JPS6223285B2 - - Google Patents
Info
- Publication number
- JPS6223285B2 JPS6223285B2 JP57054421A JP5442182A JPS6223285B2 JP S6223285 B2 JPS6223285 B2 JP S6223285B2 JP 57054421 A JP57054421 A JP 57054421A JP 5442182 A JP5442182 A JP 5442182A JP S6223285 B2 JPS6223285 B2 JP S6223285B2
- Authority
- JP
- Japan
- Prior art keywords
- film
- meth
- resin film
- acrylate
- polarizing
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired
Description
本発明は液晶表示装置などに使用される偏光板
の製法に関するものである。 近年、卓上電子計算機、電子時計などに液晶表
示セルと偏光板とを組み合せた液晶表示装置が汎
用されている。 かかる偏光板は、一般に偏光フイルムと表面保
護層としてのアセテートフイルム又はポリアクリ
ル系樹脂フイルムなどのプラスチツクフイルム類
とで構成されている。 しかして、偏光フイルムとプラスチツクフイル
ム類との接着は、偏光板としての光学特性及び耐
久性などの点から、大部分ポリウレタン系接着剤
が用いられている。 しかし、ポリウレタン系接着剤は、初期接着強
度が比較的弱く、その硬化反応に長時間を要する
ために接着作業が煩雑であるといつた問題があ
る。 従つて本発明の目的は、初期接着強度が強く、
しかも短時間で硬化する偏光板の製法を提供する
ことにある。 本発明のかかる目的は、偏光フイルムと該フイ
ルムの表面保護層としてのポリアクリル系樹脂フ
イルムとを接着するに当り、該樹脂フイルムの表
層部分を溶解又は膨潤して粘着化させるビニル単
量体及び/又はオリゴマーを主成分とする液状物
を用い、前記樹脂フイルム又は液状物の各れか一
方に重合開始剤を含有させておき、前記偏光フイ
ルムと樹脂フイルムとの間に前記液状物を存在さ
せて加熱して前記液状物を重合させ、前記偏光フ
イルムと樹脂フイルムとを接着することによつて
達成される。 本発明によれば、偏光フイルムに接着されるポ
リアクリル系樹脂フイルムの表層部分は、ビニル
単量体及び/又はオリゴマーを主成分とする液状
物にて溶解又は膨潤して粘着化するために、偏光
フイルム面に確実且つ大なる接着面積で接触し、
しかも偏光フイルムとの界面はポリアクリル系樹
脂成分と液状物の重合物とで形成されるために、
偏光フイルムとポリアクリル系樹脂フイルムとは
強固に、しかも短時間で接着できるという特徴を
有する。 本発明を実施するに当つて用いられる偏光フイ
ルムとしては、ポリビニルアルコール系フイル
ム、部分ホルマール化ポリビニルアルコール系フ
イルム、エチレン―酢酸ビニル共重合体系ケン化
フイルムの如き親水性高分子系フイルムに沃素及
び/又は二色性染料を吸着配向せしめた沃素及
び/又は染料系偏光フイルム、ポリビニルアルコ
ール系フイルムを脱水処理したり、ポリ塩化ビニ
ルフイルムを脱塩酸処理したりしてポリエンを配
向せしめたポリエン系偏光フイルムなどがあげら
れ、これらは通常10〜80μmの厚みを有するもの
が使用される。 また該偏光フイルムの表面保護層として使用さ
れるポリアクリル系樹脂フイルムとしては、(メ
タ)アクリル酸エステル例えばアクリル酸メチ
ル、メタクリル酸メチル、アクリル酸エチル、メ
タクリル酸エチルなどと、(メタ)アクリル酸、
無水マレイン酸、イタコン酸、(メタ)アクリル
酸―2―ヒドロキシエチル、アクリルアミドの如
き官能性モノマーと、スチレン、酢酸ビニル、
(メタ)アクリロニトリルの如き不飽和化合物と
を、好ましくは100〜50:0〜20:0〜30(重量
比)で重合してなる重合物、共重合物或いはさら
に該共重合物をポリイソシアネート化合物の如き
有機試薬で架橋してなる架橋共重合物を常法によ
り造膜(厚さ約15〜500μm)してなるものが使
用される。 またビニル単量体及び/又はオリゴムーとして
は前記ポリアクリル系樹脂フイルムの表層部分を
溶解又は膨潤して粘着化するものであれば特に制
限されず、次のものを例示することができる。 一官能性ビニル単量体:例えばメチル(メタ)
アクリレート、エチル(メタ)アクリレート、n
―ブチル(メタ)アクリレート、イソブチル(メ
タ)アクリレート、シクロヘキシル(メタ)アク
リレート、2―エチルヘキシル(メタ)アクリレ
ート、デシル(メタ)アクリレート、ラウリル
(メタ)アクリレートの如きアルキル又はシクロ
アルキルアクリレート又はメタクリレート、酢酸
ビニル、プロピオン酸ビニル、(メタ)アクリロ
ニトリル、スチレン、ビニルトルエン、(メタ)
アクリル酸、2―ヒドロキシエチル(メタ)アク
リレート又は2―ヒドロキシプロピル(メタ)ア
クリレートの如き(メタ)アクリル酸のヒドロキ
シエステル、グリシジル(メタ)アクリレート、
ジエチルアミノエチル(メタ)アクリレートな
ど、 多官能性ビニル単量体:例えばエチレングリコ
ールジ(メタ)アクリレート、ジエチレングリコ
ールジ(メタ)アクリレート、トリエチレングリ
コールジ(メタ)アクリレートの如き(メタ)ア
クリル酸のエチレングリコール又はプロピレング
リコールジエステル、トリメチロールプロパント
リ(メタ)アクリレート、テトラメチロールプロ
パンテトラ(メタ)アクリレートなど、 一官能性性オリゴマー:例えばポリエステル樹
脂と(メタ)アクリル酸との反応によつて得られ
るポリエステルモノ(メタ)アクリレートなど、 多官能性オリゴマー:例えばポリエチレングリ
コールジ(メタ)アクリレート、エポキシ樹脂と
(メタ)アクリル酸との反応によつて得られるエ
ポキシ(メタ)アクリレート、ポリイソシアネー
ト化合物とヒドロキシアルキル(メタ)アクリレ
ートとの反応によつて得られるウレタン(メタ)
アクリレート、ポリエステル樹脂と(メタ)アク
リル酸との反応によつて得られるポリエステルジ
(メタ)アクリレート或いはポリエーテルジ(メ
タ)アクリレートなど、 これらのビニル単量体及び/又はオリゴマーを
主成分とする液状物は、前記ビニル単量体及び/
又はオリゴマーの一種又は2種以上で構成される
が、その粘度は塗布作業性を考慮すると、0.01〜
100ポイズ、実用的には50ポイズ以下の範囲に調
整するのが好ましいものであり、該液状物はポリ
アクリル系樹脂フイルムと偏光フイルムとの界面
に、ポリアクリル系樹脂フイルム厚100μmを基
準として1〜500g/m2、好ましくは10〜300g/
m2の範囲で塗布される。 これらのビニル単量体及び/又はオリゴマーと
前記ポリアクリル系樹脂フイルムとの組み合せ
は、同一であつてよいが、本発明者達が繰り返し
行つた実験によれば、前記フイルムの表層部分が
溶解又は膨潤した場合に、その系が僅かに白濁す
る程度の、若干相溶性が劣る組み合せが、より強
固な接着強度が得られることが判明している。ま
た上記ビニル単量及び/又はオリゴマーには、塗
設作業性を向上させる目的で相溶性良好なアクリ
ル系共重合物を30重量%以下で添加することがで
きる。 かかるビニル単量体及び/又はオリゴマーを主
成分とする液状物には、加熱により該液状物に重
合を開始させる重合開始剤が配合される。しかし
て該開始剤は前記ポリアクリル系樹脂フイルムに
配合しておいてもよいものである。 重合開始剤としては、ベンゾイルバーオキサイ
ド、メチルエチルケトンバーオキサイド、ラウロ
イルバーオキサイド、クメンヒドロキシバーオキ
サイドなどの有機過酸化物、2.2′―アゾビスイソ
ブチロニトリル、2′.2′―アゾビス―(4―メトキ
シ―2.4―ジメチルバレロニトリル)、1.1′―アゾ
ビス(シクロヘキサン―1―カルボニトリル)な
どのアゾ系化合物、その他過酸化水素、過硫酸ア
ンモンなどの反応開始温度が20〜100℃のものが
使用され、これらは0.01〜10重量%、実用的には
0.1〜4重量%の範囲で配合される。 また上記ポリアクリル系樹脂フイルム又は液状
物には、N.N―ジメチルアニリン、N.N―ジメチ
ルパラトルイジン、ナフテン酸コバルト、ナフテ
ン酸銅、チオ尿素、アセチル尿素の如き重合促進
剤を適量添加することができ、該促進剤の添加は
加熱によつて重合する液状物の重合を促進する効
果がある。 本発明の製法は、ポリアクリル系樹脂フイルム
に、重合開始剤を含むビニル単量体及び/又はオ
リゴマーを主成分とする液状物を、0.1〜100g/
m2の厚みで塗布して、フイルム表面を溶解又は膨
潤して粘着化させ、この塗布粘着面に偏光フイル
ムを重ね合せて、25〜100℃で0.1〜250分間加熱
することによつて前記液状物を重合させ、ポリア
クリル系樹脂フイルムと偏光フイルムとが強固に
接着した偏光板を提供する。 前記製法において、予め偏光フイルムの表面を
1.6―ヘキサンジイソシアネート、ジシクロヘキ
シルメタンジイソシアネート、トリレンジイソシ
アネート、ジフエニルメタンジイソシアネート、
トリフエニルメタントリイソシアネートなどおよ
びそれらの変性体などのポリイソシアネート化合
物或いはビニルトリエトキシシラン、γ―グリシ
ドキシプロピルトリメトキシシラン、N―β(ア
ミノエチル)γ―アミノプロピルトリメトキシシ
ラン、γ―アミノプロピルトリエトキシシランの
如きシラン化合物などを用いて表面処理を行うこ
とは、より強い接着強度を有する偏光板が有効に
得られる。 以下本発明の実施例を示す。文中部とあるのは
重量部を意味する。 実施例 1 厚さ30μmのメタクリル酸メチルを主成分とす
るポリアクリル系樹脂フイルムの片面に、メタク
リル酸メチル100部、メタクリル酸グリシジル10
部及びアソビスイソブチロニトリル1部の混合液
状物を10g/m2塗布し、これを下記する方法で得
た偏光フイルムの両面に貼り合せて圧着し、90℃
に保持したオーブン中に60分間放置して、偏光板
を得た。 <偏光フイルム> ポリビニルアルコール系フイルムを沃素濃度1
重量%、沃化カリウム濃度2重量%及びホウ酸濃
度4重量%に調整した水溶液中に浸漬し、50℃で
3〜4倍に延伸して透過率41%、偏光度92%の偏
光フイルム(厚さ30μm)を作製した。 実施例 2 厚さ50μmのメタクリル酸メチルを主成分とす
るポリアクリル系樹脂フイルムの片面に、メタク
リル酸ブチル100部、スチレン10部及びベンゾイ
ルパーオキサイド0.5部の混合液状物を5g/m2
塗布し、これを実施例1で用いた偏光フイルムの
両面に貼り合せて圧着し、70℃に保持したオーブ
ン中で10分間加熱後、85℃に24時放置して、偏光
板を得た。 実施例 3 厚さ20μmのメタクリル酸メチルを主成分とす
るポリアクリル系樹脂フイルムの片面に、メタク
リル酸メチル100部、メタクリル酸ヒドロキシエ
チル5部、トリレンジイソシアネート3部、メタ
クリル酸メチル:アクリル酸エチル=70:30の共
重合物10部及び2.2′―アゾビス―(4―メトキシ
―2.4―ジメチルバレロニトリル)1部からなる
混合液状物を20g/m2塗布し、これを下記方法で
得た偏光フイルムの両面に貼り合せて圧着し、80
℃で20分間加熱して偏光板を得た。 <偏光フイルム> ポリビニルアルコール系フイルムを脱水触媒と
しての塩酸を0.1重量%を含む水溶液に浸漬しつ
つ、2倍に延伸した後、150℃中にてさらに2.5倍
に延伸且つ熱処理してポリエンを形成する。 次にポリエンを形成した上記フイルムを0.1重
量%の二色性染料を含む水溶液(液温30℃)に10
分間浸漬して、該染料を吸着配向して乾燥し、中
性色の色相を有する透過率43%、偏光度94%のポ
リエン―二色性染料系偏光フイルム(厚さ25μ
m)を得る。 実施例 5 メタクリル酸メチル―アクリル酸エチル共重合
物からなる樹脂溶液100部に対して、2.2′―アゾ
ビス―(4―メトキシ―2.4―ジメチルバレロニ
トリル)を2部配合し、これを離型ライナー上に
乾燥後の厚みが30μmとなるようにキヤステイン
グしてポリアクリル系樹脂フイルムを得る。この
フイルムの片面にメタクリル酸メチル100部とメ
タクリル酸グリシジル20部からなる混合物を10
g/m2塗布して実施例1の偏光フイルムの両面に
貼り合せ、80℃で120分間加熱して偏光板を得
た。 実施例 6 メタクリル酸エチル―メタクリル酸共重合物か
らなる厚さ20μmのポリアクリル系樹脂フイルム
の片面に、ポリエステルジメタクリレート(平均
分子量540)30部、メタクリル酸メチル50部、ア
クリル酸2―エチルヘキシル20部及び2.2′―アゾ
ビス―(4―メトキシ―2.4―ジメチルバレロニ
トリル)1部からなる液状物を20g/m2塗布し、
これを実施例1の偏光フイルムの両面に貼り合せ
て80℃で120分加熱して偏光板を得た。 第1表に実施例1〜6の試験結果を示す。
の製法に関するものである。 近年、卓上電子計算機、電子時計などに液晶表
示セルと偏光板とを組み合せた液晶表示装置が汎
用されている。 かかる偏光板は、一般に偏光フイルムと表面保
護層としてのアセテートフイルム又はポリアクリ
ル系樹脂フイルムなどのプラスチツクフイルム類
とで構成されている。 しかして、偏光フイルムとプラスチツクフイル
ム類との接着は、偏光板としての光学特性及び耐
久性などの点から、大部分ポリウレタン系接着剤
が用いられている。 しかし、ポリウレタン系接着剤は、初期接着強
度が比較的弱く、その硬化反応に長時間を要する
ために接着作業が煩雑であるといつた問題があ
る。 従つて本発明の目的は、初期接着強度が強く、
しかも短時間で硬化する偏光板の製法を提供する
ことにある。 本発明のかかる目的は、偏光フイルムと該フイ
ルムの表面保護層としてのポリアクリル系樹脂フ
イルムとを接着するに当り、該樹脂フイルムの表
層部分を溶解又は膨潤して粘着化させるビニル単
量体及び/又はオリゴマーを主成分とする液状物
を用い、前記樹脂フイルム又は液状物の各れか一
方に重合開始剤を含有させておき、前記偏光フイ
ルムと樹脂フイルムとの間に前記液状物を存在さ
せて加熱して前記液状物を重合させ、前記偏光フ
イルムと樹脂フイルムとを接着することによつて
達成される。 本発明によれば、偏光フイルムに接着されるポ
リアクリル系樹脂フイルムの表層部分は、ビニル
単量体及び/又はオリゴマーを主成分とする液状
物にて溶解又は膨潤して粘着化するために、偏光
フイルム面に確実且つ大なる接着面積で接触し、
しかも偏光フイルムとの界面はポリアクリル系樹
脂成分と液状物の重合物とで形成されるために、
偏光フイルムとポリアクリル系樹脂フイルムとは
強固に、しかも短時間で接着できるという特徴を
有する。 本発明を実施するに当つて用いられる偏光フイ
ルムとしては、ポリビニルアルコール系フイル
ム、部分ホルマール化ポリビニルアルコール系フ
イルム、エチレン―酢酸ビニル共重合体系ケン化
フイルムの如き親水性高分子系フイルムに沃素及
び/又は二色性染料を吸着配向せしめた沃素及
び/又は染料系偏光フイルム、ポリビニルアルコ
ール系フイルムを脱水処理したり、ポリ塩化ビニ
ルフイルムを脱塩酸処理したりしてポリエンを配
向せしめたポリエン系偏光フイルムなどがあげら
れ、これらは通常10〜80μmの厚みを有するもの
が使用される。 また該偏光フイルムの表面保護層として使用さ
れるポリアクリル系樹脂フイルムとしては、(メ
タ)アクリル酸エステル例えばアクリル酸メチ
ル、メタクリル酸メチル、アクリル酸エチル、メ
タクリル酸エチルなどと、(メタ)アクリル酸、
無水マレイン酸、イタコン酸、(メタ)アクリル
酸―2―ヒドロキシエチル、アクリルアミドの如
き官能性モノマーと、スチレン、酢酸ビニル、
(メタ)アクリロニトリルの如き不飽和化合物と
を、好ましくは100〜50:0〜20:0〜30(重量
比)で重合してなる重合物、共重合物或いはさら
に該共重合物をポリイソシアネート化合物の如き
有機試薬で架橋してなる架橋共重合物を常法によ
り造膜(厚さ約15〜500μm)してなるものが使
用される。 またビニル単量体及び/又はオリゴムーとして
は前記ポリアクリル系樹脂フイルムの表層部分を
溶解又は膨潤して粘着化するものであれば特に制
限されず、次のものを例示することができる。 一官能性ビニル単量体:例えばメチル(メタ)
アクリレート、エチル(メタ)アクリレート、n
―ブチル(メタ)アクリレート、イソブチル(メ
タ)アクリレート、シクロヘキシル(メタ)アク
リレート、2―エチルヘキシル(メタ)アクリレ
ート、デシル(メタ)アクリレート、ラウリル
(メタ)アクリレートの如きアルキル又はシクロ
アルキルアクリレート又はメタクリレート、酢酸
ビニル、プロピオン酸ビニル、(メタ)アクリロ
ニトリル、スチレン、ビニルトルエン、(メタ)
アクリル酸、2―ヒドロキシエチル(メタ)アク
リレート又は2―ヒドロキシプロピル(メタ)ア
クリレートの如き(メタ)アクリル酸のヒドロキ
シエステル、グリシジル(メタ)アクリレート、
ジエチルアミノエチル(メタ)アクリレートな
ど、 多官能性ビニル単量体:例えばエチレングリコ
ールジ(メタ)アクリレート、ジエチレングリコ
ールジ(メタ)アクリレート、トリエチレングリ
コールジ(メタ)アクリレートの如き(メタ)ア
クリル酸のエチレングリコール又はプロピレング
リコールジエステル、トリメチロールプロパント
リ(メタ)アクリレート、テトラメチロールプロ
パンテトラ(メタ)アクリレートなど、 一官能性性オリゴマー:例えばポリエステル樹
脂と(メタ)アクリル酸との反応によつて得られ
るポリエステルモノ(メタ)アクリレートなど、 多官能性オリゴマー:例えばポリエチレングリ
コールジ(メタ)アクリレート、エポキシ樹脂と
(メタ)アクリル酸との反応によつて得られるエ
ポキシ(メタ)アクリレート、ポリイソシアネー
ト化合物とヒドロキシアルキル(メタ)アクリレ
ートとの反応によつて得られるウレタン(メタ)
アクリレート、ポリエステル樹脂と(メタ)アク
リル酸との反応によつて得られるポリエステルジ
(メタ)アクリレート或いはポリエーテルジ(メ
タ)アクリレートなど、 これらのビニル単量体及び/又はオリゴマーを
主成分とする液状物は、前記ビニル単量体及び/
又はオリゴマーの一種又は2種以上で構成される
が、その粘度は塗布作業性を考慮すると、0.01〜
100ポイズ、実用的には50ポイズ以下の範囲に調
整するのが好ましいものであり、該液状物はポリ
アクリル系樹脂フイルムと偏光フイルムとの界面
に、ポリアクリル系樹脂フイルム厚100μmを基
準として1〜500g/m2、好ましくは10〜300g/
m2の範囲で塗布される。 これらのビニル単量体及び/又はオリゴマーと
前記ポリアクリル系樹脂フイルムとの組み合せ
は、同一であつてよいが、本発明者達が繰り返し
行つた実験によれば、前記フイルムの表層部分が
溶解又は膨潤した場合に、その系が僅かに白濁す
る程度の、若干相溶性が劣る組み合せが、より強
固な接着強度が得られることが判明している。ま
た上記ビニル単量及び/又はオリゴマーには、塗
設作業性を向上させる目的で相溶性良好なアクリ
ル系共重合物を30重量%以下で添加することがで
きる。 かかるビニル単量体及び/又はオリゴマーを主
成分とする液状物には、加熱により該液状物に重
合を開始させる重合開始剤が配合される。しかし
て該開始剤は前記ポリアクリル系樹脂フイルムに
配合しておいてもよいものである。 重合開始剤としては、ベンゾイルバーオキサイ
ド、メチルエチルケトンバーオキサイド、ラウロ
イルバーオキサイド、クメンヒドロキシバーオキ
サイドなどの有機過酸化物、2.2′―アゾビスイソ
ブチロニトリル、2′.2′―アゾビス―(4―メトキ
シ―2.4―ジメチルバレロニトリル)、1.1′―アゾ
ビス(シクロヘキサン―1―カルボニトリル)な
どのアゾ系化合物、その他過酸化水素、過硫酸ア
ンモンなどの反応開始温度が20〜100℃のものが
使用され、これらは0.01〜10重量%、実用的には
0.1〜4重量%の範囲で配合される。 また上記ポリアクリル系樹脂フイルム又は液状
物には、N.N―ジメチルアニリン、N.N―ジメチ
ルパラトルイジン、ナフテン酸コバルト、ナフテ
ン酸銅、チオ尿素、アセチル尿素の如き重合促進
剤を適量添加することができ、該促進剤の添加は
加熱によつて重合する液状物の重合を促進する効
果がある。 本発明の製法は、ポリアクリル系樹脂フイルム
に、重合開始剤を含むビニル単量体及び/又はオ
リゴマーを主成分とする液状物を、0.1〜100g/
m2の厚みで塗布して、フイルム表面を溶解又は膨
潤して粘着化させ、この塗布粘着面に偏光フイル
ムを重ね合せて、25〜100℃で0.1〜250分間加熱
することによつて前記液状物を重合させ、ポリア
クリル系樹脂フイルムと偏光フイルムとが強固に
接着した偏光板を提供する。 前記製法において、予め偏光フイルムの表面を
1.6―ヘキサンジイソシアネート、ジシクロヘキ
シルメタンジイソシアネート、トリレンジイソシ
アネート、ジフエニルメタンジイソシアネート、
トリフエニルメタントリイソシアネートなどおよ
びそれらの変性体などのポリイソシアネート化合
物或いはビニルトリエトキシシラン、γ―グリシ
ドキシプロピルトリメトキシシラン、N―β(ア
ミノエチル)γ―アミノプロピルトリメトキシシ
ラン、γ―アミノプロピルトリエトキシシランの
如きシラン化合物などを用いて表面処理を行うこ
とは、より強い接着強度を有する偏光板が有効に
得られる。 以下本発明の実施例を示す。文中部とあるのは
重量部を意味する。 実施例 1 厚さ30μmのメタクリル酸メチルを主成分とす
るポリアクリル系樹脂フイルムの片面に、メタク
リル酸メチル100部、メタクリル酸グリシジル10
部及びアソビスイソブチロニトリル1部の混合液
状物を10g/m2塗布し、これを下記する方法で得
た偏光フイルムの両面に貼り合せて圧着し、90℃
に保持したオーブン中に60分間放置して、偏光板
を得た。 <偏光フイルム> ポリビニルアルコール系フイルムを沃素濃度1
重量%、沃化カリウム濃度2重量%及びホウ酸濃
度4重量%に調整した水溶液中に浸漬し、50℃で
3〜4倍に延伸して透過率41%、偏光度92%の偏
光フイルム(厚さ30μm)を作製した。 実施例 2 厚さ50μmのメタクリル酸メチルを主成分とす
るポリアクリル系樹脂フイルムの片面に、メタク
リル酸ブチル100部、スチレン10部及びベンゾイ
ルパーオキサイド0.5部の混合液状物を5g/m2
塗布し、これを実施例1で用いた偏光フイルムの
両面に貼り合せて圧着し、70℃に保持したオーブ
ン中で10分間加熱後、85℃に24時放置して、偏光
板を得た。 実施例 3 厚さ20μmのメタクリル酸メチルを主成分とす
るポリアクリル系樹脂フイルムの片面に、メタク
リル酸メチル100部、メタクリル酸ヒドロキシエ
チル5部、トリレンジイソシアネート3部、メタ
クリル酸メチル:アクリル酸エチル=70:30の共
重合物10部及び2.2′―アゾビス―(4―メトキシ
―2.4―ジメチルバレロニトリル)1部からなる
混合液状物を20g/m2塗布し、これを下記方法で
得た偏光フイルムの両面に貼り合せて圧着し、80
℃で20分間加熱して偏光板を得た。 <偏光フイルム> ポリビニルアルコール系フイルムを脱水触媒と
しての塩酸を0.1重量%を含む水溶液に浸漬しつ
つ、2倍に延伸した後、150℃中にてさらに2.5倍
に延伸且つ熱処理してポリエンを形成する。 次にポリエンを形成した上記フイルムを0.1重
量%の二色性染料を含む水溶液(液温30℃)に10
分間浸漬して、該染料を吸着配向して乾燥し、中
性色の色相を有する透過率43%、偏光度94%のポ
リエン―二色性染料系偏光フイルム(厚さ25μ
m)を得る。 実施例 5 メタクリル酸メチル―アクリル酸エチル共重合
物からなる樹脂溶液100部に対して、2.2′―アゾ
ビス―(4―メトキシ―2.4―ジメチルバレロニ
トリル)を2部配合し、これを離型ライナー上に
乾燥後の厚みが30μmとなるようにキヤステイン
グしてポリアクリル系樹脂フイルムを得る。この
フイルムの片面にメタクリル酸メチル100部とメ
タクリル酸グリシジル20部からなる混合物を10
g/m2塗布して実施例1の偏光フイルムの両面に
貼り合せ、80℃で120分間加熱して偏光板を得
た。 実施例 6 メタクリル酸エチル―メタクリル酸共重合物か
らなる厚さ20μmのポリアクリル系樹脂フイルム
の片面に、ポリエステルジメタクリレート(平均
分子量540)30部、メタクリル酸メチル50部、ア
クリル酸2―エチルヘキシル20部及び2.2′―アゾ
ビス―(4―メトキシ―2.4―ジメチルバレロニ
トリル)1部からなる液状物を20g/m2塗布し、
これを実施例1の偏光フイルムの両面に貼り合せ
て80℃で120分加熱して偏光板を得た。 第1表に実施例1〜6の試験結果を示す。
【表】
上記実施例からも明らかなように、本発明の製
法で作製した偏光板は、ポリアクリル系樹脂フイ
ルムと偏光フイルムとの接着性に優れ、しかも耐
久性及び熱安定性を有する事実が顕著である。
法で作製した偏光板は、ポリアクリル系樹脂フイ
ルムと偏光フイルムとの接着性に優れ、しかも耐
久性及び熱安定性を有する事実が顕著である。
Claims (1)
- 1 偏光フイルムと該フイルムの表面保護層とし
てのポリアクリル系樹脂フイルムとを接着するに
当り、該樹脂フイルムの表層部分を溶解又は膨潤
して粘着化させるビニル単量体及び/又はオリゴ
マーを主成分とする液状物を用い、前記樹脂フイ
ルム又は液状物の各れか一方に重合開始剤を含有
させておき、前記偏光フイルムと樹脂フイルムと
の間に前記液状物を存在させて加熱して前記液状
物を重合させ、前記偏光フイルムと樹脂フイルム
とを接着することを特徴とする偏光板の製法。