JPS5894144A - 記録媒体 - Google Patents

記録媒体

Info

Publication number
JPS5894144A
JPS5894144A JP56192598A JP19259881A JPS5894144A JP S5894144 A JPS5894144 A JP S5894144A JP 56192598 A JP56192598 A JP 56192598A JP 19259881 A JP19259881 A JP 19259881A JP S5894144 A JPS5894144 A JP S5894144A
Authority
JP
Japan
Prior art keywords
tellurium
layer
recording
recording medium
recording layer
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
JP56192598A
Other languages
English (en)
Inventor
Yasuyuki Goto
康之 後藤
Nagaaki Etsuno
越野　長明
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Fujitsu Ltd
Original Assignee
Fujitsu Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Fujitsu Ltd filed Critical Fujitsu Ltd
Priority to JP56192598A priority Critical patent/JPS5894144A/ja
Publication of JPS5894144A publication Critical patent/JPS5894144A/ja
Pending legal-status Critical Current

Abstract

(57)【要約】本公報は電子出願前の出願データであるた
め要約のデータは記録されません。

Description

【発明の詳細な説明】 本発明は光ディスクなど光ビームを用いて情報の読み書
きを行う記録媒体に関し、長期間保存しても、安定で劣
化がないため、書込み読出しくＲ／Ｗ）特性に変化を生
じない記録媒体を提供するものである。
この種の記録媒体としては、第１図に示すように円盤状
の透明基板１．ｌにテルル層２．２を蒸着したものを２
枚重ね合わせて円周部分を密閉したいわゆるエアーサン
ドイッチ構造の光ディスクなどが知られている。光ディ
スクの透明基板としては、ガラスもしくはアクリルなど
のプラスチックが用いられているが、ガラスは気体透過
率が小さい利点がある反面、熱伝導率がアクリルなどに
比して太きく、また機械的衝撃に弱いなど取扱上の不便
もあるため１今日ではアクリルなどのプラスチックが好
んで用いられている。しかし、アクリルなどのプラスチ
ックは、気体透過率が比較的大きいため、密閉しタエア
ーサンドイッチ構造であっても、テルル層の存在する内
部に水蒸気、酸素、その他の気体が侵入しやすく、テル
ル層を酸化させるなどして腐蝕するという間伽があった
。
また、これらの現象は、上記ガラス基板を用いた光ディ
スクにおいても、程度の差はあれ必然的に生起する問題
であった。このようなテルル層の劣化は、テルル層麦面
の不均一な局部的現象として生起し、例えば局部的酸化
が起きるとテルル表面の金属光沢が減少して情報の正確
な統み出しができなくなるほか、酸化テルルはテルルに
比して融点が著しく高くなるため、情報書き込み時の通
常のレーザエネルギーでは十分穿孔ができず、結局書き
込みが不完全になるという結果を招いていた。特にこの
種の記録媒体は、一旦書き込みが行われると消去書き直
しができないため、一部でも書き込み情報が不完全にな
ると、全体として使用不能になるので、テルル層の安定
性は極めて重要である。
本発明は、テルル層の表面に均一にかつレーザ照射によ
る読み書きに支障のない厚さの酸化テルル層を予め設は
不動態層とすることＫより、テルル層の安定性を極めて
高いものにするものである。
以下本発明の実施例に基づいて詳細に説明する０ 第２図に示すように光デイスク用のアクリル製透明基板
３上に二酸化テルルを厚さ５ｎｍに先ず真空蒸着して防
護層重となし、次いで金属テルルを厚さ３０Ｍ１に真空
蒸着して記録層５を形成し、更に二酸化テルル５ｎｍを
該金属テルル層の上に真空蒸着して防護層６を形成した
。このようにして得た記録層付のアクリル基板を記録層
を対向させてエアーサンドインチ構造の光ディスクと成
した。また、対比のため、酸化テルル層を蒸着せず、金
属テルルのみ厚さ３Ｑｎｍに真空蒸着して成る同寸法の
エアーサンドインチ構造の光ディスクを作り、実験に供
した。
先ず、防護層付の光ディスクと防護層のない光ディスク
のＲ／Ｗ特性を比較した。共にレーザ出力を１４ｍＷと
して一定の周波数のパルス信号の書き込みを行ったが、
両者を比べて書き込み特性に変化はなかった。また、該
ディスクのＯ／ＩＩ比を比較したところ、共に６５〜６
６（ＩＢの値を示し、差異が認められなかった。
次に１上記防御層付光ディスクと防護層のない光ディス
クを６０℃８５％ＰＨ（相対湿度）の恒温恒湿層に入れ
、２０００時間経過後比較したところ、防護層のない光
ディスクは、正常な書き込みを達成するのにレーザ出力
３０〜５０ｍＷを必要とし、Ｏ／Ｎ比も５０（ＬＢ以下
と明らかな劣化を示したが、防護層付の光ディスクの特
性は製造時と比べて変化がなく、本発明が記録層の安定
性のため極めて有効であることが知られた。
防護層としての酸化テルル層は１厚すぎるとＲ／Ｗ特性
に悪影普があるので、１５■以下がよ〈１特に５１Ｍ１
程度が好ましい。またＳ酸化テルル層上に他の有機、無
機の保護膜を設けることも劣化防止のためには有効であ
る。更に、上記の例では、金属テルル層の両面に酸化テ
ルル層を付したが、その−面にのみ酸化テルル層を設け
るだけでも効果は大である。
なお、酸化テルル層の形成性、真空蒸着法、スパッタリ
ング法などのほか、テルルを直接熱酸化することＫよっ
ても可能である。
以上のとおり、本発明は、テルル記録層を用いた光ディ
スク等の記録媒体の耐久性、安定性を飛躍的に向上する
ものである。
【図面の簡単な説明】
第１図は従来の光ディスクの構造を示す一部切欠部分斜
視図、第２図は本発明の一実施例構成図である。 １．３：透明基板、２．５：金属テルルＮ１４．６：酸
化テルル層

Claims (1)

  1. 【特許請求の範囲】 １）　基盤上に設けたテルル記録層に光ビームを照射し
    、上記テルル記録ＦｔＩＫ穿孔して情報を記録する記録
    媒体において、上記テルル記録層の一表面または両表面
    に酸化テルル層を設けたことを特徴とする記録媒体。 ２）　前記酸化テルル層の層厚が１５ｎｍ以下の厚さで
    あることを特徴とする特許請求の範囲第１項に記載の記
    録媒体。 ３）　前記酸化テルル層が二酸化テルル層であることを
    特徴とする特許請求の範囲第１項に記載の記録幹体。
JP56192598A 1981-11-30 1981-11-30 記録媒体 Pending JPS5894144A (ja)