JPH11512465A - 無気胞または有気胞ポリウレタンの製造方法およびこれに適するイソシアナート初期重合体 - Google Patents
無気胞または有気胞ポリウレタンの製造方法およびこれに適するイソシアナート初期重合体Info
- Publication number
- JPH11512465A JPH11512465A JP9511643A JP51164397A JPH11512465A JP H11512465 A JPH11512465 A JP H11512465A JP 9511643 A JP9511643 A JP 9511643A JP 51164397 A JP51164397 A JP 51164397A JP H11512465 A JPH11512465 A JP H11512465A
- Authority
- JP
- Japan
- Prior art keywords
- diisocyanate
- isocyanate
- weight
- prepolymer
- group
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
Claims (1)
- 【特許請求の範囲】 1.(a)800から6000の分子量を有するポリヒドロキシル化合物およ び必要に応じて、 (b)800までの分子量を有する連鎖延長剤および/または架橋剤と、 (c)有機ポリイソシアナートとを、 (d)触媒、 (e)水を含有する発泡剤、および (f)添加剤 の存在下また不存在下に反応させることにより非熱可塑性ポリウレタンエラスト マーを製造する方法であって、 使用される上記の有機ポリイソシアナート(c)が、ナフチレン−1,5−ジ イソシアナート、および少なくとも1種類の、トリレンジイソシアナート、ジフ ェニルメタンジイソシアナート、3,3′−ジメチルビフェニルジイソシアナー ト、1,2−ジフェニルエタンジイソシアナート、フェニレンジイソシアナート の中から選ばれる追加的な芳香族ジイソシアナート、および/または炭素原子4 から12の脂肪族ジイソシアナート、および/または炭素原子数6から18の脂 環式ジイソシアナートであること、これら有機ポリイソシアナート(c)が、ナ フチレン−1,5−ジイソシアナート、および追加的な少なくとも1種類の他の 芳香族、脂肪族および/または脂環式ジイソシアナート、少なくとも1種類のポ リヒドロキシル化合物(a)および必要に応じて連鎖延長剤および/または架橋 剤(b)から製造される、イソシアナート基含有プリポリマーの形態で使用され ること、およびこのプリポリマーが、上記構成分(a)、(b)、(e)の少な くともいずれか1種類と反応せしめられることを特徴とする製造方法。 2.上記ポリヒドロキシル化合物(a)が2から3の官能性を有することを特 徴とする、請求項1の製造方法。 3.上記ポリヒドロキシル化合物(a)が、2官能性で、800から3500 の分子量を有し、ポリエステルポリオール、ヒドロキシル含有ポリカルボナート 、ポリオキシブチレングリコールの中から選ばれるいずれかであることを特徴 とする請求項1の製造方法。 4.上記連鎖延長剤(b)が、アルカンジオール、ジアルキレングリコール、 ポリオキシアルキレングリコールのいずれかであり、架橋剤(b)が、三価もし くは四価アルコール、官能性3から4のポリオキシアルキレンポリオールオリゴ マーのいずれかであることを特徴とする、請求項1の製造方法。 5.使用される上記の有機ポリイソシアナート(c)が、ナフチレン−1,5 −ジイソシアナートと、トリレンジイソシアナート、ジフェニルメタンジイソシ アナート、3,3′−ジメチルビフェニルジイソシアナート、1,2−ジフェニ ルエタンジイソシアナート、フェニレンジイソシアナートの中から選ばれる少な くとも1種類の追加的芳香族ジイソシアナートおよび/またはヘキサメチレン− 1,6−ジイソシアナートおよび/または1−イソシアナート−3,3,5−ト リメチル−5−イソシアナートメチルシクロヘキサンとの流動性混合物を含有す ることを特徴とする、請求項1の製造方法。 6.使用される有機ポリイソシアナート(c)が、ナフチレン−1,5−ジイ ソシアナートと、ジフェニルメタン−4,4′−ジイソシアナートの溶融体を含 有することを特徴とする、請求項1の製造方法。 7.有機ポリイソシアナート(c)が、ポリヒドロキシル化合物(a)の部分 量または全量、あるいはこの化合物(a)と連鎖延長剤および/または架橋剤( b)との混合物の部分量または全量と、トリレンジイソシアナート、ジフェニル メタンジイソシアナート、3,3′−ジメチルビフェニルジイソシアナート、1 ,2−ジフェニルメタンジイソシアナート、フェニレンジイソシアナートの中か ら選ばれる少なくとも1種類の芳香族ジイソシアナートおよび/またはヘキサメ チレン−1,6−ジイソシアナートおよび/または1−イソシアナート−3,3 ,5−トリメチル−5−イソシアナートメチルシクロヘキサンとの反応によりウ レタン基含有重付加物を形成し、この重付加物をナフチレン−1,5−ジイソシ アナートと反応させることにより得られるイソシアナート基含有プリポリマーの 形態において使用されることを特徴とする、請求項1の製造方法。 8.有機ポリイソシアナート(c)が、ポリヒドロキシル化合物(a)の部分 量または全量、あるいはこの化合物(a)と連鎖延長剤およびまたは架橋剤 (b)との混合物の部分量または全量と、ジフェニルメタン−4,4′−ジイソ シアナートとの反応によりウレタン基含有重付加物を形成し、この重付加物をナ フチレン−1,5−ジイソシアナートと反応させることにより得られるイソシア ナート基含有プリポリマーの形態において使用することを特徴とする、請求項1 の製造方法。 9.有機ポリイソシアナート(c)が、ポリヒドロキシル化合物(a)あるい はこの化合物(a)と連鎖延長剤および/または架橋剤との混合物と、トルイレ ンジイソシアナート、ジフェニルメタンジイソシアナート、3,3′−ジメチル ビフェニルジイソシアナート、1,2−ジフェニルメタンジイソシアナート、フ ェニレンジイソシアナートから選ばれる芳香族ジイソシアナートおよび/または ヘキサメチレン−1,6−ジイソシアナートおよび/または1−イソシアナート −3,3,5−トリメチル−5−イソシアナートメチルシクロヘキサンとを、( a)または(a)+(b)のヒドロキシル基対有機ジイソシアナートのイソシア ナート基の当量割合が1:(>1〜6)となるように反応させて、ウレタンおよ びイソシアナート基含有重付加物を形成し、この重付加物を、ナフチレン−1, 5−ジイソシアナートと、(a)または(a)+(b)のヒドロキシル基対ナフ チレン−1,5−ジイソシアナートのイソシアナート基の当量割合が1:0.0 2〜6となるように反応させて得られるイソシアナート基含有プリポリマーの形 態で使用されることを特徴とする、請求項1の製造方法。 10.有機ポリイソシアナート(c)が、ポリヒドロキシル化合物(a)、ま たはこの化合物(a)と連鎖延長剤および/または架橋剤(b)との混合物と、 ジフェニルメタン−4,4′−ジイソシアナートと、ヒドロキシル基対イソシア ナート基の当量割合が1:(>1〜6)となるように反応させることによりウレ タンおよびイソシアナート基含有重付加物を形成し、この重付加物と、ナフチレ ン−1,5−ジイソシアナートとを、(a)または(a)+(b)のヒドロキシ ル基対ナフチレン−1,5−ジイソシアナートのイソシアナート基の当量割合が 1:0.02〜6となるように反応させることにより得られるイソシアナート基 含有プリポリマーの形態で使用されることを特徴とする、請求項1の製造方法。 11.請求項1から10のいずれかの有気胞ポリウレタンエラストマーの製造 方法であって、発泡剤(d)が水であり、必要に応じて、炭素原子数4から8の アルカンおよび炭素原子数4から6のシクロアルカンから選ばれる少なくとも1 種類の補助発泡剤を使用することを特徴とする製造方法。 12.0.2から1.1g/lの密度を有する、請求項1の有気胞ポリウレタ ンエラストマーの製造方法。 13.少なくとも1種類のポリヒドロキシル化合物(a)、またはこの化合物 (a)と連鎖延長剤および/または架橋剤(b)の混合物を、トリレンジイソシ アナート、ジフェニレンメタンジイソシアナート、3,3′−ジメチルビフェニ ルジイソシアナート、1,2−ジフェニルエタンジイソシアナート、フェニレン ジイソシアナートの中から選ばれる少なくとも1種類の芳香族ジイソシアナート および/またはヘキサメチレン−1,6−ジイソシアナートおよび/または1− イソシアナート−3,3,5−トリメチル−5−イソシアナートメチルシクロヘ キサンと反応させることにより、NCO含有分0.05から8重量%の、ウレタ ンおよびイソシアナート基含有重付加物を形成し、この重付加物をナフチレン− 1,5−ジイソシアナートと反応させることにより製造される、NCO含有分3 .3から10重量%の、イソシアナート基含有プリポリマー。 14.(a)または(a)および(b)のヒドロキシル基対トリレンジイソシ アナート、ジフェニレンメタンジイソシアナート、3,3′−ジメチルビフェニ ルジイソシアナート、1,2−ジフェニルエタンジイソシアナート、フェニレン ジイソシアナートの中から選ばれる少なくとも1種類の芳香族ジイソシアナート および/またはヘキサメチレン−1,6−ジイソシアナートおよび/または1− イソシアナート−3,3,5−トリメチル−5−イソシアナートメチルシクロヘ キサンのNCO基対ナフチレン−1,5−ジイソシアナートのNCO基の当量割 合が、1:(>1〜6):0.02〜6であることを特徴とする、請求項13の イソシアナート基含有プリポリマー。 15.ポリヒドロキシル化合物(a)またはこの(a)と連鎖延長剤および/ または架橋剤(b)の混合物と、ジフェニルメタン−4,4′−ジイソシアナー トとを反応させることにより、NCO含有分0.05から8重量%の、ウレタン およびイソシアナート基含有重付加物を形成し、この重付加物をナフチレン− 1,5−ジイソシアナートと反応させることにより得られ、かつNCO含有分が 3.3から10重量%であることを特徴とするイソシアナート基含有プリポリマ ー。 16.ポリエステルポリオール、ヒドロキシル含有ポリカルボナート、ポリオ キシテトラメチレングリコールの中から選ばれる、分子量>800から3500 の2官能性ポリヒドロキシル化合物を、ジフェニルメタン−4,4′−ジイソシ アナートと反応させることにより、ウレタンおよびイソシアナート基含有重付加 物を形成し、この重付加物をナフチレン−1,5−ジイソシアナートと反応させ ることにより得られ、かつNCO含有分が3.3から10重量%であることを特 徴とするイソシアナート基含有プリポリマー。 17.(a)または(a)と(b)のヒドロキシル基対ジフェニルメタン−4 ,4′−ジイソシアナートのNCO基対ナフチレン−1,5−ジイソシアナート のNCO基の当量割合が1:(>1〜6):0.02〜6であることを特徴とす る、請求項15または16のイソシアナート基含有プリポリマー。