분자당 평균 1개 이상의 실란계 작용기를 갖는 화합물 또는 그의 혼합물일 수 있으며, 상기 1이상의 실란계 작용기를 포함한 화합물일 수 있다. 상기 실란계 작용기는 실란 작용기 또는 알콕시 실란 작용기를 포함할 수 있으며, 바람직하게는 알콕시 실란 작용기로 트리에톡시실란기를 사용할 수 있다. 상기 실란계 작용기는 상기 (메트)아크릴레이트계 (공)중합체에 포함된 실란계 작용기와 졸겔반응을 통해 실록산 결합을 형성하여 상기 (메트)아크릴레이트계 (공)중합체와 실란 가교제를 가교시킬 수 있다.
이때, 상기 실란 가교제는 상기 실란계 작용기의 당량이 200 g/equivalent 내지 1000 g/equivalent 일 수 있다. 이에 따라, 상기 (메트)아크릴레이트계 (공)중합체와 실란 가교제간의 가교밀도가 최적화되어, 기존 매트릭스 대비 온도와 습도에 대해 우수한 내구성을 확보할 수 있다. 뿐만 아니라, 상술한 가교밀도 최적화를 통해, 높은 굴절률을 갖는 광반응성 단량체와 낮은 굴절률을 갖는 성분간의 유동성(mobility)을 높임으로서 굴절률 변조를 극대화시켜 기록특성이 향상될 수 있다.
상기 실란 가교제에 포함된 상기 실란계 작용기의 당량이 1000 g/equivalent 이상으로 지나치게 증가하게 되면, 매트릭스의 가교 밀도 저하로 인해 기록후의 회절격자 경계면이 무너질 수 있고, 느슨한 가교밀도 및 낮은 유리전이 온도로 인해 단량체 및 가소제 성분들이 표면으로 용출되어 헤이즈를 발생시킬 수 있다. 상기 실란 가교제에 포함된 상기 실란계 작용기의 당량이 200 g/equivalent 미만으로 지나치게 감소하게 되면, 가교밀도가 너무 높아져 모노머와 가소제 성분들의 유동성을 저해하고 그로 인해 기록특성이 현저하게 낮아지는 문제가 발생할 수 있다.
보다 구체적으로, 상기 실란 가교제는 중량평균분자량이 100 내지 2000, 또는 300 내지 1000, 또는 300 내지 700인 선형의 폴리에테르 주쇄 및 상기 주쇄의 말단 또는 분지쇄로 결합한 실란계 작용기를 포함할 수 있다.
상기 중량평균분자량이 100 내지 2000인 선형의 폴리에테르 주쇄는 하기 화학식 13으로 표시되는 반복단위를 포함할 수 있다.
[화학식13]
-(R8O)n-R8-
상기 화학식13에서 R8은 탄소수 1 내지 10의 알킬렌기이고, n은 1이상, 또는 1 내지 50, 또는 5 내지 20, 또는 8 내지 10의 정수이다.
상기 실란 가교제가 유연한 폴리 에테르 폴리올을 주쇄로 도입함으로써 매트릭스의 유리전이온도 및 가교 밀도 조절을 통해 성분들의 유동성을 향상시킬 수 있다.
한편, 상기 실란계 작용기와 폴리에테르 주쇄의 결합은 우레탄 결합을 매개로 할 수 있다. 구체적으로, 상기 실란계 작용기와 폴리에테르 주쇄는 우레탄 결합을 통해 상호간 결합을 형성할 수 있으며, 보다 구체적으로는 상기 실란계 작용기에 포함된 규소 원자가 우레탄 결합의 질소원자와 직접 또는 탄소수 1 내지 10의 알킬렌기를 매개로 결합하며, 상기 폴리에테르 주쇄에 포함된 R8 작용기가 우레탄 결합의 산소원자와 직접 결합할 수 있다.
이처럼 상기 실란계 작용기와 폴리에테르 주쇄가 우레탄 결합을 매개로 결합하는 것은, 상기 실란 가교제가 실란계 작용기를 포함한 이소시아네이트 화합물과 중량평균분자량이 100 내지 2000인 선형의 폴리에테르 폴리올 화합물간의 반응을 통해 제조된 반응생성물이기 때문이다.
보다 구체적으로, 상기 이소시아네이트 화합물은 지방족, 고리지방족, 방향족 또는 방향지방족의 모노- 이소시아네이트 디- 이소시아네이트, 트리- 이소시아네이트 또는 폴리-이소시아네이트; 또는 우레탄, 요소, 카르보디이미드, 아실요소, 이소시아누레이트, 알로파네이트, 뷰렛, 옥사디아진트리온, 우레트디온 또는 이미노옥사디아진디온 구조를 가지는 디-이소시아네이트 또는 트리이소시아네이트의 올리고-이소시아네이트 또는 폴리-이소시아네이트;를 포함할 수 있다.
상기 실란계 작용기를 포함한 이소시아네이트 화합물의 구체적인 예로는, 3-이소시아네이토프로필트리에톡시실란을 들 수 있다.
또한, 상기 폴리에테르 폴리올은 예를 들면 스티렌 옥시드, 에틸렌 옥시드, 프로필렌 옥시드, 테트라히드로퓨란, 부틸렌 옥시드, 에피클로로히드린의 다중첨가 생성물과 이들의 혼합 첨가생성물 및 그라프트 생성물, 그리고 다가 알콜 또는 이들의 혼합물의 축합에 의해 수득되는 폴리에테르 폴리올 및 다가 알콜, 아민 및 아미노 알콜의 알콕시화에 의해 수득되는 것들이다.
상기 폴리에테르 폴리올의 구체적인 예로는 1.5 내지 6의 OH 관능도 및 200 내지 18000 g/몰 사이의 수 평균 분자량, 바람직하게는 1.8 내지 4.0의 OH 관능도 및 600 내지 8000 g/몰의 수 평균 분자량, 특히 바람직하게는 1.9 내지 3.1의 OH 관능도 및 650 내지 4500 g/몰의 수 평균 분자량을 가지는, 랜덤 또는 블록 공중합체 형태의 폴리(프로필렌 옥시드), 폴리(에틸렌 옥시드) 및 이들의 조합, 또는 폴리(테트라히드로퓨란) 및 이들의 혼합물이다.
이처럼, 상기 실란계 작용기와 폴리에테르 주쇄가 우레탄 결합을 매개로 결합하는 경우, 보다 용이하게 실란 가교제를 합성할 수 있다.
상기 실란 가교제의 중량평균분자량(GPC측정)은 1000 내지 5,000,000일 수 있다. 중량 평균 분자량은 GPC법에 의해 측정한 폴리스티렌 환산의 중량 평균 분자량(단위: g/mol)을 의미한다. 상기 GPC법에 의해 측정한 폴리스티렌 환산의 중량 평균 분자량을 측정하는 과정에서는, 통상적으로 알려진 분석 장치와 시차 굴절 검출기(Refractive Index Detector) 등의 검출기 및 분석용 컬럼을 사용할 수 있으며, 통상적으로 적용되는 온도 조건, 용매, flow rate를 적용할 수 있다. 상기 측정 조건의 구체적인 예로, 30 ℃의 온도, 클로로포름 용매(Chloroform) 및 1 mL/min의 flow rate를 들 수 있다.
한편, 상기 (메트)아크릴레이트계 (공)중합체는 실란계 작용기가 분지쇄에 위치하는 (메트)아크릴레이트 반복단위 및 (메트)아크릴레이트 반복단위를 포함할 수 있다.
실란계 작용기가 분지쇄에 위치하는 (메트)아크릴레이트 반복단위의 예로는 하기 화학식11로 표시되는 반복단위를 들 수 있다.
[화학식11]
상기 화학식11에서, R1 내지 R3은 각각 독립적으로 탄소수 1 내지 10의 알킬기이고, R4는 수소 또는 탄소수 1 내지 10의 알킬기이고, R5는 탄소수 1 내지 10의 알킬렌기이다.
바람직하게는 상기 화학식11에서, R1 내지 R3은 각각 독립적으로 탄소수 1의 메틸기이고, R4는 탄소수 1의 메틸기이고, R5는 탄소수 3의 프로필렌기인, 3-Methacryloxypropyltrimethoxysilane(KBM-503) 유래 반복단위 또는 R1 내지 R3은 각각 독립적으로 탄소수 1의 메틸기이고, R4는 수소이고, R5는 탄소수 3의 프로필렌기인, 3-Acryloxypropyltrimethoxysilane(KBM-5103) 유래 반복단위일 수 있다.
또한, 상기 (메트)아크릴레이트 반복단위의 예로는 하기 화학식12로 표시되는 반복단위를 들 수 있다.
[화학식12]
상기 화학식12에서, R6은 탄소수 1 내지 20의 알킬기이고, R7은 수소 또는 탄소수 1 내지 10의 알킬기이고, 바람직하게는 상기 화학식 12에서, R6은 탄소수 4의 부틸기이고, R7는 수소인, 부틸 아크릴레이트 유래 반복단위일 수 있다.
상기 화학식 12의 반복단위 : 상기 화학식 11의 반복단위간 몰비율은 0.5 : 1 내지 14 : 1 일 수 있다. 상기 화학식 11의 반복단위 몰비율이 지나치게 감소하게 되면, 매트릭스의 가교밀도가 지나치게 낮아져 지지체로써의 역할을 할 수 없어 기록후 기록특성의 감소가 발생할 수 있고, 상기 화학식11의 반복단위 몰비율이 지나치게 증가하게 되면, 매트릭스의 가교밀도가 너무 높아져 각 성분들의 유동성이 떨어짐으로 인해 굴절률 변조값의 감소가 발생할 수 있다.
상기 (메트)아크릴레이트계 (공)중합체의 중량평균분자량(GPC측정)은 100,000 내지 5,000,000, 또는 300,000 내지 900,000일 수 있다. 중량 평균 분자량은 GPC법에 의해 측정한 폴리스티렌 환산의 중량 평균 분자량(단위 : g/mol)을 의미한다. 상기 GPC법에 의해 측정한 폴리스티렌 환산의 중량 평균 분자량을 측정하는 과정에서는, 통상적으로 알려진 분석 장치와 시차 굴절 검출기(Refractive Index Detector) 등의 검출기 및 분석용 컬럼을 사용할 수 있으며, 통상적으로 적용되는 온도 조건, 용매, flow rate를 적용할 수 있다. 상기 측정 조건의 구체적인 예로, 30 ℃의 온도, 클로로포름 용매(Chloroform) 및 1 mL/min의 flow rate를 들 수 있다.
한편, 상기 (메트)아크릴레이트계 (공)중합체는 상기 실란계 작용기의 당량이 300 g/equivalent 내지 2000 g/equivalent, 또는 500 g/equivalent 내지 2000 g/equivalent, 또는 550 g/equivalent 내지 1800 g/equivalent, 또는 580 g/equivalent 내지 1600 g/equivalent, 또는 586 g/equivalent 내지 1562 g/equivalent일 수 있다.
상기 실란계 작용기 당량이란 실란계 작용기기 한 개에 대한 당량(g/equivalent)이며, 상기 (메트)아크릴레이트계 (공)중합체의 중량평균 분자량을 1 분자당 실란계 작용기의 수로 나눈 값이다. 상기 당량값이 작을수록 작용기의 밀도가 높으며, 상기 당량값이 클수록 작용기 밀도가 작아진다.
이에 따라, 상기 (메트)아크릴레이트계 (공)중합체와 실란 가교제간의 가교밀도가 최적화되어, 기존 매트릭스 대비 온도와 습도에 대해 우수한 내구성을 확보할 수 있다. 뿐만 아니라, 상술한 가교밀도 최적화를 통해, 높은 굴절률을 갖는 광반응성 단량체와 낮은 굴절률을 갖는 성분간의 유동성(mobility)을 높임으로서 굴절률 변조를 극대화시켜 기록특성이 향상될 수 있다.
상기 실란계 작용기가 분지쇄에 위치하는 (메트)아크릴레이트계 (공)중합체에 포함된 상기 실란계 작용기의 당량이 300 g/equivalent 미만으로 지나치게 감소하게 되면, 매트릭스의 가교밀도가 너무 높아져 성분들의 유동성을 저해하고, 그로 인해 기록특성의 감소가 발생할 수 있다.
또한, 상기 실란계 작용기가 분지쇄에 위치하는 (메트)아크릴레이트계 (공)중합체에 포함된 상기 실란계 작용기의 당량이 2000 g/equivalent 초과로 지나치게 증가하게 되면, 가교밀도가 너무 낮아 지지체로써의 역할을 못하게 되어 기록 후 생성된 회절격자들의 경계면이 무너져 굴절률 변조값이 시간이 경과하면서 감소할 수 있다.
한편, 상기 (메트)아크릴레이트계 (공)중합체 100 중량부에 대하여, 상기 실란 가교제 함량이 10 중량부 내지 90 중량부, 또는 20 중량부 내지 70 중량부, 또는 22 중량부 내지 65 중량부일 수 있다.
상기 반응 생성물에서, 상기 (메트)아크릴레이트계 (공)중합체 100 중량부에 대하여, 상기 실란 가교제 함량이 지나치게 감소하게 되면, 매트릭스의 경화속도가 현저히 느려져 지지체로써의 기능을 잃고 기록후의 회절격자 경계면이 쉽게 무너질 수 있으며, 상기 반응 생성물에서, 상기 (메트)아크릴레이트계 (공)중합체 100 중량부에 대하여, 상기 실란 가교제 함량이 지나치게 증가하게 되면, 매트릭스의 경화속도는 빨라지나 반응성 실란기 함량의 과도한 증가로 다른 성분들과의 상용성 문제가 발생하여 헤이즈가 발생하게 된다.
또한, 상기 반응 생성물의 모듈러스(저장탄성률)가 0.01 MPa 내지 5 MPa 일 수 있다. 상기 모듈러스 측정 방법의 구체적인 예로, TA Instruments의 DHR(discovery hybrid rheometer) 장비를 이용하여 상온(20 ℃ 내지 25 ℃)에서 1Hz의 frequency에서 storage modulus(G') 값을 측정할 수 있다.
또한, 상기 반응 생성물의 유리전이온도가 -40 ℃ 내지 10 ℃일 수 있다. 상기 유리전이온도 측정 방법의 구체적인 예로, DMA(dynamic mechanical analysis) 측정장비를 이용하여 strain 0.1%, frequency 1Hz, 승온속도 5℃/min의 셋팅 조건으로 -80 ℃ ~ 30℃ 영역에서 광중합 조성물이 코팅된 필름의 phase angle(Loss modulus) 변화를 측정하는 방법을 들 수 있다.
상기 고분자 매트릭스 또는 이의 전구체의 다른 일 예로, 1이상의 이소시아네이트기를 포함한 화합물과 폴리올 간의 반응 생성물을 포함하는 고분자 매트릭스를 들 수 있다.
상기 1이상의 이소시아네이트기를 포함한 화합물은 분자당 평균 1개 이상의 NCO 관능기를 갖는 공지의 화합물 또는 그의 혼합물일 수 있으며, 상기 1이상의 이소시아네이트기를 포함한 화합물일 수 있다.
보다 구체적으로 상기 1이상의 이소시아네이트기를 포함한 화합물은 지방족, 고리지방족, 방향족 또는 방향지방족의 모노- 디-, 트리- 또는 폴리- 이소시아네이트이다. 또한, 상기 1이상의 이소시아네이트기를 포함한 화합물은 우레탄, 요소, 카르보디이미드, 아실요소, 이소시아누레이트, 알로파네이트, 뷰렛, 옥사디아진트리온, 우레트디온 또는 이미노옥사디아진디온 구조를 가지는 단량체형 디- 및/또는 트리이소시아네이트의 비교적 분자량이 큰 2차 산물 (올리고- 및 폴리이소시아네이트)일 수 있다.
상기 1이상의 이소시아네이트기를 포함한 화합물의 구체적인 예로는, 부틸렌 디이소시아네이트, 헥사메틸렌 디이소시아네이트 (HDI), 이소포론 디이소시아네이트 (IPDI), 1,8-디이소시아네이토-4-(이소시아네이토메틸)옥탄, 2,2,4- 및/또는 2,4,4-트리메틸헥사메틸렌 디이소시아네이트, 이성질체 비스(4,4'-이소시아네이토시클로헥실)메탄 및 임의의 요망되는 이성질체 함량을 갖는 그의 혼합물, 이소시아네이토메틸-1,8-옥탄 디이소시아네이트, 1,4-시클로헥실렌 디이소시아네이트, 이성질체 시클로헥산디메틸렌 디이소시아네이트, 1,4-페닐렌 디이소시아네이트, 2,4- 및/또는 2,6-톨루엔 디이소시아네이트, 1,5-나프틸렌 디이소시아네이트, 2,4'- 또는 4,4'-디페닐메탄 디이소시아네이트 및/또는 트리페닐메탄 4,4',4"-트리이소시아네이트 등을 들 수 있다.
상기 1이상의 이소시아네이트기를 포함한 화합물과 반응하여 고분자 매트릭스를 형성하는 폴리올은 2 내지 20 탄소수를 갖는 지방족, 방향지방족 또는 고리지방족 디올, 트리올 및/또는 고급 폴리올일 수 있다.
상기 폴리올은 300 g/mol 내지 10,000 g/mol의 수산기 당량과 100,000 내지 1,500,0000 g/mol 의 중량평균분자량을 가질 수 있다.
상기 디올의 예로는 에틸렌 글리콜, 디에틸렌 글리콜, 트리에틸렌 글리콜, 테트라에틸렌 글리콜, 디프로필렌 글리콜, 트리프로필렌 글리콜, 1,2-프로판디올, 1,3-프로판디올, 1,4-부탄디올, 네오펜틸글리콜, 2-에틸-2-부틸프로판디올, 트리메틸펜탄디올, 디에틸옥탄디올 위치 이성질체, 1,3-부틸렌 글리콜, 씨클로헥산디올, 1,4-씨클로헥산디메탄올, 1,6-헥산디올, 1,2- 및 1,4-씨클로헥산디올, 수소화 비스페놀 A (2,2-비스(4-히드록시씨클로헥실)프로판), 2,2-디메틸-3-히드록시프로필, 2,2-디메틸-3-히드록시프로피오네이트가 있다.
또한, 상기 트리올의 예로는 트리메틸올에탄, 트리메틸올프로판 또는 글리세롤이 있다. 적합한 고도-관능성 알콜은 디트리메틸올프로판, 펜타에리트리톨, 디펜타에리트리톨 또는 소르비톨이다.
또한, 상기 폴리올로는 비교적 큰 분자량의 지방족 및 고리지방족 폴리올, 예컨대 폴리에스테르 폴리올, 폴리에테르 폴리올, 폴리카르보네이트 폴리올, 히드록시-관능성 아크릴 수지, 히드록시-관능성 폴리우레탄, 히드록시-관능성 에폭시 수지 등을 사용할 수 있다.
상기 폴리에스테르폴리올은 예를 들면 에탄디올, 디-, 트리- 또는 테트라에틸렌 글리콜, 1,2-프로판디올, 디-, 트리- 또는 테트라프로필렌 글리콜, 1,3-프로판디올, 1,4-부탄디올, 1,3-부탄디올, 2,3-부탄디올, 1,5-펜탄디올, 1,6-헥산디올, 2,2-디메틸-1,3-프로판디올, 1,4-디히드록시씨클로헥산, 1,4-디메틸올씨클로헥산, 1,8-옥탄디올, 1,10-데칸디올, 1,12-도데칸디올 또는 이들의 혼합물과 같은 다가 알콜을 사용하고, 임의로 트리메틸올프로판 또는 글리세롤과 같이 더 높은 관능성의 폴리올을 동시에 사용하여, 예를 들면 숙신산, 글루타르산, 아디프산, 피멜산, 수베르산, 아젤라산, 세바크산, 노난디카르복실산, 데칸디카르복실산, 테레프탈산, 이소프탈산, o-프탈산, 테트라히드로프탈산, 헥사히드로프탈산 또는 트리멜리트산, 및 산 무수물, 예컨대 o-프탈산 무수물, 트리멜리트산 무수물 또는 숙신산 무수물, 또는 이들의 혼합물과 같은 지방족, 고리지방족 또는 방향족의 디- 또는 폴리카르복실산 또는 그의 무수물로부터 공지의 방식으로 제조될 수 있는 것과 같은, 선형 폴리에스테르 디올이다. 물론, 고리지방족 및/또는 방향족의 디- 및 폴리히드록시 화합물 역시 폴리에스테르 폴리올의 제조를 위한 다가 알콜로서 적합하다. 유리 폴리카르복실산 대신, 저급 알콜의 상응하는 폴리카르복실산 무수물 또는 상응하는 폴리카르복실레이트, 또는 이들의 혼합물을 폴리에스테르 제조에 사용하는 것 역시 가능하다.
또한, 상기 고분자 매트릭스의 합성에 사용될 수 있는 폴리에스테르 폴리올로는 락톤의 단일- 또는 공중합체가 있으며, 이는 바람직하게는 부티로락톤, ε-카프로락톤 및/또는 메틸-ε-카프로락톤과 같은 락톤 또는 락톤 혼합물의, 예를 들면 폴리에스테르 폴리올용 합성 성분으로서 상기 언급된 작은 분자량의 다가 알콜과 같은 적합한 2관능성 및/또는 더 높은 관능성의 개시제 분자와의 첨가 반응에 의해 수득된다.
또한, 히드록실 기를 가지는 폴리카르보네이트 역시 예비중합체 합성을 위한 폴리히드록시 성분으로서 적합한데, 예를 들면 디올, 예컨대 1,4-부탄디올 및/또는 1,6-헥산디올 및/또는 3-메틸펜탄디올의, 디아릴 카르보네이트, 예컨대 디페닐 카르보네이트, 디메틸 카르보네이트 또는 포스겐과의 반응에 의해 제조될 수 있는 것들이다.
또한, 상기 고분자 매트릭스의 합성에 사용될 수 있는 폴리에테르 폴리올은 예를 들면 스티렌 옥시드, 에틸렌 옥시드, 프로필렌 옥시드, 테트라히드로퓨란, 부틸렌 옥시드, 에피클로로히드린의 다중첨가 생성물과 이들의 혼합 첨가생성물 및 그라프트 생성물, 그리고 다가 알콜 또는 이들의 혼합물의 축합에 의해 수득되는 폴리에테르 폴리올 및 다가 알콜, 아민 및 아미노 알콜의 알콕시화에 의해 수득되는 것들이다. 상기 폴리에테르 폴리올의 구체적인 예로는 1.5 내지 6의 OH 관능도 및 200 내지 18000 g/몰 사이의 수 평균 분자량, 바람직하게는 1.8 내지 4.0의 OH 관능도 및 600 내지 8000 g/몰의 수 평균 분자량, 특히 바람직하게는 1.9 내지 3.1의 OH 관능도 및 650 내지 4500 g/몰의 수 평균 분자량을 가지는, 랜덤 또는 블록 공중합체 형태의 폴리(프로필렌 옥시드), 폴리(에틸렌 옥시드) 및 이들의 조합, 또는 폴리(테트라히드로퓨란) 및 이들의 혼합물이다.
한편, 상기 광반응성 단량체는 다관능 (메트)아크릴레이트 단량체 또는 단관능 (메트)아크릴레이트 단량체를 포함할 수 있다.
상술한 바와 같이, 상기 포토폴리머 조성물의 광중합 과정에서 단량체가 중합되어 폴리머가 상대적으로 많이 존재하는 부분에서는 굴절율이 높아지고, 고분자 바인더가 상대적으로 많이 존재하는 부분에서는 굴절율이 상대적으로 낮아져서 굴절율 변조가 생기게 되며, 이러한 굴절율 변조에 의해서 회절 격자가 생성된다.
구체적으로, 상기 광반응성 단량체의 일 예로는 (메트)아크릴레이트계 α,β-불포화 카르복실산 유도체, 예컨대 (메트)아크릴레이트, (메트)아크릴아미드, (메트)아크릴로니트릴 또는 (메트)아크릴산 등이나, 또는 비닐기(vinyl) 또는 씨올기(thiol)를 포함한 화합물을 들 수 있다.
상기 광반응성 단량체의 일 예로 굴절율이 1.5 이상, 또는 1.53이상, 또는 1.5 내지 1.7인 다관능 (메트)아크릴레이트 단량체를 들 수 있으며, 이러한 굴절율이 1.5 이상, 또는 1.53이상, 또는 1.5 내지 1.7인 다관능 (메트)아크릴레이트 단량체는 Halogen 원자(bromine, iodine 등), 황(S), 인(P), 또는 방향족 고리(aromatic ring)을 포함할 수 있다.
상기 굴절율이 1.5 이상인 다관능 (메트)아크릴레이트 단량체의 보다 구체적인 예로는 bisphenol A modified diacrylate계열, fluorene acrylate 계열(HR6022 등 - Miwon社), bisphenol fluorene epoxy acrylate계열 (HR6100, HR6060, HR6042 등 - Miwon社), Halogenated epoxy acrylate계열 (HR1139, HR3362 등 - Miwon社) 등을 들 수 있다.
상기 광반응성 단량체의 다른 일 예로 단관능 (메트)아크릴레이트 단량체를 들 수 있다. 상기 단관능 (메트)아크릴레이트 단량체는 분자 내부에 에테르 결합 및 플루오렌 작용기를 포함할 수 있으며, 이러한 단관능 (메트)아크릴레이트 단량체의 구체적인 예로는 페녹시 벤질 (메트)아크릴레이트, o-페닐페놀 에틸렌 옥사이드 (메트)아크릴레이트, 벤질 (메트)아크릴레이트, 2-(페닐사이오)에틸 (메트)아크릴레이트, 또는 바이페닐메틸 (메트)아크릴레이트 등을 들 수 있다.
한편, 상기 광반응성 단량체로는 50 g/mol 내지 1000 g/mol, 또는 200 g/mol 내지 600 g/mol의 중량평균분자량을 가질 수 있다. 상기 중량평균분자량은 GPC법에 의해 측정한 폴리스티렌 환산의 중량 평균 분자량을 의미한다.
한편, 상기 구현예의 포토폴리머 조성물은 광개시제를 포함할 수 있다. 상기 광개시제는 빛 또는 화학방사선에 의해 활성화되는 화합물이며, 상기 광반응성 단량체 등 광반응성 작용기를 함유한 화합물의 중합을 개시한다.
상기 광개시제로는 통상적으로 알려진 광개시제를 큰 제한 없이 사용할 수 있으나, 이의 구체적인 예로는 광 라디칼 중합 개시제, 광양이온 중합 개시제, 또는 광음이온 중합 개시제를 들 수 있다.
상기 광 라디칼 중합 개시제의 구체적인 예로는, 이미다졸 유도체, 비스이미 다졸 유도체, N-아릴 글리신 유도체, 유기 아지드 화합물, 티타노센, 알루미네이트 착물, 유기 과산화물, N- 알콕시 피리디늄 염, 티옥산톤 유도체, 아민 유도체 등을 들 수 있다. 보다 구체적으로, 상기 광 라디칼 중합 개시제로는 1,3-di(t-butyldioxycarbonyl)benzophenone, 3,3',4,4''-tetrakis(t-butyldioxycarbonyl)benzophenone, 3-phenyl-5-isoxazolone, 2-mercapto benzimidazole, bis(2,4,5-triphenyl)imidazole, 2,2-dimethoxy-1,2-diphenylethane-1-one (제품명: Irgacure 651 / 제조사: BASF), 1-hydroxy-cyclohexyl-phenyl-ketone (제품명:Irgacure 184 / 제조사: BASF), 2-benzyl-2-dimethylamino-1-(4-morpholinophenyl)-butanone-1 (제품명: Irgacure 369 / 제조사: BASF), 및 bis(η5-2,4-cyclopentadiene-1-yl)-bis(2,6-difluoro-3-(1H-pyrrole-1-yl)-phenyl)titanium (제품명: Irgacure 784 제조사: BASF), Ebecryl P-115(제조사 : SK entis) 등을 들 수 있다.
상기 광양이온 중합 개시제로는, 디아조늄염(diazonium salt), 설포늄염(sulfonium salt), 또는 요오드늄(iodonium salt)을 들 수 있고, 예를 들면 술폰산 에스테르, 이미드 술포 네이트, 디알킬-4-히드록시 술포늄 염, 아릴 술폰산-p-니트로 벤질 에스테르, 실라놀-알루미늄 착물, (η6- 벤젠) (η5-시클로 펜타디에닐)철 (II) 등을 들 수 있다. 또한, 벤조인 토실레이트, 2,5-디니트로 벤질 토실레이트, N- 토실프탈산 이미드 등도 들 수 있다. 상기 광양이온 중합 개시제의 보다 구체적인 예로는, Cyracure UVI-6970, Cyracure UVI-6974 및 Cyracure UVI-6990 (제조사: Dow Chemical Co. in USA)이나 Irgacure 264 및 Irgacure 250 (제조사: BASF) 또는 CIT-1682 (제조사:Nippon Soda) 등의 시판 제품을 들 수 있다.
상기 광음이온 중합 개시제로는, 보레이트염(Borate salt)을 들 수 있고, 예를 들면 부티릴 클로린 부틸트리페닐보레이트(BUTYRYL CHOLINE BUTYLTRIPHENYLBORATE) 등을 들 수 있다. 상기 광음이온 중합 개시제의 보다 구체적인 예로는, Borate V(제조사: Spectra group) 등의 시판 제품을 들 수 있다.
또한, 상기 구현예의 포토폴리머 조성물은 일분자 (유형 I) 또는 이분자 (유형 II) 개시제를 사용할 수도 있다. 상기 자유 라디칼 광중합을 위한 (유형 I) 시스템은 예를 들면 3차 아민과 조합된 방향족 케톤 화합물, 예컨대 벤조페논, 알킬벤조페논, 4,4'-비스(디메틸아미노)벤조페논 (미힐러(Michler's) 케톤), 안트론 및 할로겐화 벤조페논 또는 상기 유형의 혼합물이다. 상기 이분자 (유형 II) 개시제로는 벤조인 및 그의 유도체, 벤질 케탈, 아실포스파인 옥시드, 예컨대 2,4,6-트리메틸벤조일디페닐포스파인 옥시드, 비스아실로포스파인 옥시드, 페닐글리옥실 에스테르, 캄포퀴논, 알파-아미노알킬페논, 알파-,알파-디알콕시아세토페논, 1-[4-(페닐티오)페닐]옥탄-1,2-디온 2-(O-벤조일옥심) 및 알파-히드록시알킬페논 등을 들 수 있다.
상기 구현예의 포토폴리머 조성물은 상기 고분자 매트릭스 또는 이의 전구체 1 중량% 내지 80중량%; 상기 광반응성 단량체 1 중량% 내지 80중량%; 상기 염료 0.0001 내지 10중량%; 및 광개시제 0.1 중량% 내지 20중량%;를 포함 포함할 수 있다. 후술하는 바와 같이, 상기 포토폴리머 조성물이 유기 용매를 더 포함하는 경우, 상술한 성분들의 함량은 이들 성분의 총합(유기 용매를 제외한 성분의 총합)을 기준으로 한다.
한편, 상기 구현예의 포토폴리머 조성물은 촉매, 포스페이트계 화합물 및 저굴절율 불소계 화합물로 이루어진 군에서 선택된 1종 이상을 더 포함할 수 있다.
상기 포스페이트계 화합물 및 저굴절율 불소계 화합물은 광반응성 단량체에 비해 낮은 굴절률을 가지고 있어, 고분자 매트릭스의 굴절률을 낮추어 포토폴리머 조성물의 굴절률 변조를 극대화시킬 수 있다. 더구나, 상기 포스페이트계 화합물은 가소제의 역할을 수행하여, 상기 고분자 매트릭스의 유리전이온도를 낮추어 광반응성 단량체와 저굴절 성분들의 유동성(mobility)을 높이고, 포토폴리머 조성물의 성형성 향상에도 기여할 수 있다.
보다 구체적으로, 상기 저굴절율 불소계 화합물은 반응성이 거의 없는 안정성을 가지며 저굴절특성을 가지므로, 상기 포토폴리머 조성물 내에 첨가시 고분자 매트릭스의 굴절률을 보다 낮출 수 있어, 모노머와의 굴절률 변조를 극대화시킬 수 있다.
한편, 상기 화학식1의 화합물과 상기 저굴절율 불소계 화합물을 함께 사용하면, 가소제 역할을 하는 저굴절율 불소계 화합물에 의해 매트릭스의 Tg가 낮아지면서 플렉서블(Flexible)한 매트릭스에서 상기 화학식 1 화합물 염료의 환원 반응 속도가 빨라지거나, 개시제로의 수소 이동(H-Transfer) 속도 등이 빨라질 수 있으며, 이에 따라 라디칼 생성에 의한 모노머 중합 속도가 개선되어 기록 시간을 단축하거나 기록 효율 상승의 효과가 구현될 수 있다.
상기 불소계 화합물은 에테르기, 에스터기 및 아마이드기로 이루어진 군에서 선택된 1종 이상의 작용기 및 2이상의 다이플루오로메틸렌기를 포함할 수 있다. 보다 구체적으로, 상기 불소계 화합물은 2개의 다이플루오로메틸렌기간의 직접결합 또는 에테르 결합을 포함한 중심 작용기의 양말단에 에테르기를 포함한 작용기가 결합한 하기 화학식14 구조를 가질 수 있다.
[화학식14]
상기 화학식14에서, R11 및 R12는 각각 독립적으로 다이플루오로메틸렌기이며, R13 및 R16은 각각 독립적으로 메틸렌기이고, R14 및 R15는 각각 독립적으로 다이플루오로메틸렌기이며, R17 및 R18은 각각 독립적으로 폴리알킬렌 옥사이드기이고, m은 1이상, 또는 1 내지 10, 또는 1 내지 3의 정수이다.
바람직하게는 상기 화학식14에서, R11 및 R12는 각각 독립적으로 다이플루오로메틸렌기이며, R13 및 R16은 각각 독립적으로 메틸렌기이고, R14 및 R15는 각각 독립적으로 다이플루오로메틸렌기이며, R17 및 R18은 각각 독립적으로 2-메톡시에톡시메톡시기이고, m은 2의 정수이다.
상기 불소계 화합물은 굴절률이 1.45미만, 또는 1.3 이상 1.45미만일 수 있다. 상술한 바와 같이 광반응성 단량체가 1.5이상의 굴절률을 가지므로, 상기 불소계 화합물은 광반응성 단량체 보다 낮은 굴절률을 통해, 고분자 매트릭스의 굴절률을 보다 낮출 수 있어, 모노머와의 굴절률 변조를 극대화시킬 수 있다.
구체적으로, 상기 불소계 화합물 함량은 광반응성 단량체 100 중량부에 대하여, 30 중량부 내지 150 중량부, 또는 50 중량부 내지 110 중량부일 수 있다.
상기 불소계 화합물 함량은 광반응성 단량체 100 중량부에 대하여 지나치게 감소하게 되면, 저굴절 성분의 부족으로 인해 기록 후의 굴절률 변조값이 낮아지고, 상기 불소계 화합물 함량이 광반응성 단량체 100 중량부에 대하여 지나치게 증가하게 되면, 기타 성분들과의 상용성 문제로 헤이즈가 발생하거나 일부 불소계 화합물이 코팅층의 표면으로 용출되는 문제가 발생 할 수 있다.
상기 불소계 화합물은 중량평균분자량(GPC측정)이 300 이상, 또는 300 내지 1000일 수 있다. 중량평균분자량 측정의 구체적인 방법은 상술한 바와 같다.
한편, 상기 포스페이트계 화합물의 구체적인 예로는 트리페닐포스페이트, 트리크레실포스페이트, 크레실디페닐포스페이트, 옥틸디페닐포스페이트, 디페닐비페닐포스페이트, 트리옥틸포스페이트, 트리부틸포스페이트 등을 들 수 있다.
상기 포스페이트계 화합물은 상술한 불소계 화합물과 함께 1:5 내지 5:1의 중량비율로 첨가될 수 있다. 상기 포스페이트계 화합물은 굴절률이 1.5미만이며, 분자량이 700이하일 수 있다.
상기 포토폴리머 조성물은 기타의 첨가제, 촉매 등을 더 포함할 수 있다. 예를 들어, 상기 포토폴리머 조성물은 상기 고분자 매트릭스나 광반응성 단량체의 중합을 촉진하기 위하여 통상적으로 알려진 촉매를 포함할 수 있다. 상기 촉매의 예로는, 주석 옥타노에이트, 아연 옥타노에이트, 디부틸주석 디라우레이트, 디메틸비스[(1-옥소네오데실)옥시]스타난, 디메틸주석 디카르복실레이트, 지르코늄 비스(에틸헥사노에이트), 지르코늄 아세틸아세토네이트, p-톨루엔설폰산(p-toluenesulfonic acid) 또는 3차 아민, 예컨대 1,4-디아자비씨클로[2.2.2]옥탄, 디아자비씨클로노난, 디아자비씨클로운데칸, 1,1,3,3-테트라메틸구아니딘, 1,3,4,6,7,8-헥사히드로-1-메틸-2H-피리미도(1,2-a)피리미딘 등을 들 수 있다.
상기 기타의 첨가제의 예로는 소포제를 들 수 있고, 상기 소포제로는 실리콘계 반응성 첨가제를 사용할 수 있으며, 이의 예로 Tego Rad 2500을 들 수 있다.
한편, 상기 구현예의 포토폴리머 조성물은 상술한 화학식1의 화합물에 추가하여 이와 상이한 광반응성 염료를 더 포함할 수 있다.
상기 광감응 염료는 상기 광개시제를 증감시키는 증감 색소의 역할을 하는데, 보다 구체적으로 상기 광감응 염료는 광중합체 조성물에 조사된 빛에 의하여 자극되어 모노머 및 가교 모노머의 중합을 개시하는 개시제의 역할도 함께 할 수 있다.
상기 화학식1의 화합물과 상이한 광감응 염료의 예가 크게 한정되는 것은 아니며, 통상적으로 알려진 다양한 화합물을 사용할 수 있다. 상기 광감응 염료의 구체적인 예로는, 세라미도닌의 술포늄 유도체(sulfonium derivative), 뉴 메틸렌 블루(new methylene blue), 티오에리트로신 트리에틸암모늄(thioerythrosine triethylammonium), 6-아세틸아미노-2-메틸세라미도닌(6-acetylamino-2-methylceramidonin), 에오신(eosin), 에리트로신(erythrosine), 로즈 벵갈(rose bengal), 티오닌(thionine), 베이직 옐로우(baseic yellow), 피나시놀 클로라이드(Pinacyanol chloride), 로다민 6G(rhodamine 6G), 갈로시아닌(gall℃yanine), 에틸 바이올렛(ethyl violet), 빅토리아 블루 R(Victoria blue R), 셀레스틴 블루(Celestine blue), 퀴날딘 레드(QuinaldineRed), 크리스탈 바이올렛(crystal violet), 브릴리언트 그린(Brilliant Green), 아스트라존 오렌지 G(Astrazon orange G), 다로우 레드(darrow red), 피로닌 Y(pyronin Y), 베이직 레드 29(basic red 29), 피릴륨I(pyrylium iodide), 사프라닌 O(Safranin O), 시아닌, 메틸렌 블루, 아주레 A(Azure A), 또는 이들의 2이상의 조합을 들 수 있다.
한편, 상기 구현예의 포토폴리머 조성물의 제조시에는 유기 용매가 사용될 수 있다. 상기 유기 용매의 비제한적인 예를 들면 케톤류, 알코올류, 아세테이트류 및 에테르류, 또는 이들의 2종 이상의 혼합물을 들 수 있다.
이러한 유기 용매의 구체적인 예로는, 메틸에틸케논, 메틸이소부틸케톤, 아세틸아세톤 또는 이소부틸케톤 등의 케톤류; 메탄올, 에탄올, n-프로판올, i-프로판올, n-부탄올, i-부탄올, 또는 t-부탄올 등의 알코올류; 에틸아세테이트, i-프로필아세테이트, 또는 폴리에틸렌글리콜 모노메틸에테르 아세테이트 등의 아세테이트류; 테트라하이드로퓨란 또는 프로필렌글라이콜 모노메틸에테르 등의 에테르류; 또는 이들의 2종 이상의 혼합물을 들 수 있다.
상기 유기 용매는 상기 홀로그램 기록 매체를 제조하기 위한 포토폴리머 조성물에 포함되는 각 성분들을 혼합하는 시기에 첨가되거나 각 성분들이 유기 용매에 분산 또는 혼합된 상태로 첨가되면서 상기 포토폴리머 조성물에 포함될 수 있다. 상기 포토폴리머 조성물 중 유기 용매의 함량이 너무 작으면, 상기 포토폴리머 조성물의 흐름성이 저하되어 최종 제조되는 필름에 줄무늬가 생기는 등 불량이 발생할 수 있다. 또한, 상기 유기 용매의 과량 첨가시 고형분 함량이 낮아져, 코팅 및 성막이 충분히 되지 않아서 필름의 물성이나 표면 특성이 저하될 수 있고, 건조 및 경화 과정에서 불량이 발생할 수 있다. 이에 따라, 상기 포토폴리머 조성물은 포함되는 성분들의 전체 고형분의 농도가 1중량% 내지 70중량%, 또는 2 중량% 내지 50중량%가 되도록 유기 용매를 포함할 수 있다.
한편, 발명의 다른 구현예에 따르면, 상기 구현예의 포토폴리머 조성물로부터 제조된 홀로그램 기록 매체가 제공될 수 있다.
상기 구현예의 포토폴리머 조성물에 대한 내용은 상술한 바와 같다.
상기 홀로그램 기록 매체는 5㎛ 내지 30 ㎛의 두께에서도 0.020 이상, 또는 0.021이상, 또는 0.023이상, 또는 0.025이상, 또는 0.027 이상, 또는 상기 하한치 중 어느 하나 내지 0.035의 굴절율 변조값(n)을 구현할 수 있다.
또한, 상기 홀로그램 기록 매체는 5㎛ 내지 30 ㎛의 두께에서 50% 이상, 또는 85% 이상, 또는 85 내지 99%의 회절 효율을 구현할 수 있다.
상기 홀로그램 기록 매체를 제조하기 위한 포토폴리머 조성물은 이에 포함되는 각각의 성분을 균일하게 혼합하고 20 ℃ 이상의 온도에서 건조 및 경화를 한 이후에, 소정의 노광 과정을 거쳐서 전체 가시 범위 및 근자외선 영역(300 내지 800 nm)에서의 광학적 적용을 위한 홀로그램으로 제조될 수 있다.
상기 포토폴리머 조성물 중 고분자 매트릭스 또는 이의 전구체를 형성하는 성분을 우선 균질하게 혼합하고, 상술한 실란 가교제를 추후에 촉매와 함께 혼합하여 홀로그램의 형성 과정을 준비할 수 있다.
상기 포토폴리머 조성물은 이에 포함되는 각각의 성분의 혼합에는 통상적으로 알려진 혼합기, 교반기 또는 믹서 등을 별 다른 제한 없이 사용할 수 있으며, 상기 혼합 과정에서의 온도는 0 ℃ 내지 100 ℃, 바람직하게는 10 ℃ 내지 80 ℃, 특히 바람직하게는 20 ℃ 내지 60 ℃일 수 있다.
한편, 상기 포토폴리머 조성물 중 고분자 매트릭스 또는 이의 전구체를 형성하는 성분을 우선 균질하고 혼합한 이후, 20 ℃이상의 온도에서 경화되는 액체 배합물이 될 수 있다. 상기 경화의 온도는 상기 포토폴리머의 조성에 따라 달라질 수 있으며, 예를 들어 30 ℃ 내지 180 ℃의 온도로 가열함으로써 촉진된다.
상기 경화시에는 상기 포토폴리머가 소정의 기판이나 몰드에 주입되거나 코팅이 된 상태일 수 있다.
한편, 상기 포토폴리머 조성물로부터 제조된 홀로그램 기록 매체에 시각적 홀로그램의 기록하는 방법은 통상적으로 알려진 방법을 큰 제한 없이 사용할 수 있으며, 후술하는 구현예의 홀로그래픽 기록 방법에서 설명하는 방법을 하나의 예로 채용할 수 있다.
한편, 발명의 또 다른 구현예에 따르면, 고분자 매트릭스 또는 이의 전구체; 하기 화학식1의 화합물을 포함하는 염료; 및 광반응성 단량체를 포함하는 코팅층을 포함하고, 5㎛ 내지 30 ㎛의 두께 범위에서 0.023이상의 굴절율 변조값(n) 을 갖는, 홀로그램 기록 매체가 제공될 수 있다.
[화학식1]
상기 화학식1에서, X는 산소 또는 황이고, R1 내지 R4는 각각 수소; 탄소수 1 내지 20의 알킬기; 탄소수 1 내지 20의 알콕시기; 탄소수 4 내지 20의 사이클로알킬기; 탄소수 6 내지 20의 방향족 탄화수소기; 시아노아크릴레이트 또는 이의 에스터기가 결합된 탄소수 6 내지 20의 방향족 탄화수소기; 아민기; 할로겐; 산소, 황 또는 질소를 1이상 포함하는 탄소수 4 내지 20의 지환족 또는 방향족 헤테로 고리; 또는 산소, 황 또는 질소를 1이상 포함하는 탄소수 4 내지 20의 지환족 또는 방향족 헤테로 고리가 1이상 치환된 탄소수 4 내지 20의 사이클로알킬기 또는 탄소수 6 내지 20의 방향족 탄화수소기; 이다.
상기 고분자 매트릭스 또는 이의 전구체; 화학식1의 화합물을 포함하는 염료; 및 광반응성 단량체 각각에 대한 내용은 상기 구현예의 포토폴리머 조성물에 관련하여 상술한 내용을 모두 포함한다.
상기 홀로그램 기록 매체는 5㎛ 내지 30 ㎛의 두께에서도또는 0.023이상, 또는 0.025이상, 또는 0.027 이상, 또는 상기 하한치 중 어느 하나 내지 0.035의 굴절율 변조값(n)을 구현할 수 있다.
또한, 상기 홀로그램 기록 매체는 5㎛ 내지 30 ㎛의 두께에서 50% 이상, 또는 85% 이상, 또는 85 내지 99%의 회절 효율을 구현할 수 있다.
한편, 상기 코팅층은 에테르기, 에스터기 및 아마이드기로 이루어진 군에서 선택된 1종 이상의 작용기 및 2이상의 다이플루오로메틸렌기를 포함하는 저굴절율 불소계 화합물을 더 포함할 수 있다.
한편, 상술한 바와 같이, 상기 화학식1의 화합물과 상기 저굴절율 불소계 화합물을 함께 사용하면, 가소제 역할을 하는 저굴절율 불소계 화합물에 의해 매트릭스의 Tg가 낮아지면서 플렉서블(Flexible)한 매트릭스에서 상기 화학식 1 화합물 염료의 환원 반응 속도가 빨라지거나, 개시제로의 수소 이동(H-Transfer) 속도 등이 빨라질 수 있으며, 이에 따라 라디칼 생성에 의한 모노머 중합 속도가 개선되어 기록 시간을 단축하거나 기록 효율 상승의 효과가 구현될 수 있다.
한편, 상기 홀로그램 기록 매체는 상기 포토폴리머 조성물을 코팅 및 건조하여 형성될 수 있으며, 또한 상기 포토폴리머 조성물을 코팅 및 열경화 또는 광경화 하여 형성될 수도 있다.
상기 홀로그램 기록 매체는 상기 코팅층이 일면에 형성되는 기재를 더 포함할 수도 있다. 상기 기재는 고분자 필름, 유리 기판 등 다양한 종류의 기재 중 어느 하나 일수 있다.
한편, 발명의 또 다른 구현예에 따르면, 가간섭성의 레이저에 의해 상기 포토폴리머 조성물에 포함된 광반응성 단량체를 선택적으로 중합시키는 단계를 포함하는, 홀로그래픽 기록 방법이 제공될 수 있다.
상술한 바와 같이, 상기 포토폴리머 조성물을 혼합 및 경화하는 과정을 통해서 시각적 홀로그램이 기록되지 않는 상태의 매체를 제조할 수 있으며, 소정의 노출 과정을 통해서 상기 매체 상에 시각적 홀로그램를 기록할 수 있다.
상기 포토폴리머 조성물을 혼합 및 경화하는 과정을 통하여 제공되는 매체에, 통상적으로 알려진 조건 하에 공지의 장치 및 방법을 이용하여 시각적 홀로그램을 기록할 수 있다.
한편, 발명의 또 다른 구현예에 따르면, 홀로그램 기록 매체를 포함한 광학 소자가 제공될 수 있다.
상기 광학 소자의 구체적인 예로는 광학 렌즈, 거울, 편향 거울, 필터, 확산 스크린, 회절 부재, 도광체, 도파관, 영사 스크린 및/또는 마스크의 기능을 갖는 홀로그래픽 광학 소자, 광메모리 시스템의 매질과 광확산판, 광파장 분할기, 반사형, 투과형 컬러필터 등을 들수 있다.
상기 홀로그램 기록 매체를 포함한 광학 소자의 일 예로 홀로그램 디스플레이 장치를 들 수 있다.
상기 홀로그램 디스플레이 장치는 광원부, 입력부, 광학계 및 표시부를 포함한다. 상기 광원부는 입력부 및 표시부에서 물체의 3차원 영상 정보를 제공, 기록 및 재생하는데 사용되는 레이저빔을 조사하는 부분이다. 또한, 상기 입력부는 표시부에 기록할 물체의 3차원 영상 정보를 미리 입력하는 부분이며, 예를 들어, 전기 구동 액정 SLM(electrically addressed liquid crystal SLM) 에 공간별 빛의 세기와 위상과 같은 물체의 3차원 정보를 입력할 수 있고, 이때 입력빔이 사용될 수 있다. 상기 광학계는 미러, 편광기, 빔스플리터, 빔셔터, 렌즈 등으로 구성될 수 있으며, 상기 광학계는 광원부에서 방출되는 레이저빔을 입력부로 보내는 입력빔, 표시부로 보내는 기록빔, 기준빔, 소거빔, 독출빔 등으로 분배할 수 있다.
상기 표시부는 입력부로부터 물체의 3차원 영상 정보를 전달받아서 광학 구동 SLM(optically addressed SLM)으로 이루어진 홀로그램 플레이트에 기록하고, 물체의 3차원 영상을 재생할 수 있다. 이때, 입력빔과 기준빔의 간섭을 통하여 물체의 3차원 영상 정보를 기록할 수 있다. 상기 홀로그램 플레이트에 기록된 물체의 3차원 영상 정보는 독출빔이 생성하는 회절 패턴에 의해 3차원 영상으로 재생될 수 있고, 소거빔은 형성된 회절 패턴을 빠르게 제거하기 위해 사용될 수 있다. 한편, 상기 홀로그램 플레이트는 3차원 영상을 입력하는 위치와 재생하는 위치 사이에서 이동될 수 있다.
본 발명에 따르면, 신규한 구조의 화합물과, 얇은 두께를 가지면서도 큰 굴절율 변조값을 구현하고 상대적으로 빠른 반응 속도를 가져서 기록 시간을 단축할 수 있으며 온도 및 습도에 대한 내구성이 향상된 홀로그램 기록 매체를 제공할 수 있는 포토폴리머 조성물과, 얇은 두께를 가지면서도 큰 굴절율 변조값을 구현하고 상대적으로 빠른 반응 속도를 가져서 기록 시간을 단축할 수 있으며 온도 및 습도에 대한 내구성이 향상된 홀로그램 기록 매체, 이를 포함한 광학 소자, 및 상기 홀로그램 기록 매체를 이용한 홀로그래픽 기록 방법이 제공될 수 있다.
발명을 하기의 실시예에서 보다 상세하게 설명한다. 단, 하기의 실시예는 본 발명을 예시하는 것일 뿐, 본 발명의 내용이 하기의 실시예에 의하여 한정되는 것은 아니다.
[제조예]
1. 제조예 1-1: 염료 화합물(5,6-dimethoxy-4,7-di(thiophen-3-yl)-benzo[c]-1,2,5-thiadiazole) 의 합성
(1) 1,2-Dimethoxybenzene (화합물 2) 제조
카테콜(Catechol) (10g, 0.0908 mol)과 K2CO3 (31.3g, 0.2270 mol)의 혼합물을 질소에서 10분간 교반하였다. 요오도메테인(Iodomethane; 11.8 mL, 0.1906 mol)을 첨가하고, 혼합물을 실온에서 1.5시간 동안 교반 한 후 밤새 환류(reflux)하에 가열하였다. 반응을 실온으로 냉각 시키고, K2CO3를 여과해 내고, 여액을 농축시켰다. 잔류물을 디클로로 메탄에 용해시키고, 이 용액을 물로 세척하였다. 유기층을 분리하고 MgSO4상에서 건조시키고 농축하여 12.3g (98 %)의 화합물 2를 수득하였다.
1H NMR (CDCl3): 6.94-6.87 (4H, s, Ar), 3.90 (6H, s, 2CH3).
(2) 1,2-dimethoxy-4,5-dinitrobenzene (화학식 3) 제조
10.5g의 1,2-Dimethoxybenzene (화학식 2) 를 420 mL의 디클로로메탄(dichloromethane)에 용해시킨 후 용액을 30분에 걸쳐 ice bath에서 69% HNO3 (169 mL)에 적가하였다. 농축된 H2SO4(83 mL)를 이 혼합물에 적가하고 교반을 실온에서 밤새 계속하였다. 반응 혼합물을 분쇄된 얼음 상에 붓고, 생성된 현탁액을 디클로로메탄으로 추출하였다. 유기층을 분리하고, 1N NaOH 염수로 세척하고, MgSO4상에서 건조시켰다. 용매를 증발시켜 생성물을 수득하고 에탄올(200 ml)로부터 재결정화시켰다.
수율 : 12.6g (72 %).
1H NMR (CDCl3): 7.35 (2H, s, Ar), 4.03 (6H, s, 2CH3).
(3) 4,5-dimethoxybenzene-1,2-diamine (화학식 4) 제조
1,2-dimethoxy-4,5-dinitrobenzene(화합물 3) (4.6 g, 0.0202 mol)과 주석(tin; 11.9 g, 0.1010 mol)을 HCl 100 mL에 용해시키고 용액을 3 시간 동안 가열 환류하였다. 반응을 냉각시키고, 90 mL NaOH(77 g in 90 mL 물) 용액을 조심스럽게 첨가하였다. 생성물을 디클로로메 탄으로 추출하고 유기층을 분리한 후 물로 세척하고 MgSO4으로 건조시키고 농축시켰다.
수율 : 2.9 g (85 %).
1H NMR (CDCl3): 6.37 (2H, s, Ar), 3.79 (6H, s, 2CH3), 3.16 (4H, s, 2NH2).
(4) 5,6-dimethoxybenzo[c]-1,2,5-thiadiazole (화학식 5) 제조
4,5-dimethoxybenzene-1,2-diamine(화합물 4) (2.7 g, 0.0160 mol), N-티오닐아닐린(N-thionylaniline; 3.6 mL, 0.0321 mol) 및 피리딘 (pyridime) 20 mL의 혼합물을 밤새 환류시켰다. 반응물을 냉각시키고 차가운 3 N HCl (100 mL)로 켄칭(quenching)시켰다. 어두운 색의 현탁액을 여과하고 여액을 디클로로메탄 및 에틸 아세테이트(ethyl acetate)로 추출하였다. 유기상을 MgSO4에서 건조시켰다. 용매를 제거 한 후 잔류물을 컬럼(용리액: 디클로로메탄)으로 정제하였다.
수율: 2.1 g (67.7 %).
1H NMR (CDCl3): 7.19 (2H, s, Ar), 4.02 (6H, s, 2CH3).
(5) 4,7-dibromo-5,6-dimethoxybenzo[c]-1,2,5-thiadiazole (화학식 6) 제조
디클로로메탄(60 mL)과 AcOH(30 mL)의 혼합물에 5,6-dimethoxybenzo[c]-1,2,5-thiadiazole (화합물 5) (0.5 g, 0.0025 mol)을 용해 시키고 브롬(bromine; 0.4 ml, 0.018 mol)을 첨가하고 암실에서 48 시간동안 실온에서 교반하였다. 혼합물을 물(150 mL)에 붓고 생성물을 디클로로메탄으로 추출하였다. 유기층을 분리하고 포화 수성 NaHCO3으로 세척 한 다음 포화 수성 Na2S2O3으로 세척하고 MgSO4 상에서 건조시켰다. 용매를 제거한 후 잔류물을 컬럼(용리액: 헥산)으로 정제하였다.
수율: 0.8g (95 %).
1H NMR (CDCl3): 4.05 (6H, s, 2CH3). 13C NMR (CDCl3): 155.03, 150.51, 106.36, 61.85
(6) 4,7-dibromo-5,6-dimethoxybenzo[c]-1,2,5-thiadiazole (화학식 6) 제조
디클로로메탄(60 mL)과 AcOH(30 mL)의 혼합물에 5,6-dimethoxybenzo[c]-1,2,5-thiadiazole (화합물 5) (0.5 g, 0.0025 mol)을 용해시키고 브롬(bromine; 0.4 ml, 0.018 mol)을 첨가하고 암실에서 48 시간동안 실온에서 교반하였다. 혼합물을 물(150 mL)에 붓고 생성물을 디클로로메탄으로 추출하였다. 유기층을 분리하고 포화 수성 NaHCO3으로 세척 한 다음 포화 수성 Na2S2O3으로 세척하고 MgSO4상에서 건조시켰다. 용매를 제거한 후 잔류물을 컬럼(용리액: 헥산)으로 정제하였다.
수율: 0.8g (95 %).
1H NMR (CDCl3): 4.05 (6H, s, 2CH3). 13C NMR (CDCl3): 155.03, 150.51, 106.36, 61.85
(7) 5,6-dimethoxy-4,7-di(thiophen-3-yl)-benzo[c]-1,2,5-thiadiazole (화학식 7의 염료) 의 제조
화합물 6(0.5 g, 0.0015 mol), 1M NaHCO3(15 mL), 디옥산(dioxane; 15 mL)와 3-티오펜보론산(3-thiophenboronic acid; 0.5 g, 0.0039mol)의 혼합물을 환류하에 가열하였다. Pd(PPh3)4 (0.034 g, 0.00003 mol)를 첨가하고 반응물을 질소하에 밤새 환류시켰다. 반응을 실온에서 냉각시키고 잔류 물을 여과한 후 디클로로메탄에 용해시켰다. 용액을 물로 세척하고 유기상을 분리한 후 MgSO4으로 건조시키고 농축시켰다. 잔류물을 메탄올에 용해하고 여과시켰다.
수율 : 0.5 g (90 %).
1H NMR (CDCl3): 8.13-8.12 (2H, d, Ar), 7.85-7.83 (2H, d, Ar), 7.49-7.47 (2H, m, Ar), 3.87 (6H, s, 2CH3).
UV-VIS spectrum : λmax=410nm
*UV-VIS spectrum
UV-Vis Spectrophotometer 를 이용하여 메틸에틸케톤(MEK) 용매에 합성한 염료를 0.001wt% 로 희석하여 380nm 내지 780nm wavelength 영역의 Absorbance(%) 측정하여 최대 흡수 파장을 구하였다.
2.
제조예 1-2: 염료 화합물(7-(2,4-di(piperidin-1-yl)phenyl)benzo[c][1,2,5]oxadiazol-4-amine)의 합성
(1) 1,3-di(piperidin-1-yl)benzene (화학식 9) 제조
압력관에서 1,3-디클로로벤젠(1,3-dichlorobenzene; 0.7 mL, 0.0068 mol)과 피페리딘(piperidine; 2 mL, 0.0204 mol)을 톨루엔(toluene) 30 mL에 용해시켰다. KOt-Bu(3 g, 0.0272 mol)을 첨가하고, 압력 튜브를 밀봉한 후 30시간 동안 135 ℃에서 가열하였다. 반응물을 실온으로 냉각시키고 물 30 mL를 첨가하였다. 수용성상을 분리하고 디클로로메탄으로 추출하였다. 유기상을 MgSO4에서 건조시키고 농축시켰다. 잔류물을 컬럼(용리액: 헥산:EA 95:5)으로 정제하였다.
수율 : 0.8 g (50 %).
1H NMR (CDCl3): 7.15-7.09 (1H, t, Ar), 6.55-7.53 (1H, m, Ar), 6.48-6.44 (2H, d, Ar), 3.14-3.11 (8H, m, 4CH2) 1.74-1.67 (8H, m, 4CH2), 1.59-1.53 (4H, m, 2CH2).
(2) 4-(2,4-di(piperidin-1-yl)phenyl)-7-nitrobenzo[c][1,2,5]-oxadiazole (화학식 10) 제조
4-클로로-7-니트로벤조푸라잔(4-Chlro-7-nitrobenzofurazan; 0.57 g, 0.0028 mol)을 클로로포름(chloroform) 40 mL에 용해시켰다. 트리에틸아민(Triethylamine; 4 mL, 0.0028 mol)과 화합물 8(0.7 g, 0.0028 mol)을 용액에 첨가하였다. 용액의 색깔은 담황색에서 진한 파란색으로 바뀌었다. 반응물을 실온에서 24시간 동안 교반하였다. 물을 첨가하고 유기상을 분리하여 MgSO4에서 건조시키고 농축시켰다. 잔류물을 컬럼(용리액 : 헥산:EA 9:1)으로 정제하였다.
수율 : 0.4g (36 %).
1H NMR (CDCl3): 8.53-8.51 (1H, d, Ar), 8.30-8.27 (1H, d, Ar), 7.68-7.65 (1H, d, Ar), 6.67-6.62 (2H, m, Ar) 3.36-3.33 (4H, m, 2CH2), 2.86-2.82 (4H, m, 2CH2), 1.75-1.64 (6H, m, 3CH2), 1.49-1.45 (6H, m, 3CH2).
(3) 7-(2,4-di(piperidin-1-yl)phenyl)benzo[c][1,2,5]oxadiazol-4-amine (화학식 11의 염료) 제조
4-(2,4-di(piperidin-1-yl)phenyl)-7-nitrobenzo[c][1,2,5]-oxadiazole (화합물 10) (0.4 g, 0.00098 mol)를 AcOH(10 mL)에 용해시켰다. 용액을 80 ℃로 가열시키고 질소하에서 철분말(iron powder; 0.16 g, 0.00294 mol)을 첨가하였다. 혼합물을 80 ℃에서 30 분 동 안 교반하였다. 반응물을 실온으로 냉각시키고 진공 농축시켰다. 잔류 물을 에틸 아세테이트에 용해시키고 포화 수성 NaHCO3으로 세척 하였다. 수성층을 합하고 에틸 아세테이트로 세척하였다. 유기층을 합하고 MgSO4으로 건조시키고 농축시켰다. 잔류 물을 컬럼(용리액: 헥 세인:EA 9:1~7:3)으로 정제하였다. 생성물을 디클로로 메탄에 용해시키고 헥산을 첨가하여 침전시킨 후 여과시켰다.
수율 : 0.1 g (28 %).
1H NMR (CDCl3) : 7.63-7.60 (1H, d, Ar), 7.39-7.37 (1H, d, Ar), 6.67-6.62 (2H, m, Ar), 6.45-6.42 (1H, d, Ar) 4.49 (2H, s, NH2), 3.22-3.18 (4H, t, 2CH2), 2.80-2.78 (4H, m, 2CH2), 1.76-1.69 (4H, m, 2CH2), 1.63-1.57 (2H, m, CH2), 1.38-1.35 (6H, m, 3CH2).
UV-VIS spectrum : λmax=454nm
*UV-VIS spectrum
UV-Vis Spectrophotometer 를 이용하여 메틸에틸케톤(MEK) 용매에 합성한 염료를 0.001wt% 로 희석하여 380nm 내지 780nm wavelength 영역의 Absorbance(%) 측정하여 최대 흡수 파장을 구하였다.
제조예2 : 비반응성 저굴절 물질(P-1)의 제조
1000ml 플라스크에 2,2'-((oxybis(1,1,2,2-tetrafluoroethane-2,1-diyl))bis(oxy))bis(2,2-difluoroethan-1-ol) 20.51 g을 넣어준 후, 테트라하이드로퓨란 500g에 녹여 0 ℃에서 교반하면서 sodium hydride (60 % dispersion in mineral oil) 4.40 g을 여러 차례에 걸쳐 조심스럽게 첨가하였다. 0 ℃에서 20분 교반한 후, 2-methoxyethoxymethyl chloride 12.50 ml를 천천히 dropping 하였다. 1H NMR로 반응물이 모두 소모된 것이 확인되면, 감압하여 반응용매를 모두 제거하였다. 다이클로로메테인 300g으로 3회 추출하여 유기층을 모은 후 magnesium sulfate로 필터한 후 감압하여 다이클로로메테인을 모두 제거하여 순도 95 % 이상의 액상 생성물 29 g을 98 %의 수율로 수득하였다.
제조예3: 실란계 작용기가 분지쇄에 위치한 (메트)아크릴레이트계 (공)중합체의 제조
2L 자켓 반응기에 부틸 아크릴레이트 69.3g, KBM-503(3-메타크릴옥시프로필트리메톡시실란) 20.7g을 넣고, 에틸아세테이트 700g으로 희석하였다. 약 70 ℃로 반응온도를 셋팅하고, 약 1시간 정도 교반을 진행하였다. n-도데실 머캅탄 0.02g을 추가로 넣고, 30분 정도 더 교반을 진행하였다. 이후, 중합개시제인 AIBN 0.06g을 넣고, 반응온도에서 4시간 이상 중합을 진행하여 잔류 아크릴레이트 함량이 1% 미만이 될때까지 유지하여, 실란계 작용기가 분지쇄에 위치한 (메트)아크릴레이트계 (공)중합체 (중량평균분자량 약 900,000, Si-(OR)3 당량 1019 g/equivalent)를 제조하였다.
제조예4 : 실란 가교제의 제조
1000 ml 플라스크에 KBE-9007(3-이소시아네이토프로필트리에톡시실란) 19.79 g, PEG-400 12.80 g과 DBTDL 0.57 g을 넣고, 테트라하이드로퓨란 300g으로 희석하였다. TLC로 반응물이 모두 소모된 것이 확인될 때까지 상온에서 교반한후, 감압하여 반응용매를 모두 제거하였다.
다이클로로메테인 : 메틸알코올 = 30 : 1의 전개액 조건 하에서 컬럼 크로마토그래피를 통해 순도 95 % 이상의 액상 생성물 28 g을 91%의 수율로 분리하여 실란 가교제를 얻었다.
[실시예 및 비교예: 포토폴리머 조성물의 제조]
하기 표1 에 기재된 바와 같이, 상기 제조예3의 실란계 작용기가 분지쇄에 위치한 (메트)아크릴레이트계 (공)중합체, 광반응성 단량체(고굴절 아크릴레이트, 굴절률 1.600, HR6022[미원]), 제조예2의 비반응성 저굴절 물질, 트리부틸 포스페이트(Tributyl phosphate[TBP], 3,3'-Carbonyl bis(7-diethylaminocoumarin) [Aldrich제품], 상기 제조예 1-1 및 1-2의 화합물, Ebecryl P-115 (SK entis), Borate V (Spectra group), Irgacure 250(Onium salt, BASF) 및 메틸아이소뷰틸케톤(MIBK)을 빛을 차단한 상태에서 혼합하고, Paste 믹서로 약 10분간 교반하여 투명한 코팅액을 수득하였다.
상기 코팅액에 상기 제조예 4의 상술한 실란 가교제를 첨가하여 5~10분간 더 교반하였다. 이후, 상기 코팅액에 촉매인 DBTDL을 넣고 약 1분간 교반한 후, meyer bar를 이용하여, 80㎛ 두께의 TAC기재에 7 ㎛ 두께로 코팅하여 40 ℃에서 1시간 건조시켰다.
[실험예: 홀로그래픽 기록]
(1) 상기 실시예 및 비교예 각각에서 제조된 포토폴리머(홀로그램 기록 매체) 코팅면을 slide 글라스에 라미네이트 하고, 기록시 레이저가 유리면을 먼저 통과하도록 고정하였다.
(2) 회절 효율(η) 측정
두 간섭광(참조광 및 물체광)의 간섭을 통해서 홀로그래픽을 기록하며, 투과형 기록은 두 빔을 샘플의 동일면에 입사하였다. 두 빔의 입사각에 따라 회절 효율은 변하게 되며, 두 빔의 입사각이 동일한 경우 non-slanted가 된다. non-slanted 기록은 두빔의 입사각이 법선 기준으로 동일하므로, 회절 격자는 필름에 수직하게 생성된다.
460nm 파장의 레이저 또는 473nm 파장의 레이저를 사용하여 투과형 non-slanted 방식으로 기록(2θ=45°)하며, 하기 일반식1로 회절 효율(η)을 계산하였다.
[일반식1]
상기 일반식1에서, η은 회절 효율이고, PD는 기록후 샘플의 회절된 빔의 출력량(mW/㎠)이고, PT는 기록한 샘플의 투과된 빔의 출력량(mW/㎠)이다.
(3) 굴절률 변조값(n) 측정
투과형 홀로그램의 Lossless Dielectric grating은 하기 일반식2로부터 굴절율 변조값(△n)을 계산할 수 있다.
[일반식 2]
상기 일반식2에서, d는 포토폴리머층의 두께이고, △n은 굴절율 변조값이며, η(DE)은 회절 효율이고, λ는 기록 파장이다.
구분 | 실시예1 | 실시예2 | 실시예3 | 실시예4 | 비교예1 | 비교예2 | |
(메트)아크릴레이트계 공중합체 | 제조예3 | 21.5 | 21.5 | 21.5 | 21.5 | 21.5 | 21.5 |
선형실란가교제 | 제조예4 | 6.1 | 6.1 | 6.1 | 6.1 | 6.1 | 6.1 |
광반응성 단량체 | HR6022 | 40.2 | 40.2 | 40.2 | 40.2 | 40.2 | 40.2 |
Dye | 3,3'-Carbonyl bis(7- diethylaminocoumarin) |
0.3 | 0.3 | ||||
제조예 1-1 | 0.3 | 0.3 | |||||
제조예 1-2 | 0.3 | 0.3 | |||||
개시제 | Amine (Ebecryl P-115) | 1.5 | 1.5 | ||||
Borate salt (Borate V) | 0.2 | 0.2 | 0.2 | ||||
Onium salt (Irgacure 250) | 0.1 | 0.1 | 0.1 | 0.1 | 0.1 | 0.1 | |
비만응성 저굴절 물질 | 제조예2 | 30 | 30 | 30 | 30 | 30 | 30 |
촉매 | DBTDL(dibutyltin dilaurate) | 0.02 | 0.02 | 0.02 | 0.02 | 0.02 | 0.02 |
첨가제 | BYK3500 | 0.5 | 0.5 | 0.5 | 0.5 | 0.5 | 0.5 |
용매 | MIBK | 295 | 295 | 295 | 296 | 300 | 300 |
코팅 두께(단위 : ㎛) | 8 | 8 | 8 | 8 | 8 | 8 | |
기록 시간(초) | 10 | 10 | 10 | 30 | 30 | 45 | |
△n | 0.028 | 0.027 | 0.025 | 0.030 | 0.020 | 0.022 |
상기 표 1 에 나타난 바와 같이, 실시예 1 내지 4의 홀로그램 기록 매체는 8㎛의 두께에서 0.025 이상의 굴절률 변조값(△n)을 구현할 수 있다는 점이 확인되었다. 이에 반해서, 비교예 1 내지 3의 홀로그램 기록 매체는 실시예에 비해서 상대적으로 낮은 회절 효율을 갖는다는 점이 확인되었다.
즉, 실시예 1 내지 4 에 대한 홀로그램 기록(460 ㎚ Laser)후의 평가 결과, 제조예 1-1 및 1-2에서 얻어진 화합물를 사용하면 상대적으로 높은 수준의 굴절율 변조값(△n)을 구현하며, 비교예에 사용된 염료 대비 상대적으로 빠른 반응 속도를 가져서 기록 시간을 단축할 수 있다는 점을 알 수 있다.
Claims (16)
- 고분자 매트릭스 또는 이의 전구체;
하기 화학식1의 화합물을 포함하는 염료;
광반응성 단량체; 및
광개시제;를 포함하는, 홀로그램 기록용 포토폴리머 조성물:
[화학식1]
상기 화학식1에서, X는 산소 또는 황이고,
R1 내지 R4는 각각 수소; 탄소수 1 내지 20의 알킬기; 탄소수 1 내지 20의 알콕시기; 탄소수 4 내지 20의 사이클로알킬기; 탄소수 6 내지 20의 방향족 탄화수소기; 시아노아크릴레이트 또는 이의 에스터기가 결합된 탄소수 6 내지 20의 방향족 탄화수소기; 아민기; 할로겐;
산소, 황 또는 질소를 1이상 포함하는 탄소수 4 내지 20의 지환족 또는 방향족 헤테로 고리; 또는
산소, 황 또는 질소를 1이상 포함하는 탄소수 4 내지 20의 지환족 또는 방향족 헤테로 고리가 1이상 치환된 탄소수 4 내지 20의 사이클로알킬기 또는 탄소수 6 내지 20의 방향족 탄화수소기; 이다.
- 제1항에 있어서,
상기 화학식1에서, R1 내지 R4 중 적어도 하나는 산소, 황 또는 질소를 1이상 포함하는 탄소수 4 내지 20의 지환족 또는 방향족 헤테로 고리; 또는
산소, 황 또는 질소를 1이상 포함하는 탄소수 4 내지 20의 지환족 또는 방향족 헤테로 고리가 1이상 치환된 탄소수 4 내지 20의 사이클로알킬기 또는 탄소수 6 내지 20의 방향족 탄화수소기;인,
포토폴리머 조성물.
- 제1항에 있어서,
상기 화학식1에서,
상기 R2 및 R3는 수소, 탄소수 1 내지 20의 알킬기, 또는 할로겐이고,
상기 R1 및 R4 중 하나는 아민기이고, 다른 하나는 R1 내지 R4 중 적어도 다른 하나는 산소, 황 또는 질소를 1이상 포함하는 탄소수 4 내지 20의 지환족 또는 방향족 헤테로 고리; 또는 산소, 황 또는 질소를 1이상 포함하는 탄소수 4 내지 20의 지환족 또는 방향족 헤테로 고리가 1이상 치환된 탄소수 4 내지 20의 사이클로알킬기 또는 탄소수 6 내지 20의 방향족 탄화수소기;인,
포토폴리머 조성물.
- 제1항에 있어서,
상기 화학식1에서, 상기 R2 및 R3는 각각 탄소수 1 내지 5의 알콕시기이고,
상기 R1 및 R4는 각각 R1 내지 R4 중 적어도 다른 하나는 산소, 황 또는 질소를 1이상 포함하는 탄소수 4 내지 20의 지환족 또는 방향족 헤테로 고리; 또는 산소, 황 또는 질소를 1이상 포함하는 탄소수 4 내지 20의 지환족 또는 방향족 헤테로 고리가 1이상 치환된 탄소수 4 내지 20의 사이클로알킬기 또는 탄소수 6 내지 20의 방향족 탄화수소기;인,
포토폴리머 조성물.
- 제1항에 있어서,
상기 고분자 매트릭스 또는 이의 전구체는 1) 1이상의 이소시아네이트기를 포함한 화합물과 폴리올 간의 반응 생성물; 또는 2) 실란계 작용기가 분지쇄에 위치하는 (메트)아크릴레이트계 (공)중합체 및 실란 가교제를 포함하는 고분자 매트릭스;를 포함하는, 포토폴리머 조성물.
- 제5항에 있어서,
상기 실란 가교제는 중량평균분자량이 100 내지 2000인 선형의 폴리에테르 주쇄 및 상기 주쇄의 말단 또는 분지쇄로 결합한 실란계 작용기를 포함하는, 포토폴리머 조성물.
- 제5항에 있어서,
상기 실란계 작용기가 분지쇄에 위치하는 (메트)아크릴레이트계 (공)중합체는
실란계 작용기가 분지쇄에 위치하는 (메트)아크릴레이트 반복단위 및 (메트)아크릴레이트 반복단위를 포함하고,
100,000 내지 1,000,000의 중량평균분자량을 갖는, 포토폴리머 조성물.
- 제1항에 있어서,
상기 광반응성 단량체는 다관능 (메트)아크릴레이트 단량체, 또는 단관능 (메트)아크릴레이트 단량체를 포함하는, 포토폴리머 조성물.
- 제1항에 있어서,
상기 고분자 매트릭스 또는 이의 전구체 1 중량% 내지 80중량%; 상기 광반응성 단량체 1 중량% 내지 80중량%; 상기 염료 0.0001 내지 10중량%; 및 광개시제 0.1 중량% 내지 20중량%;를 포함하는, 포토폴리머 조성물.
- 제1항에 있어서,
상기 포토폴리머 조성물은 촉매, 포스페이트계 화합물 및 저굴절율 불소계 화합물로 이루어진 군에서 선택된 1종 이상을 더 포함하는, 홀로그램 기록 매체.
- 제10항에 있어서,
상기 저굴절율 불소계 화합물은 에테르기, 에스터기 및 아마이드기로 이루어진 군에서 선택된 1종 이상의 작용기 및 2이상의 다이플루오로메틸렌기를 포함하는, 홀로그램 기록 매체.
- 제1항의 포토폴리머 조성물로부터 제조된 홀로그램 기록 매체.
- 고분자 매트릭스 또는 이의 전구체; 하기 화학식1의 화합물을 포함하는 염료; 및 광반응성 단량체를 포함하는 코팅층을 포함하고,
5㎛ 내지 30 ㎛의 두께 범위에서 0.023이상의 굴절율 변조값(n) 을 갖는, 홀로그램 기록 매체:
[화학식1]
상기 화학식1에서, X는 산소 또는 황이고,
R1 내지 R4는 각각 수소; 탄소수 1 내지 20의 알킬기; 탄소수 1 내지 20의 알콕시기; 탄소수 4 내지 20의 사이클로알킬기; 탄소수 6 내지 20의 방향족 탄화수소기; 시아노아크릴레이트 또는 이의 에스터기가 결합된 탄소수 6 내지 20의 방향족 탄화수소기; 아민기; 할로겐;
산소, 황 또는 질소를 1이상 포함하는 탄소수 4 내지 20의 지환족 또는 방향족 헤테로 고리; 또는
산소, 황 또는 질소를 1이상 포함하는 탄소수 4 내지 20의 지환족 또는 방향족 헤테로 고리가 1이상 치환된 탄소수 4 내지 20의 사이클로알킬기 또는 탄소수 6 내지 20의 방향족 탄화수소기; 이다.
- 제13항에 있어서,
상기 코팅층은 에테르기, 에스터기 및 아마이드기로 이루어진 군에서 선택된 1종 이상의 작용기 및 2이상의 다이플루오로메틸렌기를 포함하는 저굴절율 불소계 화합물을 더 포함하는, 홀로그램 기록 매체:
- 제12항 또는 제13항의 홀로그램 기록 매체를 포함한 광학 소자.
- 가간섭성 광원에 의해 제1항의 포토폴리머 조성물에 포함된 광반응성 단량체를 선택적으로 중합시키는 단계를 포함하는, 홀로그래픽 기록 방법.