JPH0689181B2 - ゴム組成物 - Google Patents
ゴム組成物Info
- Publication number
- JPH0689181B2 JPH0689181B2 JP26662890A JP26662890A JPH0689181B2 JP H0689181 B2 JPH0689181 B2 JP H0689181B2 JP 26662890 A JP26662890 A JP 26662890A JP 26662890 A JP26662890 A JP 26662890A JP H0689181 B2 JPH0689181 B2 JP H0689181B2
- Authority
- JP
- Japan
- Prior art keywords
- rubber
- present
- rubber composition
- sulfur
- weight
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Lifetime
Description
組成物に関するものである。
の実用的早期加硫もしくはスコーチの安定向上を図るた
めに、次式、 で表されるN,N′−ジチオジモルフォリンや、次式、 で表されるテトラメチルチウラムジスルフィドを始めと
して、ジメチルアミン基、ジエチルアミン基またはジブ
チルアミン基が導入されたチウラム系化合物をゴム組成
物に配合することが知られている。
もしくはスコーチ安定性および耐熱性という面で必ずし
も十分に満足のいくものではなく、尚多くの点で改善の
余地があった。
し、より一層スコーチ安定性に優れかつ耐熱性の向上し
たゴム組成物を提供することにある。
結果、加硫可能なゴム組成物に特定のチウラム系化合物
を所定量配合することにより、スコーチ安定性および耐
熱性が大幅に向上することを見出し、本発明を完成する
に至った。
少なくとも1種0.1重量部以上と、硫黄0.1〜8.0重量部
とを配合したことを特徴とするゴム組成物に関するもの
である。
進剤または安定化剤としてゴム組成物に配合するという
ことはこれまでまったく知られていなかった。
場合、チウラム系化合物と硫黄を併用し配合するが、実
際にゴム材料を製造する場合にはかかる加硫剤の他に通
常のゴム配合剤として使用されている加硫活性剤、促進
剤、充填剤、軟化剤、可塑剤、老化防止剤、その他の加
工助剤を一緒に用いても良く、この際通常のゴム配合剤
と一緒に混合しても、また他のすべての添加物の混合を
終了した後に練り込んでも良い。
エン共重合体ゴム、ポリイソプレンゴム、ニトリルゴ
ム、クロロプレンゴム、ブチルゴムおよびエチレン−プ
ロピレンタ−ポリマー等の加硫可能なゴムあるいはこれ
らの混合物等が含まれる。
合割合はゴム100重量部に対し、0.1重量部以上である
が、この理由は0.1重量部より少ないと加硫促進剤とし
ての効果がなく、本発明の目的を達成することができな
いからである。尚、配合割合の上限値は限定されない
が、15重量部以上添加しても加硫剤として一定以上の効
果が上がらないので、普通0.2〜5.0重量部が好適範囲で
ある。
8.0重量部、好ましくは0.2〜8.0重量部である。上記チ
ウラム系化合物の配合に加え上記範囲内の硫黄を併用し
た組成物を用いて加硫すると、特にゴムのスコーチ安定
性に優れ、かつ耐熱性に著しく優れたゴム材料が得られ
る。
ム配合剤および本発明におけるチウラム系化合物と硫黄
とを配合した。得られた組成物を加硫処理し、同時に比
較のため本発明におけるチウラム系化合物を添加せず、
テトラメチルチウラムジスルィドを配合したもの、有機
硫黄加硫剤としてテトラメチルチウラムジスルフィドを
用いたもの、および少量の硫黄と、促進剤を通常用いる
よりも多量に用いたものを同時に加硫処理した。
れた結果を第1表に示す。
スクレオメーターを用いた。第1表中、RMTは加硫ゴム
の架橋密度あるいはモジュラスに対応する最大トルク値
を、T2はトルク値が最小トルク値より2単位上昇するま
での時間(分)を、T90は最大トルク値の90%を得るの
に要する時間(分)を夫々示す。尚、レオメーターのT2
値の大なることはスコーチ安定性の高いことを示してい
る。
試料のブローアウト性を評価した。得られた結果を第1
表に併記する。尚、評価方法は、前述の試料について、
グッドリッチ式フレクソメーターを用い、ASTMD−623−
58の方法に準拠して行い、試料がブローアウトしたとき
のブローアウト温度を測定し、比較した。
て得られるチウラム系化合物を硫黄と併用して加硫する
ことにより、特に優れたスコーチ安定性と高い架橋密度
を同時に達成でき、工業的に極めて有用なゴム材料が得
られることが分かる。
昇し、耐熱性が向上した。
定性と耐熱性の向上が同時に得られないことが分かる。
ラム系化合物と硫黄との併用混合物を配合した。得られ
た組成物を加硫処理し、同時に比較のため本発明におけ
るチウラム系化合物を添加せず、テトラメチルチウラム
ジスルフィドと硫黄を用いたもの、通常の促進剤と硫黄
を用いたものを同時に混練り、加硫処理した。SBR合成
ゴムの例と同様に加硫中レオメーターによりその加硫性
を測定し、得られた結果を第2表に示す。
試料のブローアウト性を評価した。得られた結果を第2
表に併記する。なお、評価方法は、実施例1と同様の方
法を採用した。
得られるチウラム系化合物を硫黄と併用して加硫するこ
とにより、特に優れたスコーチ安定性と高い架橋密度を
同時に達成でき、工業的に極めて有用なゴム材料が得ら
れることが分かる。
し、耐熱性が向上した。
性と耐熱性の向上が同時に得られないことが分かる。特
に、テトラメチルチウラムジスルフィドを用いた場合に
は混練り中にゴム焼けを起こし、通常のゴム組成物は得
られなかった。
は、そのスコーチ性においてテトラメチルチウラムジス
ルフィドを用いたものよりも優れ、かつ耐熱性も向上す
る。
を併用した本発明のゴム組成物においては、スコーチ安
定性に優れ、かつ耐熱性が向上するという効果が得られ
る。
Claims (1)
- 【請求項1】原料ゴム100重量部に対し、次式、 で表されるチウラム系化合物から成る群から選択された
少なくとも1種0.1重量部以上と、硫黄0.1〜8.0重量部
とを配合したことを特徴とするゴム組成物。