JPS5968848A - 光デイスク媒体 - Google Patents

光デイスク媒体

Info

Publication number
JPS5968848A
JPS5968848A JP57178166A JP17816682A JPS5968848A JP S5968848 A JPS5968848 A JP S5968848A JP 57178166 A JP57178166 A JP 57178166A JP 17816682 A JP17816682 A JP 17816682A JP S5968848 A JPS5968848 A JP S5968848A
Authority
JP
Japan
Prior art keywords
thin film
track
film layer
wavelength
refractive index
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
JP57178166A
Other languages
English (en)
Inventor
Masami Miyagi
宮城　雅美
Shuzo Fukunishi
福西　修三
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Nippon Telegraph and Telephone Corp
Original Assignee
Nippon Telegraph and Telephone Corp
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Nippon Telegraph and Telephone Corp filed Critical Nippon Telegraph and Telephone Corp
Priority to JP57178166A priority Critical patent/JPS5968848A/ja
Publication of JPS5968848A publication Critical patent/JPS5968848A/ja
Pending legal-status Critical Current

Abstract

(57)【要約】本公報は電子出願前の出願データであるた
め要約のデータは記録されません。

Description

【発明の詳細な説明】 本発明は、光ビームにより情報の記録・再生を行なう光
記録装置の光デイスク媒体の構造に関するものである。
従来、この種の光ディスクにおいては、光ビームのトラ
ッキングを行なうために、第１図に示すような構造が用
いられている。即ち、ガラスもしくはプラスチックから
なるディスク基板１１上に同心円もしくはスパイラル状
の凹状もしくは凸状の溝１２を設け、その上にＴｅもし
くはＴｅ化合物等の金属薄膜からなる情報記録薄膜１３
を付加して溝付ディスクを構成する。この溝の底部に基
板１１ｆ通してレーザ光１４を対物レンズ１５により集
光して照射し、記録と再生を行なう。この場合、従来の
溝付ディスクにおいては、その溝１２の深さをトラック
信号のＳＮ比が最良になるように２／８ｎ（ここでλは
記録・再生円光源の波長、ｎは基板１１の屈折率である
）に設定している。
このような従来の溝付ディスクの作繋法を以下に示す。
先ず、ガラス円板上に７オトレジストによシ溝を形成し
、溝原版を作成する。即ちガラス円板上にスピンコード
によりフォトレジλ ストヲ／８ｎの厚さに塗布する。次に、このガラス原版
を回転しながら集光レーザビームによってトラック形成
位置を露光する。これを現像することにより２／８ｎの
深さの溝が形成でき、溝原版が作られる。次にこの溝原
版をマスク板として、これに電極用として銀を蒸着し、
ニッケル電鋳によってスタンパを作翳する。次にこのス
タンパｆ用いてアクリル樹脂等のプラスチック材料を射
出成形、キャスト成形法等により成形し、溝付ディスク
基板が得られる。さらに、この溝付ディスク基板に情報
記録媒体を付加することにより、溝付光ディスクが得ら
れる。
以上述べたように、従来の溝付光ディスクの作製におい
ては、溝原版からスタンバへ溝を転写し、さらにスタン
パからディスク基板へ溝を転写するため、工程が多くな
るとともにこれらの転写の過程でごみの付着等により、
溝に欠陥が発生し、トラック信号が劣化するという欠点
を有する。
本発明はディスク基板上に光照射によって屈折率が変化
する物質を形成し、当該物質に集光レーザビームを照射
し、屈折率を変化させることによりトラックを直接ディ
スク基板上に形成することを特徴とし、その目的は溝転
写に伴う欠陥発生を抑制し、良質のトラック信号を得る
とともに高い信号対雑音比で情報を記録再生できる光デ
イスク媒体を得ることにある。
次に本発明の実施例を図面について説明する。
第２図は本発明の光デイスク媒体の断面図であり、図に
おいて、２１はガラスもしくはプラスチックからなるデ
ィスク基板、２２は光照射により屈折率変化を起こす物
質からなるトラック形成薄膜層、２３はトラック形成薄
膜層、２２に集束レーザビームを照射し、トラック形成
薄膜層２２の屈折率を変化させることにより形成したト
ラック、２４は情報記録薄膜層、２５は情報記録薄膜層
２４上に形成したピットである。
次にこの光ティスフ媒体の製造工程全以下に示す。先ず
基板２１上にトラック形成薄膜層２２を形成する。不実
施例ではトラック形成薄膜層２２としてＡｓ−８ｅ−８
−Ｇｅ系薄膜をスパッタリングにより形成する。この薄
膜は光学吸収端が４７００Ａ付近にあり、この波長付近
もしくはこれより短波長側の光を照射すると、照射され
た部分の屈折率が増加する。この光銹起による現象は透
過率でみると減少し暗くなるので光点化効果とよばれる
。次にこの光点化効果を用いてトラック形成薄膜層２２
に屈折率変化を生せしめるため、波長４８　ｓ　ｏＸの
Ａｒレーザ光を収束してトラック形成位置に照射し、ト
ラック２３を形成する。次にＴｅもしくはＴｅ化合物等
の金属薄膜からなる情報記録薄膜層２４を形成すること
により、本発明の光デイスク媒体は完成する。なお、ト
ラック形成薄膜層２２および情報記録薄膜層２４を形成
した後にＡｒレーザ光を照射してトラック２３を形成す
ることも可能である。情報の記録はトラック形成位置に
基板２１およびトラツク２３全通して記録薄膜層２４上
に波長８３００Ｘの半導体レーザ光を収束して照射し、
ピット２５を形成することにより行なう。ピット２５は
トラック２３に沿って形成され情報の記録が行なわれる
。情報の再生は半導体レーザの出力を情報記録薄膜層２
４が溶融蒸発しない程度に弱めて照射し、トラック２３
に沿ってピット２５を反射光で検出することにより行な
う。
なお、赤外光に対してトラック形成薄膜層２２は高い透
過率を示し、光点化効果も生じないため、半導体レーザ
光の照射によりトラック２３は消失することはない。記
録および再生の際のトラッキングは従来の構付光ディス
クの場合と同様にトラック部からの反射光とトラック以
外の部分からの反射光との位相差を利用して行なう。こ
の位相差は４π△ｎｄ／λで与えられ、この位相差が“
／４のときトラック信号は最大となる。
ここで、△ｎはトラック形成薄膜層２２とトラック２３
との屈折率の差、ｄはトラック形成薄膜層２２の厚さで
ある。従って、例えば△ｎ　＝　０．０５のとき、トラ
ック形成薄膜層２２の厚さｄは１μｍとすればよい。
次に、本発明の具体的な実施例について説明する。
実施例（１） ガラス基板上にＡＳ４Ｕ　　５ｅｌＯ８４０Ｇｅ１Ｏ薄
膜をスパッタリングにより１μｍの厚さに形成した。次
に、この基板を３００回転／分で回転しながら波長４８
８０ＡのＡｒレーザ光を薄−膜上に集束して照射し、ス
パイラル状のトラックを形成した。
トラックピッチは３μｍ、）ラック幅は０．５μｍとし
た。トラック部とトラックを形成していない部分との屈
折率の差は波長８３００Ａにおいて０．０５であった。
次に、情報記録薄膜としてＣ８２Ｔｅ薄膜をプラズマ重
合法により、２００にの厚さに形成した。かくして得た
光デイスク媒体を１８００回転／回転目転しながら半導
体レーザ光を照射し、トラック信号を検出した結果良質
のトラック信号を得た。また、半導体レーザを用いた記
録・再生装置によシビデオ信号の記録・再生を行なった
ところ、トラックに沿った記録および再生の動作を確認
し、かつ良好な品質のビデオ再生像を得た。さらに、本
実施例と同様の方法により情報記録薄膜としてＣａｔＴ
ｅ薄膜を形成した従来の溝付光ディスクによるビデオ再
生像と比較したところ、本発明による光デイスク媒体に
よる再生像の方がドロップアウトが少なく、信号対雑音
比が高かった。
実施例（２） ガラス基板上にＡＳ４０５ｅ１６８ｓｓ　Ｇｅ＋ｏ薄膜
をスパッタリングにより７ｓｏＸの厚さに形成し、以下
は実施例（１）と同様の方法により光デイスク媒体を作
製した。トラック部とトラックを形成していない部分と
の屈折率の差は０．０７であった。
かくして得た光デイスク媒体について実施例（１）と同
様な記録・再生実験を行なったところ、トラックに沿っ
た記録および再生の動作を確認し、かつ良好な品質のビ
デオ再生像を得た。
以上説明したように本発明によれば、少ない工程で直接
ディスク基板上にトラックを形成することができ、また
転写に伴う欠陥発生もないため、記録あるいは再生時の
トラック制御を容易にし、かつ高い信号対雑音比で情報
を記録・再生できる光ディスクを提供することが可能と
なる。
【図面の簡単な説明】
第１図は従来の溝付光ディスクの断面図、第２図は本発
明の光デイスク媒体の断面図である。 図面中 １１はディスク基板、 １２Ｆｉ、溝、 １３は情報記録薄膜、 １４はレーザ光、 １５は対物レンズ、 ２１はディスク基板、 ２２はトラック形成薄膜層、 ２３はトラック、 ２４は情報記録薄膜層、 ２５はピット である。 特許出願人 日本電信電話公社 代理人 弁理士　　光　石　士　部（他１名） 第１図 第２図

Claims (1)

    【特許請求の範囲】
  1. ディスク状の透明基板上に、光照射によって屈折率が変
    化する薄膜材料からなるトラック形成薄膜層および情報
    記録薄膜層を積層したことを特徴とする光デイスク媒体
    。
JP57178166A 1982-10-09 1982-10-09 光デイスク媒体 Pending JPS5968848A (ja)