KR101793781B1 - 시멘트 액체 방수제를 이용한 시공방법 - Google Patents
시멘트 액체 방수제를 이용한 시공방법 Download PDFInfo
- Publication number
- KR101793781B1 KR101793781B1 KR1020150087499A KR20150087499A KR101793781B1 KR 101793781 B1 KR101793781 B1 KR 101793781B1 KR 1020150087499 A KR1020150087499 A KR 1020150087499A KR 20150087499 A KR20150087499 A KR 20150087499A KR 101793781 B1 KR101793781 B1 KR 101793781B1
- Authority
- KR
- South Korea
- Prior art keywords
- weight
- liquid
- agent
- repellent agent
- waterproofing
- Prior art date
Abstract
본 발명은 시멘트 액체 방수제 및 그를 이용한 시공방법에 관한 것으로서, 계면활성제 30 ~ 50중량%; 초산비닐에멀젼 6 ~ 10중량%; 실리콘수지 5 ~ 9중량%; 소포제 3 ~ 4중량%; 증점제 3 ~ 4중량%; 소듐실리케이트 2 ~ 4중량%; 수분산 SBR 라텍스 11 ~ 13중량%; 규사 10 ~ 13중량%; 및 탄산칼슘 10 ~ 13중량%;로 조성되는 액체방수제를 제공함으로써, 공사비가 적게 들고, 시공이 간편하며, 시공면의 상태에 구애됨이 없이 방수시공이 가능하도록 하는 데 그 목적이 있다.
이를 위해 본 발명은, 계면활성제 30 ~ 50중량%; 초산비닐에멀젼 6 ~ 10중량%; 실리콘수지 5 ~ 9중량%; 소포제 3 ~ 4중량%; 증점제 3 ~ 4중량%; 소듐실리케이트 2 ~ 4중량%; 수분산 SBR 라텍스 11 ~ 13중량%; 규사 10 ~ 13중량%; 및 탄산칼슘 10 ~ 13중량%;를 포함하는 것을 특징으로 한다.
이를 위해 본 발명은, 계면활성제 30 ~ 50중량%; 초산비닐에멀젼 6 ~ 10중량%; 실리콘수지 5 ~ 9중량%; 소포제 3 ~ 4중량%; 증점제 3 ~ 4중량%; 소듐실리케이트 2 ~ 4중량%; 수분산 SBR 라텍스 11 ~ 13중량%; 규사 10 ~ 13중량%; 및 탄산칼슘 10 ~ 13중량%;를 포함하는 것을 특징으로 한다.
Description
본 발명은 시멘트 액체 방수제 및 그를 이용한 시공방법에 관한 것으로서, 더욱 상세하게는, 계면활성제 30 ~ 50중량%; 초산비닐에멀젼 6 ~ 10중량%; 실리콘수지 5 ~ 9중량%; 소포제 3 ~ 4중량%; 증점제 3 ~ 4중량%; 소듐실리케이트 2 ~ 4중량%; 수분산 SBR 라텍스 11 ~ 13중량%; 규사 10 ~ 13중량%; 및 탄산칼슘 10 ~ 13중량%;로 조성되는 액체방수제를 제공함으로써, 공사비가 적게 들고, 시공이 간편하며, 시공면의 상태에 구애됨이 없이 방수시공이 가능하도록 하는 시멘트 액체 방수제 및 그를 이용한 시공방법에 관한 것이다.
일반적으로, 콘크리트는 방수력이 약하기 때문에 콘크리트 구조체에 대한 수분 침투 및 누수를 방지하기 위하여 방수시공을 하는데, 방수공법은 시멘트를 이용한 액체방수, 합성고분자를 이용한 시트방수, 도막방수, 아스팔트방수로 대별할 수 있으며, 특히 시멘트를 이용한 액체방수는 욕실, 베란다, 발코니, 다용도실, 지하실 등에 많이 시공해 왔는데, 시멘트를 이용한 액체방수공법은 투수, 흡수에 대한 저항 성능을 가진 액체형 방수제를 시멘트 모르타르 또는 시멘트에 혼합하여 만든 방수 시멘트 모르타르 또는 방수시멘트 페이스트를 바닥, 벽, 천장을 이루는 콘크리트 구조체 위에 방수층을 시공하여 구조체의 누수를 방지하기 위한 방수공법이다.
시멘트 액체방수란 콘크리트 구조체의 바탕면에 지방산, 지방산염, 아스팔트 에멀젼, 수용성 수지 등과 같은 유기질계의 방수제와 혼합한 시멘트 모르타르 등을 덧발라 구조체 바탕에 수밀한 유기질 혹은 무기질계 방수층을 형성하는 공법이다. 특히, 시멘트 액체방수공법은 구성재료가 물, 시멘트, 방수액으로 시멘트와 물이 반응하는 특성을 가지고 있기 때문에 습윤하거나 다소의 요철이 있는 바탕면에도 시공이 가능하고 마감이 간단하다는 장점이 있지만 방수층 자체가 균열이 생기기 쉽다는 단점이 있다.
최근 건축하는 구조물을 콘크리트 구조체를 양상한 후 거푸집을 떼어내고 나면, 구조체의 표면이 거칠거칠한 것이 아니라 매끈매끈하기 때문에 구조체의 표면에 시멘트 모르타르로 미장 또는 방수층을 형성하기 위한 방수시공을 하기가 매우 어렵다. 특히, 지금까지 출현한 액체 방수제는 부착력이 약하기 때문에 시멘트 맥체방수공법으로 바닥면에 방수시공을 하면 시공 당시에는 방수층이 구조체의 표면에서 떨어지지는 않지만 시공 후에는 방수층이 구조체의 표면에서 박리 또는 들뜸현상이 잘 발생한다는 문제가 있고, 벽이나 천장에 방수시공을 하면 시멘트 모르타르가 매끈매끈한 구조체의 표면에 붙지않고 떨어져 버리기 때문에 시공작업에 많은 애로가 있어서, 방수시공을 하기 전에 정이나 망치와 같은 연장으로 매끈매끈한 구조체의 표면에 흠집을 내는 작업을 별도로 하고 있다.
지금까지 침투성 방수제의 선행기술을 살펴보면, 공개특허 제1992-18161호 침투성 실리콘계 방수제 조성물, 공개특허 제1998-24917호 침투성 물 흡수 방지제, 공개특허 제1999-78673호 실리콘 에멀젼 수용성 발수, 방수제의 조성물 및 제조방법, 공개특허 제2001-64300호 침투성 방수제, 공개특허 제2001-93323호 유기용제를 포함하는 알킬알콕시실란트계 발수제, 공개특허 제2003-92860호 알킬알콜시실란 및 고분자화합물을 포함하는 침투성 방수제 등 액체방수제 등 액체 방수제를 사용하는 방수제 및 시공방법에 대한 기술이 개시되어 있다.
그러나, 액체 방수제는 물에 희석하여 사용하므로 분말형태보다는 분산성이 양호하지만, 대부분이 발수성이 높은 지방산 금속염 용해물을 주재로 하기 때문에 지방산계의 특성상 시멘트와 교반시 다량의 기포가 발생하여 조직이 다공질화될 우려가 있으며, 시멘트의 수화를 지연시켜 강도저하, 응결지연 현상이 나타나게 되고, 부착력이 약해서 방수층과 콘크리트 구조체 간 박리 또는 들뜸현상이 발생할 뿐만 아니라 방수시공된 경화체의 강도와 수밀성 및 부착력이 저하되는 문제점이 있다.
상기와 같은 문제점을 해결하기 위해 제안하는 것으로서, 본 발명의 목적은, 계면활성제 30 ~ 50중량%; 초산비닐에멀젼 6 ~ 10중량%; 실리콘수지 5 ~ 9중량%; 소포제 3 ~ 4중량%; 증점제 3 ~ 4중량%; 소듐실리케이트 2 ~ 4중량%; 수분산 SBR 라텍스 11 ~ 13중량%; 규사 10 ~ 13중량%; 및 탄산칼슘 10 ~ 13중량%;로 조성되는 액체방수제를 제공함으로써, 공사비가 적게 들고, 시공이 간편하며, 시공면의 상태에 구애됨이 없이 방수시공이 가능하도록 하는 시멘트 액체 방수제 및 그를 이용한 시공방법를 제공하는 데 있다.
상기와 같은 목적을 달성하기 위한 본 발명은, 계면활성제 30 ~ 50중량%; 초산비닐에멀젼 6 ~ 10중량%; 실리콘수지 5 ~ 9중량%; 소포제 3 ~ 4중량%; 증점제 3 ~ 4중량%; 소듐실리케이트 2 ~ 4중량%; 수분산 SBR 라텍스 11 ~ 13중량%; 규사 10 ~ 13중량%; 및 탄산칼슘 10 ~ 13중량%;를 포함하는 것을 특징으로 한다.
본 발명에 있어서, 방수시공을 위하여 콘크리트 구조물 표면을 전처리하는 전처리단계; 상기 전처리단계를 통해 시공면이 정리되면, 지수제를 일정두께로 도포하여 누수를 차단하는 지수제 도포단계; 상기 지수제 도포단계를 통해 시공면에 지수제의 도포가 완료되면, 청구항 1에 의해 조성된 액체방수제를 시공면에 일정두께 도포하는 액체방수제 도포단계; 및 상기 액체방수제 도포단계를 통해 시공면에 일정두께의 액체방수제가 도포되면, 온도조건에 따라 시공면에서 액체방수제가 용이하게 양생되도록 유도하는 양생단계;를 포함하는 것이 바람직하다.
본 발명에 의하면, 계면활성제 30 ~ 50중량%; 초산비닐에멀젼 6 ~ 10중량%; 실리콘수지 5 ~ 9중량%; 소포제 3 ~ 4중량%; 증점제 3 ~ 4중량%; 소듐실리케이트 2 ~ 4중량%; 수분산 SBR 라텍스 11 ~ 13중량%; 규사 10 ~ 13중량%; 및 탄산칼슘 10 ~ 13중량%;로 조성되는 액체방수제를 제공함으로써, 공사비가 적게 들고, 시공이 간편하며, 시공면의 상태에 구애됨이 없이 방수시공이 가능하도록 하는 효과가 있다.
이하, 본 발명의 바람직한 실시 예를 첨부된 도면을 참조하여 설명하면 다음과 같다.
본 발명의 시멘트 액체 방수제는, 계면활성제 30 ~ 50중량%와, 초산비닐에멀젼 6 ~ 10중량%와, 실리콘수지 5 ~ 9중량%와, 소포제 3 ~ 4중량%와, 증점제 3 ~ 4중량%와, 소듐실리케이트 2 ~ 4중량%와, 수분산 SBR 라텍스 11 ~ 13중량%와, 규사 10 ~ 13중량% 및 탄산칼슘 10 ~ 13중량%이다.
상기 계면활성제는 30 ~ 50중량%로서, 폴리옥시에틸렌노닐페닐에테르를 사용함이 바람직하다. 상기 폴리옥시에틸렌노닐페닐에테르는 비이온성 계면활성제의 일종으로, 폴리옥시에티렌에 노닐페놀이 에테르결합한 것인데 막가용화에 이용되는 것 외에 소수성 크로마토그래피의 용제로서도 사용한다. 제품으로는 에멀젼계계면활성제 트리톤 N-101 등이 알려져 있다.
상기 초산비닐에멀젼은 6 ~ 10중량%로서, 접착제로 작용하며, 초산비닐 아세틸렌과 초산으로부터 생성되는 초산비닐을 촉매재료로 사용하여 부가중합시켜 얻은 에멀젼 상태의 합성수지를 포함하여 구성된다. 무색, 무미, 무취, 무해이고 감온성이 커서 0℃에서 부서지며 40℃에서 접착성이 생기며 연화되는 특성을 가진다.
상기 실리콘수지는 5 ~ 9중량%로서, 실리콘의 유기유도체가 중합되어 만들어지는 열경화성 합성수지이며, 분자구조는 규소와 산소가 번갈아 있는 실록세인 결합의 형태이다.
상기 소포제는 3 ~ 4중량%로서, 혼합과정 또는 사용과정에서 발생할 수 있는 유해한 기포를 제거하는 기능을 가진다. 소포제로는 일반적으로 휘발성이 적고 확산력이 큰 기름상의 물질 또는 수용성의 계면활성제가 이용된다. 소포작용에는 거품을 깨는 작용과 거품을 억제하는 작용이 있다. 예를 들면, 에탄올은 전자의 작용이 있어 생성된 거품을 없앨 수 있으나 거품발생을 방지할 수는 없다. 또한 실리콘유는 후자의 작용이 있어 거품발생을 방지할 수 있어도 생성된 거품을 없앨 수 없다. 소포제로는 일반적으로 휘발성이 적고 확산력이 큰 기름상의 물질 또는 수용성의 계면활성제가 이용된다. 전자에는 옥탄올, 시클로헥산올, 기타 고급 알코올, 에틸렌글리콜 등이 있으며, 후자에는 소비탄지방산에스터를 주성분으로 하는 비이온 계면활성제, 기타 비이온 계면활성제 등이 있다. 그 밖에 실리콘 소포제는 화학적으로 안정하여 뛰어난 효과가 있으므로 용도가 매우 넓다.
상기 증점제는 3 ~ 4중량%로서, 콜로이드 용액, 고분자 용액 등에 가하여 이들의 점도를 증진시켜 틱소트로피성을 부여하는 성분으로 접착제, 시멘트, 라텍스, 도료, 화장품 등에 사용되며, 시멘트 액체 방수제의 점도를 조절하여 취급 및 사용의 용이성을 확보한다.
상기 소듐실리케이트는 2 ~ 4중량%로서, 실리카 및 산화나트륨을 함유하는 성분으로 부식방지제, 완충화제 및 pH조정제로 작용한다.
상기 수분산 SBR(스티렌.브타디엔) 라텍스는 11 ~ 13중량%로서, 신소재 합성고무의 일종으로, 스티렌과 브타디엔을 1 대 3의 비율로 유화제를 사용하여 공중합한 것이다. 상기 수분산 SBR 라텍스는 천연고무에 비해 균일한 품질을 얻을 수 있고, 내열성, 내노화성, 내마모성 등이 뛰어나다.
상기 규사는 10 ~ 13중량%로서, 무수규산인 이산화규소(SiO2) 성분이 포함된 석영알갱이 모래이다. 천연규사인 해안규사와 산(山)규사 및 인조규사가 있으며 유리제품과 벽돌 등의 원료로 쓰인다. 또한, 상기 규사는 작은 알갱이형태 즉, 1 ~10㎛의 크기로 형성된다. 상기한 규사는 특유의 반사성능에 의해 액체 방수제가 도포된 벽면 등에 햇빛이 비추면 반사됨에 따라 미려함을 제공한다.
상기 탄산칼슘은 10 ~ 13중량%로서, 칼슘의 탄산염으로 대리석, 방해석, 선석, 석회석, 백악, 빙주석, 조개껍데기, 달걀껍데기, 산호 등에서 산출된다. 시멘트의 주원료, 산화칼슘의 원료, 제철, 건축재료 등의 각종 중화제로 사용된다.
상기와 같이 조성되는 시멘트 액체 방수제를 이용한 시공방법을 살펴보면 다음과 같다.
전처리단계는, 방수시공을 위하여 콘크리트 구조물 표면을 전처리한다. 즉, 시공면에 부착된 먼지, 레이턴스, 거푸집 박리제, 기름, 페인트 등 방수층이 박리될 수 있는 이물질을 완전히 제거한다. 또한 돌출부위는 그라인더를 사용하여 평탄하게 제거하고, 페인부위나, 약한부위, 들뜸부위 등은 사전에 점검하여 폭과 깊이가 최소한 1 ~ 2㎝가 되도록 파낸 후 표면을 깨끗이 손질하고, 보수몰탈제 등으로 씰링 및 보수하여 평탄하게 하는 것이 바람직하다.
지수제 도포단계는, 상기 전처리단계를 통해 시공면이 정리되면, 지수제를 일정두께로 도포하여 누수를 차단한다. 상기 지수제 도포단계는 국부적인 누수부위가 있으면 실시하는 단계로서, 경우에 따라서는 생략 가능하다. 이 경우, 누수가 되는 부위를 깊이와 폭을 1 ~ 2㎝로 형성하고, V나 U형으로 컷팅하고, 표면을 깨끗하게 마감하여 지수준비를 충분히 실시한다. 이후, 지수제를 필요한 양만큼 용기에 넣고, 예를 들면 V컷한 홈의 규격이 2㎝ * 2㎝ * 1㎝인 경우 0.5 ~ 0.7㎏을 용기에 넣고, 깨끗한 물을 용적비율로 약 30% 첨가하여 반죽하며, 발열건조가 시작될 때 컷팅된 표면에 채우면서 손이나 도구로 눌러서 지수제를 처리한다.
액체방수제 도포단계는, 상기 지수제 도포단계를 통해 시공면에 지수제의 도포가 완료되면, 계면활성제 30 ~ 50중량%와, 초산비닐에멀젼 6 ~ 10중량%와, 실리콘수지 5 ~ 9중량%와, 소포제 3 ~ 4중량%와, 증점제 3 ~ 4중량%와, 소듐실리케이트 2 ~ 4중량%와, 수분산 SBR 라텍스 11 ~ 13중량%와, 규사 10 ~ 13중량% 및 탄산칼슘 10 ~ 13중량%로 조성되는 시멘트 액체 방수제를 일정두께 도포한다.
상기 시멘트 액체방수제의 도포는 스프레이 건, 롤, 붓 등의 다양한 도구를 사용하여 실시할 수 있다.
양생단계는, 상기 액체방수제 도포단계를 통해 시공면에 일정두께의 액체방수제가 도포되면, 온도조건에 따라 시공면에서 액체방수제가 용이하게 양생되도록 유도한다.
예컨대, 방수공사 또는 양생기간 중 시공면 주위의 온도가 5℃ 이상임이 바람직하다. 또한, 시공면 주위에 직사광선, 바람, 고온 등의 건조가 예상될 때에는 물을 뿌려 식혀주고, 영도 또는 영하와 같은 저온 조건에 의한 동결이 예상되는 경우에는 시트 등을 씌워 액체방수제의 동결이 방지되도록 함으로써, 액체방수제의 용이한 양생을 유도하게 된다.
Claims (2)
- 삭제
- 방수시공을 위하여 콘크리트 구조물 표면에 이물질을 제거하고, 돌출부위는 그라인더를 사용하여 평탄하게 하며, 들뜸부위는 일정폭과 깊이로 파낸 후 보수몰탈제로 씰링 및 보수하여 평탄하게 하는 전처리단계와;
상기 전처리단계를 통해 시공면이 정리되면, 누수가 되는 부위를 1 ~ 2㎝의 깊이와 폭으로 'V'나 'U'형태로 컷팅하고 지수제를 일정두께로 도포하여 누수를 차단하는 지수제 도포단계;
상기 지수제 도포단계를 통해 시공면에 지수제의 도포가 완료되면, 액체방수제를 시공면에 일정두께 도포하는 액체방수제 도포단계; 및
상기 액체방수제 도포단계를 통해 시공면에 일정두께의 액체방수제가 도포되면, 0℃ 또는 영하의 저온조건일 경우 시트를 씌워 액제방수제의 동결이 방지되도록 하여 액체방수제가 용이하게 양생되도록 유도하는 양생단계를 포함하고;
상기 액체방수제는, 계면활성제 30 ~ 50중량%와;
초산비닐에멀젼 6 ~ 10중량%와;
실리콘수지 5 ~ 9중량%와;
소포제 3 ~ 4중량%와;
증점제 3 ~ 4중량%와;
소듐실리케이트 2 ~ 4중량%와;
수분산 SBR 라텍스 11 ~ 13중량%와;
규사 10 ~ 13중량%; 및
탄산칼슘 10 ~ 13중량%;
를 포함하는 것을 특징으로 하는 시멘트 액체 방수제를 이용한 시공방법.