KR101966869B1 - 이형필름 박리안정성 측정방법 및 이형필름 적층체 - Google Patents

이형필름 박리안정성 측정방법 및 이형필름 적층체 Download PDF

Info

Publication number
KR101966869B1
KR101966869B1 KR1020140147318A KR20140147318A KR101966869B1 KR 101966869 B1 KR101966869 B1 KR 101966869B1 KR 1020140147318 A KR1020140147318 A KR 1020140147318A KR 20140147318 A KR20140147318 A KR 20140147318A KR 101966869 B1 KR101966869 B1 KR 101966869B1
Authority
KR
South Korea
Prior art keywords
releasing
release
speed
force
releasing force
Prior art date
Application number
KR1020140147318A
Other languages
English (en)
Other versions
KR20160050144A (ko
Inventor
박준형
김장순
Original Assignee
주식회사 엘지화학
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 주식회사 엘지화학 filed Critical 주식회사 엘지화학
Priority to KR1020140147318A priority Critical patent/KR101966869B1/ko
Priority to PCT/KR2015/011340 priority patent/WO2016068559A1/ko
Priority to CN201580058061.6A priority patent/CN107109149B/zh
Priority to JP2017518904A priority patent/JP6804094B2/ja
Priority to US15/522,204 priority patent/US10562265B2/en
Priority to TW104135352A priority patent/TWI652466B/zh
Publication of KR20160050144A publication Critical patent/KR20160050144A/ko
Priority to JP2018236260A priority patent/JP6821237B2/ja
Application granted granted Critical
Publication of KR101966869B1 publication Critical patent/KR101966869B1/ko

Abstract

점착층 및 상기 점착층의 양면에 경박리 이형필름 및 중박리 이형필름이 부착된 적층체를 마련하는 단계; 0.3 내지 3.0 m/min의 박리 속도에서 상기 경박리 이형필름과 상기 점착층의 이형력을 측정하여 경박리 저속 이형력을 도출하는 단계; 0.3 내지 3.0 m/min의 박리 속도에서 상기 중박리 이형필름과 상기 점착층의 이형력을 측정하여 중박리 저속 이형력을 도출하는 단계; 10 내지 30m/min의 박리 속도에서 상기 경박리 이형필름과 상기 점착층의 이형력을 측정하여 경박리 고속 이형력을 도출하는 단계; 10 내지 30m/min의 박리 속도에서 상기 중박리 이형필름과 상기 점착층의 이형력을 측정하여 중박리 고속 이형력을 도출하는 단계; 및 하기 일반식 1 및 2에 의하여 고속 이형력 밸런스 및 저속 이형력 밸런스를 측정하는 단계;를 포함하는 이형필름 박리안정성 측정방법을 제공한다.
[일반식 1]
고속 이형력 밸런스 = 중박리 고속 이형력/경박리 고속 이형력
[일반식 2]
저속 이형력 밸런스 = 중박리 저속 이형력/경박리 저속 이형력
또한, 점착층 및 상기 점착층의 양면에 경박리 이형필름 및 중박리 이형필름을 포함하고, 상기 이형필름 박리안정성 측정방법에 의해 측정된 고속 이형력 밸런스 및 저속 이형력 밸런스가 모두 1.5 내지 5.0인 적층체를 제공한다.

Description

이형필름 박리안정성 측정방법 및 이형필름 적층체 {THE METHOD FOR MESURING PEELING STABILITY OF THE RELEASE FILM AND THE RELEASE FILM LAMINATE}
이형필름의 박리안정성을 측정하는 방법 및 이형필름 적층체에 관한 것이다.
이형필름은 제품의 취급 및 운반을 용이하게 하며, 손쉽게 분리될 수 있는 필름으로 다양한 용도로 활용되고 있다. 예를 들어, 이러한 이형필름은 점착필름의 캐리어 필름으로서 사용될 수 있다. 이 때, 복수의 이형필름을 사용하는 경우 각각의 이형력 차이에 따라 점착제 들뜸 현상이 발생하거나 이형필름으로 점착제가 전이되는 문제가 발생할 수 있다. 따라서, 점착필름의 캐리어 용도로서 복수의 이형필름 간의 이형력이 균형을 이루어 점착제 들뜸 현상이 발생하지 않는 박리안정성을 갖는 이형필름을 선별하는 검증 수단이 필요한 실정이다.
본 발명의 일 구현예는 신뢰도 및 정확성이 높은 이형필름의 박리안정성 측정방법을 제공한다.
본 발명의 다른 구현예는 상기 이형필름의 박리안정성 측정방법에 의해 측정된 박리안정성이 우수한 이형필름을 포함하는 적층체를 제공한다.
본 발명의 일 구현예에서, 점착층 및 상기 점착층의 양면에 경박리 이형필름 및 중박리 이형필름이 부착된 적층체를 마련하는 단계; 약 0.3 내지 약 3.0 m/min의 박리 속도에서 상기 경박리 이형필름과 상기 점착층의 이형력을 측정하여 경박리 저속 이형력을 도출하는 단계; 약 0.3 내지 약 3.0 m/min의 박리 속도에서 상기 중박리 이형필름과 상기 점착층의 이형력을 측정하여 중박리 저속 이형력을 도출하는 단계; 약 10 내지 약 30 m/min의 박리 속도에서 상기 경박리 이형필름과 상기 점착층의 이형력을 측정하여 경박리 고속 이형력을 도출하는 단계; 약 10 내지 약 30 m/min의 박리 속도에서 상기 중박리 이형필름과 상기 점착층의 이형력을 측정하여 중박리 고속 이형력을 도출하는 단계; 및 하기 일반식 1 및 2에 의하여 고속 이형력 밸런스 및 저속 이형력 밸런스를 측정하는 단계;를 포함하는 이형필름 박리안정성 측정방법을 제공한다.
[일반식 1]
고속 이형력 밸런스 = 중박리 고속 이형력/경박리 고속 이형력
[일반식 2]
저속 이형력 밸런스 = 중박리 저속 이형력/경박리 저속 이형력
상기 이형필름 박리안정성 측정방법은 상기 경박리 고속 이형력 및 상기 경박리 저속 이형력을 이용하여 하기 일반식 3에 의해 경박리 속도 변화율을 측정하는 단계; 및 상기 중박리 고속 이형력 및 상기 중박리 저속 이형력을 이용하여 하기 일반식 4에 의해 중박리 속도 변화율을 측정하는 단계;를 더 포함할 수 있다.
[일반식 3]
경박리 속도 변화율(%) = (경박리 고속 이형력 - 경박리 저속 이형력)/ 경박리 저속 이형력 ｘ100
[일반식 4]
중박리 속도 변화율(%) = (중박리 고속 이형력 - 중박리 저속 이형력)/ 중박리 저속 이형력 ｘ100
상기 적층체를 마련하는 단계는, 상기 적층체를 약 20 내지 약 100℃에서 약 0.5 내지 약 720 시간 동안 보관하는 단계를 포함할 수 있다.
상기 경박리 이형필름 및 상기 중박리 이형필름은 각각 이형층 및 기재층의 적층 구조를 포함할 수 있다.
상기 이형층은 실리콘계 이형제, 멜라민계 이형제, 폴리올레핀계 이형제, 에폭시계 이형제, 아크릴계 이형제, 불소계 이형제, 셀룰로오스계 이형제, 파라핀계 이형제, 에폭시-멜라민계 이형제 및 이들의 조합으로 이루어진 군으로부터 선택된 적어도 하나를 포함할 수 있다.
상기 기재층은 폴리에틸렌테레프탈레이트(PET), 폴리에틸렌(PE), 폴리비닐알콜(PVA) 및 이들의 조합으로 이루어진 군으로부터 선택된 적어도 하나를 포함할 수 있다.
상기 점착층은 아크릴계 점착제, 실리콘계 점착제, 고무계 점착제 및 이들의 조합으로 이루어진 군으로부터 선택된 적어도 하나를 포함할 수 있다.
본 발명의 다른 구현예에서, 점착층 및 상기 점착층의 양면에 경박리 이형필름 및 중박리 이형필름을 포함하고, 제1항에 따른 이형필름 박리안정성 측정방법에 의해 측정된 고속 이형력 밸런스 및 저속 이형력 밸런스가 모두 약 1.5 내지 약 5.0인 적층체를 제공한다.
상기 적층체에서, 상기 경박리 이형필름의 경박리 속도 변화율은 약 100% 내지 약 300%이고, 상기 중박리 이형필름의 중박리 속도 변화율은 약 200% 내지 약 400%일 수 있다.
상기 적층체에서, 상기 경박리 이형필름의 경박리 저속 이형력은 약 10 내지 약 50 gf/50mm이고, 상기 중박리 이형필름의 중박리 저속 이형력은 약 50 내지 약 200 gf/50mm일 수 있다.
상기 적층체에서, 상기 경박리 이형필름의 경박리 고속 이형력은 약 10 내지 약 100 gf/50mm이고, 상기 중박리 이형필름의 중박리 고속 이형력은 약 50 내지 약 200 gf/50mm일 수 있다.
상기 이형필름 박리안정성 측정방법을 통하여 복수의 이형필름 간의 박리안정성이 우수한지 판단함에 있어서, 효율성을 확보할 수 있고 신뢰성 및 정확성이 높은 결과를 얻을 수 있다.
상기 이형필름 박리안정성 측정방법에 의해 측정된 박리안정성이 우수한 이형필름을 포함하는 적층체는 점착필름의 캐리어 용도로서 적합한 물성을 가지며, 상기 점착필름을 목표 물품에 적용 시 불량률을 저감시킬 수 있다.
도 1은 본 발명의 일 구현예에 따른 적층체의 단면을 개략적으로 나타낸 것이다.
도 2는 경박리 이형필름의 단면을 개략적으로 나타낸 것이다.
본 발명의 이점 및 특징, 그리고 그것들을 달성하는 방법은 후술하는 실시예들을 참조하면 명확해질 것이다 그러나, 본 발명은 이하에서 개시되는 실시예들에 한정되는 것이 아니라 서로 다른 다양한 형태로 구현될 것이며, 단지 본 실시예들은 본 발명의 개시가 완전하도록 하며, 본 발명이 속하는 기술분야에서 통상의 지식을 가진 자에게 발명의 범주를 완전하게 알려주기 위해 제공되는 것이며, 본 발명은 청구항의 범주에 의해 정의될 뿐이다. 명세서 전체에 걸쳐 동일 참조 부호는 동일 구성요소를 지칭한다.
이형필름 박리안정성 측정방법
본 발명의 일 구현예에서, 점착층 및 상기 점착층의 양면에 경박리 이형필름 및 중박리 이형필름이 부착된 적층체를 마련하는 단계; 약 0.3 내지 약 3.0 m/min의 박리 속도에서 상기 경박리 이형필름과 상기 점착층의 이형력을 측정하여 경박리 저속 이형력을 도출하는 단계; 약 0.3 내지 약 3.0 m/min의 박리 속도에서 상기 중박리 이형필름과 상기 점착층의 이형력을 측정하여 중박리 저속 이형력을 도출하는 단계; 약 10 내지 약 30 m/min의 박리 속도에서 상기 경박리 이형필름과 상기 점착층의 이형력을 측정하여 경박리 고속 이형력을 도출하는 단계; 약 10 내지 약 30 m/min의 박리 속도에서 상기 중박리 이형필름과 상기 점착층의 이형력을 측정하여 중박리 고속 이형력을 도출하는 단계; 및 하기 일반식 1 및 2에 의하여 고속 이형력 밸런스 및 저속 이형력 밸런스를 측정하는 단계;를 포함하는 이형필름 박리안정성 측정방법을 제공한다.
[일반식 1]
고속 이형력 밸런스 = 중박리 고속 이형력/경박리 고속 이형력
[일반식 2]
저속 이형력 밸런스 = 중박리 저속 이형력/경박리 저속 이형력
일반적으로, 이형필름은 점착필름의 점착층 캐리어 용도로 사용되며 점착층의 양면에 상호 이형력이 상이한 2개의 이형필름이 부착되어 유통 및 운반될 수 있다. 이 경우, 2개의 이형필름이 적절한 이형력 균형성을 만족해야 점착층의 들뜸 현상을 방지할 수 있다.
이러한 복수의 이형필름이 하나의 점착층에 대하여 적절한 이형력 균형성을 만족하는지 판단하기 위하여 상기 이형필름 박리안정성 측정방법은 점착층 및 상기 점착층의 양면에 경박리 이형필름 및 중박리 이형필름이 부착된 적층체를 마련하여, 상기 적층체에 대한 박리안정성을 측정할 수 있다.
도 1은 상기 적층체(100)의 단면을 개략적으로 나타낸 것이다. 상기 적층체(100)는 경박리 이형필름(10), 점착층(30) 및 중박리 이형필름(20)이 순차적으로 적층된 구조이며, 상기 경박리 이형필름(10) 및 상기 중박리 이형필름(20)은 상기 점착층(30)에 대하여 상이한 이형력을 갖는다.
구체적으로, 상기 경박리 이형필름(10)은 상기 중박리 이형필름(20)에 비하여 상기 점착층(30)에 대한 이형력이 낮은 것이며, 두 이형필름이 적절한 이형력 밸런스(balance)를 갖는 경우, 박리안정성이 우수한 것을 나타낸다.
상기 이형필름 박리안정성 측정방법은 상기 경박리 이형필름 및 상기 중박리 이형필름에 대하여, 저속 이형력을 도출하는 단계를 포함할 수 있다.
구체적으로, 상기 측정방법은 약 0.3 내지 약 3.0 m/min의 박리 속도에서 상기 경박리 이형필름과 상기 점착층의 이형력을 측정하여 경박리 저속 이형력을 도출하는 단계; 및 약 0.3 내지 약 3.0 m/min의 박리 속도에서 상기 중박리 이형필름과 상기 점착층의 이형력을 측정하여 중박리 저속 이형력을 도출하는 단계;를 포함할 수 있다.
상기 경박리 이형필름 및 중박리 이형필름의 저속 이형력은 각각 약 0.3 내지 약 3.0 m/min의 박리 속도에서 측정될 수 있고, 구체적으로 약 0.3 내지 약 1.0 m/min의 박리 속도에서 측정될 수 있다. 각 이형필름의 저속 이형력이 상기 속도 범위의 박리 속도에서 측정됨으로써 실질적으로 제품화 되었을 때, 이형필름의 박리안정성에 대한 신뢰성 및 정확성이 확보되는 결과를 얻을 수 있다.
또한, 상기 이형필름 박리안정성 측정방법은 상기 경박리 이형필름 및 상기 중박리 이형필름에 대하여, 고속 이형력을 도출하는 단계를 포함할 수 있다.
구체적으로, 상기 측정방법은 약 10 내지 약 30 m/min의 박리 속도에서 상기 경박리 이형필름과 상기 점착층의 이형력을 측정하여 경박리 고속 이형력을 도출하는 단계; 및 약 10 내지 약 30 m/min의 박리 속도에서 상기 중박리 이형필름과 상기 점착층의 이형력을 측정하여 중박리 고속 이형력을 도출하는 단계;를 포함할 수 있다.
상기 경박리 이형필름 및 중박리 이형필름의 고속 이형력은 각각 약 10 내지 약 30 m/min의 박리 속도에서 측정될 수 있고, 구체적으로 약 20 내지 약 30 m/min의 박리 속도에서 측정될 수 있다. 각 이형필름의 고속 이형력이 상기 속도 범위의 박리 속도에서 측정됨으로써 실질적으로 제품화 되었을 때, 이형필름의 박리안정성에 대한 신뢰성 및 정확성이 확보되는 결과를 얻을 수 있다.
상기 이형필름 박리안정성 측정방법은 각 이형필름에 대하여 저속 이형력 및 고속 이형력을 모두 도출하는 단계를 포함하며, 상기 일반식 1 및 2에 의하여 고속 이형력 밸런스 및 저속 이형력 밸런스를 모두 측정하는 단계를 포함할 수 있다.
상기 측정방법이 고속 이형력 밸런스 및 저속 이형력 밸런스를 모두 측정함으로써, 실제 제품에 적용 및 사용되는 경우에 있어서 실질적으로 신뢰성 및 정확성이 높은 결과를 확보할 수 있다.
상기 이형필름 박리안정성 측정방법은 상기 경박리 고속 이형력 및 상기 경박리 저속 이형력을 이용하여 하기 일반식 3에 의해 경박리 속도 변화율을 측정하는 단계; 및 상기 중박리 고속 이형력 및 상기 중박리 저속 이형력을 이용하여 하기 일반식 4에 의해 중박리 속도 변화율을 측정하는 단계;를 더 포함할 수 있다.
[일반식 3]
경박리 속도 변화율(%) = (경박리 고속 이형력 - 경박리 저속 이형력)/ 경박리 저속 이형력 ｘ100
[일반식 4]
중박리 속도 변화율(%) = (중박리 고속 이형력 - 중박리 저속 이형력)/ 중박리 저속 이형력 ｘ100
상기 측정방법이 상기 일반식 3 및 4에 의해 속도 변화율을 측정하는 단계를 더 포함함으로써, 상기 경박리 이형필름 및 상기 중박리 이형필름의 이형력 밸런스에 대한 더 자세하고 정확한 정보를 얻을 수 있으며, 이형필름의 박리안정성에 대하여 더 신뢰할 수 있고, 더 정확한 결과를 확보할 수 있다는 점에서 유리할 수 있다.
상기 이형필름 박리안정성 측정방법에 있어서, 상기 적층체를 마련하는 단계는, 상기 적층체를 약 20℃ 내지 약 100℃에서 약 0.5 시간 내지 약 720 시간 동안 보관하는 단계를 포함할 수 있다. 상기 적층체를 상기 조건에서 보관함으로써, 저속 이형력 및 고속 이형력 측정 결과의 신뢰성을 높인다는 점에서 유리할 수 있다.
도 2는 상기 경박리 이형필름(10)의 단면을 개략적으로 나타낸 것이다.
도 1 및 도 2를 참조할 때, 상기 경박리 이형필름(10)은 기재층(11) 및 이형층(12) 적층 구조를 포함할 수 있다. 이 때, 상기 적층체(100)는 상기 점착층(30)의 일면에 상기 경박리 이형필름의 이형층(12)이 부착된 것일 수 있다.
상기 이형층(12)은 구체적으로 실리콘계 이형제, 멜라민계 이형제, 폴리올레핀계 이형제, 에폭시계 이형제, 아크릴계 이형제, 불소계 이형제, 셀룰로오스계 이형제, 파라핀계 이형제, 에폭시-멜라민계 이형제 및 이들의 조합으로 이루어진 군으로부터 선택된 적어도 하나를 포함할 수 있다.
상기 중박리 이형필름(20)의 경우, 상기 경박리 이형필름(10)과 동일한 적층 구조를 가질 수 있다. 즉, 상기 중박리 이형필름(20)도 기재층 및 이형층의 적층 구조를 포함할 수 있고, 이 때 상기 적층체(100)는 상기 경박리 이형필름의 이형층(12)이 부착된 일면과 다른 일면에 상기 중박리 이형필름의 이형층이 부착된 것일 수 있다.
예를 들어, 상기 경박리 이형필름의 이형층 및 상기 중박리 이형필름의 이형층은 각각 실리콘계 이형제를 포함할 수 있다. 이 경우, 상기 이형필름 박리안정성 측정방법에 따라 얻어진 결과가 높은 신뢰성 및 정확성을 확보하기에 유리할 수 있다.
또한, 상기 경박리 이형필름의 기재층 및 상기 중박리 이형필름의 기재층은 각각 종이, 부직포, 폴리에틸렌테레프탈레이트(PET), 폴리에틸렌(PE), 폴리비닐알콜(PVA) 및 이들의 조합으로 이루어진 군으로부터 선택된 적어도 하나를 포함할 수 있다. 예를 들어, 상기 경박리 이형필름의 기재층 및 상기 중박리 이형필름의 기재층은 폴리에틸렌테레프탈레이트(PET) 또는 폴리에틸렌(PE)을 포함할 수 있고, 이 경우 우수한 내열성을 가지는바, 상기 이형필름 박리안정성 측정방법을 통하여 정확성 및 신뢰성 높은 결과를 얻을 수 있다.
상기 이형필름을 이용하여 운반 또는 유통할 수 있는 점착층은 구체적으로, 아크릴계 점착제, 실리콘계 점착제, 고무계 점착제 및 이들의 조합으로 이루어진 군으로부터 선택된 적어도 하나를 포함할 수 있으며, 이에 제한되는 것은 아니다.
예를 들어, 상기 점착층은 아크릴계 점착제를 포함할 수 있으며 이 경우 상기 이형필름 박리안정성 측정방법에 의하여 박리안정성에 대한 정확한 결과를 도출할 수 있다는 점에서 유리할 수 있다.
적층체
본 발명의 다른 구현예는 점착층 및 상기 점착층의 양면에 경박리 이형필름 및 중박리 이형필름을 포함하고, 상기 이형필름 박리안정성 측정방법에 의해 측정된 고속 이형력 밸런스 및 저속 이형력 밸런스가 모두 약 1.5 내지 약 5.0인 적층체를 제공한다.
상기 고속 이형력 밸런스 및 저속 이형력 밸런스는 모두 약 1.5 내지 약 5.0일 수 있고, 구체적으로 약 1.7 내지 약 3.0일 수 있다. 상기 고속 이형력 밸런스 및 저속 이형력 밸런스가 모두 상기 범위를 만족하는 경우에 상기 적층체의 이형필름이 우수한 박리안정성을 구현할 수 있고, 상기 경박리 이형필름만을 제거하는 경우 상기 점착층이 중박리 이형필름과 박리되지 않으며, 점착층이 들뜨거나, 점착제가 이형필름에 전이되는 문제를 방지할 수 있다.
또한, 상기 경박리 이형필름의 경박리 속도 변화율은 약 300% 이하일 수 있고, 예를 들어, 약 100% 내지 약 300%일 수 있다. 또한, 상기 중박리 이형필름의 중박리 속도 변화율은 200% 이상일 수 있고, 예를 들어, 약 200% 내지 400%일 수 있다. 상기 경박리 속도 변화율 및 상기 중박리 속도 변화율은 상기 일반식 3 및 4를 이용해 도출할 수 있다.
상기 경박리 이형필름 및 중박리 이형필름이 상기 범위의 고속 이형력 밸런스 및 저속 이형력 밸런스를 만족함과 동시에, 상기 범위의 경박리 속도 변화율 및 상기 범위의 중박리 속도 변화율을 나타냄으로써, 상기 적층체의 이형필름이 점착층의 들뜸현상 또는 전이현상 없이 우수한 박리안정성을 확보할 수 있다.
구체적으로, 상기 경박리 이형필름의 경박리 저속 이형력은 약 10 내지 약 50 gf/50mm일 수 있고, 상기 중박리 이형필름의 중박리 저속 이형력은 약 50 내지 약 200 gf/50mm일 수 있다. 즉, 상기 경박리 이형필름 및 중박리 이형필름에 대하여 약 0.3 내지 약 3.0 m/min의 박리 속도로 측정한 이형력이 각각 상기 범위를 만족할 수 있다. 상기 경박리 저속 이형력 및 상기 중박리 저속 이형력이 상기 범위를 만족함으로써, 상기 경박리 이형필름이 저절로 박리되는 문제가 발생하지 않으면서도 일정 힘에 의해 박리시키기 용이하고, 상기 경박리 이형필름만을 박리할 때 상기 중박리 이형필름이 점착층에 단단하게 결합되어 점착층 들뜸 현상의 문제를 방지할 수 있다.
또한, 상기 경박리 이형필름의 경박리 고속 이형력은 약 10 내지 약 100 gf/50mm일 수 있고, 상기 중박리 이형필름의 중박리 고속 이형력은 약 50 내지 약 200 gf/50mm일 수 있다. 즉, 상기 경박리 이형필름 및 중박리 이형필름에 대하여 약 10 내지 약 30 m/min의 박리 속도로 측정한 이형력이 각각 상기 범위를 만족할 수 있다. 상기 경박리 고속 이형력 및 상기 중박리 고속 이형력이 상기 범위를 만족함으로써, 상기 경박리 이형필름이 저절로 박리되는 문제가 발생하지 않으면서도 일정 힘에 의해 박리시키기 용이하고, 상기 경박리 이형필름만을 박리할 때 상기 중박리 이형필름이 점착층에 단단하게 결합되어 점착층 들뜸 현상의 문제를 방지할 수 있다.
이하에서는 본 발명의 구체적인 실시예들을 제시한다. 다만, 하기에 기재된 실시예들은 본 발명을 구체적으로 예시하거나 설명하기 위한 것에 불과하며, 이로서 본 발명이 제한되어서는 아니된다.
실시예 1
아크릴계 점착층 및 상기 점착층의 양면에 경박리 이형필름 및 중박리 이형필름이 부착된 적층체를 마련하였다. 상기 경박리 이형필름 및 중박리 이형필름의 각 이형층 및 기재층의 성분 및 함량은 하기 표 1에 기재된 바와 같다. 이어서, 상기 경박리 이형필름 및 중박리 이형필름에 대하여, 0.3 m/min의 박리 속도로 이형력을 측정하여 경박리 저속 이형력(A) 및 중박리 저속 이형력(B)을 측정하였다. 이어서, 동일한 적층체에 대하여 30 m/min의 박리 속도로 이형력을 측정하여 경박리 고속 이형력(C) 및 중박리 고속 이형력(D)을 측정하였다. 이어서, B/A 및 D/C의 값을 계산하여 저속 이형력 밸런스 및 고속 이형력 밸런스를 측정하였다. 또한, (C-A)/A ｘ 100의 식을 이용하여 경박리 속도 변화율(%)을 측정하였고, (D-B)/B ｘ 100의 식을 이용하여 중박리 속도 변화율(%)을 측정하였다. 그 결과는 하기 표 3에 기재된 바와 같다.
폴리디메틸실록산(PDMS) 실리콘 레진 Pt계 촉매
경박리
이형필름		 이형층 To 100 - 5
기재층 100㎛ PET 필름
중박리
이형필름		 이형층 To 100 20 5
기재층 100㎛ PET 필름
.
실시예 2
상기 경박리 이형필름 및 중박리 이형필름의 각 이형층 및 기재층의 성분 및 함량은 하기 표 2에 기재된 바와 같으며, 이를 제외하고 상기 실시예 1과 동일한 방법으로 저속 이형력 밸런스, 고속 이형력 밸런스, 경박리 속도 변화율 및 중박리 속도변화율을 측정하였다. 그 결과는 하기 표 3에 기재된 바와 같다.
폴리디메틸실록산(PDMS) 실리콘 레진 Pt게 촉매
경박리
이형필름		 이형층 To 100 - 5
기재층 100㎛ PET 필름
중박리
이형필름		 이형층 To 100 30 5
기재층 100㎛ PET 필름
상기 실시예 1 및 2의 이형필름 박리안정성 측정방법으로 측정된 저속 이형력 밸런스, 고속 이형력 밸런스, 경박리 속도 변화율 및 중박리 속도 변화율은 하기 표 3에 기재된 바와 같다.
저속 이형력
밸런스		 고속 이형력
밸런스		 경박리 속도
변화율(%)		 중박리 속도
변화율(%)
실시예 1 2.5 2.0 150 250
실시예 2 2.8 1.0 180 100
실시예 1 및 2는 상기 이형필름 박리안정성 측정방법에 따라 박리안정성을 측정한 것으로서, 표 3의 결과를 참조할 때 상기 실시예 1은 저속 이형력 밸런스 및 고속 이형력 밸런스가 모두 1.5 내지 5.0의 범위를 만족하는 것이므로, 우수한 박리안정성을 나타냄을 알 수 있다.
반면, 실시예 2는 상기 이형필름 박리안정성 측정방법에 따라 박리안정성을 측정한 결과 저속 이형력 밸런스는 1.5 내지 5.0의 범위를 만족하나, 고속 이형력 밸런스 값이 1.0으로서 양자가 모두 1.5 내지 5.0 범위를 만족하지 못하여 박리안정성이 좋지 않음을 알 수 있다.
또한, 상기 실시예 1은 경박리 속도 변화율이 300% 이하이고, 중박리 속도 변화율이 200% 이상인 것으로서, 상기 범위의 고속 이형력 밸런스 및 저속 이형력 밸런스를 만족함과 동시에, 상기 범위의 경박리 속도 변화율 및 상기 범위의 중박리 속도 변화율을 나타냄으로써, 상기 적층체의 이형필름이 점착층의 들뜸현상 또는 전이현상 없이 우수한 박리안정성을 확보함을 알 수 있다.
반면, 상기 실시예 2는 경박리 속도 변화율은 300% 이하이나, 중박리 속도 변화율이 200% 미만인 것으로서, 상기 실시예 1에 비하여 박리안정성이 좋지 않음을 알 수 있다.
100: 적층체
10: 경박리 이형필름
20: 중박리 이형필름
30: 점착층
11: 기재층
12: 이형층

Claims (11)

  1. 점착층 및 상기 점착층의 양면에 경박리 이형필름 및 중박리 이형필름이 부착된 적층체를 마련하는 단계;
    0.3 내지 3.0 m/min의 박리 속도에서 상기 경박리 이형필름과 상기 점착층의 이형력을 측정하여 경박리 저속 이형력을 도출하는 단계;
    0.3 내지 3.0 m/min의 박리 속도에서 상기 중박리 이형필름과 상기 점착층의 이형력을 측정하여 중박리 저속 이형력을 도출하는 단계;
    10 내지 30 m/min의 박리 속도에서 상기 경박리 이형필름과 상기 점착층의 이형력을 측정하여 경박리 고속 이형력을 도출하는 단계;
    10 내지 30 m/min의 박리 속도에서 상기 중박리 이형필름과 상기 점착층의 이형력을 측정하여 중박리 고속 이형력을 도출하는 단계; 및
    하기 일반식 1 및 2에 의하여 고속 이형력 밸런스 및 저속 이형력 밸런스를 측정하는 단계;를 포함하는
    이형필름 박리안정성 측정방법.

    [일반식 1]
    고속 이형력 밸런스 = 중박리 고속 이형력/경박리 고속 이형력

    [일반식 2]
    저속 이형력 밸런스 = 중박리 저속 이형력/경박리 저속 이형력
  2. 제1항에 있어서,
    상기 경박리 고속 이형력 및 상기 경박리 저속 이형력을 이용하여 하기 일반식 3에 의해 경박리 속도 변화율을 측정하는 단계; 및
    상기 중박리 고속 이형력 및 상기 중박리 저속 이형력을 이용하여 하기 일반식 4에 의해 중박리 속도 변화율을 측정하는 단계;를 더 포함하는
    이형필름 박리안정성 측정방법.

    [일반식 3]
    경박리 속도 변화율(%) = (경박리 고속 이형력 - 경박리 저속 이형력)/ 경박리 저속 이형력 ｘ100

    [일반식 4]
    중박리 속도 변화율(%) = (중박리 고속 이형력 - 중박리 저속 이형력)/ 중박리 저속 이형력 ｘ100
  3. 제1항에 있어서,
    상기 적층체를 마련하는 단계는,
    상기 적층체를 20 내지 100℃에서 0.5 내지 720 시간 동안 보관하는 단계를 포함하는
    이형필름 박리안정성 측정방법.
  4. 제1항에 있어서,
    상기 경박리 이형필름 및 상기 중박리 이형필름은 각각 이형층 및 기재층의 적층 구조를 포함하는
    이형필름 박리안정성 측정방법.
  5. 제4항에 있어서,
    상기 이형층은 실리콘계 이형제, 멜라민계 이형제, 폴리올레핀계 이형제, 에폭시계 이형제, 아크릴계 이형제, 불소계 이형제, 셀룰로오스계 이형제, 파라핀계 이형제, 및 에폭시-멜라민계 이형제로 이루어진 군으로부터 선택된 1종 이상을 포함하는
    이형필름 박리안정성 측정방법.
  6. 제4항에 있어서,
    상기 기재층은 폴리에틸렌테레프탈레이트(PET), 폴리에틸렌(PE), 및 폴리비닐알콜(PVA)로 이루어진 군으로부터 선택된 1종 이상을 포함하는
    이형필름 박리안정성 측정방법.
  7. 제1항에 있어서,
    상기 점착층은 아크릴계 점착제, 실리콘계 점착제, 및 고무계 점착제로 이루어진 군으로부터 선택된 1종 이상을 포함하는
    이형필름 박리안정성 측정방법.
  8. 삭제
  9. 삭제
  10. 삭제
  11. 삭제
KR1020140147318A 2014-10-28 2014-10-28 이형필름 박리안정성 측정방법 및 이형필름 적층체 KR101966869B1 (ko)