JPS61249068A - カラ−複写機用熱定着部ロ−ラ - Google Patents
カラ−複写機用熱定着部ロ−ラInfo
- Publication number
- JPS61249068A JPS61249068A JP9200885A JP9200885A JPS61249068A JP S61249068 A JPS61249068 A JP S61249068A JP 9200885 A JP9200885 A JP 9200885A JP 9200885 A JP9200885 A JP 9200885A JP S61249068 A JPS61249068 A JP S61249068A
- Authority
- JP
- Japan
- Prior art keywords
- roller
- copying machine
- color copying
- heat fixing
- silicon rubber
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
(57)【要約】本公報は電子出願前の出願データであるた
め要約のデータは記録されません。
め要約のデータは記録されません。
Description
【発明の詳細な説明】
（発明の技術分野）
本発明は、カラー複写機の熱定着部に使用されるカラー
複写機用熱定着部ローラに関する。
複写機用熱定着部ローラに関する。
（発明の技術的背景およびその問題点）従来、カラー複
写機の熱定着部ローラ（定着ローラ、加圧ローラを含む
）表面はシリコーンゴム等のスキン層で構成されている
。
写機の熱定着部ローラ（定着ローラ、加圧ローラを含む
）表面はシリコーンゴム等のスキン層で構成されている
。
ところで、カラー複写機においてはトナーとしてポリエ
ステル系樹脂等にフタロシアニンブルー、ベンチジンイ
エロー、マゼンタなどの染料あるいは顔料を配合してな
るトナーを使用しているためオフセットが起り易い。こ
のため熱定着部ローラ表面に多量のシリコーンオイルを
塗布しながら加熱定着する必要がある。しかしながら、
トナー中の染料あるいは顔料が塗布されたシリコーンオ
イルに溶解し、熱定着部ローラ表面にたい積し、これが
オフセットの原因となったり、又熱定着部ローラとトナ
ー″との離型性が劣るため、ジャムが発生するなどの問
題があり、熱定着部ローラの寿命が極めて短いという欠
点があった。
ステル系樹脂等にフタロシアニンブルー、ベンチジンイ
エロー、マゼンタなどの染料あるいは顔料を配合してな
るトナーを使用しているためオフセットが起り易い。こ
のため熱定着部ローラ表面に多量のシリコーンオイルを
塗布しながら加熱定着する必要がある。しかしながら、
トナー中の染料あるいは顔料が塗布されたシリコーンオ
イルに溶解し、熱定着部ローラ表面にたい積し、これが
オフセットの原因となったり、又熱定着部ローラとトナ
ー″との離型性が劣るため、ジャムが発生するなどの問
題があり、熱定着部ローラの寿命が極めて短いという欠
点があった。
（発明の目的）
本発明はペースポリマーとして側鎖に反応基を有せずか
つ分子量の大きいシリコーンゴムとコバルト青を使用し
た層をローラ基体上に設けることにより高画質コピーが
得られるとともにコピーライフの長いカラー複写機用熱
定着部ローラを提供することを目的としている。
つ分子量の大きいシリコーンゴムとコバルト青を使用し
た層をローラ基体上に設けることにより高画質コピーが
得られるとともにコピーライフの長いカラー複写機用熱
定着部ローラを提供することを目的としている。
（発明の概要）
本発明のカラー複写機用熱定着部ローラはローラ基体上
に、一般式 ％式％ ４００〜１５００の正の整数を表わす。）で表わされる
シリコーンゴムとコバルト青および補強充填剤とを主成
分とした高離型性シリコーンゴム層を設けたことを特徴
としている。
に、一般式 ％式％ ４００〜１５００の正の整数を表わす。）で表わされる
シリコーンゴムとコバルト青および補強充填剤とを主成
分とした高離型性シリコーンゴム層を設けたことを特徴
としている。
本発明のベースポリマーの重合度をｎ＝ ４００〜１５
００の正の整数としたのは４００未満では架橋密度が高
くなり、離型性が劣り一方１５００を越える場合はゴム
の粘度が高くなり、無研削ローラの成形加工が困難とな
るためである。
００の正の整数としたのは４００未満では架橋密度が高
くなり、離型性が劣り一方１５００を越える場合はゴム
の粘度が高くなり、無研削ローラの成形加工が困難とな
るためである。
本発明に使用するコバルト青としては前記シリコーンゴ
ム１００＠ｆｉ部あたり１重量部未満では添加した効果
がなく、３０重量部を越えると脆化してローラが傷付き
やすくなるので、１〜３０重山部の範囲で配合するのが
好ましい。
ム１００＠ｆｉ部あたり１重量部未満では添加した効果
がなく、３０重量部を越えると脆化してローラが傷付き
やすくなるので、１〜３０重山部の範囲で配合するのが
好ましい。
又補強充填剤としては乾式シリカ、湿式シリカ、石英粉
末、珪藻土、酸化亜鉛、酸化チタン等があり、その添加
量としては３０重量部未満がトナーとの離型性の面で好
ましい。又これらには硬化剤としてエチルオルンシリケ
ートやプロピルオルソシリケートのようなアルキルオル
ソシリケート類が用いられ、又硬化反応の触媒として用
いられるものには、ジブチル錫アセテート、ジブチル錫
ラウレート、オクテン酸鉛、オクテン酸鉛のような金属
有機酸塩等があり、これらを加えると縮合硬化してゴム
状の弾性体が得られる。又微粒子状白金、炭素粉末担体
上に吸着させた微粒子状白金、酸化白金酸、酸化白金酸
のアルコール変性物、白金のキレート化合物、酸化白金
酸とオレフィン類の配位化合物、酸化白金酸とビニルシ
ロキサンの配位化合物等を触媒として添加すると、付加
反応してゴム状の弾性体が得られる。
末、珪藻土、酸化亜鉛、酸化チタン等があり、その添加
量としては３０重量部未満がトナーとの離型性の面で好
ましい。又これらには硬化剤としてエチルオルンシリケ
ートやプロピルオルソシリケートのようなアルキルオル
ソシリケート類が用いられ、又硬化反応の触媒として用
いられるものには、ジブチル錫アセテート、ジブチル錫
ラウレート、オクテン酸鉛、オクテン酸鉛のような金属
有機酸塩等があり、これらを加えると縮合硬化してゴム
状の弾性体が得られる。又微粒子状白金、炭素粉末担体
上に吸着させた微粒子状白金、酸化白金酸、酸化白金酸
のアルコール変性物、白金のキレート化合物、酸化白金
酸とオレフィン類の配位化合物、酸化白金酸とビニルシ
ロキサンの配位化合物等を触媒として添加すると、付加
反応してゴム状の弾性体が得られる。
又ローラ基体上と高離型性シリコーン層の間に耐シリコ
ーンオイル性ゴム層として四ふっ化エチレン樹脂あるい
はバー７０ロアルコキシ樹脂等のフッ素樹脂あるいはフ
ッ素樹脂ゴム７０ロシリコーン樹脂、ＲＴＶシリコーン
樹脂、ＨＴＶシリコーン樹脂等を設けることが好ましく
、この場合には耐応力、耐歪性が向上し常時加圧定着方
式にも使用できるようになる。
ーンオイル性ゴム層として四ふっ化エチレン樹脂あるい
はバー７０ロアルコキシ樹脂等のフッ素樹脂あるいはフ
ッ素樹脂ゴム７０ロシリコーン樹脂、ＲＴＶシリコーン
樹脂、ＨＴＶシリコーン樹脂等を設けることが好ましく
、この場合には耐応力、耐歪性が向上し常時加圧定着方
式にも使用できるようになる。
（発明の実施例）
以下、実施例について説明する。
実施例
アルミニウム又はステンレスから成る直結６０■の金属
心金上にプライマーコ−トを施しプレベーク後その外周
に一般式 で表わされるシリコーンゴム１００重量部（ｎ −１２
００）に対しコバルト青を３重量と、補強充填剤として
石英粉と乾式シリカを１３重量部と硬化剤および硬化触
媒を５重量部とよりなるシリコーンゴムを塗布あるいは
注型、インジェクションモールド等により厚み５ｎに成
型し、硬化後研削加工を施すことなくカラー複写機用熱
定着部加圧ローラを得た。前記加圧ローラの表面硬度は
ＪＩＳ硬度で３５度であった。又、熱定着部定着ローラ
も加圧ローラと同一のゴム層を１ ｍｍの厚さとして、
加圧ローラと同様に製作した。塗布オイルは常温で３０
００３のシリコーンオイルを使用し、定着ローラ温度は
１５０℃として通紙試験を行った結−果、□初期的な離
型性は良好でかつ５００００枚通紙後においても紙の巻
き付きおよｑオフセットがなかった。
心金上にプライマーコ−トを施しプレベーク後その外周
に一般式 で表わされるシリコーンゴム１００重量部（ｎ −１２
００）に対しコバルト青を３重量と、補強充填剤として
石英粉と乾式シリカを１３重量部と硬化剤および硬化触
媒を５重量部とよりなるシリコーンゴムを塗布あるいは
注型、インジェクションモールド等により厚み５ｎに成
型し、硬化後研削加工を施すことなくカラー複写機用熱
定着部加圧ローラを得た。前記加圧ローラの表面硬度は
ＪＩＳ硬度で３５度であった。又、熱定着部定着ローラ
も加圧ローラと同一のゴム層を１ ｍｍの厚さとして、
加圧ローラと同様に製作した。塗布オイルは常温で３０
００３のシリコーンオイルを使用し、定着ローラ温度は
１５０℃として通紙試験を行った結−果、□初期的な離
型性は良好でかつ５００００枚通紙後においても紙の巻
き付きおよｑオフセットがなかった。
比較例
熱定着部加圧ローラのシリコーンゴムとしてＫＥ１４０
６（信越シリコーン社製商品名）を使用した外は、実施
例と同様にして通紙試験を行った結果、７０００〜１０
０００枚でオフセットが起きた。尚、熱定着部加圧ロー
ラ表面硬度はＪＩＳ硬度で３２度であった。又、熱定着
部定着ローラは１ｎ厚の加圧ローラと同一のゴムを使用
した。
６（信越シリコーン社製商品名）を使用した外は、実施
例と同様にして通紙試験を行った結果、７０００〜１０
０００枚でオフセットが起きた。尚、熱定着部加圧ロー
ラ表面硬度はＪＩＳ硬度で３２度であった。又、熱定着
部定着ローラは１ｎ厚の加圧ローラと同一のゴムを使用
した。
（発明の効果）
本発明のカラー複写機用ローラは高画質コピーの要求さ
れるカラー複写機に使用された際、トナーとの離型性の
優れた無研削のシリコーンゴム面が直接トナーと接触す
ることによりオフセット、ジャム等の発生を防止でき、
又コピーライフが長い。
れるカラー複写機に使用された際、トナーとの離型性の
優れた無研削のシリコーンゴム面が直接トナーと接触す
ることによりオフセット、ジャム等の発生を防止でき、
又コピーライフが長い。
Claims (1)
- 【特許請求の範囲】 １、ローラ基体上に、一般式 ▲数式、化学式、表等があります▼ （但し、Ｘ＝−ＯＨ、−ＣＨ＝ＣＨ＿２でありｎ＝４０
０〜１５００の正の整数を表わす。） で表わされるシリコーンゴムとコバルト青および補強充
填剤とを主成分とした高離型性シリコーンゴム層を設け
たことを特徴とするカラー複写機用熱定着部ローラ。 ２、高離型性シリコーンゴム層はフッ素系ゴム層あるい
はシリコーン系ゴム層の少なくとも一層より成る耐シリ
コーンオイル性ゴム層を介してローラ基体上に設けられ
て成ることを特徴とする特許請求の範囲第１項記載のカ
ラー複写機用熱定着部ローラ。