KR100238992B1 - 방수씰링용 실리콘 에멀젼을 이용한 콘크리트의 방수 시공방법 - Google Patents
방수씰링용 실리콘 에멀젼을 이용한 콘크리트의 방수 시공방법 Download PDFInfo
- Publication number
- KR100238992B1 KR100238992B1 KR1019970013036A KR19970013036A KR100238992B1 KR 100238992 B1 KR100238992 B1 KR 100238992B1 KR 1019970013036 A KR1019970013036 A KR 1019970013036A KR 19970013036 A KR19970013036 A KR 19970013036A KR 100238992 B1 KR100238992 B1 KR 100238992B1
- Authority
- KR
- South Korea
- Prior art keywords
- waterproof
- concrete
- weight
- parts
- layer
- Prior art date
Abstract
본 발명은 다음 화학식 1로 표시되는 실란 100 중량부, 콜로이드 실리카 2~20 중량부, 유화제 2~40 중량부 및 알코올 80~150 중량부를 포함하는 실리콘 에멀젼을 피방수층인 콘크리트 또는 몰탈의 모체 표면에 도포하여 모체의 표면 내부에 방수씰링층(Sealing layer)을 형성하고, 방수씰링층이 형성된 콘크리트의 표면에 시멘트계 컴파운드에 의한 도막방수층을 형성하는 방법으로 콘크리트를 방수 시공하는 것에 관한 것이다.
[화학식 1]
상기 식에서 R은 탄소 원자수 2~17 인 하이드로카르복실 그룹이고, R′는 가수분해성 그룹이며, n은 1 또는 2이다.
이 방법에 의하면 콘크리트나 몰탈의 표면에 분사, 도포된 실리콘 에멀젼이 내부에 스며들어 방수씰링층이 형성되고, 그 위에 시멘트계 검파운드를 도포하면 피방수층의 표면이 충분히 건조되지 않았거나 평활도가 불량하여도 시공 불량, 즉 방수층간 접착 불량이 발생하지 않게 됨은 물론 방수 시공방법에 간단하여 적은 인원으로 쉽게 방수 시공을 할 수 있다.
Description
본 발명은 방수씰링용 실리콘 에멀젼을 이용한 콘크리트의 방수 시공방법에 관한 것으로, 보다 상세하게는 콘크리트 건축물의 지하층, 옥상, 베란다, 목욕탕, 수영장, 물탱크 저수조, 폐수처리장 등 콘크리트 모체 표면의 내부에 방수씰링층(Sealling layer)을 형성하여 콘크리트를 방수 처리하는 방법에 관한 것이다.
콘크리트나 몰탈의 방수 시공방법은 통상 건식법과 습식법으로 분류할 수 있다. 이중에 건식법은 콘트리트나 몰탈의 표면에 우레탄, 시트, 아스팔트 등을 도포하는 방법으로서, 피방수체인 콘크리트나 몰탈 표면의 청소 상태, 평활도, 건조 상태 등이 불량하면 방수 시공 후 콘크리트나 몰탈 표면과 방수층의 접착이 불량하여 들뜸 현상이 발생하고, 내구성이 약하여 옥외에 시공하는 경우에는 쉽게 노화되는 문제점이 있다.
또한 습식법은 시멘트 액체 방수, 몰탈 방수, 수용성 소지나 고무계 에멀젼도막 방수 등이 있으나, 이는 시공 후 계면에서의 접착 불량이 많고, 피방수층의 지수결함으로 피방수축 표면과 방수층 계면에서 수로(水路)가 성장하여 계면을 타고 물이 이동하면서 방수층을 급속도로 부식시키는 단점이 있을 뿐 아니라, 누수의 근원지를 찾기 어려워 보수시공 또한 매우 어려운 단점을 갖고 있다.
본 발명은 이러한 종래의 문제점을 해결하기 위한 것으로, 그 목적은 방수시공이 용이하고 피방수층인 몰탈이나 콘크리트 표면 근방의 내부에 침투하여 방수씰링층을 형성케 하는 실리콘 에멀젼을 이용한 콘크리트의 방수씰링 시공방법을 제공하는데에 있다.
제1도는 본 발명에 따른 콘크리트의 방수 구조를 보인 단면도이다.
* 도면의 주요부분에 대한 부호의 설명
10 : 콘크리트 모체 12 : 방수씰링층
20 : 도막방수층
본 발명의 목적을 달성하기 위한 방수씰링용 실리콘 에멀젼을 이용한 콘크리트의 방수 시공법을 피방수층인 콘크리트 또는 몰탈(모체)의 모체 표면에 다음 화학식 1로 표시되는 실란 100 중량부, 콜로이드 실리카 2~20 중량부, 비이온계 유화제 2~40 중량부 및 알코올 80~150 중량부를 포함하여 이루어진 실리콘 에멀젼을 도포하여 모체의 내부에 방수씰링층(Sealing layer)을 형성하는 단계; 및 방수씰링층이 형성된 콘크리트의 표면에 시멘트계 컴파운드를 도포하여 도막방수층을 형성하는 단계를 포함하는 데 그 특징이 있다.
상기 식에서 R은 탄소 원자수 2~17 인 하이드로카르복실 그룹이고, R′는 가수분해성 그룹이며, n은 1 또는 2이다.
이와 같은 본 발명은 더욱 상세하게 설명하면 다음과 같다.
본 발명의 방수 시공에 사용되는 방수씰링용 실리콘 에멀젼은 알콕시실란을 비이온성유화제로 에멀젼화하고, 콜로이드 실리카와 알코올을 도입하여 졸의 저장 안정성을 증대시킴으로써, 졸을 콘크리트에 도포시 알코올의 도입으로 인해 표면 젖음속도 및 모세관 압력을 높여 침투력을 증대시킬 수 있다. 그리고, 알콕시실란과 비이온성 유화제의 축합반응시 콜로이드 실리카, 알코올에 의하여 콘크리트 기공 내부에 수소결합 및 가교구조체 형성과 시멘트계 컴파운트와의 계면접착능을 부여하게 된다. 결과적으로 피방수층의 표면이 충분히 건조되지 않았거나 평활도가 불량하여도 시공 불량, 즉 방수층간 접착 불량이 발생하지 않게 됨은 물론 방수 시공방법이 간단하여 적은 인원으로 쉽게 방수 시공을 할 수 있게 된다.
이와 같은 기작을 갖는 본 발명의 방수씰링용 실리콘 에멀젼 제조에 있어서, 실란으로는 상기 화학식 1로 표시되는 화합물을 사용할 수 있는바, 구체적인 예로는 에틸트리에톡시실란, 에틸트리메톡시실란, 에틸트리-n-프로폭시실란, 프로필트리에톡시실란, 프로필트리메틸아미노실란, 부틸트리에톡시실란, 부틸트리메톡시실란, 이소부틸에톡시실란, 이소부틸트리메톡시실란, 이소부틸트리아세톡시실란, n-헥실트리메톡시실란, 6-클로로트리에톡시실란, 사이클로헥실크리에톡시실란, 벤질트리에톡시실란, 페닐트리에톡시실란, 비닐트리에톡시실란, 페닐트리메톡시실란,옥틸트리에톡시실란,옥틸메틸디이소프폭시실란, 라우릴트메톡시실란, 2-에틸헥실트리메톡시실란, 데실트리에톡시실란, 도데실트리브로모실란, 테트라데실트리메톡시실란, 헥사데실트리에톡시실란, 옥타데실트리에톡시실란, 이들의 이량체와 삼량체 및 이들의 올리고머를 1종 이상 혼합하여 사용한다. 바람직하기로는 실란 단량체의 분자량의 150~450인 것을 사용하는 것이 좋다.
콜로이드 실리카로는 pH가 8~11인 것을 사용하며, 특히 SiO2의 함량이 2~20％인 실리카졸을 사용하는 것이 바람직하다. 또한 이를 대체할 수 있는 상용화된 제품으로는 날코케미칼사의 날콕 1115, 니아콜사의 니아콜 215, 닛산 케미칼사의 스노텍스 20, 몬산토사의 시톤 W15등이 있다.
유화제는 비이온계 유화제인 폴리옥시프로필렌톨디올레이트, 폴리옥시에틸렌솔비톨올레이트, 폴리옥시에틸렌모노올레이트, 폴리옥시에틸렌스테아레이트, 솔비탄모노스테아레이트, 솔비탄모노올레이트, 글리셀로모노스테아레이트,폴리옥시에틸렌솔비톨헥사스테아레이트, 솔비탄트리스테아레이트, 솔비탄트리올레이트 등의 솔비탄지방산에스테르류, 지방산글리세라이드류, 폴리옥시에틸렌알코올류 및 폴리옥시에틸렌솔비탄지방산에스테르류부터 선택된 1종 이상을 사용한다.
이러한 유화제는 실란의 종류에 따라 선택되는 종류가 달라질 수 있으며, 통상 실란 100 중량부에 대해 2~40 중량부, 바람직하기로는 10~30 중량부 함유되는 것이 좋다. 특히 상기 유화제는 폴리하이드록시 화합물을 함께 또는 혼합하여 사용하면 더욱 좋다.
알코올은 메탄올, 에탄올, n-부탄올, 이소프로판올, 2-에톡시에탄올, t-부탄올, 2-에틸헥산올, 이소아밀알코올, n-옥틸알코올, 2-에틸부탄올, n-헥산올, 2-아밀알코올, 시클로헥산올, n-프로판올 , 벤질알코올을 1종 이상 선택하여 사용한다.특히, 수소결합력이 강하고 용해성 파라미터값이 9~16인 것을 사용하는 것이 좋다.
또한 물은 빗물, 수돗물, 증류수 등을 모두 사용할 수 있으나, 특히 물에 포함된 불순물에 의해 실리콘 에멀젼의 저장안정성이 저하되기 쉬우므로 증류수를 사용하는 것이 좋다.
이상에서 설명한 실리콘 에멀젼을 사용하여 피방수층인 콘크리트나 몰탈에 방수 시공하는 방법에 대해 상세하게 설명한다.
즉, 실리콘 에멀젼을 이용한 콘크리트의 방수 시공방법은, 피방수층인 콘크리트 또는 몰탈의 표면 내무에 본 발명의 실리콘 에멀젼을 사용하여 방수씰링층(Sealing layer)을 형성하는 단계와, 방수씰링층이 형성된 콘크리트의 표면에 시멘트계 컴파운드를 도포하여 도막방수층을 형성하는 단계를 포함하는데 특징이 있다.
상기에서 시멘트계 컴파운드로는 아크릴 에멀젼 단독 또는 고무계 라텍스와 1 : 0.1~5의 중량비로 혼합한 것과 쏘로씰을 5~50 : 100 중량부의 비율로 혼합 교반하면서 물을 일정량 가하여 만든 것이나, 또는 아크릴 에멀젼 단독 또는 고무계 라텍스와 1 : 0.1~5의 중량비로 혼합한 것과 포틀란트 시멘트나 소석회를 10~30 : 100 중량부를 비율로 혼합 교반하면서 물을 일정량 가하여 만든 것을 사용한다.
본 발명은 방수 시공방법에 있어서, 실리콘 에멀젼은 콘크리트 또는 몰탈부에 침투되어 건조되면서 콘크리트 모체 내부의 기공(Porosity)간에 망상구조 결합을 형성하여 내부의 잔존 수분을 외부로 배출시킬 수는 있으나 외부에서 내부로 물이 유입되는 것을 차단시키는 멤브레인(Membrane)기능을 부여하게 된다. 이렇게 방수씰링층이 형성되면 산성비, 염분, 각종 화학약품, 대기오염가스, 오존 등에 대한 저항력이 우수하고, 모체 자체의 부식 및 풍화 현상을 근원적으로 방지할 수 있다.
시멘트계 컴파운드는 시멘트와 소석회, 가소제, 접착부여제인 아크릴 에멀젼, 탄성부여제인 수용성 고무에멀젼 등으로 구성된 컴파운드로서, 피착제인 콘크리트 모체 표면과의 접착 성능이 우수하고 모체 표면의 요철면 기공과 견고하게 결합시켜 주는 역할을 하게 된다. 또한 아크릴 에멀젼 및 수용성 고무에멀젼의 양을 조절하여 콘크리트 모체 표면 위에 고탄성 무기질 도막방수층을 형성시킬 수 있다.
보다 간단하게 시멘트, 소석회, 가소제, 계면활성제 등을 혼합 가공된 제품들이 시판되고 있으며, 대표적인 상품으로 쏘로씰이 있다. 따라서, 시멘트계 컴파운드는 시공하고자 하는 피방수면의 요구 조건과 건축물 전체적인 구조 특성에 부합되도록 각각의 배합제 및 그 양을 임의 선택하여 현장 배합, 적용할 수도 있다.표준 배합으로 쏘로씰 25㎏ : 아크릴에멀젼 2㎏ : 수용성 고무에멀젼 2㎏: 물 8㎏비율로 혼합 사용하는 것이 바람직하다. 단, 하절기에는 쏘로씰의 고화속도가 빠르므로 작업성을 고려하여 시멘트를 중량비로 20~50％ 혼합하여 사용하면 고화속도를 조절할 수 있다.
특히 지하층 시공시 장마철의 높은 수압을 고려하여 모체 씰링층 위에 시멘트계 컴파운드를 중도로 하고 고화건조되면 상도로 건식법인 우레탄, 고무 시트, 아스팔트 방수를 추가 시공하면 3중 구조에 의해 보다 완벽한 방수 효과를 기대할 수 있다.
즉, 본 발명은 제1도에 도시된 바와 같이 피방수층인 콘크리트나 몰탈 모체(10)의 내부에 방수씰링층(12)을 형성시켜 주고, 그 위에 계면접착능이 우수한 도막방수층(20)을 시공하므로 계면간 접착 불량, 지수 결함 등의 용인으로 하자가 발현되지 않을뿐더러 시공 후 표면 자체가 부식, 풍화되는 현상이 방지할 수 있다.
본 발명에서 사용된 아크릴 에멀젼에 대해 설명한다.
아크릴 에멀젼은 아크릴레이트계 모노머 100 중량부에 비이온계 유화제 0.6~30중량부가 반응개시제 0.1~1중량부를 혼합하여 상온 ~200℃에서 30분~24시간 중합 반응시켜서 제조한다.
아크릴레이트계 모노머는 메틸메타크릴레이트, 에틸메타크릴레이트, 에틸메타크릴레이트, 이소프로필메타크릴레이트, n-부틸메타크릴레이트, 이소부틸메타크릴레이트, n-헥실메타크릴레이트, 라우릴메타크릴레이트, 2-하이드록시에틸메타크릴레티트, 하이드록시프로필메타크릴레이트, 글리시딜메타크릴레이트, 에틸아크릴레미트, 이소프로필아크릴레이트, n-부틸아크릴레이트, 2-에틸헥실아크릴레이트 등에서 1종 이상을 선택하여 사용한다.
유화제로는 비이온계 유화제가 좋은데, 이로는 도데실메틸암모늄브로마이드, 헥사데실트리메틸암모늄브로마이드, 도데실피리디움클로라이드, 도데실하이드로클로라이드 등에서 1종 이상 선택하여 사용한다.
반응개시제로는 2,2-아조비스(2-아미디노프로판)디하이드로클로라이드, 2,2- 아조비스이소부티로니트릴, 2-터셔리부틸아조-2-시아노프로판, 2-터셔리부틸아조-2-시아노부탄, 2-터셔리부틸아조-2-시아노-4-메틸펜텐, 큐밀퍼옥사이드네오데카노에이트, 터셔리부틸퍼옥시-2-에틸헥사노에이트 등을 1종 이상 선택하여 사용한다.
이하 실리콘 에멀젼과 시멘트계 컴파운드의 제조방법에 관해 상세히 설명하고자 한다.
[실리콘 에멀젼의 제조]
[제조예 1]
콜로이드 실리카(제품명 :날콕 1115, 날코케미칼사 제품) 7g에 2-에톡시에탄올과 n-부탄올을 각각 5g씩 함께 혼합하고, 여기에 2-에틸헥실트리에톡시시란 100g을 첨가하여 30분에 걸쳐 천천히 교반한 다음, 다시 유화제로서 폴리옥시에틸렌솔비톨올레이트 18g을 첨가 교반하고, 증류수 365g을 첨가, 교반하여 우유빛 실리콘 에멀젼(A-1)을 얻었다.
[제조예 2]
옥틸트리에톡시실란 100g에 폴리옥시에틸렌모노올레이트 15g과 물 365g을 가하여 유화 분산시키고, n-부탄올과 n-옥틸알코올을 각각 5g씩 첨가 혼합한 다음, 콜로이드 실리카(제품명 : 니아콜 215, 니아콜사 제품)10g에 첨가하여 안정된 우유빛 실리콘 에멀젼(A-2)을 얻었다.
[시멘트계 컴파운드의 제조]
[제조예 3]
모노머인 에틸메타크릴레이트 60g, 2-하이드록시에틸메타크릴레이트 40g과 유화제인 도데실메틸암모늄브로마이드 2.7g을 혼합하고 물 200g을 첨가하여 유화 분산시킨 다음, 반응 개시제로서 2,2 -아조비스(2-아미디노프로판)디하이드로클로라이드 0.08g을 첨가한 후 3 시간 동안 중함 반응시켜 우유빛 아크릴 에멀젼을 얻었다. 다음 쏘로씰(쏘로시스템사 제품)1㎏에 상기에서 제조된 아크릴 에멀젼 120g 및 물 360g을 첨가 교반하여 시멘트계 컴파운드(B-1)를 제조하였다.
[제조예 4]
포틀란드 시멘트 870g, 소석회 130g, 상기 제조에 3에서 제조한 아크릴 에멀젼 145g 및 물 360g을 혼합교반하여 시멘트계 컴파운드(B-2)를 제조하였다.
[제조예 5]
쏘로씰 1㎏에 상기 제조예 3에서 제조한 아크릴 에멀젼 60g, SBR 라텍스2108(일본 JSR사 제품) 및 물 340g을 혼합 교반하여 시멘트계 컴파운드(B-3)를 제조하였다.
[제조예 6]
모노머인 에틸메타크릴레이트 70g, 2-에틸헥실에틸렌모노올레이트 15g과 유화제인 도데실메틸암모늄브로마이드 2.5g을 혼합하고 물 220g을 첨가하여 유화분산시킨 다음, 반응개시제로서 2-터셔리부틸아조-2시아노프로판 0.1g을 첨가한후 3시간 동안 중합 반응시켜 우유빛 아크릴 에멀젼을 얻었다. 다음 쏘로씰(쏘로시스템사 제품)1㎏에 상기에서 제조된 아크릴 에멀젼 120g 및 물 360g을 첨가 교반하여 시멘트계 컴파운드(B-4)를 제조하였다.
[제조예 7]
포틀란드 시멘트 800g, 소석회 200g, 상기 제조예 6에서 제조한 아크릴 에머젼 160g 및 물 380g을 혼합교반하여 시멘트계 컴파운드(B-5)를 제조하였다.
이하 실시예를 통해 본 발명을 보다 상세히 설명하고자 한다.
[실시예 1]
시멘트 벽돌(190㎜×90㎜×55㎜)과 이와 같은 크기의 콘크리트 시료를 만들고, 각 시료의 6면 모두에 실리콘 에멀젼(A-1)을 도포한 후 , 우유빛이 없어진 후 곧바로 브러시를 사용하여 시멘트계 컴퍼운드(B-1)를 두께 1㎜가 되도록 2회 도포한 다음 상온에서 72시간 건조하였다.
다음 상기 두 시료의 한쪽을 절단하여 실리콘 에멀젼이 침투된 깊이, 즉 방수씰링층의 두께를 재어 보았더니 벽돌은 12㎜, 콘크리트의 경우에는 3㎜이었다. 또한 한쪽이 절단된 두 시료를 각각 물 속에 72시간 침지한 후 꺼내고 시료 절단 다른 쪽을 또 다시 절단하여 관찰하였다. 방수씰링층이 형성된 곳에는 물이 스며들지 않았음을 확인할 수 있었다.
[실시예 2]
시멘트계 컴파운드로 B-2를 사용한 것 이외에는 실시예 1과 같은 조건과 방법으로 실험하였다. 그 결과도 실시예 1과 다를게 없었다.
[실시예 3]
시멘트계 컴파운드로 B-3를 사용한 것 이외에는 실시예 1과 같은 조건 및 방법으로 실험하였다. 그 결과도 실시예1과 비슷하였으며, 시멘트계 컴파운드의 위커빌리티와 셀프레벨링성은 보다 향상되었음을 확인할 수 있었다.
[실시예 4]
실리콘 에멀젼은 A-2, 시멘트계 컴파운드로 B-4를 사용한 것 이외에는 실시예 1과 같은 조건 및 방법으로 실험하였다. 이때의 방수씰링층의 두께는 벽돌의 경우 10㎜, 콘크리트의 경우 2.5㎜ 이었다.
[실시예 5]
시멘트계 컴파운드로 B-5를 사용한 것 이외에는 상기 실시예 4와 같은 조건 및 방법으로 실험하였다. 그결과는 실시예4와 비슷하였다.
이상의 실시예를 통해 살펴본 바와 같이, 본 발명에 의하면 모체인 벽돌이나 콘크리트의 방수하고자 하는 면에 본 발명의 실리콘 에멀젼을 도포하면 모체내 깊숙히 방수 씰링층이 형성됨을 확인할 수 있다.
이상에서 상세히 설명하 바와 같이, 본 발명은 방수 시공하고자 하는 콘크리트나 몰탈의 표면에 실리콘 에머젼을 분사, 도포하면 그 내부로 실란, 비이온성 유화제, 콜로이드 실리카 및 알코올로 이루어진 실리콘 에멀젼이 흡착, 침투되고, 그위에 시멘트계 컴파운드를 분사 도포 또는 브러시 도장하여 방수 시공하면, 피방수층의 표면이 충분히 건조되지 않았거나 평활도가 불량하여도 시공 불량, 방수층 접착불량(계면 접착력 부족, 방수층의 들뜸 및 파손 등) 이 발생하지 않게 된다. 또 한 방수 시공 방법이 간단하여 적은 인원으로 쉽게 방수 시공을 할 수 있을 뿐 아니라 숙련공이 아니더라도 방수 시공이 가능함은 물론 방수 효과도 우수한 장점을 갖는다.
Claims (9)
- 피방수층인 콘크리트 또는 몰탈(모체)의 다음 화학식 1로 표시되는 실란 100 중량부, 콜로이드 실리카 2~20 중량부, 비이온계 유화제 2~40 중량부 및 알코올 80~150 중량부를 포함하는 실리콘 에멀젼을 도포하여 모체의 내부에 방수씰링층(Sealing layer)을 형성하는 단계; 방수씰링층이 형성된 콘크리트의 표면에 시멘트계 컴파운드에 도포하여 도막방수층을 형성하는 단계를 포함으로 방수씰링용 실리콘 에멀젼을 이용한 콘크리트의 방수 시공방법.[화학식 1]
상기 식에서 R은 탄소 원자수 2~17 인 하이드로카르복실 그룹이고, R′는 가수분해성 그룹이며, n은 1 또는 2이며, 단량체의 분자량은 150~450이다. - 제1항에 있어서, 상기 시멘트계 컴파운드는 아크릴 에멀젼에 고무계 라텍스 1종 이상과, 시멘트, 쏘로씰 1종 이상을 5~50:100 중량부의 비율로 혼합교반하면서 물을 일정량 가하여 만든 것임을 특징으로 하는 방수씰링용 실리콘 에멀젼을 이용한 콘크리트의 방수 시공방법.
- 제2항에 있어서, 상기 아크릴 에멀젼은 아크릴레이트계 모노머 100중량부에 비이온계 유화제 0.6~30중량부와 반응개시제 0.1~1중량부를 혼합하여 중합반응시킨 것임을 특징으로 하는 방수씰링용 실리콘 에멀젼을 이용한 콘크리트의 방수 시공방법.
- 제3항에 있어서, 상기 반응개시제는 2,2-아조비스(2-아미디노프로판)디하이드로클로라이드, 2,2-아조비스이소부티로니트릴, 2-터셔리부틸아조-20시아노프로판, 2-터셔리부틸아조-2-시아노부탄, 2-터셔리부틸아조-2-시아노-4-메틸펜텐, 큐밀퍼옥사이드네오데카노에이트, 터셔리부틸퍼옥시-2-에틸헥사노에이트에서 선택된 1종 이상인 것임을 특징으로 하는 방수씰링용 실리콘 에멀젼을 이용한 콘크리트의 방수 시공방법.
- 제1항에 있어서, 도막방수층의 상부에 우레탄, 고무시트, 아스팔트, 에폭시 중 어느 하나를 사용하여 추가 도포 시공하는 것을 특징으로 하는 방수 씰링용 실리콘 에멀젼을 이용한 콘크리트의 방수 시공방법.
- 제1항에 있어서, 상기 실란은 에틸트리에톡시실란, 에틸트리메톡시실란, 에틸트리-n-프로폭시실란, 이소부틸에톡시실란, 이소부틸트리메톡시실란, 이소부틸트리아세톡시실란, n-헥실트리메톡시실란, 비닐트리에톡시실란, 페닐트리메톡시실란, 옥틸트리에톡시실란, 옥틸메틸디이소프폭시실란, 라우릴트메톡시실란, 2-에틸헥실트리메톡시실란, 옥틸트리에톡시실란, 도데실트리브로모실란, 테트라데실트리메톡시실란, 헥사데실트리에톡시실란, 옥타데실트리에톡시실란, 이들의 이량체와 삼량체 및 이들의 올리고머로부터 선택된 1종 이상인 것을 것을 특징으로 하는 방수 씰링용 실리콘 에멀젼을 이용한 콘크리트의 방수 시공방법.
- 제1항에 있어서, 상기 콜로이드 실리카는 pH가 8~11이고, SiO2함량이 20％ 이하인 실리카졸인 것을 특징으로 하는 방수 씰링용 실리콘 에멀젼을 이용한 콘크리트의 방수 시공방법.
- 제1항에 있어서, 상기 유화제는 폴리옥시프로필렌톨디올레이트, 폴리옥시에틸렌솔비톨올레이트, 폴리옥시에틸렌모노올레이드, 폴리옥시에틸렌스테아레이트, 솔비탄모노스테아레이트, 솔비탄모노올레이트, 글리세롤모노스테아레이트, 폴리옥시에틸렌솔비톨헥사스테아레이트, 솔비탄트리스테아레이트,솔비탄트리올레이트 구성된 비이온계 유화제로부터 선택된 1종 이상인 것을 특징으로 하는 방수 씰링용 실리콘 에멀젼을 이용한 콘크리트의 방수 시공방법.
- 제1항에 있어서, 상기 알코올은 메탄올, 에탄올, n-부탄올, 이소프로판올, 2-에톡시에탄올, t-부탄올, 2-에틸헥산올, 이소아밀알코올, n-옥틸알코올, 2-아밀알코올, 시클로헥산올, n-프로판올 , 벤질알코올에서 선택된 1종 이상으로, 용해성 파라미터값이 9~16 인 것을 특징으로 하는 방수 씰링용 실리콘 에멀젼을 이용한 콘크리트의 방수 시공방법.