JPS6238426B2 - - Google Patents
Info
- Publication number
- JPS6238426B2 JPS6238426B2 JP10910879A JP10910879A JPS6238426B2 JP S6238426 B2 JPS6238426 B2 JP S6238426B2 JP 10910879 A JP10910879 A JP 10910879A JP 10910879 A JP10910879 A JP 10910879A JP S6238426 B2 JPS6238426 B2 JP S6238426B2
- Authority
- JP
- Japan
- Prior art keywords
- temperature
- less
- equivalent
- steel
- low
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired
Links
- 229910000831 Steel Inorganic materials 0.000 claims description 47
- 239000010959 steel Substances 0.000 claims description 47
- 238000005496 tempering Methods 0.000 claims description 24
- 230000000171 quenching effect Effects 0.000 claims description 11
- 238000010791 quenching Methods 0.000 claims description 10
- 229910052804 chromium Inorganic materials 0.000 claims description 9
- 238000010438 heat treatment Methods 0.000 claims description 9
- 229910052758 niobium Inorganic materials 0.000 claims description 6
- 229910052715 tantalum Inorganic materials 0.000 claims description 6
- 229910052726 zirconium Inorganic materials 0.000 claims description 6
- 238000000034 method Methods 0.000 claims description 5
- 229910052782 aluminium Inorganic materials 0.000 claims description 4
- 229910052759 nickel Inorganic materials 0.000 claims description 4
- 229910052802 copper Inorganic materials 0.000 claims description 3
- 229910052742 iron Inorganic materials 0.000 claims description 3
- 229910052720 vanadium Inorganic materials 0.000 claims description 3
- 239000000956 alloy Substances 0.000 claims 1
- 229910045601 alloy Inorganic materials 0.000 claims 1
- 238000013016 damping Methods 0.000 description 13
- 229910001566 austenite Inorganic materials 0.000 description 11
- 230000000717 retained effect Effects 0.000 description 9
- 230000007423 decrease Effects 0.000 description 8
- 238000012360 testing method Methods 0.000 description 8
- 229910019589 Cr—Fe Inorganic materials 0.000 description 7
- 239000000463 material Substances 0.000 description 7
- 239000003949 liquefied natural gas Substances 0.000 description 6
- 239000000203 mixture Substances 0.000 description 6
- 238000010586 diagram Methods 0.000 description 5
- 230000000052 comparative effect Effects 0.000 description 4
- 230000000694 effects Effects 0.000 description 4
- 238000010248 power generation Methods 0.000 description 4
- 230000008018 melting Effects 0.000 description 3
- 238000002844 melting Methods 0.000 description 3
- 150000001247 metal acetylides Chemical class 0.000 description 3
- XAGFODPZIPBFFR-UHFFFAOYSA-N aluminium Chemical compound [Al] XAGFODPZIPBFFR-UHFFFAOYSA-N 0.000 description 2
- 238000009863 impact test Methods 0.000 description 2
- 239000011159 matrix material Substances 0.000 description 2
- 238000007670 refining Methods 0.000 description 2
- 229910052721 tungsten Inorganic materials 0.000 description 2
- 230000008016 vaporization Effects 0.000 description 2
- 238000009834 vaporization Methods 0.000 description 2
- 229910000859 α-Fe Inorganic materials 0.000 description 2
- -1 Mo: 3.0% or less Inorganic materials 0.000 description 1
- UCKMPCXJQFINFW-UHFFFAOYSA-N Sulphide Chemical compound [S-2] UCKMPCXJQFINFW-UHFFFAOYSA-N 0.000 description 1
- 230000015572 biosynthetic process Effects 0.000 description 1
- 230000003749 cleanliness Effects 0.000 description 1
- 238000003776 cleavage reaction Methods 0.000 description 1
- 238000005260 corrosion Methods 0.000 description 1
- 230000007797 corrosion Effects 0.000 description 1
- 239000013078 crystal Substances 0.000 description 1
- 230000003009 desulfurizing effect Effects 0.000 description 1
- 230000002542 deteriorative effect Effects 0.000 description 1
- 238000004134 energy conservation Methods 0.000 description 1
- 238000002474 experimental method Methods 0.000 description 1
- 238000005242 forging Methods 0.000 description 1
- 239000000446 fuel Substances 0.000 description 1
- 230000001771 impaired effect Effects 0.000 description 1
- 230000006872 improvement Effects 0.000 description 1
- 239000012535 impurity Substances 0.000 description 1
- 229910000734 martensite Inorganic materials 0.000 description 1
- 239000002244 precipitate Substances 0.000 description 1
- 230000008569 process Effects 0.000 description 1
- 230000009467 reduction Effects 0.000 description 1
- 230000007017 scission Effects 0.000 description 1
- 239000013535 sea water Substances 0.000 description 1
- 239000007787 solid Substances 0.000 description 1
- 239000006104 solid solution Substances 0.000 description 1
- 238000007711 solidification Methods 0.000 description 1
- 230000008023 solidification Effects 0.000 description 1
- 238000009864 tensile test Methods 0.000 description 1
- 230000009466 transformation Effects 0.000 description 1
- 230000007704 transition Effects 0.000 description 1
Landscapes
- Turbine Rotor Nozzle Sealing (AREA)
Priority Applications (1)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
JP10910879A JPS5635754A (en) | 1979-08-29 | 1979-08-29 | Low temperature turbine blade steel and its heat treatment |
Applications Claiming Priority (1)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
JP10910879A JPS5635754A (en) | 1979-08-29 | 1979-08-29 | Low temperature turbine blade steel and its heat treatment |
Publications (2)
Publication Number | Publication Date |
---|---|
JPS5635754A JPS5635754A (en) | 1981-04-08 |
JPS6238426B2 true JPS6238426B2 (fr) | 1987-08-18 |
Family
ID=14501767
Family Applications (1)
Application Number | Title | Priority Date | Filing Date |
---|---|---|---|
JP10910879A Granted JPS5635754A (en) | 1979-08-29 | 1979-08-29 | Low temperature turbine blade steel and its heat treatment |
Country Status (1)
Country | Link |
---|---|
JP (1) | JPS5635754A (fr) |
Families Citing this family (6)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
JPS602380B2 (ja) * | 1981-05-30 | 1985-01-21 | 川崎製鉄株式会社 | 低炭素マルテンサイト系ステンレス鋼オ−トバイデイスクブレ−キ用材料 |
DE3789776T2 (de) * | 1986-02-05 | 1994-08-18 | Hitachi Ltd | Hitzebeständiger Stahl und daraus hergestellte Gasturbinenteile. |
JPS63171856A (ja) * | 1987-01-09 | 1988-07-15 | Hitachi Ltd | 耐熱鋼 |
CN105463327A (zh) * | 2015-12-12 | 2016-04-06 | 郭策 | 大型水电站混流式水轮机涡壳 |
CN105603319B (zh) * | 2016-01-01 | 2017-11-14 | 衢州市联橙环保科技有限公司 | 一种厨余垃圾破碎装置 |
CN110205539B (zh) * | 2019-07-05 | 2020-11-20 | 浙江朋诚科技有限公司 | 一种飞剪用高强合金刀片及其制备方法 |
-
1979
- 1979-08-29 JP JP10910879A patent/JPS5635754A/ja active Granted
Also Published As
Publication number | Publication date |
---|---|
JPS5635754A (en) | 1981-04-08 |
Similar Documents
Publication | Publication Date | Title |
---|---|---|
KR100222302B1 (ko) | 저항복비를 가지는 저온인성이 우수한 고강도 라인파이프강재 | |
US5496421A (en) | High-strength martensitic stainless steel and method for making the same | |
JP3514182B2 (ja) | 高温強度と靱性に優れた低Crフェライト系耐熱鋼およびその製造方法 | |
JP5439973B2 (ja) | 優れた生産性と溶接性を兼ね備えた、pwht後の落重特性に優れた高強度厚鋼板およびその製造方法 | |
EP0411515A1 (fr) | Aciers à haute résistance, réfractaires et à basse teneur en éléments d'alliage | |
JP4816642B2 (ja) | 低合金鋼 | |
JPH10503809A (ja) | 熱間加工性に優れた耐硫化物応力割れ性を有するマルテンサイト系ステンレス鋼 | |
WO2022181164A1 (fr) | Tube sans soudure en acier inoxydable à haute résistance pour puits de pétrole et son procédé de production | |
JPS616257A (ja) | 12%Cr耐熱鋼 | |
JPS6238426B2 (fr) | ||
JP3539250B2 (ja) | 高耐応力腐食割れ性を有する655Nmm−2級低C高Cr合金油井管およびその製造方法 | |
JP2000319726A (ja) | 溶接性に優れた高強度鋼板の製造方法 | |
JPS616256A (ja) | 12%Cr耐熱鋼 | |
CN1212024A (zh) | 奥氏体不锈钢及其应用 | |
JP2000160300A (ja) | 高耐食性を有する655Nmm−2級低C高Cr合金油井管およびその製造方法 | |
JP3485034B2 (ja) | 高耐食性を有する862N/mm2級低C高Cr合金油井管およびその製造方法 | |
JPH04120249A (ja) | マルテンサイト系ステンレス鋼とその製造法 | |
JPS6013060B2 (ja) | フエライト系耐熱鋼 | |
JPH07110970B2 (ja) | 耐応力腐食割れ性の優れた針状フェライトステンレス鋼の製造方法 | |
JPS62278251A (ja) | 耐応力腐食割れ性に優れた低合金鋼 | |
JP3250263B2 (ja) | 靭性および耐応力腐食割れ性に優れたマルテンサイト系ステンレス鋼継目無鋼管の製造法 | |
JP2672429B2 (ja) | 耐食性に優れたマルテンサイト系ステンレス鋼継目無鋼管の製造法 | |
JP3458970B2 (ja) | 軸受鋼および軸受部材 | |
JP3662151B2 (ja) | 耐熱鋳鋼及びその熱処理方法 | |
JP2003301242A (ja) | 高Cr−Ni系耐熱鋼および耐クリープ特性に優れた高温用部材の製造方法 |