JPWO2013129338A1 - カメラモジュール用液晶性樹脂組成物 - Google Patents
カメラモジュール用液晶性樹脂組成物 Download PDFInfo
- Publication number
- JPWO2013129338A1 JPWO2013129338A1 JP2014502219A JP2014502219A JPWO2013129338A1 JP WO2013129338 A1 JPWO2013129338 A1 JP WO2013129338A1 JP 2014502219 A JP2014502219 A JP 2014502219A JP 2014502219 A JP2014502219 A JP 2014502219A JP WO2013129338 A1 JPWO2013129338 A1 JP WO2013129338A1
- Authority
- JP
- Japan
- Prior art keywords
- liquid crystalline
- crystalline resin
- component
- resin composition
- camera module
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
本発明のカメラモジュール用液晶性樹脂組成物は、(A)液晶性樹脂、(B)無機充填剤、(C)共重合体が必須成分として配合される。
本発明で使用する(A)液晶性樹脂とは、光学異方性溶融相を形成し得る性質を有する溶融加工性ポリマーを指す。異方性溶融相の性質は、直交偏光子を利用した慣用の偏光検査法により確認することが出来る。より具体的には、異方性溶融相の確認は、Leitz偏光顕微鏡を使用し、Leitzホットステージに載せた溶融試料を窒素雰囲気下で40倍の倍率で観察することにより実施できる。本発明に適用できる液晶性ポリマーは直交偏光子の間で検査したときに、たとえ溶融静止状態であっても偏光は通常透過し、光学的に異方性を示す。
(1)主として芳香族ヒドロキシカルボン酸及びその誘導体の1種又は2種以上からなるポリエステル;
(2)主として(a)芳香族ヒドロキシカルボン酸及びその誘導体の1種又は2種以上と、(b)芳香族ジカルボン酸、脂環族ジカルボン酸及びその誘導体の1種又は2種以上と、(c)芳香族ジオール、脂環族ジオール、脂肪族ジオール及びその誘導体の少なくとも1種又は2種以上、とからなるポリエステル;
(3)主として(a)芳香族ヒドロキシカルボン酸及びその誘導体の1種又は2種以上と、(b)芳香族ヒドロキシアミン、芳香族ジアミン及びその誘導体の1種又は2種以上と、(c)芳香族ジカルボン酸、脂環族ジカルボン酸及びその誘導体の1種又は2種以上、とからなるポリエステルアミド;
(4)主として(a)芳香族ヒドロキシカルボン酸及びその誘導体の1種又は2種以上と、(b)芳香族ヒドロキシアミン、芳香族ジアミン及びその誘導体の1種又は2種以上と、(c)芳香族ジカルボン酸、脂環族ジカルボン酸及びその誘導体の1種又は2種以上と、(d)芳香族ジオール、脂環族ジオール、脂肪族ジオール及びその誘導体の少なくとも1種又は2種以上、とからなるポリエステルアミド等が挙げられる。さらに上記の構成成分に必要に応じ分子量調整剤を併用してもよい。
レンジアミン等の芳香族アミン類が挙げられる。
(B)無機充填剤は、(B1)平均繊維径1.0μm以下且つ平均繊維長が5〜50μmの繊維状充填剤、及び(B2)平均粒子径50μm以下の非繊維状充填剤から選択される少なくとも1種である。
(C)共重合体は、(C1)オレフィン系共重合体及び(C2)スチレン系共重合体から選択される少なくとも1種である。(C)成分をカメラモジュール用液晶性樹脂組成物に配合させることが、当該組成物を成形してなる成形体を超音波洗浄したときの、成形体表面の起毛を抑えることに寄与する。
起毛を抑える理由については明確になっておるわけではないが、ある一定量配合させることにより、成形体表面状態を変化させ、その変化が起毛を抑えることに寄与していると考えている。
本発明に用いる(D)カーボンブラックは、樹脂着色に用いられる一般的に入手可能な特に限定されるものではないが、通常は一次粒子が凝集して出来上がる塊状物が含まれており50μm以上の大きさの塊状物が著しく多く含まれると本発明の樹脂組成物を成形してなる成形体の表面にブツ(カーボンブラックが凝集した細かいブツブツ状突起物(細かい凹凸))が多く発生する場合があり好ましくない。上記塊状物粒子径は50μm以上の粒子が20ppm以下であることは成形体表面の起毛抑制の点で必要である。好ましい含有率は5ppm以下である。
本発明のカメラモジュール用液晶性樹脂組成物には、本発明の効果を害さない範囲で、その他の重合体、一般に合成樹脂に添加される公知の物質、すなわち酸化防止剤や紫外線吸収剤等の安定剤、帯電防止剤、難燃剤、染料や顔料等の着色剤、潤滑剤、離型剤、及び結晶化促進剤、結晶核剤等も要求性能に応じ適宜添加することができる。
本発明のカメラモジュール用樹脂組成物の調製は特に限定されない。例えば、上記(A)、(B)、(C)成分を添加配合して、これらを1軸又は2軸押出機を用いて溶融混練処理することで、カメラモジュール用液晶性樹脂組成物の調製が行われる。
本発明のカメラモジュール用液晶性樹脂組成物中の(B)成分の形状と、配合される前の(B)成分の形状とは異なる。上述の(B)成分の形状は配合される前の形状である。配合される前の形状が上述の通りであれば、表面が起毛し難いカメラモジュール用部品が得られる。
上記カメラモジュール用液晶性樹脂組成物を用いて、カメラモジュール用部品を製造する。本発明の樹脂組成物を原料として用いれば、カメラモジュール用部品の表面が起毛しにくくなる。カメラモジュール用部品は、超音波洗浄されるため、超音波洗浄されても表面が起毛しにくいことが求められる。本発明の樹脂組成物を用いれば、カメラモジュール用部品の超音波洗浄をより強い条件で行っても、ゴミ等の原因となる脱落物が生じないか、ほとんど生じない。したがって、カメラモジュール用部品が完成品に組み込まれた後に、このカメラモジュール用部品の表面が起毛することにより生じるゴミで、完成品の品質に影響を与えることはほとんど無い。
液晶性樹脂(液晶性ポリエステルアミド樹脂):ベクトラ(登録商標)E950i(ポリプラスチックス(株)製)
繊維状充填剤1:大塚化学(株)製 ティスモN−102(チタン酸カリウム繊維、平均繊維径0.3〜0.6μm、平均繊維長10〜20μm)
繊維状充填剤2:日東紡績(株)製 PF70E−001(ミルドガラスファイバー、繊維径10μm、重量平均長さ70μm)
非繊維状充填剤1:松村産業(株)製 クラウンタルクPP(タルク、平均粒子径12.8μm、平均アスペクト比6)
非繊維状充填剤2:(株)山口雲母工業製AB−25S(マイカ、平均粒子径24μm)
非繊維状充填剤3:(株)山口雲母工業製A−41S(マイカ、平均粒子径47μm)
オレフィン系共重合体:住友化学(株)製 ボンドファースト2C(エチレン−グリシジルメタクリレート共重合体(グリシジルメタクリレートを6重量%含有))
カーボンブラック:キャボットジャパン(株)製 VULCAN XC305(カーボンブラック、平均粒子径20nm、粒子径50μm以上の割合が20ppm以下、粒状)
上記成分を、表1に示す割合で二軸押出機((株)日本製鋼所製TEX30α型)を用いて、シリンダー温度350℃にて溶融混練し、カメラモジュール用液晶性樹脂組成物ペレットを得た。
実施例及び比較例のカメラモジュール用液晶性樹脂組成物の溶融粘度を、上記ペレットを用いて測定した。具体的には、キャピラリー式レオメーター(東洋精機製キャピログラフ1D:ピストン径10mm)により、シリンダー温度350℃、せん断速度1000sec−1の条件での見かけの溶融粘度をISO 11443に準拠して測定した。測定には、内径1mm、長さ20mmのオリフィスを用いた。なお、測定結果は表1に示した。
実施例及び比較例のカメラモジュール用液晶性樹脂組成物の流動性を、上記ペレットを用いて評価した。具体的には上記ペレットを、成形機(住友重機械工業社製 「SE30DUZ」)を用いて、以下の成形条件で厚さ0.3mmの試験片に成形した。得られる成形体の長さを測ることにより流動性を評価した。なお、評価結果を表1に示した。
〔成形条件〕
シリンダー温度:350℃
金型温度:80℃
射出圧力:100MPa
射出速度:200mm/sec
実施例及び比較例のペレットを、成形機(住友重機械工業社製 「SE30DUZ」)を用いて、以下の成形条件で成形し、12.5mm×120mm×0.8mmの成形体を得た。この成形体を半分に切断したものを試験片として使用した。
〔成形条件〕
シリンダー温度: 350℃
金型温度: 90℃
射出速度: 80mm/sec
〔評価〕
半分に切断した成形体を3分間、室温の水中で超音波洗浄機(出力300W、周波数45kHz)にかけた。その後、超音波洗浄機にかける前後の成形体を比較して、成形体表面の毛羽立った部分の面積(起毛面積)を画像測定器((株)ニレコ製LUZEXFS)にて評価した。なお、評価面積は750mm2(12.5mm×60mm)である。評価結果を表1に示した。
起毛面積が少ないほど、起毛抑制効果が高い評価となる。
実施例及び比較例のペレットを、成形機(住友重機械工業社製 「SE100DU」)を用いて、以下の成形条件で測定用試験片(4mm×10mm×80mm)に成形した。その後、ISO 75−1,2に準拠した方法で荷重たわみ温度を測定した。測定結果は表1に示した。
〔成形条件〕
シリンダー温度: 350℃
金型温度: 80℃
背圧: 2.0MPa
射出速度: 33mm/sec
実施例及び比較例のペレットを、成形機(住友重機械工業社製 「SE100DU」)を用いて、以下の成形条件で測定用試験片(4mm×10mm×80mm)に成形した。その後、ISO 179−1に準拠した方法でシャルピー衝撃値を測定した。結果を表1に示す。
〔成形条件〕
シリンダー温度: 350℃
金型温度: 80℃
背圧: 2.0MPa
射出速度: 33mm/sec
10 基板
11 光学素子
12 リード配線
13 ホルダー
14 バレル
15 レンズ
16 IRフィルター
Claims (3)
- (A)液晶性樹脂に、
(B1)繊維状充填剤及び(B2)非繊維状充填剤から選択される少なくとも1種の(B)無機充填剤、
(C1)オレフィン系共重合体及び(C2)スチレン系共重合体から選択される少なくとも1種の(C)共重合体を、
(A)成分が65〜93質量%、(B)成分が5〜20質量%、(C)成分が2〜10質量%になるように配合してなり、
前記(B1)繊維状充填剤は、平均繊維径が1.0μm以下、且つ平均繊維長が5〜50μmであり、
前記(B2)非繊維状充填剤は、平均粒子径が50μm以下の、板状充填剤及び粒状充填剤から選択される少なくとも1種であり、
前記(C1)オレフィン系共重合体は、α−オレフィンとα,β−不飽和酸のグリシジルエステルとから構成され、
前記(C2)スチレン系共重合体は、スチレン類とα,β−不飽和酸のグリシジルエステルとから構成されるカメラモジュール用液晶性樹脂組成物。 - 前記(B2)非繊維状充填剤の平均粒子径は10〜20μmである請求項1に記載のカメラモジュール用液晶性樹脂組成物。
- さらに(D)カーボンブラックを、その含有量が1〜5質量%になるように配合してなる請求項1又は2に記載のカメラモジュール用液晶性樹脂組成物。