KR101486635B1 - 경화성 조성물, 이로 제조된 경화막 및 이를 포함하는 디스플레이 장치 - Google Patents

경화성 조성물, 이로 제조된 경화막 및 이를 포함하는 디스플레이 장치 Download PDF

Info

Publication number
KR101486635B1
KR101486635B1 KR20120134767A KR20120134767A KR101486635B1 KR 101486635 B1 KR101486635 B1 KR 101486635B1 KR 20120134767 A KR20120134767 A KR 20120134767A KR 20120134767 A KR20120134767 A KR 20120134767A KR 101486635 B1 KR101486635 B1 KR 101486635B1
Authority
KR
South Korea
Prior art keywords
curable composition
formula
cured film
compound represented
independently
Prior art date
Application number
KR20120134767A
Other languages
English (en)
Other versions
KR20140067483A (ko
Inventor
이건우
Original Assignee
주식회사 엘지화학
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 주식회사 엘지화학 filed Critical 주식회사 엘지화학
Priority to KR20120134767A priority Critical patent/KR101486635B1/ko
Publication of KR20140067483A publication Critical patent/KR20140067483A/ko
Application granted granted Critical
Publication of KR101486635B1 publication Critical patent/KR101486635B1/ko

Abstract

본 명세서는 경화성 조성물, 이로 제조된 경화막 및 이를 포함하는 디스플레이 장치에 관한 것이다.

Description

경화성 조성물, 이로 제조된 경화막 및 이를 포함하는 디스플레이 장치{CURABLE COMPOSITION, CURED FILM MANUFACTURED BY USING THE CURABLE COMPOSITION AND DISPLAY DEVICE HAVING THE SAME}
본 명세서는 경화성 조성물, 이로 제조된 경화막 및 이를 포함하는 디스플레이 장치에 관한 것이다.
열경화를 통해 박막을 형성하는 기술은 다양한 분야에 적용되며, 그 예로서 액정 표시 소자, 유기 발광 소자 디스플레이, 터치 패널 등을 들 수 있다.
액정 표시 소자의 경우 컬러 필터의 단차를 보상하고 보호막 역할을 하는 오버코트에 열경화된 박막이 사용될 수 있다. 유기 발광 소자 디스플레이의 경우 유기 발광 소자가 산소나 수분에 의해 손상되는 것을 방지하기 위한 보호막으로서 열경화된 박막이 사용될 수 있다. 또한, 터치 패널의 경우 가로와 세로의 전극을 공간적으로 서로 분리하는 절연막이나 터치 패널의 전극을 외부의 충격으로부터 보호하는 하드 코트로서 열경화된 박막이 사용될 수 있다.
이러한 박막 재료의 두께는 일반적으로 1~15 μm 정도이며, 사용 중 온도나 습기의 변화에 의해 변형되거나 박리되지 않아야 하기 때문에 박막의 강도를 높이거나 접착력을 향상시키려는 다양한 기술적인 시도가 이루어지고 있다.
한국특허공개 제1998-0074182호
본 명세서는 경화성 조성물, 이로 제조된 경화막 및 이를 포함하는 디스플레이 장치에 관한 것이다.
본 명세서는 에폭시기를 포함하는 바인더 수지; 및 하기 화학식 1로 표시되는 화합물 및 하기 화학식 2로 표시되는 화합물 중 적어도 하나를 포함하는 실록산 화합물을 포함하는 경화성 조성물을 제공하는 것이다.
[화학식 1]
Figure 112012097682335-pat00001
[화학식 2]
Figure 112012097682335-pat00002
상기 화학식 1 및 2에서,
X1, X2, X3, X6, X7, X8, X10, X11, X12, X15, X16, X17, R1, R2, R3, R6, R7, R8, R10, R11, R12, R15, R16 및 R17은 각각 독립적으로 C1~C3의 알킬기이고,
X4, X5, X13, X14, R4, R5, R13 및 R14는 각각 독립적으로 C1~C10의 알킬렌기이며,
X9 R9 , R18 및 R19는 각각 독립적으로 C1~C10의 알킬기이고,
m 및 n은 0~4인 정수이며, o 및 p는 0~3인 정수이다.
또한, 본 명세서는 상기 경화성 조성물로 제조된 경화막을 제공하는 것이다.
또한, 본 명세서는 상기 경화막을 포함하는 보호막을 제공하는 것이다.
또한, 본 명세서는 상기 경화막을 포함하는 디스플레이 장치를 제공하는 것이다.
또한, 본 명세서는 상기 경화막을 포함하는 컬러 필터를 제공하는 것이다.
본 명세서의 일 실시상태에 따라 제조된 경화막은 급격한 온도 변화에 의해 경화막이 변형되지 않는 장점이 있다.
본 명세서의 일 실시상태에 따라 제조된 경화막은 급격한 온도 변화에 의해 박리가 일어나지 않는 장점이 있다.
도 1은 본 명세서의 일 실시상태에 따라 제조된 경화막을 사용한 터치 패널의 구조도이다.
이하 본 명세서를 보다 상세히 설명한다.
본 명세서는 에폭시기를 포함하는 바인더 수지; 및 상기 화학식 1로 표시되는 화합물 및 상기 화학식 2로 표시되는 화합물 중 적어도 하나를 포함하는 실록산 화합물을 포함하는 경화성 조성물을 제공한다.
상기 화학식 1로 표시되는 화합물은 하기 화학식 3으로 표시되는 화합물일 수 있다.
[화학식 3]
Figure 112012097682335-pat00003
상기 화학식 3에서, X1, X2, X3, X6, X7, X8, X10, X11, X12, X15, X16 및 X17은 각각 독립적으로 C1~C3의 알킬기이고, X9는 각각 독립적으로 C1~C10의 알킬기이며, m은 0~4인 정수이다.
상기 화학식 2로 표시되는 화합물은 하기 화학식 4로 표시되는 화합물일 수 있다.
[화학식 4]
Figure 112012097682335-pat00004
상기 화학식 4에서, R1, R2, R3, R6, R7, R8, R10, R11, R12, R15, R16 및 R17은 각각 독립적으로 C1~C3의 알킬기이고, R9 , R18 및 R19는 각각 독립적으로 C1~C10의 알킬기이며, n은 0~4인 정수이고, o 및 p는 0~3인 정수이다.
상기 화학식 1로 표시되는 화합물은 하기 화학식 5로 표시되는 화합물 또는 하기 화학식 6으로 표시되는 화합물일 수 있다.
[화학식 5]
Figure 112012097682335-pat00005
[화학식 6]
Figure 112012097682335-pat00006
상기 화학식 5 및 6에서, X4, X5, X13 및 X14는 각각 독립적으로 C1~C10의 알킬렌기이며, X9 는 C1~C10의 알킬기이고, m은 0~4인 정수이다.
상기 화학식 2로 표시되는 화합물은 하기 화학식 7로 표시되는 화합물 또는 하기 화학식 8로 표시되는 화합물일 수 있다.
[화학식 7]
Figure 112012097682335-pat00007
[화학식 8]
Figure 112012097682335-pat00008
상기 화학식 7 및 8에서, R4, R5, R13 및 R14는 각각 독립적으로 C1~C10의 알킬렌기이고, R9 , R18 및 R19는 C1~C10의 알킬기이며, n은 0~4인 정수이고, o 및 p는 0~3인 정수이다.
상기 화학식 1로 표시되는 화합물은 하기 화학식 9로 표시되는 화합물 또는 하기 화학식 10으로 표시되는 화합물일 수 있다.
[화학식 9]
Figure 112012097682335-pat00009
[화학식 10]
Figure 112012097682335-pat00010
상기 알킬기는 직쇄 또는 분지쇄일 수 있으며, 예를 들면 메틸기, 에틸기, 프로필기 및 이소프로필기 등일 수 있으며, 이에만 한정되는 것은 아니다.
본 명세서의 일 구현예에 따르면, 본 명세서의 실록산 화합물의 함량은 상기 경화성 조성물의 전체 고형분 100 중량부에 대하여 0.1 내지 80 중량부일 수 있다. 필요에 따라, 0.1 내지 15 중량부일 수 있다. 이 경우 급격한 온도 변화에 의해 경화막의 변형이나 박리가 일어나지 않는 효과를 기대할 수 있고, 경화막의 물성을 저해하지 않는 장점이 있다.
본 명세서의 바인더 수지는 에폭시기에 의한 열경화 특성을 가지는 것이 될 수 있다.
본 명세서의 일 구현예에 따르면, 본 명세서의 바인더 수지는 에폭시계 단량체 및 (메트)아크릴레이트계 단량체를 포함하는 바인더 수지용 조성물로부터 중합된 공중합체일 수 있다.
예를 들면, 상기 에폭시계 단량체로는 옥세테닐 메타크릴레이트, 알릴 글리시딜에테르, 글리시딜 (메타)아크릴레이트, 3,4-에폭시시클로헥실메틸 (메타)아크릴레이트, 글리시딜 5-노보넨-2-메틸-2-카복실레이트(엔도, 엑소 혼합물), 1,2-에폭시-5-헥센 및 1,2-에폭시-9-데센으로 이루어지는 군으로부터 선택되는 1 종 이상의 화합물을 사용할 수 있으나, 이에만 한정되는 것은 아니다.
상기 (메트)아크릴레이트계 단량체로는 메타크릴산, (메타)아크릴레이트, 메틸(메타)아크릴레이트, 에틸(메타)아크릴레이트, 부틸(메타)아크릴레이트, 디메틸아미노에틸(메타)아크릴레이트, 이소부틸(메타)아크릴레이트, t-부틸(메타)아크릴레이트, 시클로헥실(메타)아크릴레이트, 이소보닐(메타)아크릴레이트, 에틸헥실(메타)아크릴레이트, 2-페녹시에틸(메타)아크릴레이트, 테트라히드로퍼프릴(메타)아크릴레이트, 히드록시에틸(메타)아크릴레이트, 2-히드록시프로필(메타)아크릴레이트, 2-히드록시-3-클로로프로필(메타)아크릴레이트, 4-히드록시부틸(메타)아크릴레이트, 아실옥틸옥시-2-히드록시프로필(메타)아크릴레이트, 글리세롤(메타)아크릴레이트, 2-메톡시에틸(메타)아크릴레이트, 3-메톡시부틸(메타)아크릴레이트, 에톡시디에틸렌글리콜 (메타)아크릴레이트, 메톡시트리에틸렌글리콜(메타)아크릴레이트, 메톡시트리프로필렌글리콜(메타)아크릴레이트, 폴리(에틸렌 글리콜) 메틸에테르(메타)아크릴레이트, 페녹시디에틸렌글리콜(메타)아크릴레이트, p-노닐페녹시폴리에틸렌글리콜(메타)아크릴레이트, p-노닐페녹시폴리프로필렌글리콜(메타)아크릴레이트, 테트라플루오로프로필(메타)아크릴레이트, 1,1,1,3,3,3-헥사플루오로이소프로필 (메타)아크릴레이트, 옥타플루오로펜틸(메타)아크릴레이트, 헵타데카플루오로데실(메타)아크릴레이트, 트리브로모페닐(메타)아크릴레이트, 메틸 α-히드록시메틸 아크릴레이트, 에틸 α-히드록시메틸 아크릴레이트, 프로필 α-히드록시메틸 아크릴레이트 및 부틸 α-히드록시메틸 아크릴레이트로 이루어진 그룹으로부터 선택될 수 있으나, 이에만 한정되는 것은 아니다.
구체적으로, 상기 바인더 수지는 글리시딜 메타크릴레이트와 메타크릴산의 공중합체가 될 수 있다. 또는, 상기 바인더 수지는 옥세테닐 메타크릴레이트와 메타크릴산의 공중합체가 될 수 있다.
본 명세서의 일 구현예에 따르면, 본 명세서의 바인더 수지는 에폭시계 단량체, (메트)아크릴레이트계 단량체 및 방향족 비닐계 단량체를 포함하는 바인더 수지용 조성물로부터 중합된 공중합체일 수 있다.
예를 들면, 상기 방향족 비닐계 단량체로는 스티렌, α-메틸스티렌, (o,m,p)-비닐 톨루엔, (o,m,p)-메톡시 스티렌, 및 (o,m,p)-클로로 스티렌으로 이루어진 그룹으로부터 선택될 수 있으나, 이에만 한정되는 것은 아니다.
본 명세서의 일 구현예에 따르면, 본 명세서의 바인더 수지는 글리시딜 메타크릴레이트, 메타크릴산 및 스티렌을 포함하는 바인더 수지용 조성물로부터 중합된 공중합체일 수 있다.
본 명세서의 일 구현예에 따르면, 본 명세서의 바인더 수지는 옥세테닐 메타크릴레이트, 메타크릴산 및 스티렌을 포함하는 바인더 수지용 조성물로부터 중합된 공중합체일 수 있다.
본 명세서의 일 구현예에 따르면, 본 명세서의 바인더 수지의 함량은 경화성 조성물의 전체 고형분 100 중량부에 대하여 20 내지 99.9 중량부일 수 있다. 상기 바인더 수지의 함량이 20 중량부 이상인 경우 고분자 성분이 적당하여 박막 형성이 용이하며, 상기 바인더 수지의 함량이 99.9 중량부 이하인 경우 계면 활성제 등의 첨가제를 투입하여 효과를 기대할 수 있다.
본 명세서의 일 구현예에 따르면, 본 명세서의 바인더 수지의 질량 평균 분자량이 5,000 내지 150,000일 수 있으나, 이에 한정되지 않는다.
본 명세서의 일 구현예에 따르면, 상기 경화성 조성물의 고형분의 함량은 상기 경화성 조성물에 대하여 1 중량% 이상인 것이 바람직하다. 1 중량% 이상인 경우 용매의 함량이 적절하여 균일한 코팅을 기대할 수 있다.
본 명세서의 일 구현예에 따르면, 상기 경화성 조성물의 고형분은 상한선을 특별히 한정하지 않으며, 용매 없이 고형분만으로 사용할 수 있다.
본 명세서의 일 구현예에 따르면, 본 명세서의 경화성 조성물은 가교성 화합물; 용매; 계면활성제; 커플링제; 산화방지제; 및 중합금지제로 이루어진 군에서 선택되는 1종 또는 2종 이상을 더 포함할 수 있다.
본 명세서의 일 구현예에 따르면, 상기 경화성 조성물은 착색제; 열중합 억제제; 가소제; 접착촉진제; 및 충전제로 이루어진 군에서 선택되는 1종 또는 2종 이상을 더 포함할 수 있다.
상기 가교성 화합물; 용매; 계면활성제; 커플링제; 산화방지제; 중합금지제; 착색제; 열중합 억제제; 가소제; 접착촉진제; 및 충전제는 당 기술분야에 알려져 있는 일반적인 것들을 사용할 수 있다.
예를 들면, 상기 가교성 화합물; 용매; 계면활성제; 커플링제; 산화방지제; 중합금지제; 착색제; 열중합 억제제; 가소제; 접착촉진제; 및 충전제는 하기에 예시된 화합물일 수 있으나, 이에 한정되지 않는다.
상기 가교성 화합물은 에틸렌글리콜 디(메타)아크릴레이트, 에틸렌 기의 수가 2 내지 14인 폴리에틸렌 글리콜 디(메타)아크릴레이트, 트리메틸올프로판 디(메타)아크릴레이트, 트리메틸올프로판 트리(메타)아크릴레이트, 펜타에리스리톨 트리(메타)아크릴레이트, 펜타에리스리톨 테트라(메타)아크릴레이트, 2-트리스아크릴로일옥시메틸에틸프탈산, 프로필렌기의 수가 2 내지 14인 프로필렌 글리콜 디(메타)아크릴레이트, 디펜타에리스리톨 펜타(메타)아크릴레이트, 디펜타에리스리톨 헥사(메타)아크릴레이트, 디펜타에리스리톨 펜타(메타)아크릴레이트의 산성 변형물과 디펜타에리스리톨 헥사(메타)아크릴레이트의 혼합물(상품명으로 일본 동아합성사의 TO-2348, TO-2349) 등의 다가 알코올을 α,β-불포화 카르복실산으로 에스테르화하여 얻어지는 화합물; 트리메틸올프로판 트리글리시딜에테르아크릴산 부가물, 비스페놀 A 디글리시딜에테르아크릴산 부가물 등의 글리시딜기를 함유하는 화합물에 (메타)아크릴산을 부가하여 얻어지는 화합물; β-히드록시에틸(메타)아크릴레이트의 프탈산디에스테르, β-히드록시에틸 (메타)아크릴레이트의 톨루엔 디이소시아네이트 부가물 등의 수산기 또는 에틸렌성 불포화 결합을 갖는 화합물과 다가 카르복실산과의 에스테르 화합물, 또는 폴리이소시아네이트와의 부가물; 메틸(메타)아크릴레이트, 에틸(메타)아크릴레이트, 부틸(메타)아크릴레이트, 2-에틸헥실(메타)아크릴레이트 등의 (메타)아크릴산 알킬에스테르; 및 9,9'-비스[4-(2-아크릴로일옥시에톡시)페닐]플루오렌으로 이루어지는 군으로부터 선택되는 1종 이상을 포함할 수 있다.
또한, 상기 가교성 화합물에 실리카 분산체를 사용할 수 있는데, 예를 들면 Hanse Chemie 社제 Nanocryl XP series(0596, 1045, 21/1364)와 Nanopox XP series(0516, 0525) 등이 될 수 있다.
본 명세서의 일 구현예에 따르면, 상기 가교성 화합물의 함량은 상기 경화성 조성물의 전체 고형분 100 중량부에 대하여 1 내지 50 중량부일 수 있다.
상기 용매는 메틸 에틸 케톤, 메틸 셀로솔브, 에틸셀로솔브, 에틸렌글리콜 디메틸 에테르, 에틸렌글리콜 디에틸 에테르, 프로필렌글리콜 디메틸 에테르, 프로필렌글리콜 디에틸 에테르, 디에틸렌글리콜 디메틸에테르, 디에틸렌글리콜 디에틸에테르, 디에틸렌글리콜 메틸 에틸 에테르, 2-에톡시 프로판올, 2-메톡시 프로판올, 3-메톡시 부탄올, 시클로헥사논, 시클로펜타논, 프로필렌글리콜 메틸 에테르 아세테이트, 프로필렌글리콜 에틸 에테르 아세테이트, 3-메톡시부틸 아세테이트, 에틸 3-에톡시프로피오네이트, 에틸 셀로솔브아세테이트, 메틸 셀로솔브아세테이트, 부틸 아세테이트, 및 디프로필렌글리콜 모노메틸 에테르로 이루어진 군으로부터 선택된 1종 이상을 포함할 수 있다.
본 명세서의 일 구현예에 따르면, 상기 용매의 함량은 상기 경화성 조성물 중의 전체 고형분에 대하여 99 중량% 이하일 수 있다.
상기 용매의 함량은 하한선을 특별히 한정하지 않으며, 용매 없이 고형분만으로 사용할 수 있다.
상기 계면활성제는 BYK사의 BYK-307, BYK-331 또는 DIC사의 F488과 같은 실리콘 또는 과불화 화합물 구조의 비이온성 계면활성제일 수 있다.
본 명세서의 일 구현예에 따르면, 상기 계면활성제의 함량은 상기 경화성 조성물의 전체 고형분 100 중량부에 대하여 0.3 내지 2 중량부 일 수 있다.
상기 커플링제는 Shinetsu사의 KBM-503 또는 KBM-403 등의 살란 커플링제일 수 있다.
본 명세서의 일 구현예에 따르면, 상기 커플링제의 함량은 상기 경화성 조성물의 전체 고형분 100 중량부에 대하여 0.3 내지 2 중량부일 수 있다.
상기 산화방지제는 아스코빅산, 2,6-디-테르트-부틸-p-크레솔(2,6-di-tert-butyl-p-cresol) 또는 4-메톡시페놀일 수 있다.
본 명세서의 일 구현예에 따르면, 상기 산화방지제의 함량은 상기 경화성 조성물의 전체 고형분 100 중량부에 대하여 0.3 내지 2 중량부일 수 있다.
상기 중합금지제는 아스코빅산, 2,6-디-테르트-부틸-p-크레솔(2,6-di-tert-butyl-p-cresol) 또는 4-메톡시페놀이 될 수 있다.
본 명세서의 일 구현예에 따르면, 상기 중합금지제의 함량은 상기 경화성 조성물의 전체 고형분 100 중량부에 대하여 0.3 내지 2 중량부일 수 있다.
상기 착색제는 1종 이상의 안료, 염료 또는 이들의 혼합물을 사용할 수 있다.
보다 구체적으로, 흑색 안료로는 카본 블랙, 흑연, 티탄 블랙 등과 같은 금속산화물 등을 사용할 수 있다. 카본 블랙의 예로는 시스토 5HIISAF-HS, 시스토 KH, 시스토 3HHAF-HS, 시스토 NH, 시스토 3M, 시스토 300HAF-LS, 시스토 116HMMAF-HS, 시스토 116MAF, 시스토 FMFEF-HS, 시스토 SOFEF, 시스토 VGPF, 시스토 SVHSRF-HS 및 시스토 SSRF(동해카본 ㈜) ; 다이어그램 블랙 II, 다이어그램 블랙 N339, 다이어그램 블랙 SH, 다이어그램 블랙 H, 다이어그램 LH, 다이어그램 HA, 다이어그램 SF, 다이어그램 N550M, 다이어그램 M, 다이어그램 E, 다이어그램 G, 다이어그램 R, 다이어그램 N760M, 다이어그램 LR, #2700, #2600, #2400, #2350, #2300, #2200, #1000, #980, #900, MCF88, #52, #50, #47, #45, #45L, #25, #CF9, #95, #3030, #3050, MA7, MA77, MA8, MA11, MA100, MA40, OIL7B, OIL9B, OIL11B, OIL30B 및 OIL31B(미쯔비시화학㈜) ; PRINTEX-U, PRINTEX-V, PRINTEX-140U, PRINTEX-140V, PRINTEX-95, PRINTEX-85, PRINTEX-75, PRINTEX-55, PRINTEX-45, PRINTEX-300, PRINTEX-35, PRINTEX-25, PRINTEX-200, PRINTEX-40, PRINTEX-30, PRINTEX-3, PRINTEX-A, SPECIAL BLACK-550, SPECIAL BLACK-350, SPECIAL BLACK-250, SPECIAL BLACK-100, 및 LAMP BLACK-101(대구사㈜); RAVEN-1100ULTRA, RAVEN-1080ULTRA, RAVEN-1060ULTRA, RAVEN-1040, RAVEN-1035, RAVEN-1020, RAVEN-1000, RAVEN-890H, RAVEN-890, RAVEN-880ULTRA, RAVEN-860ULTRA, RAVEN-850, RAVEN-820, RAVEN-790ULTRA, RAVEN-780ULTRA, RAVEN-760ULTRA, RAVEN-520, RAVEN-500, RAVEN-460, RAVEN-450, RAVEN-430ULTRA, RAVEN-420, RAVEN-410, RAVEN-2500ULTRA, RAVEN-2000, RAVEN-1500, RAVEN-1255, RAVEN-1250, RAVEN-1200, RAVEN-1190ULTRA, RAVEN-1170(콜롬비아 카본㈜) 또는 이들의 혼합물 등이 있다.
또한, 색깔을 띄는 착색제의 예로는 카민 6B(C.I.12490), 프탈로시아닌 그린(C.I. 74260), 프탈로시아닌 블루(C.I. 74160), 페릴렌 블랙(BASF K0084. K0086), 시아닌 블랙, 리놀옐로우(C.I.21090), 리놀 옐로우GRO(C.I. 21090), 벤지딘 옐로우4T-564D, 빅토리아 퓨어 블루(C.I.42595), C.I. PIGMENT RED 3, 23, 97, 108, 122, 139, 140, 141, 142, 143, 144, 149, 166, 168, 175, 177, 180, 185, 189, 190, 192, 202, 214, 215, 220, 221, 224, 230, 235, 242, 254, 255, 260, 262, 264, 272; C.I. PIGMENT GREEN 7, 36; C.I. PIGMENT blue 15:1, 15:3, 15:4, 15:6, 16, 22, 28, 36, 60, 64; C.I. PIGMENT yellow 13, 14, 35, 53, 83, 93, 95, 110, 120, 138, 139, 150, 151, 154, 175, 180, 181, 185, 194, 213; C.I. PIGMENT VIOLET 15, 19, 23, 29, 32, 37 등이 있고, 이 밖에 백색 안료, 형광 안료 등도 이용할 수 있다. 안료로 사용되는 프탈로시아닌계 착화합물로는 구리 외에 아연을 중심 금속으로 하는 물질도 사용 가능할 수 있다.
본 명세서의 일 구현예에 따르면, 상기 착색제의 함량은 상기 경화성 조성물의 전체 고형분 100 중량부에 대하여 0.011 내지 30 중량부일 수 있다.
상기 열중합억제제는 p-아니솔, 히드로퀴논, 피로카테콜(pyrocatechol), t-부틸카테콜(t-butyl catechol), N-니트로소페닐히드록시아민 암모늄염, N-니트로소페닐히드록시아민 알루미늄염 및 페노티아진(phenothiazine)으로 이루어진 군으로부터 선택된 1 종 이상을 포함할 수 있다.
본 명세서의 일 구현예에 따르면, 상기 열중합 억제제의 함량은 상기 경화성 조성물의 전체 고형분 100 중량부에 대하여 0.3 내지 2 중량부일 수 있다.
상기 가소제는 종래의 경화성 조성물에 포함될 수 있는 모든 화합물이 사용될 수 있다.
본 명세서의 일 구현예에 따르면, 상기 가소제의 함량은 상기 경화성 조성물의 전체 고형분 100 중량부에 대하여 0.3 내지 2 중량부일 수 있다.
상기 접착촉진제는 종래의 경화성 조성물에 포함될 수 있는 모든 화합물이 사용될 수 있다.
본 명세서의 일 구현예에 따르면, 상기 접착촉진제의 함량은 상기 경화성 조성물의 전체 고형분 100 중량부에 대하여 0.3 내지 2 중량부일 수 있다.
상기 충전제는 종래의 경화성 조성물에 포함될 수 있는 모든 화합물이 사용될 수 있다.
본 명세서의 일 구현예에 따르면, 상기 충전제의 함량은 상기 경화성 조성물의 전체 고형분 100 중량부에 대하여 0.3 내지 2 중량부일 수 있다.
본 명세서는 상기 경화성 조성물로 제조된 경화막을 제공한다.
본 명세서에 따른 경화성 조성물은 롤 코터(roll coater), 커튼 코터(curtain coater), 스핀 코터(spin coater), 슬롯 다이 코터, 각종 인쇄, 침적 등의 방법을 통해, 금속, 종이, 유리 플라스틱 기판 등의 지지체 상에 적용될 수 있다.
본 명세서의 일 구현예에 따른 상기 경화성 조성물은 필름 등의 지지체 상에 도포한 후 기타 지지체 상에 전사하여 경화막을 제조할 수 있다. 또한, 상기 경화성 조성물을 제 1의 지지체에 도포한 후 블랭킷 등에 전사하고, 다시 제 2의 지지체에 전사하는 것도 가능하며, 그 적용 방법은 특별히 한정되지 않는다.
이때, 상 경화성 조성물은 광경화성 조성물 또는 열경화성 조성물일 수 있다. 본 명세서에 따른 경화성 조성물은 열경화성 조성물이 바람직하다.
본 명세서의 일 구현예에 따르면, 상기 경화막을 제조하기 위하여, 상기 경화성 조성물을 오븐(Clean Oven)에 200 내지 250 ℃에서 5 내지 60 분 동안 방치하여 경화할 수 있다.
또한, 경우에 따라 동일한 효과를 얻기 위해 적외선 램프 등을 사용할 수도 있으며 특별히 이러한 방법에 국한되지 않는다.
본 명세서의 일 구현예에 따르면, 상기 경화성 조성물로 제조된 경화막은 디스플레이용일 수 있다.
또한, 본 명세서의 일 구현예에 따르면, 상기 경화성 조성물로 제조된 경화막은 터치패널용일 수 있다.
본 명세서의 상기 경화성 조성물은 유리 또는 필름을 기재로 하는 터치 패널의 투명 보호막에 사용할 수 있다. 또한, TFT LCD 컬러필터 제조에 사용되는 투명 또는 착색층의 박막재료나 일반적인 경화성 도료나 잉크, 접착제, 인쇄판, 인쇄배선반용 열경화제 등에 사용될 수 있으며 그 용도에 제한을 특별히 두지는 않는다.
예를 들면, 도 1과 같은 구조의 터치 패널 상에 도포된 하드 코트(Hard Coat)일 수 있으나, 이에 한정되는 것은 아니다.
본 명세서의 일 실시상태에 따라 제조된 경화막은 급격한 온도 변화에 의해 경화막이 변형되지 않는 장점이 있다.
본 명세서의 일 실시상태에 따라 제조된 경화막은 급격한 온도 변화에 의해 박리가 일어나지 않는 장점이 있다.
본 명세서의 일 구현예에 따르면, 상기 경화성 조성물을 이용하여 제작된 경화막은 고온과 저온을 반복하는 온도 충격 실험 후에도 손상되지 않는 특징이 있다.
구체적으로, 상기 경화막을 온도 섭씨 100 ℃에서 한 시간 보관한 직후 25 ℃로 냉각하는 과정을 10 번 반복하는 실험 후에도 손상되지 않는 특징이 있다.
본 명세서는 상기 경화막을 포함하는 보호막을 제공한다. 구체적으로, 상기 보호막은 투명 보호막일 수 있다.
본 명세서의 일 구현예에 따르면, 상기 투명 보호막은 가시광선 투과율이 85 %이상일 수 있다. 보다 구체적으로, 상기 투과율은 90 % 또는 95 %이상일 수 있다.
본 명세서의 일 구현예에 따르면, 상기 투명 보호막의 강도는 연필 경도(하중 500g)를 기준으로 3H이상일 수 있으며, 상기 강도는 높으면 높을수록 바람직하다.
본 명세서는 상기 경화막을 포함하는 디스플레이 장치를 제공한다.
상기 디스플레이 장치는 플라즈마 디스플레이 패널(Plasma Display Panel, PDP), 터치패널, 발광 다이오드(Light Emitting Diode, LED), 유기 발광 소자(Organic Light Emitting Diode, OLED), 액정 표시 장치(Liquid Crystal Display, LCD), 박막 트랜지스터 액정 표시 장치(Thin FIlm Transistor- Liquid Crystal Display, LCD-TFT) 및 음극선관(Cathode Ray Tube, CRT) 중 어느 하나일 수 있다.
본 명세서는 상기 경화막을 포함하는 컬러 필터를 제공한다.
상기 컬러필터는 블랙매트리스, 컬러패턴 및 공통 전극을 더 포함할 수 있다. 상기 컬러패턴은 적색 패턴, 녹색 패턴 및 청색 패턴(RGB패턴)을 포함할 수 있으나, 이에 한정되는 것은 아니다.
본 명세서의 일 구현예에 따르면, 상기 컬러필터는 블랙매트리스, 컬러패턴 및 공통 전극 상에 형성된 상기 경화막을 포함할 수 있다.
본 명세서의 일 구현예에 따르면, 상기 컬러필터 상에 형성된 경화막의 평탄화도는 50%이상인 것이 바람직하다.
상기 평탄화도의 실험조건은 유리 기판 위에 선폭 50 μm, 두께 1.5 μm, 선과 선 사이의 간격이 50 μm가 되도록 선 및 간격 패턴(line-and space pattern)을 형성하여 테스트 기판을 완성하였고, 상기 테스트 기판 위에 본 발명에서 얻어진 경화막 조성물을 두께 5 μm가 되도록 100 ℃에서 200초 동안 프리베이크(pre-baked) 공정을 수행하여 용매를 휘발시켰다. 이 후 상기 경화막을 다시 230 ℃ 오븐에 30분 동안 방치하여 열경화 반응을 진행시켰다. 상기 경화된 막 표면의 요철을 측정하고, 그 값을 1.5로 나눈 값을 1에서 뺀 후 100을 곱해 평탄화도를 계산하였다.
예를 들어, 경화막의 요철의 깊이가 0.5 μm라고 가정하면, 상기 경화막의 평탄화도는 (1-0.5/1.5)×100= 67%이다.
본 명세서의 일 구현예에 따르면, 상기 컬러필터 상에 형성된 경화막의 내화학성은 70℃에서 10분 동안 N-메틸피롤리돈에 침지하는 조건에서 두께 변화를 기준으로 10% 이내인 것이 바람직하다.
이하의 합성예, 실시예 및 비교예를 통하여 본 명세서를 더욱 구체적으로 설명한다. 다만, 하기의 합성예, 실시예 및 비교예는 본 명세서를 예시하기 위한 것일 뿐, 이들만으로 본 명세서가 한정되는 것은 아니다.
[합성예 1]
500 mL 들이 둥근 바닥 플라스크에 리소시놀 디글리시딜 에테르(Resorcinol Diglycidyl Ether) 0.2 mol을 프로필렌글리콜 모노메틸 에테르 200g에 두 시간 교반하며 용해시킨 후 80 ℃로 가열한다. 또한 다른 용기에 Bis(3-trimethoxysilyl)propyl amine 0.25 mol과 프로필렌글리콜 모노메틸 에테르 200g을 섞어 완전히 용해시킨다. 이후 비스페놀 A 디글리시딜 에테르를 용해시킨 용액을 80 ℃로 유지하고 교반시키며 Bis(3-trimethoxysilyl)propyl amine 희석액을 약 5 시간에 걸쳐 천천히 투입시킨다. 투입 완료 후 1 시간 동안 상온으로 냉각시키며 교반을 계속한다. 상기 과정을 통해 얻어진 반응물을 컬럼을 통해 분리한 후 진공 증류를 이용해 용매를 마저 제거하여 [화학식 9]로 표시되는 화합물을 얻었다.
[화학식 9]
Figure 112012097682335-pat00011
[합성예 2]
[합성예 1]에서 Bis(3-trimethoxysilyl)propyl amine 대신 Bis(3-triethoxysilyl)propyl amine을 사용한 것을 제외하고는 [합성예 1]과 동일한 방법을 이용하여 [화학식 10]으로 표시되는 화합물을 얻었다.
[화학식 10]
Figure 112012097682335-pat00012
[실시예 1]
본 출원의 효과를 확인하기 위해 다음과 같은 경화성 조성물을 제조했다. 우선 글리시딜 메타크릴레이트와 메타크릴 산, 그리고 스티렌을 글리시딜 메타크릴레이트: 메타크릴 산: 스티렌의 몰비가 50: 20: 30이 되도록 섞은 후 바인더 수지용 조성물 총 중량을 기준으로 열중합 개시제로서 V-65 2 중량%를 넣고 65 ℃에서 반응하여 분자량 20,000이 되도록 바인더 수지를 합성하였다. 이렇게 만들어진 바인더 수지를 경화성 조성물의 총 중량을 기준으로 19.98 중량%(경화성 조성물의 전체 고형분 100 중량부를 기준으로 99.9 중량부)와 [화학식 9]의 물질 0.02 중량%( 경화성 조성물의 전체 고형분 100 중량부를 기준으로 0.1 중량부)를 프로펠렌 글리콜 모노메틸 에테르 아세테이트 80 중량%와 함께 섞은 후 쉐이커를 이용하여 2 시간 동안 교반하여 잘 섞이도록 한다. 이렇게 얻어진 용액을 1 μm 필터로 수득하여 경화성 조성물을 얻는다.
[실시예 2]
상기 [실시예 1]에서 바인더 수지를 19.98 중량% 대신 19 중량%(경화성 조성물의 전체 고형분 100 중량부를 기준으로 95 중량부) [화학식 9]의 화합물을 0.02 중량부 대신 1 중량부(경화성 조성물의 전체 고형분 100 중량부를 기준으로 5 중량부)를 사용한 것으로 제외하고는 [실시예 1]과 동일하다.
[실시예 3]
상기 [실시예 1]에서 바인더 수지를 19.98 중량% 대신 17.00 중량%( 경화성 조성물의 전체 고형분 100 중량부를 기준으로 85 중량부) [화학식 9]의 화합물을 0.02 중량% 대신 3 중량%( 경화성 조성물의 전체 고형분 100 중량부를 기준으로 15 중량부)를 사용한 것으로 제외하고는 [실시예 1]과 동일하다.
[실시예 4]
상기 [실시예 1]에서 [화학식 9]의 화합물 대신 [화학식 10]의 화합물을 사용하 것을 제외하고는 [실시예 1]과 동일하다.
[실시예 5]
상기 [실시예 2]에서 [화학식 9]의 화합물 대신 [화학식 10]의 화합물을 사용하 것을 제외하고는 [실시예 2]와 동일하다.
[실시예 6]
상기 [실시예 3]에서 [화학식 9]의 화합물 대신 [화학식 10]의 화합물을 사용하 것을 제외하고는 [실시예 3]과 동일하다.
[비교예 1]
상기 [실시예 1]에서 바인더 수지를 19.98 중량% 대신 20 중량%( 경화성 조성물의 전체 고형분 100 중량부를 기준으로 100 중량부) [화학식 9]의 화합물을 0.02 중량% 대신 0 중량%(경화성 조성물의 전체 고형분 100 중량부를 기준으로 0 중량부)를 사용한 것으로 제외하고는 [실시예 1]과 동일하다.
[실험예]
고온-저온 충격 평가
상기 실시예 1 내지 6 및 비교예 1에서 얻어진 경화성 조성물을 스핀 코팅 방법을 이용하여 균일한 막을 형성한 후 100 ℃ 에서 200 초 동안 프리 베이크 공정을 수행하여 용매를 휘발시킨다. 건조된 막의 두께는 약 5 μm 이다. 이후 상기 막을 다시 230 ℃ 오븐에 30 분 동안 방치하여 열경화 반응을 진행시킨다. 이렇게 하여 얻어진 경화막을 하기의 방법을 이용하여 내구성을 평가한다.
상기 방법을 이용하여 형성된 경화막을 온도 섭씨 100 ℃에서 한 시간 보관한 후 바로 25 ℃로 냉각하는 과정을 10 번 반복한 후 경화막의 손상 정도를 확인한다.
상기 실시예와 비교예의 실험 결과를 정리하면 다음과 같다.
Figure 112012097682335-pat00013
상기 실험 결과에서 보듯이 본 명세서에서 제시한 경화성 조성물을 사용하는 경우 고온-저온의 충격 실험 이후에도 경화막이 손상되지 않음을 알 수 있다.

Claims (21)

  1. 에폭시기를 포함하는 바인더 수지; 및 하기 화학식 1로 표시되는 화합물 및 하기 화학식 2로 표시되는 화합물 중 적어도 하나를 포함하는 실록산 화합물을 포함하는 경화성 조성물:
    [화학식 1]
    Figure 112012097682335-pat00014

    [화학식 2]
    Figure 112012097682335-pat00015

    상기 화학식 1 및 2에서,
    X1, X2, X3, X6, X7, X8, X10, X11, X12, X15, X16, X17, R1, R2, R3, R6, R7, R8, R10, R11, R12, R15, R16 및 R17은 각각 독립적으로 C1~C3의 알킬기이고,
    X4, X5, X13, X14, R4, R5, R13 및 R14는 각각 독립적으로 C1~C10의 알킬렌기이며,
    X9 , R9 , R18 및 R19는 각각 독립적으로 C1~C10의 알킬기이고,
    m 및 n은 0~4인 정수이며, o 및 p는 0~3인 정수이다.
  2. 청구항 1에 있어서, 상기 화학식 1로 표시되는 화합물은 하기 화학식 3으로 표시되는 화합물인 것인 경화성 조성물:
    [화학식 3]
    Figure 112012097682335-pat00016

    상기 화학식 3에서, X1, X2, X3, X6, X7, X8, X10, X11, X12, X15, X16 및 X17은 각각 독립적으로 C1~C3의 알킬기이고, X9는 각각 독립적으로 C1~C10의 알킬기이며, m은 0~4인 정수이다.
  3. 청구항 1에 있어서, 상기 화학식 2로 표시되는 화합물은 하기 화학식 4로 표시되는 화합물인 것인 경화성 조성물:
    [화학식 4]
    Figure 112012097682335-pat00017

    상기 화학식 4에서, R1, R2, R3, R6, R7, R8, R10, R11, R12, R15, R16 및 R17은 각각 독립적으로 C1~C3의 알킬기이고, R9 , R18 및 R19는 각각 독립적으로 C1~C10의 알킬기이며, n은 0~4인 정수이고, o 및 p는 0~3인 정수이다.
  4. 청구항 1에 있어서, 상기 화학식 1로 표시되는 화합물은 하기 화학식 5로 표시되는 화합물 또는 하기 화학식 6으로 표시되는 화합물인 것인 경화성 조성물:
    [화학식 5]
    Figure 112012097682335-pat00018

    [화학식 6]
    Figure 112012097682335-pat00019

    상기 화학식 5 및 6에서, X4, X5, X13 및 X14는 각각 독립적으로 C1~C10의 알킬렌기이며, X9 는 C1~C10의 알킬기이고, m은 0~4인 정수이다.
  5. 청구항 1에 있어서, 상기 화학식 2로 표시되는 화합물은 하기 화학식 7로 표시되는 화합물 또는 하기 화학식 8로 표시되는 화합물인 것인 경화성 조성물:
    [화학식 7]
    Figure 112012097682335-pat00020

    [화학식 8]
    Figure 112012097682335-pat00021

    상기 화학식 7 및 8에서, R4, R5, R13 및 R14는 각각 독립적으로 C1~C10의 알킬렌기이고, R9 , R18 및 R19는 C1~C10의 알킬기이며, n은 0~4인 정수이고, o 및 p는 0~3인 정수이다.
  6. 청구항 1 에 있어서, 상기 실록산 화합물의 함량은 경화성 조성물의 전체 고형분 100 중량부에 대하여 0.1 내지 15 중량부인 것인 경화성 조성물.
  7. 청구항 1에 있어서, 상기 바인더 수지는 질량 평균 분자량이 5,000 내지 150,000 인 것인 경화성 조성물.
  8. 청구항 1에 있어서, 상기 바인더 수지는 에폭시계 단량체 및 (메트)아크릴레이트계 단량체를 포함하는 바인더 수지용 조성물로부터 중합된 공중합체인 것인 경화성 조성물.
  9. 청구항 8에 있어서, 상기 바인더 수지용 조성물은 방향족 비닐계 단량체를 더 포함하는 것인 경화성 조성물.
  10. 청구항 9에 있어서, 상기 바인더 수지용 조성물은 글리시딜 메타크릴레이트, 메타크릴산 및 스티렌을 포함하거나, 옥세테닐 메타크릴레이트, 메타크릴산 및 스티렌을 포함하는 것인 경화성 조성물.
  11. 청구항 1에 있어서, 상기 바인더 수지의 함량은 경화성 조성물의 전체 고형분 100 중량부에 대하여 20 내지 99.9 중량부인 것인 경화성 조성물.
  12. 청구항 1에 있어서, 상기 경화성 조성물은 가교성 화합물; 용매; 계면활성제; 커플링제; 산화방지제; 및 중합금지제로 이루어진 군에서 선택되는 1종 또는 2종 이상을 더 포함하는 것인 경화성 조성물.
  13. 청구항 1에 있어서, 상기 경화성 조성물은 착색제; 열중합 억제제; 가소제; 접착촉진제; 및 충전제로 이루어진 군에서 선택되는 1종 또는 2종 이상을 더 포함하는 것인 경화성 조성물.
  14. 청구항 1 내지 13 중 어느 한 항에 따른 경화성 조성물로 제조된 경화막.
  15. 청구항 14에 있어서, 상기 경화막은 100 ℃에서 한 시간 보관한 직후 25 ℃로 냉각하는 과정을 10 번 반복하는 고온-저온 충격 평가에서 손상되지 않는 경화막.
  16. 청구항 14에 있어서, 상기 경화막의 두께는 0.5 내지 15 μm 인 것인 경화막.
  17. 청구항 14에 있어서, 상기 경화막은 디스플레이용 또는 터치패널용인 것인 경화막.
  18. 청구항 14에 따른 경화막을 포함하는 보호막.
  19. 청구항 18에 있어서, 상기 보호막은 가시광선 투과율이 85 % 이상인 것인 보호막.
  20. 청구항 14에 따른 상기 경화막을 포함하는 디스플레이 장치.
  21. 청구항 14에 따른 상기 경화막을 포함하는 컬러 필터.
KR20120134767A 2012-11-26 2012-11-26 경화성 조성물, 이로 제조된 경화막 및 이를 포함하는 디스플레이 장치 KR101486635B1 (ko)