JPH0555065B2 - - Google Patents
Info
- Publication number
- JPH0555065B2 JPH0555065B2 JP63092287A JP9228788A JPH0555065B2 JP H0555065 B2 JPH0555065 B2 JP H0555065B2 JP 63092287 A JP63092287 A JP 63092287A JP 9228788 A JP9228788 A JP 9228788A JP H0555065 B2 JPH0555065 B2 JP H0555065B2
- Authority
- JP
- Japan
- Prior art keywords
- image
- silver
- group
- layer
- diffusion transfer
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Lifetime
Description
(産業上の利用分野)
本発明は銀塩拡散転写法に使用する受像要素に
関するものであり、詳しくは改良された画質を有
する銀塩拡散転写法受像要素に関する。 (従来の技術) 銀塩拡散転写法の原理は、米国特許第2352014
号等に記載されている。即ち、銀塩拡散転写法に
おいては、像に対応して露光されたハロゲン化銀
乳剤層は、現像主薬およびハロゲン化銀溶剤の存
在下に受像層と接触配置するか、接触するように
もたらされ、未露光ハロゲン化銀を可溶性銀錯体
に変換させられる。ハロゲン化銀乳剤層の露光さ
れた部分においては、ハロゲン化銀は銀に現像さ
れ、従つてそれはもはや溶解できず、従つて拡散
できない。ハロゲン化銀乳剤層の未露光部分にお
いては、ハロゲン化銀は可溶性銀錯体に変換さ
れ、それが受像層へ転写され、そこでそれらが通
常は物理現像核の存在下に銀像を形成する。直接
ポジ用ハロゲン化銀乳剤では露光、未露光のハロ
ゲン化銀の作用は逆になる。 銀塩拡散転写法は広範囲な応用が可能である。
中でも版下材料の製作のための方法においては、
受像層中で高い最高濃度、高いコントラストおよ
び高鮮鋭度の銀画像を得ることが必要である。さ
らには、画像再現特性即ち原稿にできる限り忠実
な画像に再現するという特性、特に白地にポジ像
の罫線(黒線)と黒地にネガ像の罫線(白線)と
が混在する原稿のいずれの罫線も忠実に再現する
こと、あるいは連続調原稿をスクリーンを介して
焼きつけ、拡散転写現像することによつて良好な
網点画像に再現することは極めて重要なことであ
る。 又、銀塩拡散転写法においては、ハロゲン化銀
乳剤層の工夫によつては連続調の転写銀画像を得
ることができる。この場合には階調の豊かなこと
および高濃度域から低濃度域にわたつて中性灰色
の色調を得ることは重要な品質である。 通常銀塩拡散転写法において、受像要素に色調
剤を用いることはよく知られている。例えば代表
的なものとして1ーフエニル−5−メルカプトテ
トラゾール、その他フオーカルプレス社発行、フ
オトグラフイツク・シルバーハライト・デイフユ
ージヨンプロセス61頁に記載の色調剤が挙げられ
る。しかしながらこれらの色調剤は転写濃度や転
写速度の低下をもたらすという欠点を有してい
る。さらに連続調画像で低濃度域から高濃度域に
わたつて中性灰色の銀画像を得るには、周知の色
調剤の使用では殆んど不十分である。 物理現像核の種類によつても転写銀画像の色調
は変化する。一般的な物理現像核としては、銀、
金、白金、パラジウム、銅、カドミウム、鉛、コ
バルト、ニツケル等の重金属又はその硫化物、セ
レン化物を挙げることができる。これらの物理現
像核物質は、対応する金属イオンを還元して金属
コロイド分散物をつくるか、あるいは金属イオン
溶液と可溶性硫化物、セレン化物溶液を混合して
不水溶性金属硫化物、金属セレン化物のコロイド
分散物をつくることによつて得られる。また同種
の金属あるいは金属硫化物、セレン化物であつて
も、その調製のしかたで形状等の物理性の異なる
物理現像核は転写銀画像の色調に影響を与えるこ
とが知られている。 (発明の目的) 本発明の目的は良好な色調の連続調画像を与え
る受像要素を提供することにある。 本発明の別の目的は、高い最高濃度、高コント
ラスト、高鮮鋭度で色調の良い銀画像を与える受
像要素を提供することにある。 又、本発明の別の目的は、改良された画像再現
特性の良好な銀画像を与える受像要素を提供する
ことにある。 (問題点を解決するための手段) 上記の諸目的は、蛍光染料を含有する親水性コ
ロイド溶液中で調製された物理現像核物質を含有
することを特徴とする受像要素によつて達成され
た。 本発明者は、物理現像核の調製法による色調お
よび画質の改良について鋭意研究した結果、物理
現像核調製時に蛍光染料が存在していた場合に良
好な結果が得られることを見出した。 従来より、受像層中に蛍光染料を含有させ得る
ことは公知である。ただし蛍光染料は通常蛍光増
白の目的でのみ使用される。本発明は、転写画像
の画質の改良に使用するものであり、かかる核液
の蛍光染料のみでは、受像層の増白の目的に対し
て一般的には可成りの量不足である。 本発明の物理現像核調製に用いられる親水性コ
ロイド溶液は、親水性コロイド物質の固型分量が
0.5〜20重量%の溶液である。親水性コロイド物
質の最も好ましい例は、ポリーN−ビニルピロリ
ドンまたはアクリルアミド−ビニルイミダゾール
共重合体および、これらを併用したものである
が、他に通常使用される親水性コロイド物質、例
えばゼラチン、カルボキシメチルセルロース、ヒ
ドロキシエチルセルロース、ポリビニルアルコー
ル、ポリアクリルアミド等を単独または併用して
用いることができる。 蛍光染料としては、通常使用されるものおよび
蛍光増白の目的で使用し得る物質、例えば、ビス
(トリアジニルアミノスチルベン)ジスルホン酸
誘導体、オキサゾール誘導体、トリアゾール誘導
体、ビフエニル誘導体、イミダゾール誘導体、ク
マリン誘導体、ピラゾリン誘導体、ナフタルイミ
ド誘導体等の水溶性のものが用いられる。好まし
くは下記一般式(I)〜()で表わされる化合
物である。 一般式() 〔式中、A1およびA2は、それぞれ水素原子、
低級アルキル基、ヒドロキシ基、カルボキシル基
もしくはその塩を表わし、B1およびB2はそれぞ
れ、水素原子、 (B3およびB4は、それぞれ水素原子、ヒドロ
キシル基、またはそれぞれ置換もしくは未置換の
低級アルコキシ基、アリールオキシ基、複素環
基、低級アルキルチオ基、アリールチオ基、チオ
複素環基、アミノ基を表わす。) −NHCOB5基(B5は、それぞれ置換もしくは未
置換の低級アルコキシ基、アリール基、アリール
オキシ基、複素環基、低級アルキルチオ基、チオ
複素環基またはアミノ基を表わす。)
関するものであり、詳しくは改良された画質を有
する銀塩拡散転写法受像要素に関する。 (従来の技術) 銀塩拡散転写法の原理は、米国特許第2352014
号等に記載されている。即ち、銀塩拡散転写法に
おいては、像に対応して露光されたハロゲン化銀
乳剤層は、現像主薬およびハロゲン化銀溶剤の存
在下に受像層と接触配置するか、接触するように
もたらされ、未露光ハロゲン化銀を可溶性銀錯体
に変換させられる。ハロゲン化銀乳剤層の露光さ
れた部分においては、ハロゲン化銀は銀に現像さ
れ、従つてそれはもはや溶解できず、従つて拡散
できない。ハロゲン化銀乳剤層の未露光部分にお
いては、ハロゲン化銀は可溶性銀錯体に変換さ
れ、それが受像層へ転写され、そこでそれらが通
常は物理現像核の存在下に銀像を形成する。直接
ポジ用ハロゲン化銀乳剤では露光、未露光のハロ
ゲン化銀の作用は逆になる。 銀塩拡散転写法は広範囲な応用が可能である。
中でも版下材料の製作のための方法においては、
受像層中で高い最高濃度、高いコントラストおよ
び高鮮鋭度の銀画像を得ることが必要である。さ
らには、画像再現特性即ち原稿にできる限り忠実
な画像に再現するという特性、特に白地にポジ像
の罫線(黒線)と黒地にネガ像の罫線(白線)と
が混在する原稿のいずれの罫線も忠実に再現する
こと、あるいは連続調原稿をスクリーンを介して
焼きつけ、拡散転写現像することによつて良好な
網点画像に再現することは極めて重要なことであ
る。 又、銀塩拡散転写法においては、ハロゲン化銀
乳剤層の工夫によつては連続調の転写銀画像を得
ることができる。この場合には階調の豊かなこと
および高濃度域から低濃度域にわたつて中性灰色
の色調を得ることは重要な品質である。 通常銀塩拡散転写法において、受像要素に色調
剤を用いることはよく知られている。例えば代表
的なものとして1ーフエニル−5−メルカプトテ
トラゾール、その他フオーカルプレス社発行、フ
オトグラフイツク・シルバーハライト・デイフユ
ージヨンプロセス61頁に記載の色調剤が挙げられ
る。しかしながらこれらの色調剤は転写濃度や転
写速度の低下をもたらすという欠点を有してい
る。さらに連続調画像で低濃度域から高濃度域に
わたつて中性灰色の銀画像を得るには、周知の色
調剤の使用では殆んど不十分である。 物理現像核の種類によつても転写銀画像の色調
は変化する。一般的な物理現像核としては、銀、
金、白金、パラジウム、銅、カドミウム、鉛、コ
バルト、ニツケル等の重金属又はその硫化物、セ
レン化物を挙げることができる。これらの物理現
像核物質は、対応する金属イオンを還元して金属
コロイド分散物をつくるか、あるいは金属イオン
溶液と可溶性硫化物、セレン化物溶液を混合して
不水溶性金属硫化物、金属セレン化物のコロイド
分散物をつくることによつて得られる。また同種
の金属あるいは金属硫化物、セレン化物であつて
も、その調製のしかたで形状等の物理性の異なる
物理現像核は転写銀画像の色調に影響を与えるこ
とが知られている。 (発明の目的) 本発明の目的は良好な色調の連続調画像を与え
る受像要素を提供することにある。 本発明の別の目的は、高い最高濃度、高コント
ラスト、高鮮鋭度で色調の良い銀画像を与える受
像要素を提供することにある。 又、本発明の別の目的は、改良された画像再現
特性の良好な銀画像を与える受像要素を提供する
ことにある。 (問題点を解決するための手段) 上記の諸目的は、蛍光染料を含有する親水性コ
ロイド溶液中で調製された物理現像核物質を含有
することを特徴とする受像要素によつて達成され
た。 本発明者は、物理現像核の調製法による色調お
よび画質の改良について鋭意研究した結果、物理
現像核調製時に蛍光染料が存在していた場合に良
好な結果が得られることを見出した。 従来より、受像層中に蛍光染料を含有させ得る
ことは公知である。ただし蛍光染料は通常蛍光増
白の目的でのみ使用される。本発明は、転写画像
の画質の改良に使用するものであり、かかる核液
の蛍光染料のみでは、受像層の増白の目的に対し
て一般的には可成りの量不足である。 本発明の物理現像核調製に用いられる親水性コ
ロイド溶液は、親水性コロイド物質の固型分量が
0.5〜20重量%の溶液である。親水性コロイド物
質の最も好ましい例は、ポリーN−ビニルピロリ
ドンまたはアクリルアミド−ビニルイミダゾール
共重合体および、これらを併用したものである
が、他に通常使用される親水性コロイド物質、例
えばゼラチン、カルボキシメチルセルロース、ヒ
ドロキシエチルセルロース、ポリビニルアルコー
ル、ポリアクリルアミド等を単独または併用して
用いることができる。 蛍光染料としては、通常使用されるものおよび
蛍光増白の目的で使用し得る物質、例えば、ビス
(トリアジニルアミノスチルベン)ジスルホン酸
誘導体、オキサゾール誘導体、トリアゾール誘導
体、ビフエニル誘導体、イミダゾール誘導体、ク
マリン誘導体、ピラゾリン誘導体、ナフタルイミ
ド誘導体等の水溶性のものが用いられる。好まし
くは下記一般式(I)〜()で表わされる化合
物である。 一般式() 〔式中、A1およびA2は、それぞれ水素原子、
低級アルキル基、ヒドロキシ基、カルボキシル基
もしくはその塩を表わし、B1およびB2はそれぞ
れ、水素原子、 (B3およびB4は、それぞれ水素原子、ヒドロ
キシル基、またはそれぞれ置換もしくは未置換の
低級アルコキシ基、アリールオキシ基、複素環
基、低級アルキルチオ基、アリールチオ基、チオ
複素環基、アミノ基を表わす。) −NHCOB5基(B5は、それぞれ置換もしくは未
置換の低級アルコキシ基、アリール基、アリール
オキシ基、複素環基、低級アルキルチオ基、チオ
複素環基またはアミノ基を表わす。)
【式】基または
【式】基
(Y1およびY2は、それぞれ置換または未置換
の芳香族環を形成するに必要な非金属原子群を表
わし、B6は水素原子または置換もしくは未置換
の低級アルキル基を表わす。)を表わす。〕 一般式() 〔式中、C1およびC2は、それぞれ水素原子、
低級アルキル基、低級アルコキシ基、ハロゲン原
子、スルホニル基もしくはその塩、またはカルボ
キシル基もしくはその塩を表わし、D1およびD2
は、それぞれ置換もしくは未置換のジフエニル
基、α−ナフチル基、β−ナフチル基または、
の芳香族環を形成するに必要な非金属原子群を表
わし、B6は水素原子または置換もしくは未置換
の低級アルキル基を表わす。)を表わす。〕 一般式() 〔式中、C1およびC2は、それぞれ水素原子、
低級アルキル基、低級アルコキシ基、ハロゲン原
子、スルホニル基もしくはその塩、またはカルボ
キシル基もしくはその塩を表わし、D1およびD2
は、それぞれ置換もしくは未置換のジフエニル
基、α−ナフチル基、β−ナフチル基または、
【式】基(D3は、水素原子、スルホニル
基もしくはその塩、またはカルボキシル基もしく
はその塩、D4は水素原子、ハロゲン原子、低級
アルキル基、または低級アルコキシ基、D5は水
素原子または低級アルキル基を表わす。)を表わ
す。〕 一般式() (式中、E1,E2,E3およびE4は、それぞれ水
素原子、ハロゲン原子、ヒドロキシル基、カルボ
キシル基もしくはその塩、スルホニル基もしくは
その塩、または、それぞれ置換もしくは未置換の
低級アルキル基、低級アルコキシ基を表わし、Z1
およびZ2はそれぞれ置換もしくは未置換の芳香族
環を形成するに必要な非金属原子群を表わす。) 代表的な化合物例を示す。 物理現像核調製時に使用される蛍光染料の量
は、その時に使用される親水性コロイド物質の固
型分量の5重量%以上であれば任意であるが50〜
200重量%が好適である。 物理現像核物質としては、銀、金、白金、パラ
ジウム、銅、カドミウム、鉛、コバルト、ニツケ
ル等の貴金属又はその硫化物、セレン化物等を1
種又は2種以上組合せて用いることができるが、
好ましくは硫化ニツケルまたは硫化コバルトと硫
化銀からなる核である。 物理現像核の濃度は、調製液1当り約1×
10-5モル〜約1×10-1モルの範囲である。 物理現像核の調製は、30℃〜100℃、好ましく
は50℃〜70℃の温度で所望の時間反応させて製造
するのがよい。 調製された物理現像核液は、約1×10-7〜約1
×10-3モル/m2の核量になるように受像層形成用
塗布液に混合される。 受像層のバインダーとしては、ゼラチン、フタ
ル化ゼラチン、アシル化ゼラチン、フエニルカル
バミル化ゼラチン、カルボキシメチルセルロー
ス、ヒドロキシエチルセルロース、アルギン酸ソ
ーダ、ポリビニルアルコール、部分ケン化された
ポリビニルアルコール、ポリビニルアルコールと
無水マレイン酸共重合物、例えば、スチレン−無
水マレイン酸、エチレン無水マレイン酸等との加
熱加工物、ポリアクリルアミド、ポリ−N−ビニ
ルピロリドン、ラテツクス類(例えば、ポリアク
リル酸エステル、ポリメタアクリル酸エステル、
ポリスチレン、ポリブタジエン等の単独または共
重合物)等の水溶性高分子化合物を単独または併
用して用いることができる。 受像層は適当な硬膜剤で硬膜することができ硬
膜剤の具体的な例としては、ホルムアルデヒド、
グルタールアルデヒドの如きアルデヒド系化合
物、ジアセチル、シクロペンタンジオンの如きケ
トン化合物、ビス(2−クロロエチル尿素)−2
−ヒドロキシ−4,6−ジクロロ−1,3,5ト
リアジン、米国特許第3288775号記載の如き反応
性のハロゲンを有する化合物、ジビニルスルホ
ン、米国特許第3635718号記載の如き反応性のオ
レフインをもつ化合物、米国特許第2732316号記
載の如きN−メチロール化合物、米国特許第
3103437号記載の如きイソシアナート類、米国特
許第3017280号、同第2983611号記載の如きアジリ
ジン化合物類、米国特許第3100704号記載の如き
カルボジイミド系化合物類、米国特許第3091537
号記載の如きエポキシ化合物、ムコクロル酸の如
きハロゲノカルボキシアルデヒド類、ジヒドロキ
シジオキサンの如きジオキサン誘導体、クロム明
ばん、カリ明ばん、硫酸ジルコニウムの如き無機
硬膜剤などがあり、これらを一種または二種以上
組合せて用いることができる。 受像層は界面活性剤(例えば、サポニン等の天
然界面活性剤、アルキレンオキサイド系、グリセ
リン系、グリシドール系等のノニオン界面活性
剤、高級アルキルアミン類、第四級アンモニウム
塩類、ピリジンその他の複素環類、スルホニウム
類等のカチオン界面活性剤、カルボン酸、スルホ
ン酸、燐酸、硫酸エステル基、燐酸エステル基等
の酸性基を含むアニオン界面活性剤、アミノ酸
類、アミノスルホン酸類、アミノアルコールの硫
酸または燐酸エステル類等の両性界面活性剤、フ
ツ素を含むフツ素系アニオンおよび両性界面活性
剤等)、マツト剤、核調製用以外に増白のための
蛍光染料、変色防止剤、色調剤(例えば代表的な
ものとして1−フエニル−5−メルカプトテトラ
ゾール、その他フオーカルプレス社発行、フオト
グラフイツク・シルバーハライド・デイフユージ
ヨン・プロセス61頁に記載の色調剤)、現像主薬
(例えば、ハイドロキノンおよびその誘導体、1
−フエニル−3−ピラゾリドンおよびその誘導体
等)、ハロゲン化銀の溶剤(例えばチオ硫酸ナト
リウム、チオ硫酸アンモニウム、チオシアン酸ナ
トリウム、チオシアン酸カリウム等)等を含むこ
とができる。更に受像層の上にオーバー層、下に
中和層、支持体との接着をよくする下引層が設け
られても良い。 本発明に係る銀塩拡散転写用の感光材料の感光
層に用いられるハロゲン化銀乳剤は、拡散転写に
普通に使用されている乳剤で、その銀塩が拡散転
写法に必要な速度で、露光部および非露光部中で
それぞれ現像および拡散する能力を有するもので
あればよく、臭化銀、沃化銀、塩化銀、塩臭化
銀、沃臭化銀、塩沃化銀、塩沃臭化銀およびそれ
らの混合物を挙げることができる。既述したよう
に本発明は連続調画像を形成するための受像要素
として好適であるが、連続調用の感光材料に制限
されるものではない。 ハロゲン化銀乳剤は、それが製造されるときま
たは塗布されるときに種々の方法で増感されるこ
とができる。例えばチオ硫酸ナトリウム、アルキ
ルチオ尿素によつて、または金化合物、例えばロ
ダン金、塩化金によつて、またはこれらの両者の
併用など当該技術分野においてよく知られた方法
で化学的に増感されていてもよい。また通常行な
われている分増感を行うことができる。 感光層のバインダーは通常ハロゲン化銀乳剤の
製造に用いられている高分子物質、例えば受像層
の記載のバインダーを用いることができる。また
感光層は受像層で記載の適当な硬膜剤によつて硬
膜することができる。更に感光層は、一般にハロ
ゲン化銀感光材料に用いられている添加物、例え
ば界面活性剤、カブリ防止剤、マツト剤、蛍光染
料、現像主薬(例えばハイドロキノンおよびその
誘導体、1−フエニル−3−ピラゾリドンおよび
その誘導体等)を用いられる。更に感光層以外に
必要により下塗層、中間層、保護層、剥離層等の
補助層が設けられてもよい。 本発明に係る銀塩拡散転写用感光材料および受
像材料の支持体は、通常使用される任意の支持体
である。それには、紙、ガラス、フイルム、例え
ばセルロースアセテートフイルム、ポリビニルア
セタールフイルム、ポリスチレンフイルム、ポリ
エチレンフタレートフイルム等、紙で両側を被覆
した金属支持体、片側または両側をα−オレフイ
ン重合体、例えばポリエチレンで被覆した紙支持
体も使用できる。 一般に銀塩拡散転写方式は、感光材料と受像材
料を同一の支持体上に形成されたいわゆる「モノ
シート方式」と、感光材料と受像材料を別々の支
持体に形成し、使用に際してはこの二つの材料を
重ね合わせてローラーで圧着して拡散転写せしめ
た後剥離する方式、いわゆる「2枚もの」方式が
あるが、本発明はこれらのどちらの方式にも適用
される。 本発明における銀塩拡散転写用処理液は、通常
の銀塩拡散転写処理液組成であることができる。
すなわち、露光されたハロゲン化銀を現像するた
めの現像主薬、例えばハイドロキノンおよびその
誘導体、1−フエニル−3−ピラゾリドンおよび
その誘導体等、未現像のハロゲン化銀の溶剤、例
えばチオ硫酸ナトリウム、チオ硫酸アンモニウ
ム、チオシアン酸ナトリウム、チオシアン酸カリ
等、保恒剤として亜硫酸ソーダ、現像抑制剤とし
て臭化カリ、色調剤として1−フエニル−5−メ
ルカプトテトラゾール等の添加剤類、アルカリ性
物質例えば水酸化ナトリウム、水酸化カリウム、
水酸化リチウム、第三燐酸ナトリウム等、粘稠
剤、例えば、カルボキシメチルセルロース、ヒド
ロキシエチルセルロース等を含んでいることがで
きる。 以下に本発明を実施例により説明するが、本発
明を何ら限定するものではない。 実施例 1 ポリ−N−ビニルピロリドンの3%水溶液30ml
中で硝酸ニツケルの0.05mol/水溶液7mlと硫
化ナトリウムの0.05mol/水溶液10mlとを激し
く撹拌しながら混合し、60℃で1分間反応させた
後、硝酸銀の0.1mol/水溶液3mlを加えて3
分間反応させて比較の物理現像核を調製した。同
様に但し、ポリ−N−ビニルピロリドン水溶液中
に1gの蛍光染料(ケイコールPK、新日曹化工
株式会社製)を添加し本発明の物理現像核を調製
した。いずれも適当な濃度のゼラチン水溶液に加
え、予めコロナ放電処理したポリエチレンで両側
を被覆した90g/m2の紙支持体の片側に1×10-5
mol/m2の金属硫化物を含むゼラチン受像層を親
水性コロイドの乾燥重量2g/m2になるようにし
て比較および本発明の受像材料をそれぞれ作製し
た。 感光材料は受像材料と同じ紙支持体上に、ハレ
ーシヨン防止用としてのカーボンブラツクおよび
1g/m2のカテコールと0.3g/m2の1−フエニ
ル−4−メチル−3−ピラゾリドンを含むゼラチ
ン下塗層(ゼラチン3g/m2)を設け、その上に
塩沃臭化銀(臭化銀8モル%、沃化銀1モル%)
を硝酸銀に換算して1.8g/m2を含むオルソ増感
され、さらに0.15g/m2のカテコール等を含むゼ
ラチンハロゲン化銀乳剤層(硝酸銀:ゼラチン=
1:4)および保護層(ゼラチン1.3g/m2)を
設けて作製した。 センシトメトリー用露光を施した感光材料の乳
剤面と受像材料の受像面とを重ね合わせて下記の
現像処理液1を含む通常のプロセツサーを通
し、スキージ・ローラーを出て30秒後に両材料を
剥した。処理液温度は20℃である。 <拡散転写現像液> 水 800ml 無水亜硫酸ナトリウム 50g 水酸化ナトリウム 4g チオ硫酸ナトリウム(5水塩) 20g N−メチルアミノエタノール 15g ハイドロキノン 11g 1−フエニル−3−ピラゾリドン 1g 1−フエニル−5−メルカプトテトラゾール
50mg 臭化カリウム 1g 水を加えて 1 比較の受像材料には連続調原画を再生するに十
分な階調の銀画像が形成されたが、最高濃度が不
十分(反射濃度=1.0)であり、また低濃度部に
ついてはその色調が茶色味を帯びていた。本発明
の受像材料には比較試料と同様の階調をもつ銀画
像が形成され、最高濃度も十分(反射濃度=1.8)
であり、かつその像は中性灰色の良好な色調であ
つた。 実施例 2 実施例1を繰返した。但し感光材料を実施例1
と同じ紙支持体上にハレーシヨン防止用としてカ
ーボンブラツクを含有する下塗層を設けその上に
0.3μの平均粒径のオルソ増感された塩臭化銀(臭
化銀5モル%)を硝酸銀に換算して1.5g/m2の
1−フエニル−3−ピラゾリドンと0.7g/m2の
ハイドロキノン、4g/m2のゼラチンを含むゼラ
チンハロゲン化銀乳剤層を設けて作製した。 比較の受像材料は最高濃度が不十分(反射濃度
=1.1)で、コントラストの低い画像であつたが、
本発明の受像材料は高い最高濃度(反射濃度=
1.6)と高いコントラストの画像であつた。 実施例 3 実施例1を繰返した。但し物理現像核調製に際
し、ポリ−N−ビニルピロリドン3%水溶液30ml
のかわりにポリ−N−ビニルピロリドン3%水溶
液15mlとアクリルアミド−ビニルイミダゾール共
重合体3%水溶液15mlの混合溶液を使用した。 実施例1同様、本発明の受像材料のみが良好な
連続階調と、さえた中性灰色の銀画像であつた。 実施例 4 実施例2を繰返した、但し実施例3と同様の受
像材料を使用した。 本発明の受像材料のみが高濃度、高コントラス
トでより優れた画像再現特性を示すものであつ
た。
はその塩、D4は水素原子、ハロゲン原子、低級
アルキル基、または低級アルコキシ基、D5は水
素原子または低級アルキル基を表わす。)を表わ
す。〕 一般式() (式中、E1,E2,E3およびE4は、それぞれ水
素原子、ハロゲン原子、ヒドロキシル基、カルボ
キシル基もしくはその塩、スルホニル基もしくは
その塩、または、それぞれ置換もしくは未置換の
低級アルキル基、低級アルコキシ基を表わし、Z1
およびZ2はそれぞれ置換もしくは未置換の芳香族
環を形成するに必要な非金属原子群を表わす。) 代表的な化合物例を示す。 物理現像核調製時に使用される蛍光染料の量
は、その時に使用される親水性コロイド物質の固
型分量の5重量%以上であれば任意であるが50〜
200重量%が好適である。 物理現像核物質としては、銀、金、白金、パラ
ジウム、銅、カドミウム、鉛、コバルト、ニツケ
ル等の貴金属又はその硫化物、セレン化物等を1
種又は2種以上組合せて用いることができるが、
好ましくは硫化ニツケルまたは硫化コバルトと硫
化銀からなる核である。 物理現像核の濃度は、調製液1当り約1×
10-5モル〜約1×10-1モルの範囲である。 物理現像核の調製は、30℃〜100℃、好ましく
は50℃〜70℃の温度で所望の時間反応させて製造
するのがよい。 調製された物理現像核液は、約1×10-7〜約1
×10-3モル/m2の核量になるように受像層形成用
塗布液に混合される。 受像層のバインダーとしては、ゼラチン、フタ
ル化ゼラチン、アシル化ゼラチン、フエニルカル
バミル化ゼラチン、カルボキシメチルセルロー
ス、ヒドロキシエチルセルロース、アルギン酸ソ
ーダ、ポリビニルアルコール、部分ケン化された
ポリビニルアルコール、ポリビニルアルコールと
無水マレイン酸共重合物、例えば、スチレン−無
水マレイン酸、エチレン無水マレイン酸等との加
熱加工物、ポリアクリルアミド、ポリ−N−ビニ
ルピロリドン、ラテツクス類(例えば、ポリアク
リル酸エステル、ポリメタアクリル酸エステル、
ポリスチレン、ポリブタジエン等の単独または共
重合物)等の水溶性高分子化合物を単独または併
用して用いることができる。 受像層は適当な硬膜剤で硬膜することができ硬
膜剤の具体的な例としては、ホルムアルデヒド、
グルタールアルデヒドの如きアルデヒド系化合
物、ジアセチル、シクロペンタンジオンの如きケ
トン化合物、ビス(2−クロロエチル尿素)−2
−ヒドロキシ−4,6−ジクロロ−1,3,5ト
リアジン、米国特許第3288775号記載の如き反応
性のハロゲンを有する化合物、ジビニルスルホ
ン、米国特許第3635718号記載の如き反応性のオ
レフインをもつ化合物、米国特許第2732316号記
載の如きN−メチロール化合物、米国特許第
3103437号記載の如きイソシアナート類、米国特
許第3017280号、同第2983611号記載の如きアジリ
ジン化合物類、米国特許第3100704号記載の如き
カルボジイミド系化合物類、米国特許第3091537
号記載の如きエポキシ化合物、ムコクロル酸の如
きハロゲノカルボキシアルデヒド類、ジヒドロキ
シジオキサンの如きジオキサン誘導体、クロム明
ばん、カリ明ばん、硫酸ジルコニウムの如き無機
硬膜剤などがあり、これらを一種または二種以上
組合せて用いることができる。 受像層は界面活性剤(例えば、サポニン等の天
然界面活性剤、アルキレンオキサイド系、グリセ
リン系、グリシドール系等のノニオン界面活性
剤、高級アルキルアミン類、第四級アンモニウム
塩類、ピリジンその他の複素環類、スルホニウム
類等のカチオン界面活性剤、カルボン酸、スルホ
ン酸、燐酸、硫酸エステル基、燐酸エステル基等
の酸性基を含むアニオン界面活性剤、アミノ酸
類、アミノスルホン酸類、アミノアルコールの硫
酸または燐酸エステル類等の両性界面活性剤、フ
ツ素を含むフツ素系アニオンおよび両性界面活性
剤等)、マツト剤、核調製用以外に増白のための
蛍光染料、変色防止剤、色調剤(例えば代表的な
ものとして1−フエニル−5−メルカプトテトラ
ゾール、その他フオーカルプレス社発行、フオト
グラフイツク・シルバーハライド・デイフユージ
ヨン・プロセス61頁に記載の色調剤)、現像主薬
(例えば、ハイドロキノンおよびその誘導体、1
−フエニル−3−ピラゾリドンおよびその誘導体
等)、ハロゲン化銀の溶剤(例えばチオ硫酸ナト
リウム、チオ硫酸アンモニウム、チオシアン酸ナ
トリウム、チオシアン酸カリウム等)等を含むこ
とができる。更に受像層の上にオーバー層、下に
中和層、支持体との接着をよくする下引層が設け
られても良い。 本発明に係る銀塩拡散転写用の感光材料の感光
層に用いられるハロゲン化銀乳剤は、拡散転写に
普通に使用されている乳剤で、その銀塩が拡散転
写法に必要な速度で、露光部および非露光部中で
それぞれ現像および拡散する能力を有するもので
あればよく、臭化銀、沃化銀、塩化銀、塩臭化
銀、沃臭化銀、塩沃化銀、塩沃臭化銀およびそれ
らの混合物を挙げることができる。既述したよう
に本発明は連続調画像を形成するための受像要素
として好適であるが、連続調用の感光材料に制限
されるものではない。 ハロゲン化銀乳剤は、それが製造されるときま
たは塗布されるときに種々の方法で増感されるこ
とができる。例えばチオ硫酸ナトリウム、アルキ
ルチオ尿素によつて、または金化合物、例えばロ
ダン金、塩化金によつて、またはこれらの両者の
併用など当該技術分野においてよく知られた方法
で化学的に増感されていてもよい。また通常行な
われている分増感を行うことができる。 感光層のバインダーは通常ハロゲン化銀乳剤の
製造に用いられている高分子物質、例えば受像層
の記載のバインダーを用いることができる。また
感光層は受像層で記載の適当な硬膜剤によつて硬
膜することができる。更に感光層は、一般にハロ
ゲン化銀感光材料に用いられている添加物、例え
ば界面活性剤、カブリ防止剤、マツト剤、蛍光染
料、現像主薬(例えばハイドロキノンおよびその
誘導体、1−フエニル−3−ピラゾリドンおよび
その誘導体等)を用いられる。更に感光層以外に
必要により下塗層、中間層、保護層、剥離層等の
補助層が設けられてもよい。 本発明に係る銀塩拡散転写用感光材料および受
像材料の支持体は、通常使用される任意の支持体
である。それには、紙、ガラス、フイルム、例え
ばセルロースアセテートフイルム、ポリビニルア
セタールフイルム、ポリスチレンフイルム、ポリ
エチレンフタレートフイルム等、紙で両側を被覆
した金属支持体、片側または両側をα−オレフイ
ン重合体、例えばポリエチレンで被覆した紙支持
体も使用できる。 一般に銀塩拡散転写方式は、感光材料と受像材
料を同一の支持体上に形成されたいわゆる「モノ
シート方式」と、感光材料と受像材料を別々の支
持体に形成し、使用に際してはこの二つの材料を
重ね合わせてローラーで圧着して拡散転写せしめ
た後剥離する方式、いわゆる「2枚もの」方式が
あるが、本発明はこれらのどちらの方式にも適用
される。 本発明における銀塩拡散転写用処理液は、通常
の銀塩拡散転写処理液組成であることができる。
すなわち、露光されたハロゲン化銀を現像するた
めの現像主薬、例えばハイドロキノンおよびその
誘導体、1−フエニル−3−ピラゾリドンおよび
その誘導体等、未現像のハロゲン化銀の溶剤、例
えばチオ硫酸ナトリウム、チオ硫酸アンモニウ
ム、チオシアン酸ナトリウム、チオシアン酸カリ
等、保恒剤として亜硫酸ソーダ、現像抑制剤とし
て臭化カリ、色調剤として1−フエニル−5−メ
ルカプトテトラゾール等の添加剤類、アルカリ性
物質例えば水酸化ナトリウム、水酸化カリウム、
水酸化リチウム、第三燐酸ナトリウム等、粘稠
剤、例えば、カルボキシメチルセルロース、ヒド
ロキシエチルセルロース等を含んでいることがで
きる。 以下に本発明を実施例により説明するが、本発
明を何ら限定するものではない。 実施例 1 ポリ−N−ビニルピロリドンの3%水溶液30ml
中で硝酸ニツケルの0.05mol/水溶液7mlと硫
化ナトリウムの0.05mol/水溶液10mlとを激し
く撹拌しながら混合し、60℃で1分間反応させた
後、硝酸銀の0.1mol/水溶液3mlを加えて3
分間反応させて比較の物理現像核を調製した。同
様に但し、ポリ−N−ビニルピロリドン水溶液中
に1gの蛍光染料(ケイコールPK、新日曹化工
株式会社製)を添加し本発明の物理現像核を調製
した。いずれも適当な濃度のゼラチン水溶液に加
え、予めコロナ放電処理したポリエチレンで両側
を被覆した90g/m2の紙支持体の片側に1×10-5
mol/m2の金属硫化物を含むゼラチン受像層を親
水性コロイドの乾燥重量2g/m2になるようにし
て比較および本発明の受像材料をそれぞれ作製し
た。 感光材料は受像材料と同じ紙支持体上に、ハレ
ーシヨン防止用としてのカーボンブラツクおよび
1g/m2のカテコールと0.3g/m2の1−フエニ
ル−4−メチル−3−ピラゾリドンを含むゼラチ
ン下塗層(ゼラチン3g/m2)を設け、その上に
塩沃臭化銀(臭化銀8モル%、沃化銀1モル%)
を硝酸銀に換算して1.8g/m2を含むオルソ増感
され、さらに0.15g/m2のカテコール等を含むゼ
ラチンハロゲン化銀乳剤層(硝酸銀:ゼラチン=
1:4)および保護層(ゼラチン1.3g/m2)を
設けて作製した。 センシトメトリー用露光を施した感光材料の乳
剤面と受像材料の受像面とを重ね合わせて下記の
現像処理液1を含む通常のプロセツサーを通
し、スキージ・ローラーを出て30秒後に両材料を
剥した。処理液温度は20℃である。 <拡散転写現像液> 水 800ml 無水亜硫酸ナトリウム 50g 水酸化ナトリウム 4g チオ硫酸ナトリウム(5水塩) 20g N−メチルアミノエタノール 15g ハイドロキノン 11g 1−フエニル−3−ピラゾリドン 1g 1−フエニル−5−メルカプトテトラゾール
50mg 臭化カリウム 1g 水を加えて 1 比較の受像材料には連続調原画を再生するに十
分な階調の銀画像が形成されたが、最高濃度が不
十分(反射濃度=1.0)であり、また低濃度部に
ついてはその色調が茶色味を帯びていた。本発明
の受像材料には比較試料と同様の階調をもつ銀画
像が形成され、最高濃度も十分(反射濃度=1.8)
であり、かつその像は中性灰色の良好な色調であ
つた。 実施例 2 実施例1を繰返した。但し感光材料を実施例1
と同じ紙支持体上にハレーシヨン防止用としてカ
ーボンブラツクを含有する下塗層を設けその上に
0.3μの平均粒径のオルソ増感された塩臭化銀(臭
化銀5モル%)を硝酸銀に換算して1.5g/m2の
1−フエニル−3−ピラゾリドンと0.7g/m2の
ハイドロキノン、4g/m2のゼラチンを含むゼラ
チンハロゲン化銀乳剤層を設けて作製した。 比較の受像材料は最高濃度が不十分(反射濃度
=1.1)で、コントラストの低い画像であつたが、
本発明の受像材料は高い最高濃度(反射濃度=
1.6)と高いコントラストの画像であつた。 実施例 3 実施例1を繰返した。但し物理現像核調製に際
し、ポリ−N−ビニルピロリドン3%水溶液30ml
のかわりにポリ−N−ビニルピロリドン3%水溶
液15mlとアクリルアミド−ビニルイミダゾール共
重合体3%水溶液15mlの混合溶液を使用した。 実施例1同様、本発明の受像材料のみが良好な
連続階調と、さえた中性灰色の銀画像であつた。 実施例 4 実施例2を繰返した、但し実施例3と同様の受
像材料を使用した。 本発明の受像材料のみが高濃度、高コントラス
トでより優れた画像再現特性を示すものであつ
た。
Claims (1)
- 1 銀塩拡散転写法受像要素に於て、蛍光染料を
含有する親水性コロイド溶液中で調製された物理
現像核物質を含有することを特徴とする受像要
素。