JPS62167091A - 光学式記録媒体 - Google Patents
光学式記録媒体Info
- Publication number
- JPS62167091A JPS62167091A JP61010461A JP1046186A JPS62167091A JP S62167091 A JPS62167091 A JP S62167091A JP 61010461 A JP61010461 A JP 61010461A JP 1046186 A JP1046186 A JP 1046186A JP S62167091 A JPS62167091 A JP S62167091A
- Authority
- JP
- Japan
- Prior art keywords
- thickness
- layer
- protective layer
- recording medium
- substrate
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
(57)【要約】本公報は電子出願前の出願データであるた
め要約のデータは記録されません。
め要約のデータは記録されません。
Description
【発明の詳細な説明】
〔産業上の利用分野］
本発明は、レーザー元を用いて、情報を記録、再生する
光記録媒体に関し、特に録再時、情報記録の傷号を、媒
体よりの反射光ではなく、透過光で検出する光記録再生
システム中で用いられる光学式記録媒体に関する。読み
出し専用記録媒体、追記書き込み可能記録媒体、消去書
き込み可能記録媒体、いずれの媒体にも適用できる。
光記録媒体に関し、特に録再時、情報記録の傷号を、媒
体よりの反射光ではなく、透過光で検出する光記録再生
システム中で用いられる光学式記録媒体に関する。読み
出し専用記録媒体、追記書き込み可能記録媒体、消去書
き込み可能記録媒体、いずれの媒体にも適用できる。
本発明は、透過ｆｔ、を用いて情報信号の検出全行なう
光記鎌媒体において、基板上に情報記録層を有し、その
上に記録層の保護層を設けたｉ成とし、その保護１−が
、厚み３０〜５００μｍで、使用録再光の波長に対する
光透過率が８０％以上、且つ屈折率が基板の屈折率と同
等もしくは小ざい有機材料である事により、貼合せ操作
をせずに高信頼性の記録媒体を安価に裏作でき、媒体の
軽薄さ及び、信号検出時、記録媒体に付層しているゴミ
。
光記鎌媒体において、基板上に情報記録層を有し、その
上に記録層の保護層を設けたｉ成とし、その保護１−が
、厚み３０〜５００μｍで、使用録再光の波長に対する
光透過率が８０％以上、且つ屈折率が基板の屈折率と同
等もしくは小ざい有機材料である事により、貼合せ操作
をせずに高信頼性の記録媒体を安価に裏作でき、媒体の
軽薄さ及び、信号検出時、記録媒体に付層しているゴミ
。
埃の影響を除去する事を実現したものである。
基板上に情報記録１−を有し、その上に透明接層剤を介
して、保護用透明平板を貼り付け、情＠記録層を同一厚
みの透明基板間でサンドインチする構成が周知である。
して、保護用透明平板を貼り付け、情＠記録層を同一厚
みの透明基板間でサンドインチする構成が周知である。
〔発明が解決しようとする間魂点］
前述の従来技術では、保護用透明平板を貼付ける際に、
接層剤への気泡混入か避けられず、記録媒体の信頼性に
問題があった。製作歩留も悪くコスト高となっていた。
接層剤への気泡混入か避けられず、記録媒体の信頼性に
問題があった。製作歩留も悪くコスト高となっていた。
記録媒体の厚みは保護用透明平板を貼付ける為、厚いも
のとなっていた。そこで本発明は、このような問題点を
解決するもので、その目的とするところは、情報記録の
信頼性が高く、厚さが薄い、光学式情報記録媒体を安価
に提供するところにある。
のとなっていた。そこで本発明は、このような問題点を
解決するもので、その目的とするところは、情報記録の
信頼性が高く、厚さが薄い、光学式情報記録媒体を安価
に提供するところにある。
本発明の光学式情報記録媒体は、基板上に、情報記録層
を有し、その上に記録１−の保護１−を設けた構成に於
て、保護／Ｉ＃炉、厚み３０〜５００μ渦で、使用録再
光の波長に対する光透過率が８ｑ％以上、且つ、屈折率
か基板の屈折率と同等もしくは小さい有機材料よりなる
事を特徴とする。
を有し、その上に記録１−の保護１−を設けた構成に於
て、保護／Ｉ＃炉、厚み３０〜５００μ渦で、使用録再
光の波長に対する光透過率が８ｑ％以上、且つ、屈折率
か基板の屈折率と同等もしくは小さい有機材料よりなる
事を特徴とする。
〔実施例１〕
＠１図は本発明の実施例における情報記録媒体の構造図
である。１はポリカーボネート基板（１，２■厚〕、２
は紫外線硬化樹脂よりなる保護＋ｍ（５０μｍ厚で、７
８０ｎｍの波長に対する透過率か９０壬、屈折率が１．
４ ｆ３ ）、５は記録Ｊ！＃、４は透明セラミックｔ
＊〔５ｉｏｔ １１μ悔厚〕である。保１１１４はスピ
ンコード法を用いて塗布した。顕微鏡観察に於て、気泡
の混入は見られなかった。
である。１はポリカーボネート基板（１，２■厚〕、２
は紫外線硬化樹脂よりなる保護＋ｍ（５０μｍ厚で、７
８０ｎｍの波長に対する透過率か９０壬、屈折率が１．
４ ｆ３ ）、５は記録Ｊ！＃、４は透明セラミックｔ
＊〔５ｉｏｔ １１μ悔厚〕である。保１１１４はスピ
ンコード法を用いて塗布した。顕微鏡観察に於て、気泡
の混入は見られなかった。
〔実施例２〕
第２図は本発明の実施例における情報記録媒体の構造図
である。１はポリメチルメタクリレート基板（１，２ｍ
厚）、２は紫外線硬化樹脂よりなる保護層（２００μ惰
厚で、７８０ｎｍの波長に対する透過率が８７％、屈折
率が１．３４ ）、３は記録層、ＡＶｉ透明セラミック
ｌｆｉ （Ｆ３ Ｌｏｔ ｔｌ １μｍ厚）でである。
である。１はポリメチルメタクリレート基板（１，２ｍ
厚）、２は紫外線硬化樹脂よりなる保護層（２００μ惰
厚で、７８０ｎｍの波長に対する透過率が８７％、屈折
率が１．３４ ）、３は記録層、ＡＶｉ透明セラミック
ｌｆｉ （Ｆ３ Ｌｏｔ ｔｌ １μｍ厚）でである。
保護層はロールコート法を用いて塗布した。顕微鏡観察
に於て、気泡の混入は見られなかったＯ 〔実施例３〕 第３図は本発明の実施例における情報記録媒体の構造図
である。１はガラス基板（１，２ｍ厚）、２は紫外線硬
化樹脂よりなる保護層（２００μ毒厚で７８０ｎｙｘの
波長に対する透過率が８７％、屈折率が１．３４）、３
は記録層、５ば２Ｐ法による情報転写層である。保ｉ！
！層はロールコート法を用いて塗布した。顕微ａ観察に
於て、気泡の混入は見られなかった。
に於て、気泡の混入は見られなかったＯ 〔実施例３〕 第３図は本発明の実施例における情報記録媒体の構造図
である。１はガラス基板（１，２ｍ厚）、２は紫外線硬
化樹脂よりなる保護層（２００μ毒厚で７８０ｎｙｘの
波長に対する透過率が８７％、屈折率が１．３４）、３
は記録層、５ば２Ｐ法による情報転写層である。保ｉ！
！層はロールコート法を用いて塗布した。顕微ａ観察に
於て、気泡の混入は見られなかった。
尚、上記実施例（１〜３）に於て使用基板は、ポリメチ
ルメタクリレート、ポリカーボネート、エポキシ、ガラ
スのいずれも使用できる。基板のフォーマットは、射出
成型時又は２Ｐ法で基板に形成される。保護膜の塗布方
法は、スピンコータ、ロールコータ、スクリーン印刷１
等の印刷手法を用いて行なう事ができる。実施例中の４
、透明セラミック層には、金属酸化物、酸化シリコン、
金層窒化物、窒化シリコン等のセラミックスを使用でき
る。保護膜材料としては、常温硬ｆヒ型コーティング材
、加熱硬化型コーテイング材も使用する事か可能である
。
ルメタクリレート、ポリカーボネート、エポキシ、ガラ
スのいずれも使用できる。基板のフォーマットは、射出
成型時又は２Ｐ法で基板に形成される。保護膜の塗布方
法は、スピンコータ、ロールコータ、スクリーン印刷１
等の印刷手法を用いて行なう事ができる。実施例中の４
、透明セラミック層には、金属酸化物、酸化シリコン、
金層窒化物、窒化シリコン等のセラミックスを使用でき
る。保護膜材料としては、常温硬ｆヒ型コーティング材
、加熱硬化型コーテイング材も使用する事か可能である
。
［発明の効果］
以上述べたように本発明によれば、情報記録層上の保護
層が、厚み３０μ慣〜５０口μ鴨で、使用録再光の波長
に対する透過率が８０％以上、且つ屈折率が基板の屈折
率と同等もしくは小さい有機材料である事より、保護ｊ
−が塗布により形成できる。この為従来解決が困難であ
った媒体貼合せ時の、接着剤への気泡の混入をなくシ、
且つ、厚さが薄い光学式情報記録媒体を安価に提供する
事ができる。又保護層厚みを３０〜５００μｍとする事
により、情報記録膜の酸化等劣化を防ぐと共に、ゴミ、
埃等が保護ｌｆ１表面に付着し九時の、基板側より入射
した透過光の情報検出へ与える悪形４１１を除去する効
果がある。更に、保護膜の屈折率を基板よりも小さいも
のとすると、保護膜表面に付着したゴミ、埃の信号検出
時に与える６影ｆ＃を小さくする事ができる。
層が、厚み３０μ慣〜５０口μ鴨で、使用録再光の波長
に対する透過率が８０％以上、且つ屈折率が基板の屈折
率と同等もしくは小さい有機材料である事より、保護ｊ
−が塗布により形成できる。この為従来解決が困難であ
った媒体貼合せ時の、接着剤への気泡の混入をなくシ、
且つ、厚さが薄い光学式情報記録媒体を安価に提供する
事ができる。又保護層厚みを３０〜５００μｍとする事
により、情報記録膜の酸化等劣化を防ぐと共に、ゴミ、
埃等が保護ｌｆ１表面に付着し九時の、基板側より入射
した透過光の情報検出へ与える悪形４１１を除去する効
果がある。更に、保護膜の屈折率を基板よりも小さいも
のとすると、保護膜表面に付着したゴミ、埃の信号検出
時に与える６影ｆ＃を小さくする事ができる。
第１図、第２図、第３図は１本発明の光学式記録媒体の
構造を示す断面図。 第４図は従来の光学式記録媒体の構造を示す断面図。 １・・・基板 ２・・・保護層 ３・・・記録１ｍ ４・・・セラミック層 ５・・・２Ｐ法転写１− ６・・・対物レンズ ７・・・ディテクター ８・・・透明接着剤層 ９・・・透明平板 以 上 出願人 セイコーエプソン株式会社 名７図 謡録媒林屑ｆ跨面図 葛３図
構造を示す断面図。 第４図は従来の光学式記録媒体の構造を示す断面図。 １・・・基板 ２・・・保護層 ３・・・記録１ｍ ４・・・セラミック層 ５・・・２Ｐ法転写１− ６・・・対物レンズ ７・・・ディテクター ８・・・透明接着剤層 ９・・・透明平板 以 上 出願人 セイコーエプソン株式会社 名７図 謡録媒林屑ｆ跨面図 葛３図
Claims (1)
- 基板上に情報記録層を有し、その上に記録層の保護層を
設けた構成に於て、保護層が、厚み３０μｍ〜５００μ
ｍで、使用録再光の波長に対する光透過率が８０％以上
、且つ、屈折率が基板の屈折率と同等もしくは小さい有
機材料よりなる事を特徴とする光学式記録媒体。