JPH08176846A - 端面耐食性に優れた塗装鋼板 - Google Patents
端面耐食性に優れた塗装鋼板Info
- Publication number
- JPH08176846A JPH08176846A JP6328051A JP32805194A JPH08176846A JP H08176846 A JPH08176846 A JP H08176846A JP 6328051 A JP6328051 A JP 6328051A JP 32805194 A JP32805194 A JP 32805194A JP H08176846 A JPH08176846 A JP H08176846A
- Authority
- JP
- Japan
- Prior art keywords
- steel sheet
- corrosion resistance
- chromate
- layer
- strontium chromate
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
(57)【要約】
【目的】初期および長期端面耐食性に優れた塗装鋼板の
提供。 【構成】亜鉛系めっき鋼板の少なくとも一方の面にりん
酸亜鉛化成処理層を形成し、この化成処理層の上にスト
ロンチウムクロメートと、表面処理を行ない水溶解度を
水溶分として０．１〜２．０重量％に低くしたストロン
チウムクロメートとを混合比７０／３０〜４０／６０
（重量比）で混合し、塗料不揮発分に対して３０〜６０
重量％含有させた下塗り層を形成し、その上に上塗り層
を形成してなることにより、上記目的を達成する。
提供。 【構成】亜鉛系めっき鋼板の少なくとも一方の面にりん
酸亜鉛化成処理層を形成し、この化成処理層の上にスト
ロンチウムクロメートと、表面処理を行ない水溶解度を
水溶分として０．１〜２．０重量％に低くしたストロン
チウムクロメートとを混合比７０／３０〜４０／６０
（重量比）で混合し、塗料不揮発分に対して３０〜６０
重量％含有させた下塗り層を形成し、その上に上塗り層
を形成してなることにより、上記目的を達成する。
Description
【０００１】
【産業上の利用分野】本発明は、端面耐食性に優れた下
塗り層を有し、初期および長期の端面耐食性に優れた塗
装鋼板に関する。
塗り層を有し、初期および長期の端面耐食性に優れた塗
装鋼板に関する。
【０００２】
【従来の技術】一般に塗装鋼板の下塗り層の防錆顔料と
しては、例えば、特公平２−３６３８４号公報に記載さ
れているようにクロム酸系のストロンチウムクロメート
等が使用されている。これは他のりん酸系、モリブデン
酸系、ホウ酸系の防錆顔料よりもクロム酸の防錆力が優
れているためである。
しては、例えば、特公平２−３６３８４号公報に記載さ
れているようにクロム酸系のストロンチウムクロメート
等が使用されている。これは他のりん酸系、モリブデン
酸系、ホウ酸系の防錆顔料よりもクロム酸の防錆力が優
れているためである。
【０００３】
【発明が解決しようとする課題】しかしながら、塗装鋼
板の切断部の端面耐食性においてクロム酸系の防錆顔料
にもその水溶解度に差が有り、水溶解度の高いカルシュ
ウムクロメートは初期の端面耐食性は良いが、長期にな
ると防錆顔料が早く溶出してしまい耐食性が悪くなると
いう問題があった。一方、水溶解度の低いストロンチウ
ムクロメートでは、水溶解度の高いものに比べて長期端
面耐食性は良くなるものの、それにも限界があった。
板の切断部の端面耐食性においてクロム酸系の防錆顔料
にもその水溶解度に差が有り、水溶解度の高いカルシュ
ウムクロメートは初期の端面耐食性は良いが、長期にな
ると防錆顔料が早く溶出してしまい耐食性が悪くなると
いう問題があった。一方、水溶解度の低いストロンチウ
ムクロメートでは、水溶解度の高いものに比べて長期端
面耐食性は良くなるものの、それにも限界があった。
【０００４】本発明は、前記従来技術の問題点を解消
し、水溶解度の低いストロンチウムクロメートと、表面
処理によって、これよりさらに水溶解度を低くしたスト
ロンチウムクロメートとを下塗り層に混合使用すること
により、さらに、初期および長期端面耐食性に優れた塗
装鋼板を提供することを目的とするものである。
し、水溶解度の低いストロンチウムクロメートと、表面
処理によって、これよりさらに水溶解度を低くしたスト
ロンチウムクロメートとを下塗り層に混合使用すること
により、さらに、初期および長期端面耐食性に優れた塗
装鋼板を提供することを目的とするものである。
【０００５】
【課題を解決するための手段】上記目的を達成するため
に、本発明は、亜鉛系めっき鋼板の少なくとも一方の面
にりん酸亜鉛化成処理層を形成し、この化成処理層の上
にストロンチウムクロメートと、表面処理を行ない水溶
解度を水溶分として０．１〜２．０重量％に低くしたス
トロンチウムクロメートとを混合比７０／３０〜４０／
６０（重量比）で混合し、塗料不揮発分に対して３０〜
６０重量％含有させた下塗り層を形成し、その上に上塗
り層を形成してなることを特徴とする端面耐食性に優れ
た塗装鋼板を提供するものである。
に、本発明は、亜鉛系めっき鋼板の少なくとも一方の面
にりん酸亜鉛化成処理層を形成し、この化成処理層の上
にストロンチウムクロメートと、表面処理を行ない水溶
解度を水溶分として０．１〜２．０重量％に低くしたス
トロンチウムクロメートとを混合比７０／３０〜４０／
６０（重量比）で混合し、塗料不揮発分に対して３０〜
６０重量％含有させた下塗り層を形成し、その上に上塗
り層を形成してなることを特徴とする端面耐食性に優れ
た塗装鋼板を提供するものである。
【０００６】
【発明の作用】本発明の端面耐食性に優れた塗装鋼板
は、前記問題点を解決するために、亜鉛めっき鋼板の少
なくとも一方の面にりん酸亜鉛化成処理層を形成し、こ
の化成処理層の上にストロンチウムクロメートと、スト
ロンチウムクロメートに表面処理を行ない水溶解度を、
水溶分として０．１〜２．０重量％、好ましくは０．３
〜１．０重量％まで低下させたストロンチウムクロメー
トとを、混合比（ストロンチウムクロメート／表面処理
ストロンチウムクロメート）として重量比で７０／３０
〜４０／６０に混合した混合物を塗料不揮発分に対して
３０〜６０重量％含有させた下塗り層（プライマー）を
形成し、その上に上塗り層を形成してなるものである。
は、前記問題点を解決するために、亜鉛めっき鋼板の少
なくとも一方の面にりん酸亜鉛化成処理層を形成し、こ
の化成処理層の上にストロンチウムクロメートと、スト
ロンチウムクロメートに表面処理を行ない水溶解度を、
水溶分として０．１〜２．０重量％、好ましくは０．３
〜１．０重量％まで低下させたストロンチウムクロメー
トとを、混合比（ストロンチウムクロメート／表面処理
ストロンチウムクロメート）として重量比で７０／３０
〜４０／６０に混合した混合物を塗料不揮発分に対して
３０〜６０重量％含有させた下塗り層（プライマー）を
形成し、その上に上塗り層を形成してなるものである。
【０００７】本発明の塗装鋼板においては、上記のよう
な構成により、下塗り層に含有せしめる水溶解度の低い
防錆顔料であるストロンチウムクロメートに表面処理を
行ない、さらに水溶解度を低くしているので、長期間防
錆顔料が下塗り層に残ることが可能となる。このため、
本発明では下塗り層において、クロム酸が徐々に溶出
し、クロムによる不動態被膜が形成されるので、この不
動態被膜により長期防錆力を保持することができる。
な構成により、下塗り層に含有せしめる水溶解度の低い
防錆顔料であるストロンチウムクロメートに表面処理を
行ない、さらに水溶解度を低くしているので、長期間防
錆顔料が下塗り層に残ることが可能となる。このため、
本発明では下塗り層において、クロム酸が徐々に溶出
し、クロムによる不動態被膜が形成されるので、この不
動態被膜により長期防錆力を保持することができる。
【０００８】以下に、本発明をさらに詳細に説明する。
本発明に適用できる母材は、亜鉛系めっき鋼板の少なく
とも一方の面にりん酸亜鉛化成処理したものが使用され
る。亜鉛系めっき鋼板としては、亜鉛めっき鋼板（電気
亜鉛めっき鋼板、溶融亜鉛めっき鋼板、合金化溶融亜鉛
めっき鋼板）、およびＺｎ−Ｎｉ合金めっき鋼板、Ｚｎ
−Ｆｅ合金めっき鋼板、亜鉛−マンガン合金めっき鋼
板、亜鉛−アルミニウム合金めっき鋼板、亜鉛−コバル
ト−クロム合金めっき鋼板等の亜鉛系合金めっき鋼板が
含まれる。
本発明に適用できる母材は、亜鉛系めっき鋼板の少なく
とも一方の面にりん酸亜鉛化成処理したものが使用され
る。亜鉛系めっき鋼板としては、亜鉛めっき鋼板（電気
亜鉛めっき鋼板、溶融亜鉛めっき鋼板、合金化溶融亜鉛
めっき鋼板）、およびＺｎ−Ｎｉ合金めっき鋼板、Ｚｎ
−Ｆｅ合金めっき鋼板、亜鉛−マンガン合金めっき鋼
板、亜鉛−アルミニウム合金めっき鋼板、亜鉛−コバル
ト−クロム合金めっき鋼板等の亜鉛系合金めっき鋼板が
含まれる。
【０００９】本発明において亜鉛系めっき鋼板のりん酸
亜鉛処理層上に下塗り層を形成するための下塗り塗料
（プライマー）は、塗料不揮発分を構成する樹脂と防錆
顔料とからなる。ここで、本発明においては、防錆顔料
として、水溶解度の低いストロンチウムクロメートと、
この水溶解度の低いストロンチウムクロメートに表面処
理を行ってさらに水溶解度を低下させたストロンチウム
クロメートとを混合して用いる。この理由は、防錆顔料
として、水溶解度の低いストロンチウムクロメートに、
表面処理によってさらに水溶解度の低下したストロンチ
ウムクロメートを混合した混合物を用いることにより、
長期間下塗り層に防錆顔料を残存させることが可能とな
り、下塗り層から長期間に亘って徐々にクロム酸を溶出
させ、クロムによる不動態被膜を形成させ、長期間に亘
る防錆力を保持させることができるからである。
亜鉛処理層上に下塗り層を形成するための下塗り塗料
（プライマー）は、塗料不揮発分を構成する樹脂と防錆
顔料とからなる。ここで、本発明においては、防錆顔料
として、水溶解度の低いストロンチウムクロメートと、
この水溶解度の低いストロンチウムクロメートに表面処
理を行ってさらに水溶解度を低下させたストロンチウム
クロメートとを混合して用いる。この理由は、防錆顔料
として、水溶解度の低いストロンチウムクロメートに、
表面処理によってさらに水溶解度の低下したストロンチ
ウムクロメートを混合した混合物を用いることにより、
長期間下塗り層に防錆顔料を残存させることが可能とな
り、下塗り層から長期間に亘って徐々にクロム酸を溶出
させ、クロムによる不動態被膜を形成させ、長期間に亘
る防錆力を保持させることができるからである。
【００１０】本発明においては、塗料不揮発分（樹脂）
と防錆顔料とからなる下塗り塗料中の防錆顔料の量は、
塗料不揮発分に対して３０〜６０重量％とする必要があ
る。ここで、３０重量％未満だと端面耐食性が悪いの
で、３０重量％以上とする。また、６０重量％を超える
と塗膜密着性が悪くなるので、６０重量％以下とする。
と防錆顔料とからなる下塗り塗料中の防錆顔料の量は、
塗料不揮発分に対して３０〜６０重量％とする必要があ
る。ここで、３０重量％未満だと端面耐食性が悪いの
で、３０重量％以上とする。また、６０重量％を超える
と塗膜密着性が悪くなるので、６０重量％以下とする。
【００１１】表面処理をしたストロンチウムクロメート
の水溶解度は、水溶分として０．１〜２．０重量％であ
るのが適当である。ここで、０．１重量％未満だと耐食
性に効果が無いので０．１重量％以上とする。また２．
０重量％を超えると長期耐食性に効果が無いので２．０
重量％以下とする。
の水溶解度は、水溶分として０．１〜２．０重量％であ
るのが適当である。ここで、０．１重量％未満だと耐食
性に効果が無いので０．１重量％以上とする。また２．
０重量％を超えると長期耐食性に効果が無いので２．０
重量％以下とする。
【００１２】ストロンチウムクロメートと表面処理をし
たストロンチウムクロメートとの混合比（ストロンチウ
ムクロメート／表面処理ストロンチウムクロメート）
は、重量比で７０／３０〜４０／６０であるのが適当で
ある。ここで、ストロンチウムクロメートが増加し、こ
の混合比が７０／３０重量比を超えると、長期耐食性に
効果が無いので、７０／３０重量比以下とする。またス
トロンチウムクロメートが減少し、この混合比が４０／
６０重量比未満だと、端面部の発錆が早く耐食性に劣る
ので、４０／６０重量比以上とする。
たストロンチウムクロメートとの混合比（ストロンチウ
ムクロメート／表面処理ストロンチウムクロメート）
は、重量比で７０／３０〜４０／６０であるのが適当で
ある。ここで、ストロンチウムクロメートが増加し、こ
の混合比が７０／３０重量比を超えると、長期耐食性に
効果が無いので、７０／３０重量比以下とする。またス
トロンチウムクロメートが減少し、この混合比が４０／
６０重量比未満だと、端面部の発錆が早く耐食性に劣る
ので、４０／６０重量比以上とする。
【００１３】本発明に用いられるプライマーの樹脂とし
ては、母材および上塗り塗膜との密着性、かつ上塗り塗
膜の外観に問題を生じなければ、基本的にどのような樹
脂でも良く、例えばポリエステル樹脂、アクリル樹脂、
エポキシ樹脂、ウレタン樹脂等種々挙げることができ
る。上塗り塗料についても、要求性能を満足すれば、基
本的にどのような樹脂でも良い。例えばポリエステル樹
脂、塩化ビニル樹脂、アクリル樹脂、フッ素樹脂等が挙
げられる。
ては、母材および上塗り塗膜との密着性、かつ上塗り塗
膜の外観に問題を生じなければ、基本的にどのような樹
脂でも良く、例えばポリエステル樹脂、アクリル樹脂、
エポキシ樹脂、ウレタン樹脂等種々挙げることができ
る。上塗り塗料についても、要求性能を満足すれば、基
本的にどのような樹脂でも良い。例えばポリエステル樹
脂、塩化ビニル樹脂、アクリル樹脂、フッ素樹脂等が挙
げられる。
【００１４】
【実施例】以下に、本発明を実施例に基づいて具体的に
説明する。 （実施例１）亜鉛付着量が片面当り９０ｇ／ｍ2 の溶融
亜鉛めっき鋼板にりん酸亜鉛化成処理層を０．８ｇ／ｍ
2 形成し、その上に下塗りプライマーとして塗料不揮発
分に対してストロンチウムクロメートおよび水溶解度
０．１重量％の表面処理ストロンチウムクロメートを、
それぞれ２１重量％および９重量％含むポリエステル系
プライマーを７μｍ塗布焼付けし、上塗りとしてポリエ
ステル系塗料を１８μｍ塗布焼付けした塗装鋼板を得
た。
説明する。 （実施例１）亜鉛付着量が片面当り９０ｇ／ｍ2 の溶融
亜鉛めっき鋼板にりん酸亜鉛化成処理層を０．８ｇ／ｍ
2 形成し、その上に下塗りプライマーとして塗料不揮発
分に対してストロンチウムクロメートおよび水溶解度
０．１重量％の表面処理ストロンチウムクロメートを、
それぞれ２１重量％および９重量％含むポリエステル系
プライマーを７μｍ塗布焼付けし、上塗りとしてポリエ
ステル系塗料を１８μｍ塗布焼付けした塗装鋼板を得
た。
【００１５】（実施例２〜１８）表１に示すように下塗
りプライマーのストロンチウムクロメートと表面処理ス
トロンチウムクロメートの配合比および表面処理ストロ
ンチウムクロメートの水溶解度を変化させたプライマー
を使用し、それ以外は実施例１と同様にして１７種の塗
装鋼板を得た。
りプライマーのストロンチウムクロメートと表面処理ス
トロンチウムクロメートの配合比および表面処理ストロ
ンチウムクロメートの水溶解度を変化させたプライマー
を使用し、それ以外は実施例１と同様にして１７種の塗
装鋼板を得た。
【００１６】（比較例１〜８）表２に示すように、下塗
りプライマーのストロンチウムクロメートと表面処理ス
トロンチウムクロメートの配合比および表面処理ストロ
ンチウムクロメートの水溶解度を変化させたプライマー
を使用し、それ以外は実施例１と同様にして８種類の塗
装鋼板を得た。
りプライマーのストロンチウムクロメートと表面処理ス
トロンチウムクロメートの配合比および表面処理ストロ
ンチウムクロメートの水溶解度を変化させたプライマー
を使用し、それ以外は実施例１と同様にして８種類の塗
装鋼板を得た。
【００１７】以上のようにして得られた塗装鋼板に対し
て、密着性および耐食性の試験を行なった。その結果を
表１および表２に示す。性能試験の試験方法および評価
基準は次の通りである。 （密着性）スペーサを挟まずに１８０°折り曲げ後セロ
ハンテープの貼り付け引きはがしによる評価 ○印：０Ｔ折り曲げ後セロハンテープ剥離なし ×印：上記方法でセロハンテープ剥離有り （耐食性）塩水噴霧１０００時間および２０００時間後
の切断端面部の評価 ◎印：フクレ発錆の全くないもの ○印：極く僅かにフクレ発錆のあるもの △印：フクレ発錆が可成り認められるもの ×印：フクレ発錆が著しいもの
て、密着性および耐食性の試験を行なった。その結果を
表１および表２に示す。性能試験の試験方法および評価
基準は次の通りである。 （密着性）スペーサを挟まずに１８０°折り曲げ後セロ
ハンテープの貼り付け引きはがしによる評価 ○印：０Ｔ折り曲げ後セロハンテープ剥離なし ×印：上記方法でセロハンテープ剥離有り （耐食性）塩水噴霧１０００時間および２０００時間後
の切断端面部の評価 ◎印：フクレ発錆の全くないもの ○印：極く僅かにフクレ発錆のあるもの △印：フクレ発錆が可成り認められるもの ×印：フクレ発錆が著しいもの
【００１８】表１および表２の結果から明らかなよう
に、本発明の塗装鋼板は端面耐食性が優れていることが
わかる。これに対して比較例１および２は、ストロンチ
ウムクロメートと、表面処理により水溶解度を低下した
ストロンチウムクロメートとを混合して使用していない
ので、両者を混合して使用した本発明の塗装鋼板より長
期耐食性が劣ることがわかる。また、比較例２のように
水溶解度を低下させたストロンチウムクロメートだけ使
用しても耐食性が劣る。比較例３は防錆顔料の量が少な
いので耐食性が劣る。比較例４は防錆顔料の量が多いの
で、耐食性は良いが密着性が悪い。比較例５および６は
表面処理ストロンチウムクロメートの溶解度が限定範囲
を外れており、比較例７および８は両者の混合比が限定
範囲を外れているので、耐食性が劣ることがわかる。
に、本発明の塗装鋼板は端面耐食性が優れていることが
わかる。これに対して比較例１および２は、ストロンチ
ウムクロメートと、表面処理により水溶解度を低下した
ストロンチウムクロメートとを混合して使用していない
ので、両者を混合して使用した本発明の塗装鋼板より長
期耐食性が劣ることがわかる。また、比較例２のように
水溶解度を低下させたストロンチウムクロメートだけ使
用しても耐食性が劣る。比較例３は防錆顔料の量が少な
いので耐食性が劣る。比較例４は防錆顔料の量が多いの
で、耐食性は良いが密着性が悪い。比較例５および６は
表面処理ストロンチウムクロメートの溶解度が限定範囲
を外れており、比較例７および８は両者の混合比が限定
範囲を外れているので、耐食性が劣ることがわかる。
【００１９】
【表１】
【００２０】
【表２】
【００２１】
【発明の効果】以上詳細に説明したように、本発明の塗
装鋼板は、切断部の端面耐食性が優れているので、切断
部を露出したまま使用できる。例えば、屋外用途の腐食
環境の厳しい部位にも使用できる。
装鋼板は、切断部の端面耐食性が優れているので、切断
部を露出したまま使用できる。例えば、屋外用途の腐食
環境の厳しい部位にも使用できる。
Claims (1)
- 【請求項１】亜鉛系めっき鋼板の少なくとも一方の面に
りん酸亜鉛化成処理層を形成し、この化成処理層の上に
ストロンチウムクロメートと、表面処理を行ない水溶解
度を水溶分として０．１〜２．０重量％に低くしたスト
ロンチウムクロメートとを混合比７０／３０〜４０／６
０（重量比）で混合し、塗料不揮発分に対して３０〜６
０重量％含有させた下塗り層を形成し、その上に上塗り
層を形成してなることを特徴とする端面耐食性に優れた
塗装鋼板。